Hydrothermal stability and catalytic activity of aluminum-containing mesoporous ethane-silicas

Aluminum was incorporated into the mesoporous framework of ethane-silica by one-pot condensation of Al(OiPr)(3) with 1,2-bis(trimethoxysilyl)ethane using octadecyltrimethylammonium chloride as surfactant. Powder X-ray diffraction patterns, nitrogen sorption analysis, and TEM results reveal the formation of an ordered mesoporous material with uniform porosity. Al-27 MAS NMR confirms the incorporation of aluminum in the framework. The synthesized materials exhibit extremely high hydrothermal stability in boiling water (no obvious change of mesostructure and textural properties was observed even after refluxing in water for 100 h), which could be mainly contributed to the ethane-bridged mesoporous framework. The aluminum-containing mesoporous ethane-silicas are efficient catalysts for the alkylation of 2,4-di-tert-butylphenol by cinnamyl alcohol to yield a flavan.

Preparation of palladium membrane over porous stainless steel tube modified with zirconium oxide

A palladium membrane has been prepared by electroless plating on the surface of a porous stainless steel tube. Since the large surface pores of the tube are obstacle for preparation of a defect-free palladium film on the surface, zirconium oxide particles were deposited inside the pores. The mean thickness of the resulting Pd membrane on the modified tube was ca. 10 mum. It is suggested that the permeability of hydrogen is partly governed by gas diffusion in the pores. (C) 2004 Elsevier B.V. All rights reserved.

Novel catalysis of TiO2 for the catalytic alcohols synthesis from CO and H2O

Direct synthesis of alcohols from CO and H2O was investigated using TiO2 catalyst. MeOH (about 24 mg g(-1) h(-1)) and EtOH (about 8 mg g(-1) h(-1)) could be produced under the reaction conditions of T= 573 K, P= 0.5 MPa, CO flow rate of 30 ml min(-1) and CO/H2O = 3/2 during the period of 12 to 44 h time-on-stream. Compared with PbO, TiO2 could preserve stable catalytic activity during a long time of reaction. For the same catalyst TiO2, the reaction performance of alkali carbonates increased with their solubility (K2CO3>Na2CO3>Li2CO3). The corresponding catalytic activity was found to increase with the alkalescence of solvent. The formation mechanism of alcohols was proposed as well. (C) 2004 Elsevier B.V. All rights reserved.

Catalytic alcohols synthesis from CO and H2O on TiO2 catalysts calcined at various temperatures

The reaction performance for CO hydration on a TiO2 catalyst under different calcination temperatures was investigated. Under reaction conditions of T = 573 K, P = 0.5 MPa, CO flow rate of 30 ml min(-1), TOS = 12 h, and CO/H2O (g) = 3/2 (mol), the TiO2 catalyst with a futile content of 18% shows a maximum alcohols STY of 1.81 Mg m(-2) h(-1). In addition, the catalyst deactivation and regeneration were discussed.

Degradation mechanism of polystyrene sulfonic acid membrane and application of its composite membranes in fuel cells

The lifetime behavior of a H-2/O-2 proton exchange membrane (PEM) fuel cell with polystyrene sulfonic acid (PSSA) membrane have been investigated in order to give an insight into the degradation mechanism of the PSSA membrane. The distribution of sulfur concentration in the cross section of the PSSA membrane was measured by energy dispersive analysis of X-ray, and the chemical composition of the PSSA membrane was characterized by infrared spectroscopy before and after the lifetime experiment. The degradation mechanism of the PSSA membrane is postulated as: the oxygen reduction at the cathode proceeds through some peroxide intermediates during the fuel cell operation, and these intermediates have strong oxidative ability and may chemically attack the tertiary hydrogen at the a carbon of the PSSA; the degradation of the PSSA membrane mainly takes place at the cathode side of the cell, and the loss of the aromatic rings and the SO3- groups simultaneously occurs from the PSSA membrane. A new kind of the PSSA-Nafion composite membrane, where the Nafion membrane is bonded with the PSSA membrane and located at the cathode of the cell, was designed to prevent oxidation degradation of the PSSA membrane in fuel cells. The performances of fuel cells with PSSA-Nafion101 and PSSA-recast Nafion composite membranes are demonstrated to be stable after 835 h and 240 h, respectively.

