Surface Activity and Bulk Defect Chemistry of Solid Oxide Fuel Cell Cathodes

In the first half of this thesis, a new robotic instrument called a scanning impedance probe is presented that can acquire electrochemical impedance spectra in automated fashion from hundreds of thin film microelectrodes with systematically varied properties. Results from this instrument are presented for three catalyst compositions that are commonly considered for use in state-of-the-art solid oxide fuel cell cathodes. For (La_0.8Sr_0.2)_0.95Mn_O3+δ (LSM), the impedance spectra are well fit by a through-the-film reaction pathway. Transport rates are extracted, and the surface activity towards oxygen reduction is found to be correlated with the number of exposed grain boundary sites, suggesting that grain boundaries are more surface-active than grains. For La_0.5Sr_0.5Co_O3-δ (LSC), the surface activity degrades ~50x initially and then stabilizes at a comparable activity to that of previously measured Ba_0.5Sr_0.5Co_0.8Fe_0.2O3-δ films. For Sr_0.06Nb_0.06Bi_1.87O₃ (SNB), an example of a doped bismuth oxide, the activity of the metal-SNB boundary is measured.

In the second half of this thesis, SrCo_0.9Nb_0.1O_3-δ is selected as a case study of perovskites containing Sr and Co, which are the most active oxygen reduction catalysts known. Several bulk properties are measured, and synchrotron data are presented that provide strong evidence of substantial cobalt-oxygen covalency at high temperatures. This covalent bonding may be the underlying source of the high surface activity.

Fundamental Studies of Carbon Oxygen Bond Activation in Nickel Diphosphine Ether Complexes. And, Metallomacrocycles as Ligands: Synthesis and Characterization of Aluminum-Bridged Bisglyoximato Complexes of Iron and Cobalt

In order to develop better catalysts for the cleavage of aryl-X bonds fundamental studies of the mechanism and individual steps of the mechanism have been investigated in detail. As the described studies are difficult at best in catalytic systems, model systems are frequently used. To study aryl-oxygen bond activation, a terphenyl diphosphine scaffold containing an ether moiety in the central arene was designed. The first three chapters of this dissertation focus on the studies of the nickel complexes supported by this diphosphine backbone and the research efforts in regards to aryl-oxygen bond activation.

Chapter 2 outlines the synthesis of a variety of diphosphine terphenyl ether ligand scaffolds. The metallation of these scaffolds with nickel is described. The reactivity of these nickel(0) systems is also outlined. The systems were found to typically undergo a reductive cleavage of the aryl oxygen bond. The mechanism was found to be a subsequent oxidative addition, β-H elimination, reductive elimination and (or) decarbonylation.

Chapter 3 presents kinetic studies of the aryl oxygen bond in the systems outlined in Chapter 2. Using a series of nickel(0) diphosphine terphenyl ether complexes the kinetics of aryl oxygen bond activation was studied. The activation parameters of oxidative addition for the model systems were determined. Little variation was observed in the rate and activation parameters of oxidative addition with varying electronics in the model system. The cause of the lack of variation is due to the ground state and oxidative addition transition state being affected similarly. Attempts were made to extend this study to catalytic systems.

Chapter 4 investigates aryl oxygen bond activation in the presence of additives. It was found that the addition of certain metal alkyls to the nickel(0) model system lead to an increase in the rate of aryl oxygen bond activation. The addition of excess Grignard reagent led to an order of magnitude increase in the rate of aryl oxygen bond activation. Similarly the addition of AlMe3 led to a three order of magnitude rate increase. Addition of AlMe₃ at -80 °C led to the formation of an intermediate which was identified by NOESY correlations as a system in which the AlMe3 is coordinated to the ether moiety of the backbone. The rates and activation parameters of aryl oxygen bond activation in the presence of AlMe3 were investigated.

The last two chapters involve the study of metalla-macrocycles as ligands. Chapter 5 details the synthesis of a variety of glyoxime backbones and diphenol precursors and their metallation with aluminum. The coordination chemistry of iron on the aluminum scaffolds was investigated. Varying the electronics of the aluminum macrocycle was found to affect the observed electrochemistry of the iron center.

Chapter 6 extends the studies of chapter 5 to cobalt complexes. The synthesis of cobalt dialuminum glyoxime metal complexes is described. The electrochemistry of the cobalt complexes was investigated. The electrochemistry was compared to the observed electrochemistry of a zinc analog to identify the redox activity of the ligand. In the presence of acid the cobalt complexes were found to electrochemically reduce protons to dihydrogen. The electronics of the ancillary aluminum ligands were found to affect the potential of proton reduction in the cobalt complexes. These potentials were compared to other diglyoximate complexes.

