Adsorption of Pb(II) and Cu(II) on α-quartz from aqueous solutions: influence of pH, ionic strength, and complexing ligands

Adsorption of aqueous Pb(II) and Cu(II) on α-quartz was studied as a function of time, system surface area, and chemical speciation. Experimental systems contained sodium as a major cation, hydroxide, carbonate, and chloride as major anions, and covered the pH range 4 to 8. In some cases citrate and EDTA were added as representative organic complexing agents. The adsorption equilibria were reached quickly, regardless of the system surface area. The positions of the adsorption equilibria were found to be strongly dependent on pH, ionic strength and concentration of citrate and EDTA. The addition of these non-adsorbing ligands resulted in a competition between chelation and adsorption. The experimental work also included the examination of the adsorption behavior of the doubly charged major cations Ca(II) and Mg(II) as a function of pH.

The theoretical description of the experimental systems was obtained by means of chemical equilibrium-plus-adsorption computations using two adsorption models: one mainly electrostatic (the James-Healy Model), and the other mainly chemical (the Ion Exchange-Surface Complex Formation Model). Comparisons were made between these two models.

The main difficulty in the theoretical predictions of the adsorption behavior of Cu(II) was the lack of the reliable data for the second hydrolysis constant(*β_2) The choice of the constant was made on the basis of potentiometric titratlons of Cu^(2+)

The experimental data obtained and the resulting theoretical observations were applied in models of the chemical behavior of trace metals in fresh oxic waters, with emphasis on Pb(II) and Cu(II).

Succinate:ubiquinone oxidoreductase from Paracoccus denitrificans and particulate methane monooxygenase from Methylococcus capsulatus (Bath): experimental and theoretical EPR studies of the metal cofactors

This thesis summarizes the application of conventional and modern electron paramagnetic resonance (EPR) techniques to establish proximity relationships between paramagnetic metal centers in metalloproteins and between metal centers and magnetic ligand nuclei in two important and timely membrane proteins: succinate:ubiquinone oxidoreductase (SQR) from Paracoccus denitrificans and particulate methane monooxygenase (pMMO) from Methylococcus capsulatus. Such proximity relationships are thought to be critical to the biological function and the associated biochemistry mediated by the metal centers in these proteins. A mechanistic understanding of biological function relies heavily on structure-function relationships and the knowledge of how molecular structure and electronic properties of the metal centers influence the reactivity in metalloenzymes. EPR spectroscopy has proven to be one of the most powerful techniques towards obtaining information about interactions between metal centers as well as defining ligand structures. SQR is an electron transport enzyme wherein the substrates, organic and metallic cofactors are held relatively far apart. Here, the proximity relationships of the metallic cofactors were studied through their weak spin-spin interactions by means of EPR power saturation and electron spin-lattice (T_1) measurements, when the enzyme was poised at designated reduction levels. Analysis of the electron T_1 measurements for the S-3 center when the b-heme is paramagnetic led to a detailed analysis of the dipolar interactions and distance determination between two interacting metal centers. Studies of ligand environment of the metal centers by electron spin echo envelope modulation (ESEEM) spectroscopy resulted in the identication of peptide nitrogens as coupled nuclei in the environment of the S-1 and S-3 centers.

Finally, an EPR model was developed to describe the ferromagnetically coupled trinuclear copper clusters in pMMO when the enzyme is oxidized. The Cu(II) ions in these clusters appear to be strongly exchange coupled, and the EPR is consistent with equilateral triangular arrangements of type 2 copper ions. These results offer the first glimpse of the magneto-structural correlations for a trinuclear copper cluster of this type, which, until the work on pMMO, has had no precedent in the metalloprotein literature. Such trinuclear copper clusters are even rare in synthetic models.

I. Reactively sputtered Ti-Si-N thin films for diffusion barrier applications. II. Oxidation, diffusion and crystallization of an amorphous Zr_(60)Al_(15)Ni_(25) alloy.

Films of Ti-Si-N obtained by reactively sputtering a TiSi_2, a Ti_5Si_3, or a Ti_3Si target are either amorphous or nanocrystalline in structure. The atomic density of some films exceeds 10^23 at./cm^3. The room-temperature resistivity of the films increases with the Si and the N content. A thermal treatment in vacuum at 700 °C for 1 hour decreases the resistivity of the Ti-rich films deposited from the Ti_5Si_3 or the Ti_3Si target, but increases that of the Si-rich films deposited from the TiSi_2 target when the nitrogen content exceeds about 30 at. %.

