Evaluation of the reliability of commercial concentrator triple-junction solar cells by means of accelerated life tests (ALT)

A temperature accelerated life test on commercial concentrator lattice-matched GaInP/GaInAs/Ge triple-junction solar cells has been carried out. The solar cells have been tested at three different temperatures: 119, 126 and 164 °C and the nominal photo-current condition (820 X) has been emulated by injecting current in darkness. All the solar cells have presented catastrophic failures. The failure distributions at the three tested temperatures have been fitted to an Arrhenius-Weibull model. An Arrhenius activation energy of 1.58 eV was determined from the fit. The main reliability functions and parameters (reliability function, instantaneous failure rate, mean time to failure, warranty time) of these solar cells at the nominal working temperature (80 °C) have been obtained. The warranty time obtained for a failure population of 5 % has been 69 years. Thus, a long-term warranty could be offered for these particular solar cells working at 820 X, 8 hours per day at 80 °C.

Mechanical behavior of tungsten-vanadium-lanthana alloys as function of temperature

The mechanical behavior of three tungsten (W) alloys with vanadium (V) and lanthana (La2O3) additions (W–4%V, W–1%La2O3, W–4%V–1%La2O3) processed by hot isostatic pressing (HIP) have been compared with pure-W to analyze the influence of the dopants. Mechanical characterization was performed by three point bending (TPB) tests in an oxidizing air atmosphere and temperature range between 77 (immersion tests in liquid nitrogen) and 1273 K, through which the fracture toughness, flexural strength, and yield strength as function of temperature were obtained. Results show that the V and La2O3 additions improve the mechanical properties and oxidation behavior, respectively. Furthermore, a synergistic effect of both dopants results in an extraordinary increase of the flexure strength, fracture toughness and resistance to oxidation compared to pure-W, especially at higher temperatures. In addition, a new experimental method was developed to obtain a very small notch tip radius (around 5–7 μm) and much more similar to a crack through the use of a new machined notch. The fracture toughness results were lower than those obtained with traditional machining of the notch, which can be explained with electron microscopy, observations of deformation in the rear part of the notch tip. Finally, scanning electron microscopy (SEM) examination of the microstructure and fracture surfaces was used to determine and analyze the relationship between the macroscopic mechanical properties and the micromechanisms of failure involved, depending on the temperature and the dispersion of the alloy.

Determination of the hoop fracture properties of unirradiated hydrogen-charged nuclear fuel cladding from ring compression tests

In this work, a new methodology is devised to obtain the fracture properties of nuclear fuel cladding in the hoop direction. The proposed method combines ring compression tests and a finite element method that includes a damage model based on cohesive crack theory, applied to unirradiated hydrogen-charged ZIRLOTM nuclear fuel cladding. Samples with hydrogen concentrations from 0 to 2000 ppm were tested at 20 �C. Agreement between the finite element simulations and the experimental results is excellent in all cases. The parameters of the cohesive crack model are obtained from the simulations, with the fracture energy and fracture toughness being calculated in turn. The evolution of fracture toughness in the hoop direction with the hydrogen concentration (up to 2000 ppm) is reported for the first time for ZIRLOTM cladding. Additionally, the fracture micromechanisms are examined as a function of the hydrogen concentration. In the as-received samples, the micromechanism is the nucleation, growth and coalescence of voids, whereas in the samples with 2000 ppm, a combination of cuasicleavage and plastic deformation, along with secondary microcracking is observed.

Mechanical behavior of alkali-cement as function of the temperature.

This investigation reports on a comparative study of the mechanical behavior at different temperatures of three different alkali-activated fly ash pastes chemically activated using sodium silicate. A control Portland cement (OPC) was used as a reference. In an attempt to simulate the conditions prevailing in the event of accidental fire, post-thermal mechanical tests were performed to determine the residual strength. It has therefore been established that FA based cements can be fabricated for construction purposes and these materials have great potential for fire resistance applications.

Evaluation of the reliability of high concentrator GaAs solar cells by means of temperature accelerated aging tests

ABSTRACT Evaluating the reliability, warranty period, and power degradation of high concentration solar cells is crucial to introducing this new technology to the market. The reliability of high concentration GaAs solar cells, as measured in temperature accelerated life tests, is described in this paper. GaAs cells were tested under high thermal accelerated conditions that emulated operation under 700 or 1050 suns over a period exceeding 10 000 h. Progressive power degradation was observed, although no catastrophic failures occurred. An Arrhenius activation energy of 1.02 eV was determined from these tests. The solar cell reliability [R(t)] under working conditions of 65°C was evaluated for different failure limits (1–10% power loss). From this reliability function, the mean time to failure and the warranty time were evaluated. Solar cell temperature appeared to be the primary determinant of reliability and warranty period, with concentration being the secondary determinant. A 30-year warranty for these 1 mm2-sized GaAs cells (manufactured according to a light emitting diode-like approach) may be offered for both cell concentrations (700 and 1050 suns) if the solar cell is operated at a working temperature of 65°C.

