I. Rigid body penetration into brittle materials. II. Phase change effect on shock wave propagation

Part I.

We have developed a technique for measuring the depth time history of rigid body penetration into brittle materials (hard rocks and concretes) under a deceleration of ~ 10⁵ g. The technique includes bar-coded projectile, sabot-projectile separation, detection and recording systems. Because the technique can give very dense data on penetration depth time history, penetration velocity can be deduced. Error analysis shows that the technique has a small intrinsic error of ~ 3-4 % in time during penetration, and 0.3 to 0.7 mm in penetration depth. A series of 4140 steel projectile penetration into G-mixture mortar targets have been conducted using the Caltech 40 mm gas/ powder gun in the velocity range of 100 to 500 m/s.

We report, for the first time, the whole depth-time history of rigid body penetration into brittle materials (the G-mixture mortar) under 10⁵ g deceleration. Based on the experimental results, including penetration depth time history, damage of recovered target and projectile materials and theoretical analysis, we find:

1. Target materials are damaged via compacting in the region in front of a projectile and via brittle radial and lateral crack propagation in the region surrounding the penetration path. The results suggest that expected cracks in front of penetrators may be stopped by a comminuted region that is induced by wave propagation. Aggregate erosion on the projectile lateral surface is < 20% of the final penetration depth. This result suggests that the effect of lateral friction on the penetration process can be ignored.

2. Final penetration depth, P_max, is linearly scaled with initial projectile energy per unit cross-section area, e_s , when targets are intact after impact. Based on the experimental data on the mortar targets, the relation is P_max(mm) 1.15e_s (J/mm² ) + 16.39.

3. Estimation of the energy needed to create an unit penetration volume suggests that the average pressure acting on the target material during penetration is ~ 10 to 20 times higher than the unconfined strength of target materials under quasi-static loading, and 3 to 4 times higher than the possible highest pressure due to friction and material strength and its rate dependence. In addition, the experimental data show that the interaction between cracks and the target free surface significantly affects the penetration process.

4. Based on the fact that the penetration duration, t_max, increases slowly with e_s and does not depend on projectile radius approximately, the dependence of t_max on projectile length is suggested to be described by t_max(μs) = 2.08e_s (J/mm² + 349.0 x m/(πR²), in which m is the projectile mass in grams and R is the projectile radius in mm. The prediction from this relation is in reasonable agreement with the experimental data for different projectile lengths.

5. Deduced penetration velocity time histories suggest that whole penetration history is divided into three stages: (1) An initial stage in which the projectile velocity change is small due to very small contact area between the projectile and target materials; (2) A steady penetration stage in which projectile velocity continues to decrease smoothly; (3) A penetration stop stage in which projectile deceleration jumps up when velocities are close to a critical value of ~ 35 m/s.

6. Deduced averaged deceleration, a, in the steady penetration stage for projectiles with same dimensions is found to be a(g) = 192.4v + 1.89 x 10⁴, where v is initial projectile velocity in m/s. The average pressure acting on target materials during penetration is estimated to be very comparable to shock wave pressure.

7. A similarity of penetration process is found to be described by a relation between normalized penetration depth, P/P_max, and normalized penetration time, t/t_max, as P/P_max = f(t/t_max, where f is a function of t/t_max. After f(t/t_max is determined using experimental data for projectiles with 150 mm length, the penetration depth time history for projectiles with 100 mm length predicted by this relation is in good agreement with experimental data. This similarity also predicts that average deceleration increases with decreasing projectile length, that is verified by the experimental data.

8. Based on the penetration process analysis and the present data, a first principle model for rigid body penetration is suggested. The model incorporates the models for contact area between projectile and target materials, friction coefficient, penetration stop criterion, and normal stress on the projectile surface. The most important assumptions used in the model are: (1) The penetration process can be treated as a series of impact events, therefore, pressure normal to projectile surface is estimated using the Hugoniot relation of target material; (2) The necessary condition for penetration is that the pressure acting on target materials is not lower than the Hugoniot elastic limit; (3) The friction force on projectile lateral surface can be ignored due to cavitation during penetration. All the parameters involved in the model are determined based on independent experimental data. The penetration depth time histories predicted from the model are in good agreement with the experimental data.

9. Based on planar impact and previous quasi-static experimental data, the strain rate dependence of the mortar compressive strength is described by σ_f/σ⁰_f = exp(0.0905(log(έ/έ_0) ^1.14, in the strain rate range of 10^-7/s to 10³/s (σ⁰_f and έ are reference compressive strength and strain rate, respectively). The non-dispersive Hugoniot elastic wave in the G-mixture has an amplitude of ~ 0.14 GPa and a velocity of ~ 4.3 km/s.