Magnetic moments in amorpous palladium-cobalt-silicon alloys

The magnetic moments of amorphous ternary alloys containing Pd, Co and Si in atomic concentrations corresponding to Pd_(80-x)Co_xSi_(20) in which x is 3, 5, 7, 9, 10 and 11, have been measured between 1.8 and 300°K and in magnetic fields up to 8.35 kOe. The alloys were obtained by rapid quenching of a liquid droplet and their structures were analyzed by X-ray diffraction. The measurements were made in a null-coil pendulum magnetometer in which the temperature could be varied continuously without immersing the sample in a cryogenic liquid. The alloys containing 9 at.% Co or less obeyed Curie's Law over certain temperature ranges, and had negligible permanent moments at room temperature. Those containing 10 and 11 at.% Co followed Curie's Law only above approximately 200°K and had significant permanent moments at room temperature. For all alloys, the moments calculated from Curie's Law were too high to be accounted for by the moments of individual Co atoms. To explain these findings, a model based on the existence of superparamagnetic clustering is proposed. The cluster sizes calculated from the model are consistent with the rapid onset of ferromagnetism in the alloys containing 10 and 11 at.% Co and with the magnetic moments in an alloy containing 7 at.% Co heat treated in such a manner as to contain a small amount of a crystalline phase. In alloys containing 7 at.% Co or less, a maximum in the magnetization vs temperature curve was observed around 10°K. This maximum was eliminated by cooling the alloy in a magnetic field, and an explanation for this observation is suggested.

Part I. Influence of membrane morphology on ion-exchange and charge propagation in composite polyelectrolyte electrode coatings. Part II. Dynamic surface tension measurements of polarization relaxation at mercury pool electrodes by the method of Wilhelmy.

Part I. Novel composite polyelectrolyte materials were developed that exhibit desirable charge propagation and ion-retention properties. The morphology of electrode coatings cast from these materials was shown to be more important for its electrochemical behavior than its chemical composition.

Part II. The Wilhelmy plate technique for measuring dynamic surface tension was extended to electrified liquid-liquid interphases. The dynamical response of the aqueous NaF-mercury electrified interphase was examined by concomitant measurement of surface tension, current, and applied electrostatic potential. Observations of the surface tension response to linear sweep voltammetry and to step function perturbations in the applied electrostatic potential (e.g., chronotensiometry) provided strong evidence that relaxation processes proceed for time-periods that are at least an order of magnitude longer than the time periods necessary to establish diffusion equilibrium. The dynamical response of the surface tension is analyzed within the context of non-equilibrium thermodynamics and a kinetic model that requires three simultaneous first order processes.

Magnetic behavior of basic iron(III) compounds. I. Magnetic behavior of the basic iron sulphates and basic iron chromate. II. Magnetic behavior of delta ferric oxide hydroxide

I. The thermomagnetic behavior and infrared spectroscopic features of KFe₃(SO₄)₂(OH)₆ (jarosite), (H₃O)Fe₃(SO₄)₂ (OH)₆ (hydronium jarosite), KFe₃(CrO₄)₂ (OH)₆, Fe(OH)SO₄ (basic iron sulfate), and Fe(OH)CrO₄ (basic iron chromate) are reported. Fe(OH)CrO₄ and KFe₃(CrO₄)₂ (OH)₆ are shown to be weak ferro magnets with Curie temperatures of 73 and 71 °K, respectively. This unusual magnetic behavior is rationalized in terms of the ionic spin configurations of the phases. Exchange coupling through chromate bridging groups is shown to be weak.

II. The magnetic behavior and the influence of preparative history on the magnetic behavior of δFeO(OH) is reported. δFeO(OH) is shown to be a fine-particulate, uniaxial, magnetic species. Magnetization data for this species are shown to be consistent with the existence of magnetically inactive layers surrounding magnetic particles.

Electrocatalytic reduction of dioxygen at chemically modified electrodes

The kinetics of the reduction of O₂ by Ru(NH₃)₆⁺² as catalyzed by cobalt(II) tetrakis(4-N-methylpyridyl)porphyrin are described both in homogeneous solution and when the reactants are confined to Nafion coatings on graphite electrodes. The catalytic mechanism is determined and the factors that can control the total reduction currents at Nafion-coated electrodes are specified. A kinetic zone diagram for analyzing the behavior of catalyst-mediator-substrate systems at polymer coated electrodes is presented and utilized in identifying the current-limiting processes. Good agreement is demonstrated between calculated and measured reduction currents at rotating disk electrodes. The experimental conditions that will yield the optimum performance of coated electrodes are discussed, and a relationship is derived for the optimal coating thickness.