Mechanical characterisation of tungsten-1wt.% yttrium oxide as a function of temperature and atmosphere

This study evaluates the mechanical behaviour of an Y2O3-dispersed tungsten (W) alloy and compares it to a pure W reference material. Both materials were processed via mechanical alloying (MA) and subsequent hot isostatic pressing (HIP). We performed non-standard three-point bending (TPB) tests in both an oxidising atmosphere and vacuum across a temperature range from 77 K, obtained via immersion in liquid nitrogen, to 1473 K to determine the mechanical strength, yield strength and fracture toughness. This research aims to evaluate how the mechanical behaviour of the alloy is affected by oxides formed within the material at high temperatures, primarily from 873 K, when the materials undergo a massive thermal degradation. The results indicate that the alloy is brittle to a high temperature (1473 K) under both atmospheres and that the mechanical properties degrade significantly above 873 K. We also used Vickers microhardness tests and the dynamic modulus by impulse excitation technique (IET) to determine the elastic modulus at room temperature. Moreover, we performed nanoindentation tests to determine the effect of size on the hardness and elastic modulus; however, no significant differences were found. Additionally, we calculated the relative density of the samples to assess the porosity of the alloy. Finally, we analysed the microstructure and fracture surfaces of the tested materials via field emission scanning electron microscopy (FE-SEM) and transmission electron microscopy (TEM). In this way, the relationship between the macroscopic mechanical properties and micromechanisms of failure could be determined based on the temperature and oxides formed

Mechanical behavior and deformation micromechanisms of polypropylene nonwoven fabrics as a function of temperature and strain rate

The mechanical behavior and the deformation and failure micromechanisms of a thermally-bonded polypropylene nonwoven fabric were studied as a function of temperature and strain rate. Mechanical tests were carried out from 248 K (below the glass transition temperature) up to 383 K at strain rates in the range ≈10−3 s−1 to 10−1 s−1. In addition, individual fibers extracted from the nonwoven fabric were tested under the same conditions. Micromechanisms of deformation and failure at the fiber level were ascertained by means of mechanical tests within the scanning electron microscope while the strain distribution at the macroscopic level upon loading was determined by means of digital image correlation. It was found that the nonwoven behavior was mainly controlled by the properties of the fibers and of the interfiber bonds. Fiber properties determined the nonlinear behavior before the peak load while the interfiber bonds controlled the localization of damage after the peak load. The influence of these properties on the strength, ductility and energy absorbed during deformation is discussed from the experimental observations.

New insights into the regulation of NADPH oxidase dependent reactive oxygen species signaling during the plant immune response

