Sputter optimization of AlN on diamond substrates for high frequency SAW resonators

The AlN/diamond structure is an attractive combination for SAW devices and its application at high frequencies. In this work, the synthesis of AlN thin films by reactive sputtering has been optimized on diamond substrates in order to process high frequency devices. Polished microcrystalline and as-grown nanocrystalline diamond substrates have been used to deposit AlN of different thickness under equal sputtering conditions. For the smoother substrates, the FWHM of the rocking curve of the (002) AlN peak varies from 3.8° to 2.7° with increasing power. SAW one port resonators have been fabricated on these films, whose electrical characterization (in terms of S11 parameters) is reported.

Fabrication of high frequency SAW resonators using AlN/Diamond/Si technology

The synthesis of AlN on diamond is a great challenge, not only because of the between an AlN/diamond interface, but also because of the high surface roughness of the diamond layers [8, 9]. In the case of microcrystalline diamond, the last problem was solved by polishing. However, polishing nanocrystalline diamond is not straightforward. For the diamond synthesis by CVD, silicon was used as a substrate. The diamond/Si interface presents a smoother diamond than the diamond/air interface. This paper reports on the fabrication of high frequency SAW resonators using AlN/Diamond/Si technology.

Estudios termodinámicos de los procesos de vitrificación en la crioconservación de germoplasma vegetal=Thermodynamic studies of vitrification processes in plant germplasm cryopreservation

En la actualidad, las técnicas de crioconservación poseen una importancia creciente para el almacenamiento a largo plazo de germoplasma vegetal. En las dos últimas décadas, estos métodos experimentaron un gran desarrollo y se han elaborado protocolos adecuados a diferentes sistemas vegetales, utilizando diversas estrategias como la vitrificación, la encapsulación-desecación con cuentas de alginato y el método de “droplet”-vitrificación. La presente tesis doctoral tiene como objetivo aumentar el conocimiento sobre los procesos implicados en los distintos pasos de un protocolo de crioconservación, en relación con el estado del agua presente en los tejidos y sus cambios, abordado mediante diversas técnicas biofísicas, principalmente calorimetría diferencial de barrido (DSC) y microscopía electrónica de barrido a baja temperatura (crio-SEM). En un primer estudio sobre estos métodos de crioconservación, se describen las fases de enfriamiento hasta la temperatura del nitrógeno líquido y de calentamiento hasta temperatura ambiente, al final del periodo de almacenamiento, que son críticas para la supervivencia del material crioconservado. Tanto enfriamiento como calentamiento deben ser realizados lo más rápidamente posible pues, aunque los bajos contenidos en agua logrados en etapas previas de los protocolos reducen significativamente las probabilidades de formación de hielo, éstas no son del todo nulas. En ese contexto, se analiza también la influencia de las velocidades de enfriamiento y calentamiento de las soluciones de crioconservación de plantas en sus parámetros termofísicos referente a la vitrificación, en relación su composición y concentración de compuestos. Estas soluciones son empleadas en la mayor parte de los protocolos actualmente utilizados para la crioconservación de material vegetal. Además, se estudia la influencia de otros factores que pueden determinar la estabilidad del material vitrificado, tales como en envejecimiento del vidrio. Se ha llevado a cabo una investigación experimental en el empleo del crio-SEM como una herramienta para visualizar el estado vítreo de las células y tejidos sometidos a los procesos de crioconservación. Se ha comparado con la más conocida técnica de calorimetría diferencial de barrido, obteniéndose resultados muy concordantes y complementarios. Se exploró también por estas técnicas el efecto sobre tejidos vegetales de la adaptación a bajas temperaturas y de la deshidratación inducida por los diferentes tratamientos utilizados en los protocolos. Este estudio permite observar la evolución biofísica de los sistemas en el proceso de crioconservación. Por último, se estudió la aplicación de películas de quitosano en las cuentas de alginato utilizadas en el protocolo de encapsulación. No se observaron cambios significativos en su comportamiento frente a la deshidratación, en sus parámetros calorimétricos y en la superficie de las cuentas. Su aplicación puede conferir propiedades adicionales prometedoras. ABSTRACT Currently, cryopreservation techniques have a growing importance for long term plant germplasm storage. These methods have undergone great progress during the last two decades, and adequate protocols for different plant systems have been developed, making use of diverse strategies, such as vitrification, encapsulation-dehydration with alginate beads and the dropletvitrification method. This PhD thesis has the goal of increasing the knowledge on the processes underlying the different steps of cryopreservation protocols, in relation with the state of water on tissues and its changes, approached through diverse biophysical techniques, especially differential scanning calorimetry (DSC) and low-temperature scanning electron microscopy (cryo-SEM). The processes of cooling to liquid nitrogen temperature and warming to room temperature, at the end of the storage period, critical for the survival of the cryopreserved material, are described in a first study on these cryopreservation methods. Both cooling and warming must be carried out as quickly as possible because, although the low water content achieved during previous protocol steps significantly reduces ice formation probability, it does not completely disappear. Within this context, the influence of plant vitrification solutions cooling and warming rate on their vitrification related thermophysical parameters is also analyzed, in relation to its composition and component concentration. These solutions are used in most of the currently employed plant material cryopreservation protocols. Additionally, the influence of other factors determining the stability of vitrified material is studied, such as glass aging. An experimental research work has been carried out on the use of cryo-SEM as a tool for visualizing the glassy state in cells and tissues, submitted to cryopreservation processes. It has been compared with the better known differential scanning calorimetry technique, and results in good agreement and complementary have been obtained. The effect on plant tissues of adaptation to low temperature and of the dehydration induced by the different treatments used in the protocols was explored also by these techniques. This study allows observation of the system biophysical evolution in the cryopreservation process. Lastly, the potential use of an additional chitosan film over the alginate beads used in encapsulation protocols was examined. No significant changes could be observed in its dehydration and calorimetric behavior, as well as in its surface aspect; its application for conferring additional properties to gel beads is promising.

