Developing and characterizing bulk metallic glasses for extreme applications

Metallic glasses have typically been treated as a “one size fits all” type of material. Every alloy is considered to have high strength, high hardness, large elastic limits, corrosion resistance, etc. However, similar to traditional crystalline materials, properties are strongly dependent upon the constituent elements, how it was processed, and the conditions under which it will be used. An important distinction which can be made is between metallic glasses and their composites. Charpy impact toughness measurements are performed to determine the effect processing and microstructure have on bulk metallic glass matrix composites (BMGMCs). Samples are suction cast, machined from commercial plates, and semi-solidly forged (SSF). The SSF specimens have been found to have the highest impact toughness due to the coarsening of the dendrites, which occurs during the semi-solid processing stages. Ductile to brittle transition (DTBT) temperatures are measured for a BMGMC. While at room temperature the BMGMC is highly toughened compared to a fully glassy alloy, it undergoes a DTBT by 250 K. At this point, its impact toughness mirrors that of the constituent glassy matrix. In the following chapter, BMGMCs are shown to have the capability of being capacitively welded to form single, monolithic structures. Shear measurements are performed across welded samples, and, at sufficient weld energies, are found to retain the strength of the parent alloy. Cross-sections are inspected via SEM and no visible crystallization of the matrix occurs.

Next, metallic glasses and BMGMCs are formed into sheets and eggbox structures are tested in hypervelocity impacts. Metallic glasses are ideal candidates for protection against micrometeorite orbital debris due to their high hardness and relatively low density. A flat single layer, flat BMG is compared to a BMGMC eggbox and the latter creates a more diffuse projectile cloud after penetration. A three tiered eggbox structure is also tested by firing a 3.17 mm aluminum sphere at 2.7 km/s at it. The projectile penetrates the first two layers, but is successfully contained by the third.

A large series of metallic glass alloys are created and their wear loss is measured in a pin on disk test. Wear is found to vary dramatically among different metallic glasses, with some considerably outperforming the current state-of-the-art crystalline material (most notably Cu₄₃Zr₄₃Al₇Be₇). Others, on the other hand, suffered extensive wear loss. Commercially available Vitreloy 1 lost nearly three times as much mass in wear as alloy prepared in a laboratory setting. No conclusive correlations can be found between any set of mechanical properties (hardness, density, elastic, bulk, or shear modulus, Poisson’s ratio, frictional force, and run in time) and wear loss. Heat treatments are performed on Vitreloy 1 and Cu₄₃Zr₄₃Al₇Be₇. Anneals near the glass transition temperature are found to increase hardness slightly, but decrease wear loss significantly. Crystallization of both alloys leads to dramatic increases in wear resistance. Finally, wear tests under vacuum are performed on the two alloys above. Vitreloy 1 experiences a dramatic decrease in wear loss, while Cu₄₃Zr₄₃Al₇Be₇ has a moderate increase. Meanwhile, gears are fabricated through three techniques: electrical discharge machining of 1 cm by 3 mm cylinders, semisolid forging, and copper mold suction casting. Initial testing finds the pin on disk test to be an accurate predictor of wear performance in gears.

The final chapter explores an exciting technique in the field of additive manufacturing. Laser engineered net shaping (LENS) is a method whereby small amounts of metallic powders are melted by a laser such that shapes and designs can be built layer by layer into a final part. The technique is extended to mixing different powders during melting, so that compositional gradients can be created across a manufactured part. Two compositional gradients are fabricated and characterized. Ti 6Al¬ 4V to pure vanadium was chosen for its combination of high strength and light weight on one end, and high melting point on the other. It was inspected by cross-sectional x-ray diffraction, and only the anticipated phases were present. 304L stainless steel to Invar 36 was created in both pillar and as a radial gradient. It combines strength and weldability along with a zero coefficient of thermal expansion material. Only the austenite phase is found to be present via x-ray diffraction. Coefficient of thermal expansion is measured for four compositions, and it is found to be tunable depending on composition.

Zn-VI/Cu2O Heterojunctions for Earth-Abundant Photovoltaics

The need for sustainable energy production motivates the study of photovoltaic materials, which convert energy from sunlight directly into electricity. This work has focused on the development of Cu₂O as an earth-abundant solar absorber due to the abundance of its constituent elements in the earth's crust, its suitable band gap, and its potential for low cost processing. Crystalline wafers of Cu₂O with minority carrier diffusion lengths on the order of microns can be manufactured in a uniquely simple fashion — directly from copper foils by thermal oxidation. Furthermore, Cu₂O has an optical band gap of 1.9 eV, which gives it a detailed balance energy conversion efficiency of 24.7% and the possibility for an independently connected Si/Cu₂O dual junction with a detailed balance efficiency of 44.3%.

However, the highest energy conversion efficiency achieved in a photovoltaic device with a Cu₂O absorber layer is currently only 5.38% despite the favorable optical and electronic properties listed above. There are several challenges to making a Cu₂O photovoltaic device, including an inability to dope the material, its relatively low chemical stability compared to other oxides, and a lack of suitable heterojunction partners due to an unusually small electron affinity. We have addressed the low chemical stability, namely the fact that Cu₂O is an especially reactive oxide due to its low enthalpy of formation (ΔH_f⁰ = -168.7 kJ/mol), by developing a novel surface preparation technique. We have addressed the lack of suitable heterojunction partners by investigating the heterojunction band alignment of several Zn-VI materials with Cu₂O. Finally, We have addressed the typically high series resistance of Cu₂O wafers by developing methods to make very thin, bulk Cu₂O, including devices on Cu₂O wafers as thin as 20 microns. Using these methods we have been able to achieve photovoltages over 1 V, and have demonstrated the potential of a new heterojunction material, Zn(O,S).