Composite electrode for unitized regenerative proton exchange membrane fuel cell with improved cycle life

To improve the cycle life of unitized regenerative fuel cells (URFCs), an electrode with a composite structure has been developed. The cycle life and polarization curves for both fuel cell and electrolysis modes of URFC operation were investigated. The cycle life of URFCs was improved considerably and the performance was fairly constant during 25 cycles, which illustrates that the composite electrode is effective in sustaining the cyclic performance of URFCs. It shows the URFCs with such an electrode structure are promising for practical applications. (C) 2004 The Electrochemical Society.

A novel method for preparing PEMFC catalytic layers

A novel PEMFC catalytic layer was fabricated by a Nafion-pyrolyzed method, which demonstrated a high performance with a maximum power density of 0.82 W/cm(2) on an electrode prepared by this method. The effects of the heat-treatment temperature and Nation content in the catalyst layer on performance were studied.

Investigation on the catalytic roles of silver species in the selective catalytic reduction of NOx with methane

Silver impregnated H-ZSM-5 zeolite catalysts with silver loading from 3 to 15 wt.% were investigated for the selective catalytic reduction (SCR) of NOx with CH4 in the excess of oxygen. X-ray diffraction (XRD) and UV-Vis measurements established the structure of silver catalysts. A relationship between the structure of silver catalysts and their catalytic functions for the SCR of NOx by CH4 was clarified. The NO conversion to N-2 showed a S-shape dependence on the increase of Ag loading. No linear dependence of catalytic activity on the amount of silver ions in the zeolite cation sites was observed. Contrastively, the activity was significantly enhanced by the nano-sized silver particles formed on the higher Ag loading samples (greater than or equal to7 wt.%). Temperature programmed desorption (TPD) and temperature programmed reduction (TPR) studies showed that nano-silver particles provided much stronger adsorption centers for active intermediates NO3-(s) on which adsorbed NO3-(s) could be effectively reduced by the activated methane. Silver ions in the zeolite cation sites might catalyze the reaction through activation of CH4 at lower temperatures. Activated CH4 reacted with NO3-(s) adsorbed on nano-silver particles to produce N-2 and CO2. (C) 2003 Elsevier B.V. All rights reserved.

Solid-state MAS NMR studies on the hydrothermal stability of the zeolite catalysts for residual oil selective catalytic cracking

By using the solid-state MAS NMR technique, the hydrothermal stabilities (under 100% steam at 1073 K) of HZSM-5 zeolites modified by lanthanum and phosphorus have been studied. They are excellent zeolite catalysts for residual oil selective catalytic cracking (RSCC) processes. It was indicated that the introduction of phosphorus to the zeolite via impregnation with orthophosphoric acid led to dealumination as well as formation of different Al species, which were well distinguished by Al-27 3Q MAS NMR. Meanwhile, the hydrothermal stabilities of the zeolites (P/HZSM-5, La-P/HZSM-5) were enhanced even after the samples were treated under severe conditions for a prolonged time. It was found that the Si-O-Al bonds were broken under hydrothermal conditions, while at the same time the phosphorous compounds would occupy the silicon sites to form (SiO)(x)Al(OP)(4 - x) species. With increasing time, more silicon sites around the tetrahedral coordinated Al in the lattice can be replaced till the aluminum is completely expelled from the framework. The existence of lanthanum can partially restrict the breaking of the Si-O-Al bonds and the replacement of the silicon sites by phosphorus, thus preventing dealumination under hydrothermal conditions. This was also proved by P-31 MAS NMR spectra. (C) 2004 Elsevier Inc. All rights reserved.