Part II.

Stress wave profiles in vitreous GeO₂ were measured using piezoresistance gauges in the pressure range of 5 to 18 GPa under planar plate and spherical projectile impact. Experimental data show that the response of vitreous GeO₂ to planar shock loading can be divided into three stages: (1) A ramp elastic precursor has peak amplitude of 4 GPa and peak particle velocity of 333 m/s. Wave velocity decreases from initial longitudinal elastic wave velocity of 3.5 km/s to 2.9 km/s at 4 GPa; (2) A ramp wave with amplitude of 2.11 GPa follows the precursor when peak loading pressure is 8.4 GPa. Wave velocity drops to the value below bulk wave velocity in this stage; (3) A shock wave achieving final shock state forms when peak pressure is > 6 GPa. The Hugoniot relation is D = 0.917 + 1.711u (km/s) using present data and the data of Jackson and Ahrens [1979] when shock wave pressure is between 6 and 40 GPa for ρ₀ = 3.655 gj cm³ . Based on the present data, the phase change from 4-fold to 6-fold coordination of Ge⁺⁴ with O^-2 in vitreous GeO₂ occurs in the pressure range of 4 to 15 ± 1 GPa under planar shock loading. Comparison of the shock loading data for fused SiO₂ to that on vitreous GeO₂ demonstrates that transformation to the rutile structure in both media are similar. The Hugoniots of vitreous GeO₂ and fused SiO₂ are found to coincide approximately if pressure in fused SiO₂ is scaled by the ratio of fused SiO₂to vitreous GeO₂ density. This result, as well as the same structure, provides the basis for considering vitreous Ge0₂ as an analogous material to fused SiO₂ under shock loading. Experimental results from the spherical projectile impact demonstrate: (1) The supported elastic shock in fused SiO₂ decays less rapidly than a linear elastic wave when elastic wave stress amplitude is higher than 4 GPa. The supported elastic shock in vitreous GeO₂ decays faster than a linear elastic wave; (2) In vitreous GeO₂ , unsupported shock waves decays with peak pressure in the phase transition range (4-15 GPa) with propagation distance, x, as α 1/x^-3.35 , close to the prediction of Chen et al. [1998]. Based on a simple analysis on spherical wave propagation, we find that the different decay rates of a spherical elastic wave in fused SiO₂ and vitreous GeO₂ is predictable on the base of the compressibility variation with stress under one-dimensional strain condition in the two materials.

Analysis and optimization of stress wave propagation in two-dimensional granular crystals with defects

Granular crystals are compact periodic assemblies of elastic particles in Hertzian contact whose dynamic response can be tuned from strongly nonlinear to linear by the addition of a static precompression force. This unique feature allows for a wide range of studies that include the investigation of new fundamental nonlinear phenomena in discrete systems such as solitary waves, shock waves, discrete breathers and other defect modes. In the absence of precompression, a particularly interesting property of these systems is their ability to support the formation and propagation of spatially localized soliton-like waves with highly tunable properties. The wealth of parameters one can modify (particle size, geometry and material properties, periodicity of the crystal, presence of a static force, type of excitation, etc.) makes them ideal candidates for the design of new materials for practical applications. This thesis describes several ways to optimally control and tailor the propagation of stress waves in granular crystals through the use of heterogeneities (interstitial defect particles and material heterogeneities) in otherwise perfectly ordered systems. We focus on uncompressed two-dimensional granular crystals with interstitial spherical intruders and composite hexagonal packings and study their dynamic response using a combination of experimental, numerical and analytical techniques. We first investigate the interaction of defect particles with a solitary wave and utilize this fundamental knowledge in the optimal design of novel composite wave guides, shock or vibration absorbers obtained using gradient-based optimization methods.

Formal languages, part theory, and change

A general definition of interpreted formal language is presented. The notion “is a part of" is formally developed and models of the resulting part theory are used as universes of discourse of the formal languages. It is shown that certain Boolean algebras are models of part theory.

With this development, the structure imposed upon the universe of discourse by a formal language is characterized by a group of automorphisms of the model of part theory. If the model of part theory is thought of as a static world, the automorphisms become the changes which take place in the world. Using this formalism, we discuss a notion of abstraction and the concept of definability. A Galois connection between the groups characterizing formal languages and a language-like closure over the groups is determined.

It is shown that a set theory can be developed within models of part theory such that certain strong formal languages can be said to determine their own set theory. This development is such that for a given formal language whose universe of discourse is a model of part theory, a set theory can be imbedded as a submodel of part theory so that the formal language has parts which are sets as its discursive entities.