Calorimetric study of Wood alloy

The heat capacities of Wood alloy have been measured with an automatic adiabatic calorimeter over the temperature range of 80 similar to 360 K. The thermodynamic data of solid-liquid phase transition have been obtained from the heat capacity measurements. The melting temperature, enthalpy and entropy of fusion of the substance are 345.662 K, 18.47 J.g(-1) and 0.05343 J.g(-1).K-1, respectively. The necessary thermal data are provided for the low temperature thermodynamic study of the alloy.

The effect of tungsten additive on the surface characteristics of amorphous Ni-P alloy

The variation of surface compositions on amorphous Ni80.4W1.5P18.1 alloy by O-2 oxidation and H-2 reduction treatments have been studied by XPS, UPS and ISS. It shows that addition of tungsten in the amorphous Ni-P alloy leads to dramatic changes of the relating component distributions in the surface layers before and after these treatments. Oxidation of a Ni80.4W1.5P18.1 amorphous alloy in 1 bar of oxygen at 513 K caused a significant segregation of nickel in different oxide states at the surface. The subsequent reduction of the oxidized surface with I bar hydrogen at 553 K resulted in only a small portion of Ni and P being reduced into elemental states, while most of them was found to combine to form a kind of nickel phosphate compound. On the other hand, under the same conditions, the oxidation and reduction of a Ni80P20 alloy gave rise to metallic Ni and elemental P as the predominate species on the alloy surface. The addition of W in the amorphous alloy might act as nuclei for a favorable formation of the phosphate structure which was proposed to be an active species for hydrogen-relating catalytic reactions. (C) 1999 Elsevier Science B.V. All rights reserved.

Characterization and thermodynamic study of ultra-fine particle of Ni-B amorphous alloy

Ultra-fine particle of Ni-B amorphous alloy was prepared by chemical reduction of Ni2+ with NaBH4 and characterized with TEM and XRD. The heat capacity and thermal stability were measured with a high-precision automatic adiabatic calorimeter and DTA. The upper limit of applied temperature of the substance was found to be 684 K for use as catalyst. (C) 1999 Elsevier Science B.V. All rights reserved.

Preparation and characterization of Pd-Ag alloy composite membrane with magnetron sputtering

A Pd-Ag (24 wt%) alloy composite membrane was prepared by the magnetron sputtering. A gamma-Al2O3 membrane was synthesized by the sol-gel method and used as substrate of the Pd-Ag alloy film. The process parameters of the magnetron sputtering were optimized as a function of the compactness of the Pd-Ag alloy film. The best membrane with a thickness of 1 mu m was produced with a sputtering pressure of 2.7 Pa and a substrate temperature of 400 degrees C. The membrane had an H-2/N-2 permselectivity of 51.5-1000 and an H-2 permeation rate of 0.036-1.17 x 10(-5)cm(3)/cm(2).s. Pa, depending on operating conditions.

XRD and XPS studies on the ultra-uniform Raney-Ni catalyst prepared from the melt-quenching alloy

We present a novel method for preparing an ultra-uniform Raney-Ni catalyst, which includes melt-quenching, hydrogen treatment and leaching in an alkali solution. The resultant catalyst shows superior activity in the reaction of cyclohexanone hydrogenation. X-ray diffraction (XRD) and XPS have been employed to characterize the catalysts. As demonstrated, the pretreatment with hydrogen caused a distinct phase transfer of the Ni-Al alloys, forming more of the Ni2Al3 component. In the subsequent leaching process, the Ni2Al3 component shows high activity and the resultant catalyst exhibits high surface areas and small pores. Moreover, metallic Al in the hydrogen-pretreated alloy appeared to be leached more easily and thus the aluminium species remaining on the catalyst surface is aluminium oxide predominantly, which serves as a matrix to stabilize active Ni species on the surface. Copyright (C) 2001 John Wiley & Sons, Ltd.

Structure and properties of samarium overlayer and Sm/Rh surface alloy on Rh(100)

The structure and properties of Sm overlayer and Sm/Rh surface alloy have been investigated with Auger electron spectroscopy (AES), low energy electron diffraction (LEED), X-ray photoelectron spectroscopy (XPS), and temperature programmed desorption spectroscopy (TDS). The growth of Sm on Rh(100) at room temperature (RT) appears following the Stranski-Krastanov growth mode and only the trivalent state Sm is observed from XPS results. Thermal treatment of the Sm film at 900 K leads to the formation of ordered surface alloy which shows the c(5 root2 x root2)R45 degrees and c(2 x 2) LEED patterns. Annealing the Sm film at temperature above 400 K makes the binding energy (B.E.) of Sm 3d(5/2) shift to higher energy by 0.7 eV, which indicates charge transfer from Sm to Rh(100) substrate, causing the increase of CO desorption temperature.