Optimization of AlN thin layers on diamond substrates for high frequency SAW resonators

AlN/diamond heterostructures are very promising for high frequency surface acoustic wave (SAW) resonators. In their design, the thickness of the piezoelectric film is one of the key parameters. On the other hand, the film material quality and, hence, the device performance, also depend on that thickness. In this work, polished microcrystalline diamond substrates have been used to deposit AlN films by reactive sputtering, from 150 nm up to 3 μm thick. A high degree of the c-axis orientation has been obtained in all cases. SAW one port resonators at high frequency have been fabricated on these films with a proper combination of the film thickness and transducer size.

Practical issues for testing thin film PV modules at standard test conditions.

Thin film photovoltaic (TF) modules have gained importance in the photovoltaic (PV) market. New PV plants increasingly use TF technologies. In order to have a reliable sample of a PV module population, a huge number of modules must be measured. There is a big variety of materials used in TF technology. Some of these modules are made of amorphous or microcrystalline silicon. Other are made of CIS or CdTe. Not all these materials respond the same under standard test conditions (STC) of power measurement. Power rates of the modules may vary depending on both the extent and the history of sunlight exposure. Thus, it is necessary a testing method adapted to each TF technology. This test must guarantee repeatability of measurements of generated power. This paper shows responses of different commercial TF PV modules to sunlight exposure. Several test procedures were performed in order to find the best methodology to obtain measurements of TF PV modules at STC in the easiest way. A methodology for indoor measurements adapted to these technologies is described.

