Calculation of the bulk modulus of simple and complex crystals with the chemical bond method

The relation between the lattice energies and the bulk moduli on binary inorganic crystals was studied, and the concept of lattice energy density is introduced. We find that the lattice energy densities are in good linear relation with the bulk moduli in the same type of crystals, the slopes of fitting lines for various types of crystals are related to the valence and coordination number of cations of crystals, and the empirical expression of calculated slope is obtained. From crystal structure, the calculated results are in very good agreement with the experimental values. At the same time, by means of the dielectric theory of the chemical bond and the calculating method of the lattice energy of complex crystals, the estimative method of the bulk modulus of complex crystals was established reasonably, and the calculated results are in very good agreement with the experimental values.

Processing, microstructure and mechanical properties of W50Al50 bulk alloy obtained by mechanical alloying and hot-pressing

The Al50W50 alloy bulk bodies were fabricated by using mechanical alloying and hot-pressing in this work. The Al50W50 alloy had excellent thermal stability up to 1300 degreesC under vacuum and Its optimum microhardness, bending strength and compressive strength were 10.21 GPa, 570 MPa and 2.07 GPa, respectively.

Synthesis of novel maleimide-terminated thioetherimide oligomer and its bulk copolymerization with reactive solvents

This paper reports the synthesis of a novel maleimide-terminated thioetherimide oligomer and its copolymefization with reactive solvents bearing vinyl. Starting from 3-chlorophthalic anhydride and 4-chlorophthalic anhydride, 2,2',3,3'-thiodiphenyl tertracaboxylic dianhydride (3,3'-TDPA) and 3,3',4,4'-thiodiphenyl tertracaboxylic dianhydride (4,4'-TDPA) were synthesized. Thereby, a novel maleimide-terminated thioetherimide oligomer was prepared from. 3,3-TDPA, 4,4'-TDPA, 3,3'-dimethyl-4,4-diaminodiphenylmethane (DMMDA) and maleic anhydride. Binary and ternary copolymer resin were derived from corresponding binary and ternary homogeous solution consisting of thioetherimide oligomer, reactive solvent N-vinylpyrrolidone (NVP) or N,N'-dimethylacrylamide (DMAA) and divinylbenzene (DVB) as modifier, initiated either by gamma ray irradiation or by benzoyl peroxide (BPO). Thermal and mechanical properties of copolymer resin are determined and compared in terms of the kind of reactive solvent, addition of modifier DVB. The effect of initiation approach on property of final copolymer resin were studied. Phase separation and sub-transition of ternary copolymer resin induced by BPO are observed, which could be accounted for by thermal movement of DMAA molecules during thermal initiation.

Preparation and optical properties of trivalent europium-doped bulk and nanocrystalline SrY2O4

The nanocrystalline Sry(2)O(4):Eu3+ was prepared by a poly(vinyl alcohol) (PVA)+glycine-assist combustion method. The results of x-ray diffraction indicate that the resulting Sry(2)O(4):Eu3+ nanocrystals have much broader and less intense peaks compared with those in bulk material. The charge-transfer bands in Sry(2)O(4):Eu3+ nanocrystals shift to higher energies in contrast to those in bulk material. The spectral results revealed that in bulk SrY2O4: Eu3+ the Eu3+ ions occupied three nonequivalent sites, with one at the Sr site: one at the Y(1) site and another at the Y(2) site, while in nanocrystalline SrY2O4: Eu3+, the Eu3+ ions occupied only two nonequivalent sites; one at the Y(1) site and the other at the Y(2) site. Finally, by theoretical calculation and analysis, the analyzed results are in reasonable agreement with our experimental results.

Preparation and mechanical properties of a bulk icosahedral quasicrystalline Ti45Zr35Ni17Cu3 alloy

A bulk Ti45Zr35Ni17Cu3 alloy, which consisted of the icosahedral quasicrystalline phase, was prepared by mechanical alloying(MA) and subsequent pulse discharge sintering. Ti45Zr35Ni17Cu3 amorphous powders (with particle size < 50 mu m) were obtained after mechanical alloying for more than 150 h from the mixture of the elemental powder. The transformation temperature range from amorphous phase to the quasicrystalline phase was from 400 K to 900 K. The mechanical properties of the bulk quasicrystalline alloy have been examined at room temperature. The Vickers hardness and compressive fracture strength were 620 +/- 40 and 1030 +/- 60 MPa, respectively. The bulk quasicrystalline alloy exhibited the elastic deformation by the compressive test. The fracture mode was brittle cleavage fracture.

Effects of solution viscosity on heterogeneous electron transfer across a liquid/liquid interface

Scanning electrochemical microscopy (SECM) is employed to investigate the effect of solution viscosity on the rate constants of electron transfer (ET) reaction between potassium ferricyanide in water and 7,7,8,8-tetracyanoquinodimethane (TCNQ) in 1,2-dichloroethane. Either tetrabutylammonium (TBA(+)) or ClO4- is chosen as the common ion in both phases to control the interfacial potential drop. The rate constant of heterogeneous ET reaction between TCNQ and ferrocyanide produced in-situ, k(12), is evaluated by SECM and is inversely proportional to the viscosity of the aqueous solution and directly proportional to the diffusion coefficient of K4Fe(CN)(6) in water when the concentration of TCNQ in the DCE phase is in excess. The k(12) dependence on viscosity is explained in terms of the longitudinal relaxation time of the solution. The rate constant of the heterogeneous ET reaction between TCNQ and ferricyanide, k(21), is also obtained by SECM and these results cannot be explained by the same manner.