The relation between the reduction potentials of adsorbed and unadsorbed cobalt(III) tetrakis(4-N-methylpyridyl)porphyrin and those where it catalyzes the electroreduction of dioxygen is described. There is an unusually large change in the formal potential of the Co(III) couple upon the adsorption of the porphyrin on the graphite electrode surface. The mechanism in which the (inevitably) adsorbed porphyrin catalyzes the reduction of O₂ is in accord with a general mechanistic scheme proposed for most monomeric cobalt porphyrins.

Four new dimeric metalloporphyrins (prepared in the laboratory of Professor C. K. Chang) have the two porphyrin rings linked by an anthracene bridge attached to meso positions. The electrocatalytic behavior of the diporphyrins towards the reduction of O₂ at graphite electrodes has been examined for the following combination of metal centers: Co-Cu, Co-Fe, Fe-Fe, Fe-H₂. The Co-Cu diporphyrin catalyzes the reduction of O₂ to H₂O₂ but no further. The other three catalysts all exhibit mixed reduction pathways leading to both H₂O₂ and H₂O. However, the pathways that lead to H₂O do not involve H₂O₂ as an intermediate. A possible mechanistic scheme is offered to account for the observed behavior.

I. The rate and mechanism of the vapor-phase reaction between water and parts-per-million concentrations of nitrogen dioxide. II. The rate and mechanism of the air oxidation of parts-per-million concentrations of nitric oxide in the presence of water vapor.

Part I

A study of the thermal reaction of water vapor and parts-per-million concentrations of nitrogen dioxide was carried out at ambient temperature and at atmospheric pressure. Nitric oxide and nitric acid vapor were the principal products. The initial rate of disappearance of nitrogen dioxide was first order with respect to water vapor and second order with respect to nitrogen dioxide. An initial third-order rate constant of 5.5 (± 0.29) x 10⁴ liter² mole^-2 sec^-1 was found at 25˚C. The rate of reaction decreased with increasing temperature. In the temperature range of 25˚C to 50˚C, an activation energy of -978 (± 20) calories was found.

The reaction did not go to completion. From measurements as the reaction approached equilibrium, the free energy of nitric acid vapor was calculated. This value was -18.58 (± 0.04) kilocalories at 25˚C.

The initial rate of reaction was unaffected by the presence of oxygen and was retarded by the presence of nitric oxide. There were no appreciable effects due to the surface of the reactor. Nitric oxide and nitrogen dioxide were monitored by gas chromatography during the reaction.

Part II

The air oxidation of nitric oxide, and the oxidation of nitric oxide in the presence of water vapor, were studied in a glass reactor at ambient temperatures and at atmospheric pressure. The concentration of nitric oxide was less than 100 parts-per-million. The concentration of nitrogen dioxide was monitored by gas chromatography during the reaction.

For the dry oxidation, the third-order rate constant was 1.46 (± 0.03) x 10⁴ liter² mole^-2 sec^-1 at 25˚C. The activation energy, obtained from measurements between 25˚C and 50˚C, was -1.197 (±0.02) kilocalories.

The presence of water vapor during the oxidation caused the formation of nitrous acid vapor when nitric oxide, nitrogen dioxide and water vapor combined. By measuring the difference between the concentrations of nitrogen dioxide during the wet and dry oxidations, the rate of formation of nitrous acid vapor was found. The third-order rate constant for the formation of nitrous acid vapor was equal to 1.5 (± 0.5) x 10⁵ liter² mole^-2 sec^-1 at 40˚C. The reaction rate did not change measurably when the temperature was increased to 50˚C. The formation of nitric acid vapor was prevented by keeping the concentration of nitrogen dioxide low.

Surface effects were appreciable for the wet tests. Below 35˚C, the rate of appearance of nitrogen dioxide increased with increasing surface. Above 40˚C, the effect of surface was small.

Thermodynamic and kinetic behavior of an argon plasma jet. Decomposition of nitric oxide between 1300 - 1750 degrees K in an argon plasma

In the first part of the study, an RF coupled, atmospheric pressure, laminar plasma jet of argon was investigated for thermodynamic equilibrium and some rate processes.

Improved values of transition probabilities for 17 lines of argon I were developed from known values for 7 lines. The effect of inhomogeneity of the source was pointed out.

The temperatures, T, and the electron densities, n_e , were determined spectroscopically from the population densities of the higher excited states assuming the Saha-Boltzmann relationship to be valid for these states. The axial velocities, v_z, were measured by tracing the paths of particles of boron nitride using a three-dimentional mapping technique. The above quantities varied in the following ranges: 10¹² ˂ n_e ˂ 10¹⁵ particles/cm³, 3500 ˂ T ˂ 11000 °K, and 200 ˂ v_z ˂ 1200 cm/sec.

