The effect of inserting strain-compensated GaNAs layers on the luminescence properties of GaInNAs/GaAs quantum well

Photoluminescence (PL) properties of GaInNAs/GaAs quantum wells (QWs) with strain-compensated GaNAs layers grown by molecular beam epitaxy are investigated. The temperature-dependent PL spectra of GaInNAs/GaAs QW with and without GaNAs layers are compared and carefully studied. It is shown that the introduction of GaNAs layers between well and barrier can effectively extend the emission wavelength, mainly due to the reduction of the barrier potential. The PL peak position up to 1.41 mum is observed at the room temperature. After adding the GaNAs layers into QW structures, there is no essential deterioration of luminescence efficiency. N-induced localization states are also not remarkably influenced. It implies that with optimized growth condition, high-quality GaInNAs/GaAs QWs with strain-compensated GaNAs layers can be achieved. (C) 2003 Elsevier Science B.V. All rights reserved.

Optimization of cubic GaN growth by metalorganic chemical vapor deposition based on residual strain relaxation

The reduction of residual strain in cubic GaN growth by inserting a thermoannealing process is investigated. It is found that the epilayer with smaller tensile strain is subject to a wider optimal "growth window." Based on this process, we obtain the high-quality GaN film of pure cubic phase with the thickness of 4 mum by metalorganic chemical vapor deposition. The photoluminescence spectrum at room temperature shows the thick GaN layer has a near-band emission peak with a full width at half maximum of 42 meV which confirms its high crystal quality, further supported by the x-ray (002) diffraction measurement. A simplified model is demonstrated to interpret this strain effect on the growth process. (C) 2003 American Institute of Physics.

Growth mode and strain evolution during InN growth on GaN(0001) by molecular-beam epitaxy

Epitaxial growth of InN on GaN(0001) by plasma-assisted molecular-beam epitaxy is investigated over a range of growth parameters including source flux and substrate temperature. Combining reflection high-energy electron diffraction (RHEED) and scanning tunneling microscopy (STM), we establish a relationship between film growth mode and the deposition condition. Both two-dimensional (2D) and three-dimensional (3D) growth modes of the film are observed. For 2D growth, sustained RHEED intensity oscillations are recorded while STM reveals 2D nucleation islands. For 3D growth, less than three oscillation periods are observed indicating the Stranski-Krastanov (SK) growth mode of the film. Simultaneous measurements of (reciprocal) lattice constant by RHEED suggest a gradual relaxation of the strain in film, which commences during the first bilayer (BL) deposition and almost completes after 2-4 BLs. For SK growth, 3D islanding initiates after the strain has mostly been relieved, presumably by dislocations, so the islands are likely strain free. (C) 2002 American Institute of Physics.

Strain relaxation of InP film directly grown on GaAs patterned compliant substrate

In order to overcome the large lattice mismatch in the heteroepitaxy, a new patterned compliant substrate method has been introduced, which has overcome the disadvantages of previously published methods. InP film of thickness 800 nm was directly grown on this substrate. Scanning electron microscopy (SEM) has shown that good surface morphology has been obtained. In addition, Photoluminescence (PL) and double crystal X-ray diffraction (DCXRD) study have shown that the residual strain has been reduced, and that the structure quality has been improved. (C) 2002 Elsevier Science B.V. All rights reserved.

Influence of strain on annealing effects of In(Ga)As quantum dots

Post-growth rapid thermal annealing has been performed with In(Ga)As quantum dots (QDs) at different strain statuses. It is confirmed that the strain-enhanced interdiffusion decreases the inhomogeneous size distribution. The preferential lateral interdiffusion of QDs during annealing was observed. we attribute it to the naturally anisotropic strain distribution in/around the dots and the saturation of strain difference between the base boundary and the top of the dots. There exist strain-enhanced mechanism and vacancy diffusion enhanced mechanism during the annealing. As to which one dominates the QD interdiffusion depends on the thickness of capping layer and the annealing temperature. (C) 2002 Elsevier Science B.V. All rights reserved.

Proof of InAs/GaAs self-organized quantum dot lasing and the experimental determination of local Strain effect on the band structures

Confirmation of quantum dot lasing have been given by photoluminescence and electro-luminescence spectra. Energy levels of QD laser are distinctively resolved due to band filling effect, and the lasing energy of quantum dot laser is much lower than quantum well laser. The energy barrier at InAs/GaAs interface due to the built-in strain in self-organized system has been determined experimentally by deep level transient spectroscopy (DLTS). Such barrier has been predicted by previous theories and can be explained by the apexes appeared in the interface between InAs and GaAs caused by strain.

Influence of combined InAlAs and InGaAs strain-reducing laser on luminescence properties of InAs/GaAs quantum dots

We have fabricated self-organized InAs/GaAs quantum dots (QDs) capped by 1 nm In0.2Al0.8As and 5 nm In0.2Ga0.8As strain-reducing layer (SRL). The luminescence emission at a long wavelength of 1.33 mum with narrower half width is realized. A wider energy separation between the ground and first excited radiative transitions of up to 102meV was observed at room temperature. Furthermore, the comparative study proves that luminescence properties of InAs/GaAs QDs overgrown with combined InAlAs and InGaAs SRLs are much better than that of one capped with InGaAs or InAlAs SRL. (C) 2002 Elsevier Science B.V. All rights reserved.

Shape evolution of Ge/Si(001) islands induced by strain-driven alloying

The shape evolution of Ge/Si(001) islands grown by ultrahigh vacuum chemical vapor deposition were investigated by atomic force microscopy at different deposition rates. We find that, at low deposition rates, the evolution of islands follows the conventional pathway by which the islands form the pyramid islands, evolve into dome islands, and dislocate at a superdome shape with increasing coverage. While at a high deposition rate of 3 monolayers per minute, the dome islands evolve towards the pyramids by a reduction of the contact angle. The presence of the atomic intermixing between the Ge islands and Si substrate at high deposition rate is responsible for the reverse evolution. (C) 2001 American Institute of Physics.