Carbon ceramic electrodes bulk-modified with nanoparticles of ferrocenebutyrate-intercalated Mg-Al layered double hydroxide

Ferrocenebutyrate-intercalated layered double hydroxide (FcLDH) was prepared by the coprecipitation method and characterized by PXRD, FTIR, TEM and elemental analysis. FcLDH nanoparticles in deionized water were deposited onto the surface of graphite powder to yield graphite powder-supported FcLDH, which was subsequently dispersed into methyltrimethoxysilane-derived gels to fabricate surface-renewable, stable, rigid carbon ceramic electrodes containing the electroactive ferrocenyl group. Cyclic voltammetric study revealed that peak currents of the FcLDH-modified electrode were diffusion-con trolled in 0.1 mol l(-1) KCl aqueous solution. In addition, the formal potential of the modified electrode is related to the activity of chloride ion with a Nernst slope of 56 mV per decade.

Sol-gel derived carbon ceramic electrode bulk-modified with tris(1,10-phenanthroline-5,6-dione)iron(II) hexafluorophosphate and its use as an amperometric iodate sensor

A surface-renewable tris (1,10-phenanthroline-5, 6-dione) iron (II) hexafluorophosphate (FePD) modified carbon ceramic electrode was constructed by dispersing FePD and graphite powder in methyltrimethoxysilane (MTMOS) based gels. The FePD-modified electrode presented pH dependent voltammetric behavior, and its peak currents were diffusion-controlled in 0.1 mol/L Na2SO4 + H2SO4 solution (pH = 0. 4). In the, presence of iodate, clear electrocatalytic reduction waves were observed and thus the chemically modified electrode was used as an amperometric sensor for iodate in common salt. The linear range, sensitivity, detection limit and response time of the iodate sensor were 5 x 10(-6)-1 x 10(-2) mol/L, 7.448 muA.L/mmol, 1.2 x 10(-6) mol/L and 5 s, respectively. A distinct advantage of this sensor is its good reproducibility of surface-renewal by simple mechanical polishing.

Sol-gel-derived carbon ceramic composite electrodes bulk-modified with 1 : 12-silicomolybdic acid

1:12-Silicomolybdic acid (SiMo12) doped carbon ceramic composite electrodes were fabricated by incorporating SiMo12 and graphite powder in a methyltrimethoxysilane-based gel and characterized by cyclic and square-wave voltammetry, It was demonstrated that the chemically modified electrodes were suitable for electrocatalytic reduction of bromate, The electrodes had the remarkable advantage of surface renewal owing to bulk modification, as web as simple preparation, good mechanical and chemical stability and reproducibility.

Sol-gel-derived graphite organosilicate composite electrodes bulk-modified with Keggin-type alpha-germanomolybdic acid

A novel inorganic-organic hybrid material incorporating graphite powder and Keggin-type alpha -germanomolybdic acid (GeMo12) in methyltrimethoxysilane-based gels has been produced by the sol-gel technique and used to fabricate a chemically bulk-modified electrode. GeMo12 acts as a catalyst, graphite powder ensures conductivity by percolation, the silicate provides a rigid porous backbone, and the methyl groups endow hydrophobicity and thus limit the wetting section of the modified electrode. The GeMo12-modified graphite organosilicate composite electrode was characterized by cyclic and square-wave voltammetry. The modified electrode shows a high electrocatalytic activity toward the reduction of bromate, nitrite and hydrogen peroxide in acidic aqueous solution. In addition, the chemically-modified electrode has some distinct advantages over the traditional polyoxometalate-modified electrodes, such as long-term stability and especially repeatability of surface-renewal by simple mechanical polishing.

Chemiluminescent determination of luminol and hydrogen peroxide using hematin immobilized in the bulk of a carbon paste electrode

A new method for immobilization of a chemiluminescent reagent is presented. It is based on immobilizing hematin, a catalyst for luminol reaction, in the bulk of a carbon paste electrode. Bulk-immobilization allows renewal of the surface by simple polishing or cutting to expose anew and fully active surface in the case of fouling or deactivation by other means. By using a hematin-modified carbon paste electrode, the applied potential shifted negatively compared with that of unmodified carbon paste electrode or a glassy carbon electrode. The shift in potential changed the reaction processes and effectively stabilized the chemiluminescent signal during successive measurements. Under this condition, the signal was stable during 3 hours of continuous operation. The log-log plots of the emitted light intensity vs. luminol concentration and hydrogen peroxide concentration were linear over the region 10(-8)-10(-3) mol L-1 with a correlation coefficient of 0.999 and 3.9 x 10(-6)-10(-3) mol L-1 with a correlation coefficient of 0.994, respectively. Application of this method for other chemiluminescent and bioluminescent systems is suggested.

Bulk modulus of ternary chalcopyrite A(I)B(III)C(2)(VI) and A(II)B(IV)C(2)(V) semiconductors

Based on the complex crystal chemical bond theory, the formula of Liu and Cohen's, which is only suitable for one type of bond, has been extended to calculate the bulk modulus of ternary chalcopyrite A(I)B(III)C(2)(VI) and A(II)B(IV)C(2)(V) which contains two types of bonds. The calculated results are in fair agreement with the previous theoretical values reported and experimental values. (C) 1998 Elsevier Science Ltd. All rights reserved.

VISCOSITY AND FLOW PROPERTIES OF CONCENTRATED-SOLUTIONS OF CHITOSAN WITH DIFFERENT DEGREES OF DEACETYLATION

The effects of the degree of deacetylation (DD) on the viscosity and flow behaviour of concentrated solutions of chitosan were investigated using 0.2 M CH3COOH and 0.2 M CH3COOH/0.1 M CH3COONa aqueous solutions as solvents. The results indicated that the