The absence of excitation equilibrium for the lower excitation population including the ground state under certain conditions of T and n_e was established and the departure from equilibrium was examined quantitatively. The ground state was shown to be highly underpopulated for the decaying plasma.

Rates of recombination between electrons and ions were obtained by solving the steady-state equation of continuity for electrons. The observed rates were consistent with a dissociative-molecular ion mechanism with a steady-state assumption for the molecular ions.

In the second part of the study, decomposition of NO was studied in the plasma at lower temperatures. The mole fractions of NO denoted by x_NO were determined gas-chromatographically and varied between 0.0012 ˂ x_NO ˂ 0.0055. The temperatures were measured pyrometrically and varied between 1300 ˂ T ˂ 1750°K. The observed rates of decomposition were orders of magnitude greater than those obtained by the previous workers under purely thermal reaction conditions. The overall activation energy was about 9 kcal/g mol which was considerably lower than the value under thermal conditions. The effect of excess nitrogen was to reduce the rate of decomposition of NO and to increase the order of the reaction with respect to NO from 1.33 to 1.85. The observed rates were consistent with a chain mechanism in which atomic nitrogen and oxygen act as chain carriers. The increased rates of decomposition and the reduced activation energy in the presence of the plasma could be explained on the basis of the observed large amount of atomic nitrogen which was probably formed as the result of reactions between excited atoms and ions of argon and the molecular nitrogen.

Electrical and optical investigations of beta-gallium oxide

An experimental investigation of the optical properties of β–gallium oxide has been carried out, covering the wavelength range 220-2500 nm.

The refractive index and birefringence have been determined to about ± 1% accuracy over the range 270-2500 nm, by the use of a technique based on the occurrence of fringes in the transmission of a thin sample due to multiple internal reflections in the sample (ie., the "channelled spectrum" of the sample.)

The optical absorption coefficient has been determined over the range 220 - 300 nm, which range spans the fundamental absorption edge of β – Ga₂O₃. Two techniques were used in the absorption coefficient determination: measurement of transmission of a thin sample, and measurement of photocurrent from a Schottky barrier formed on the surface of a sample. Absorption coefficient was measured over a range from 10 to greater than 10⁵, to an accuracy of better than ± 20%. The absorption edge was found to be strongly polarization-dependent.

Detailed analyses are presented of all three experimental techniques used. Experimentally determined values of the optical constants are presented in graphical form.

Chemical and electrochemical investigations of cobalt cyanide and ruthenium ammine complexes

Part I.

The stoichiometry and kinetics of the reaction between Co(CN₅H^3- and HgX₂ (X = CN, OH) have been investigated. The products of the reaction are two new complexes, [(NC)₅Co-HgX]^3- and [(NC)₅Co-Hg-Co(CN)₅]^6-, whose spectra are reported. The kinetic measurements produced a value for the forward rate constant of the reaction Co(CN)₅H^3- + OH^- k₁/k_-1 Co(CN)₅^4- +H₂O, k1 = (9.7 ± 0.8) x 10^-2 M^-1 sec^-1 at 24°C, and an equilibrium constant for the reaction K = 10^-6 M^-1.

Part II.

Unusually large and sharp "adsorption waves" appear in cyclic voltammograms of Co(CN)₅^3- and several cobalt(III) pentacyano complexes at stationary mercury electrodes. The nature of the adsorbed species and the reasons for the absence of the adsorption waves in polarograms taken with a d.m.e. have been examined. The data are compatible with the adsorption, in all cases, of a coordinatively unsaturated cobalt(II) complex, Co(CN)₄^2-, by means of a cobalt-mercury bond. When the resulting adsorbed complex is reduced, a series of subsequent chemical and electrode reactions is initiated in which three faradays of charge are consumed for each mole of adsorbed complex. The adsorption of the anionic complex strongly retards the reduction of other negatively charged complexes.

Part III.

A number of formal redox potentials for Ru^III (NH₃)₅L + e = Ru^II (NH₃)₅L and Ru^III(NH₃)₄L₂ + e = Ru^II (NH₃)₄L₂ (where L is various ligands) has been measured by cyclic voltammetry, potentiometry, and polarography and are discussed in terms of the properties of the ligands, such as π-accepting capability. Reduction of coordinated pyrazine in the complexes, Ru(NH₃)₅ Pz²⁺, cis- and trans-Ru(NH₃)₄Pz₂²⁺, on a mercury electrode has been observed. The behavior of this reduction in various acidity of the solution as well as the reoxidation of the reduction products are discussed.