Las NADPH oxidasas de plantas, denominadas “respiratory burst oxidase homologues” (RBOHs), producen especies reactivas del oxígeno (ROS) que median un amplio rango de funciones. En la célula vegetal, el ajuste preciso de la producción de ROS aporta la especificidad de señal para generar una respuesta apropiada ante las amenazas ambientales. RbohD y RbohF, dos de los diez genes Rboh de Arabidopsis, son pleiotrópicos y median diversos procesos fisiológicos en respuesta a patógenos. El control espacio-temporal de la expresión de los genes RbohD y RbohF podría ser un aspecto crítico para determinar la multiplicidad de funciones de estas oxidasas. Por ello, generamos líneas transgénicas de Arabidopsis con fusiones de los promoters de RbohD y RbohF a los genes delatores de la B-glucuronidasa y la luciferasa. Estas líneas fueron empleadas para revelar el patrón de expresión diferencial de RbohD y RbohF durante la respuesta inmune de Arabidopsis a la bacteria patógena Pseudomonas syringae pv. tomato DC3000, el hongo necrótrofo Plectosphaerella cucumerina y en respuesta a señales relacionadas con la respuesta inmune. Nuestros experimentos revelan un patrón de expresión diferencial de los promotores de RbohD y RbohF durante el desarrollo de la planta y en la respuesta inmune de Arabidopsis. Además hemos puesto de manifiesto que existe una correlación entre el nivel de actividad de los promotores de RbohD y RbohF con la acumulación de ROS y el nivel de muerte celular en respuesta a patógenos. La expression de RbohD y RbohF también es modulada de manera diferencial en respuesta a patrones moleculares asociados a patógenos (PAMPs) y por ácido abscísico (ABA). Cabe destacar que, mediante una estrategia de intercambio de promotores, hemos revelado que la región promotora de RbohD, es necesaria para dirigir la producción de ROS en respuesta a P. cucumerina. Adicionalmente, la activación del promotor de RbohD en respuesta al aislado de P. cucumerina no adaptado a Arabidopsis 2127, nos llevó a realizar ensayos de susceptibilidad con el doble mutante rbohD rbohF que han revelado un papel desconocido de estas oxidasas en resistencia no-huesped. La interacción entre la señalización dependiente de las RBOHs y otros componentes de la respuesta inmune de plantas podría explicar también las distintas funciones que median estas oxidasas en relación con la respuesta inmune. Entre la gran cantidad de señales coordinadas con la actividad de las RBOHs, existen evidencias genéticas y farmacológicas que indican que las proteínas G heterotriméricas están implicadas en algunas de las rutas de señalización mediadas por ROS derivadas de los RBOHs en respuesta a señales ambientales. Por ello hemos estudiado la relación entre estas RBOH-NADPH oxidasas y AGB1, la subunidad β de las proteínas G heterotriméricas en la respuesta inmune de Arabidopsis. Análisis de epistasis indican que las proteínas G heterotriméricas están implicadas en distintas rutas de señalización en defensa mediadas por las RBOHs. Nuestros resultados ilustran la relación compleja entre la señalización mediada por las RBOHs y las proteínas G heterotriméricas, que varía en función de la interacción planta-patógeno analizada. Además, hemos explorado la posible asociación entre AGB1 con RBOHD y RBOHF en eventos tempranos de la respuesta immune. Cabe señalar que experimentos de coímmunoprecipitación apuntan a una posible asociación entre AGB1 y la kinasa citoplasmática reguladora de RBOHD, BIK1. Esto indica un posible mecanismo de control de la función de esta NADPH oxidase por AGB1. En conjunto, estos datos aportan nuevas perspectivas sobre cómo, a través del control transcripcional o mediante la interacción con las proteínas G heterotriméricas, las NADPH oxidases de plantas median la producción de ROS y la señalización por ROS en la respuesta inmune. Nuestro trabajo ejemplifica cómo la regulación diferencial de dos miembros de una familia multigénica, les permite realizar distintas funciones fisiológicas especializadas usando un mismo mecanismo enzimático. ABSTRACT The plant NADPH oxidases, termed respiratory burst oxidase homologues (RBOHs), produce reactive oxygen species (ROS) which mediate a wide range of functions. Fine tuning this ROS production provides the signaling specificity to the plant cell to produce the appropriate response to environmental threats. RbohD and RbohF, two of the ten Rboh genes present in Arabidopsis, are pleiotropic and mediate diverse physiological processes in response to pathogens. One aspect that may prove critical to determine the multiplicity of functions of RbohD and RbohF is the spatio-temporal control of their gene expression. Thus, we generated Arabidopsis transgenic lines with RbohD- and RbohF-promoter fusions to the β-glucuronidase and the luciferase reporter genes. These transgenics were employed to reveal RbohD and RbohF promoter activity during Arabidopsis immune response to the pathogenic bacterium Pseudomonas syringae pv tomato DC3000, the necrotrophic fungus Plectosphaerella cucumerina and in response to immunity-related cues. Our experiments revealed a differential expression pattern of RbohD and RbohF throughout plant development and during Arabidopsis immune response. Moreover, we observed a correlation between the level of RbohD and RbohF promoter activity, the accumulation of ROS and the amount of cell death in response to pathogens. RbohD and RbohF gene expression was also differentially modulated by pathogen associated molecular patterns and abscisic acid. Interestingly, a promoter-swap strategy revealed the requirement for the promoter region of RbohD to drive the production of ROS in response to P. cucumerina. Additionally, since the RbohD promoter was activated during Arabidopsis interaction with a non-adapted P. cucumerina isolate 2127, we performed susceptibility tests to this fungal isolate that uncovered a new role of these oxidases on non-host resistance. The interplay between RBOH-dependent signaling with other components of the plant immune response might also explain the different immunity-related functions mediated by these oxidases. Among the plethora of signals coordinated with RBOH activity, pharmacological and genetic evidence indicates that heterotrimeric G proteins are involved in some of the signaling pathways mediated by RBOH–derived ROS in response to environmental cues. Therefore, we analysed the interplay between these RBOH-NADPH oxidases and AGB1, the Arabidopsis β-subunit of heterotrimeric G proteins during Arabidopsis immune response. We carried out epistasis studies that allowed us to test the implication of AGB1 in different RBOH-mediated defense signaling pathways. Our results illustrate the complex relationship between RBOH and heterotrimeric G proteins signaling, that varies depending on the type of plant-pathogen interaction. Furthermore, we tested the potential association between AGB1 with RBOHD and RBOHF during early immunity. Interestingly, our co-immunoprecipitation experiments point towards an association of AGB1 and the RBOHD regulatory kinase BIK1, thus providing a putative mechanism in the control of the NADPH oxidase function by AGB1. Taken all together, these studies provide further insights into the role that transcriptional control or the interaction with heterotrimeric G-proteins have on RBOH-NADPH oxidase-dependent ROS production and signaling in immunity. Our work exemplifies how, through a differential regulation, two members of a multigenic family achieve specialized physiological functions using a common enzymatic mechanism.