Strain-compensated quantum cascade lasers operating at room temperature

Quantum cascade (QC) lasers based on strain-compensated InxGa(1-x)As/InyAl(1-y)As grown on InP substrate using molecular beam epitaxy is reported. The epitaxial quality is demonstrated by the abundant narrow satellite peaks of double-crystal X-ray diffraction and cross-section transmission electron microscopy of the QC laser wafer. Laser action in quasi-continuous wave operation is achieved at lambda approximate to 3.6-3.7 mum at room temperature (34 degreesC) for 20 mum x 1.6 mm devices, with peak output powers of similar to 10.6mW and threshold current density of 2.7kA/cm(2) at this temperature. (C) 2000 Published by Elsevier Science B.V.

High-performance strain-compensated InGaAs/InAlAs quantum cascade lasers

We report on the realization of quantum cascade (QC) lasers based on strain-compensated InxGa(1-x)As/In(y)A((1-y))As grown on InP substrates using molecular beam epitaxy. X-ray diffraction and cross section transmission electron microscopy have been used to ascertain the quality of the QC laser materials. Quasi-continuous wave lasing at lambda approximate to 3.54-3.7 mum at room temperature was achieved. For a laser with 1.6 mm cavity length and 20 mum ridge-waveguide width,quasi-continuous wave lasing at 34 degreesC persists for more than 30 min, with a maximum power of 11.4 mW and threshold current density of 1.2 kA cm(-2), both record values for QC lasers of comparable wavelength.

Room temperature (34 degrees C) operation of strain-compensated quantum cascade lasers

A short wavelength (lambda similar or equal to 3.5 mu m) strain-compensated InxGa(1-x)As/InyAl(1-y)As quantum cascade laser is reported. Quasi-continuous wave operation of this device at 34 degrees C with an output power of 11.4mW persisted for more than 30 minutes without obvious degradation. A very low threshold current density of 1.2KA/cm(2) at this temperature was observed.

Anisotropic strain in (100) ZnSe epilayers grown on lattice mismatched substrates

We show that part of the reflectance difference resonance near the E-0 energy of ZnSe is due to the anisotropic in-plane strain in the ZnSe thin films, as films grown on three distinctly different substrates, GaAs, GaP, and ZnS, all show the resonance at the same energy. Such anisotropic strain induced resonance is predicted and also observed near the E-1/E-1+Delta(1) energies in ZnSe grown on GaAs. The theory also predicts that there should be no resonance due to strain at, the E-0+Delta(0) energy, which is consistent with experiments. The strain anisotropy is rather independent of the ZnSe layer thickness, or whether the film is strain relaxed. For ZnSe films with large lattice mismatch with substrates, the resonance at the E-1/E-1+Delta(1) energies is absent, very likely due to the poor crystalline quality of the 20 nm or so surface layer. (C) 2000 American Vacuum Society. [S0734-211X(00)05604-3].

X-ray double-crystal characterization of the strain relaxation in GaAs/GaNxAs1-x/GaAs(001) sandwiched structures

An X-ray diffraction method, estimating the strain relaxation in an ultrathin layer, has been discussed by using kinematic and dynamical X-ray diffraction (XRD) theory. The characteristic parameter Delta Omega, used as the criterion of the strain relaxation in ultrathin layers, is deduced theoretically. It reveals that Delta Omega should be independent of the layer thickness in a coherently strained layer. By this method, we characterized our ultrathin GaNxAs1-x samples with N contents up to 5%. XRD measurements show that our GaNxAs1-x layers are coherently strained on GaAs even for such a large amount of N. Furthermore, a series of GaNxAs1-x samples with same N contents but different layer thicknesses were also characterized. It was found that the critical thickness (L-c) of GaNAs in the GaAs/GaNAs/GaAs structures determined by XRD measurement was 10 times smaller than the theoretical predictions based on the Matthews and Blakeslee model. This result was also confirmed by in situ observation of reflection high-energy electron diffraction (RHEED) and photoluminescence (PL) measurements. RHEED observation showed that the growth mode of GaNAs layer changed from 2D- to 3D-mode as the layer thickness exceeded L-c. PL measurements showed that the optical properties of GaNAs layers deteriorated rapidly as the layer thickness exceeded L-c. (C) 2000 Elsevier Science B.V. All rights reserved.

Strain and photoluminescence characterization of cubic (In,Ga)N films grown on GaAs(001) substrates

Cubic InxGa1-xN films were successfully grown on GaAs(001) substrates by metalorganic chemical-vapor deposition. The values of x content ranging from 0.10 to 0.24 obtained at different growth conditions were measured by double-crystal x-ray diffraction (XRD). The perpendicular and parallel elastic strain of the In0.2Ga0.8N layer, epsilon(perpendicular to)=0.4% and epsilon(parallel to)=-0.4% for GaN and epsilon(perpendicular to)=0.37% and epsilon(parallel to)=-0.37% for InGaN, respectively, were derived using the XRD measurements. The inhomogeneous strain and the average grain size of the In0.2Ga0.8N/GaN films were also studied by XRD. Photoluminescence spectra were used to measure the optical characterization of the InxGa1-xN thin films with different In composition, and the near-band-edge emission dependence of cubic InxGa1-xN on the x value is nearly linear with In content x less than or equal to 0.24. (C) 2000 American Institute of Physics. [S0021-8979(00)03908-6].