Ti_(34)Si_(23)N_(43) deposited from the Ti_5Si_3 target is an excellent diffusion barrier between Si and Cu. This film is a mixture of nanocrystalline TiN and amorphous SiN_x. Resistivity measurement from 80 K to 1073 K reveals that this film is electrically semiconductor-like as-deposited, and that it becomes metal-like after an hour annealing at 1000 °C in vacuum. A film of about 100 nm thick, with a resistivity of 660 µΩcm, maintains the stability of Si n+p shallow junction diodes with a 400 nm Cu overlayer up to 850 °C upon 30 min vacuum annealing. When used between Si and Al, the maximum temperature of stability is 550 °C for 30 min. This film can be etched in a CF_4/O_2 plasma.

The amorphous ternary metallic alloy Zr_(60)Al_(15)Ni_(25) was oxidized in dry oxygen in the temperature range 310 °C to 410 °C. Rutherford backscattering and cross-sectional transmission electron microscopy studies suggest that during this treatment an amorphous layer of zirconium-aluminum-oxide is formed at the surface. Nickel is depleted from the oxide and enriched in the amorphous alloy below the oxide/alloy interface. The oxide layer thickness grows parabolically with the annealing duration, with a transport constant of 2.8x10^(-5) m^2/s x exp(-1.7 eV/kT). The oxidation rate is most likely controlled by the Ni diffusion in the amorphous alloy.

At later stages of the oxidation process, precipitates of nanocrystalline ZrO_2 appear in the oxide near the interface. Finally, two intermetallic phases nucleate and grow simultaneously in the alloy, one at the interface and one within the alloy.

I. Nickel-Exchanged Zincosilicate Catalysts for the Oligomerization of Propylene and II. Organic SDA-Free Catalysts for the Methanol-to-Olefins Reaction

Nickel-containing catalysts are developed to oligomerize light olefins. Two nickel-containing zincosilicates (Ni-CIT-6 and Ni-Zn-MCM-41) and two nickel-containing aluminosilicates (Ni-HiAl-BEA and Ni-USY) are synthesized as catalysts to oligomerize propylene into C_3n (C₆ and C₉) products. All catalysts oligomerize propylene, with the zincosilicates demonstrating higher average selectivities to C_3n products, likely due to the reduced acidity of the Zn heteroatom.

To test whether light alkanes can be incorporated into this oligomerization reaction, a supported homogeneous catalyst is combined with Ni-containing zincosilicates. The homogeneous catalyst is included to provide dehydrogenation/hydrogenation functions. When this tandem catalyst system is evaluated using a propylene/n-butane feed, no significant integration of alkanes are observed.

Ni-containing zincosilicates are reacted with 1-butene and an equimolar propylene/1-butene mixture to study other olefinic feeds. Further, other divalent metal cations such as Mn²⁺, Co²⁺, Cu²⁺, and Zn²⁺ are exchanged onto CIT-6 samples to investigate stability and potential use for other reactions. Co-CIT-6 oligomerizes propylene, albeit less effectively than Ni-CIT-6. The other M-CIT-6 samples, while not able to oligomerize light olefins, may be useful for other reactions, such as deNO_x.

Molecular sieves are synthesized, characterized, and used to catalyze the methanol-to-olefins (MTO) reaction. The Al concentration in SSZ-13 samples is varied to investigate the effect of Al number on MTO reactivity when compared to a SAPO-34 sample with only isolated Si Brønsted acid sites. These SSZ-13 samples display reduced transient selectivity behavior and extended reaction lifetimes as Si/Al increases; attributable to fewer paired Al sites. MTO reactivity for the higher Si/Al SSZ-13s resembles the SAPO-34 sample, suggesting that both catalysts owe their stable reaction behavior to isolated Brønsted acid sites.

Zeolites CHA and RHO are prepared without the use of organic structure-directing agents (OSDAs), dealuminated by steam treatments (500°C-800°C), and evaluated as catalysts for the MTO reaction. The effects of temperature and steam partial pressure during steaming are investigated. X-ray diffraction (XRD) and Ar physisorption show that steaming causes partial structural collapse of the zeolite, with degradation increasing with steaming temperature. ²⁷Al MAS NMR spectra of steamed materials reveal the presence of tetrahedral, pentacoordinate, and hexacoordinate aluminum.

Proton forms of as-synthesized CHA (Si/Al=2.4) and RHO (Si/Al=2.8) rapidly deactivate under MTO testing conditions (400°C, atmospheric pressure). CHA samples steamed at 600°C performed best among samples tested, showing increased olefin selectivities and catalyst lifetime. Acid washing these steamed samples further improved activity. Reaction results for RHO were similar to CHA, with the RHO sample steamed at 800°C producing the highest light olefin selectivities. Catalyst lifetime and C₂-C₃ olefin selectivities increase with increasing reaction temperature for both CHA-type and RHO-type steamed samples.