Schottky barriers on compound semiconductors: I. HgSe highly electronegative contacts. II. Au Schottky barriers on n-Ga_(1-x)Al_xAs

I. HgSe is deposited on various semiconductors, forming a semimetal/semiconductor "Schottky barrier" structure. Polycrystalline, evaporated HgSe produces larger Schottky barrier heights on n-type semiconductors than does Au, the most electronegative of the elemental metals. The barrier heights are about 0.5 eV greater than those of Au on ionic semiconductors such as ZnS, and 0.1 to 0.2 eV greater for more covalently bonded semiconductors. A novel structure,which is both a lattice matched heterostructure and a Schottky barrier, is fabricated by epitaxial growth of HgSe on CdSe using hydrogen transport CVD. The Schottky barrier height for this structure is 0.73 ± 0.02 eV, as measured by the photoresponse method. This uncertainty is unusually small; and the magnitude is greater by about a quarter volt than is achievable with Au, in qualitative agreement with ionization potential arguments.

II . The Schottky barrier height of Au on chemically etched n-Ga_1-x Al_xAs was measured as a function of x. As x increases, the barrier height rises to a value of about 1.2 eV at x ≈ 0.45 , then decreases to about 1.0 eV as x approaches 0.83. The barrier height deviates in a linear way from the value predicted by the "common anion" rule as the AlAs mole fraction increases. This behavior is related to chemical reactivity of the Ga_1-x Al_xAs surface.

I. A recirculating charged-couple device. II. The mercury selenide on N-silicon Schottky barrier

A recirculating charge-coupled device structure has been devised. Entrance and exit gates allow a signal to be admitted, recirculated a given number of times, and then examined. In this way a small device permits simulation of a very long shift register without passing the signal through input and output diffusions. An oscilloscope motion picture demonstrating degradation of an actual circulating signal has been made. The performance of the device in simulating degradation of a signal by a very long shift register is well fit by a simple model based on transfer inefficiency.

Electrical properties of the mercury selenide on n-type chemically-cleaned silicon Schottky barrier have been studied. Barrier heights measured were 0.96 volts for the photoresponse technique and 0.90 volts for the current-voltage technique. These are the highest barriers yet reported on n-type silicon.

Conduction through thin titanium dioxide films

Conduction through TiO₂ films of thickness 100 to 450 Å have been investigated. The samples were prepared by either anodization of Ti evaporation of TiO₂, with Au or Al evaporated for contacts. The anodized samples exhibited considerable hysteresis due to electrical forming, however it was possible to avoid this problem with the evaporated samples from which complete sets of experimental results were obtained and used in the analysis. Electrical measurements included: the dependence of current and capacitance on dc voltage and temperature; the dependence of capacitance and conductance on frequency and temperature; and transient measurements of current and capacitance. A thick (3000 Å) evaporated TiO₂ film was used for measuring the dielectric constant (27.5) and the optical dispersion, the latter being similar to that for rutile. An electron transmission diffraction pattern of a evaporated film indicated an essentially amorphous structure with a short range order that could be related to rutile. Photoresponse measurements indicated the same band gap of about 3 ev for anodized and evaporated films and reduced rutile crystals and gave the barrier energies at the contacts.

The results are interpreted in a self consistent manner by considering the effect of a large impurity concentration in the films and a correspondingly large ionic space charge. The resulting potential profile in the oxide film leads to a thermally assisted tunneling process between the contacts and the interior of the oxide. A general relation is derived for the steady state current through structures of this kind. This in turn is expressed quantitatively for each of two possible limiting types of impurity distributions, where one type gives barriers of an exponential shape and leads to quantitative predictions in c lose agreement with the experimental results. For films somewhat greater than 100 Å, the theory is formulated essentially in terms of only the independently measured barrier energies and a characteristic parameter of the oxide that depends primarily on the maximum impurity concentration at the contacts. A single value of this parameter gives consistent agreement with the experimentally observed dependence of both current and capacitance on dc voltage and temperature, with the maximum impurity concentration found to be approximately the saturation concentration quoted for rutile. This explains the relative insensitivity of the electrical properties of the films on the exact conditions of formation.