Estudio experimental sobre la reacción álcali-sílice en el hormigón producida por áridos de reacción lenta

La finalidad de esta investigación se enmarca dentro de los estudios sobre hormigones de presas llevados a cabo en el Laboratorio Central de Estructuras y Materiales del CEDEX. En España se han diagnosticado 18 obras afectadas tanto por la reacción álcali-sílice de tipo rápido como por la de tipo lento. Dos de de las obras, fabricadas con áridos graníticos, no presentan signos de deterioro pero en laboratorio se han hallado productos expansivos. En las 16 presas españolas restantes, el hormigón de 10 de ellas estaba fabricado con áridos graníticos, de las cuales, 7 están afectadas por la reacción de tipo lento. Sin embargo, en las clasificaciones internacionales de las rocas potencialmente reactivas se establece habitualmente que las rocas graníticas son inocuas o de reactividad muy baja. En los casos puntuales encontrados en la literatura, la reactividad de este tipo de áridos se encuentra frecuentemente asociada al cuarzo microcristalino que contienen y ocasionalmente se asocia esta reactividad también al cuarzo deformado y/o microfisurado. En la tesis doctoral de Víctor Daniel Lanza Fernández, también realizada en el CEDEX, se han tratado los áridos de reacción rápida, dando una descripción detallada de los componentes que intervienen en este tipo de reacción y presentando un ensayo eficaz para su detección en el laboratorio. La investigación desarrollada en la presente tesis doctoral se ha centrado en los áridos de reacción lenta, mucho menos estudiados. A partir del estudio bibliográfico realizado sobre este tipo de reacción se ha detectado ciertas lagunas, basadas principalmente en la falta de un método de detección en el laboratorio para los áridos de reacción lenta. No se ha encontrado un procedimiento en el estudio petrográfico que sea fiable y cuantificable para este tipo de áridos. El ensayo acelerado de barras de mortero, que para los áridos de reacción rápida supone un método rápido y fiable, falla en la detección de los áridos de reacción lenta al aplicar los límites normalizados. Si bien en publicaciones recientes se ha propuesto la posibilidad de ampliar el tiempo de tratamiento hasta los 90 días, la duración del ensayo es más larga de lo deseado. Para resolver estas lagunas, se han tomado áridos de obras reales afectadas por la reacción álcali-sílice (en algún caso también de las canteras de donde se extrajeron los áridos para la ejecución), con lo que la reactividad de estos áridos queda demostrada por su comportamiento en obra. Al objeto de aumentar la muestra de ensayo y utilizar también áridos inocuos, se han tomado muestras de canteras, tanto en uso como abandonadas. Sobre estos áridos se ha realizado una caracterización completa con los ensayos actualmente disponibles para el estudio de su reactividad con los álcalis del cemento: estudio petrográfico, ensayo acelerado de barras de mortero y Gel-Pat modificado. En la investigación se ha desarrollado una metodología de tinción de geles álcali-sílice para la cuantificación de los mismos en el interior de las barras de mortero. Se ha relacionado el volumen de gel generado en la reacción con la expansión producida, tanto para áridos lentos, como rápidos, estableciendo analogías y diferencias en el comportamiento de ambos. La cuantificación de este tipo de compuestos realizada en las barras de mortero, abre la posibilidad de estudiar la capacidad expansiva que presentan en testigos de hormigón de obras afectadas. Este dato podría ser una herramienta importante para el desarrollo de modelos matemáticos que puedan predecir el futuro comportamiento de las estructuras afectadas por la reacción álcali-sílice. La tinción ha sido asimismo utilizada para establecer un método de detección de áridos reactivos basado en el ensayo de Gel-Pat modificado. La metodología de detección propuesta para estos áridos es cuantitativa y proporciona los resultados en 14 días, suponiendo una ventaja importante sobre los métodos actuales, que permiten detectarlos en 90 días (de forma orientativa en 56 días). This research is part of the studies on durability of concrete dams carried out in the Laboratorio Central de Estructuras y Materiales of CEDEX during the last years. At the present time, 18 public works affected by alkali-silica reaction have been diagnosed in Spain. In 12 of them the concrete was mixed with granitic aggregates, 7 of which were damaged by the slow alkali-silica reaction, 3 by the rapid alkali-silica reaction and in the other 2 cases, although there was no visual evidence of the reaction in field, the laboratory tests showed the presence of expansive products inside the concrete. However, in the international classifications of potentially reactive aggregates granitic rocks are pointed out as innocuous or as low reactivity and usually their reactivity is attributed to the presence of microcrystalline quartz and occasionally with the strained and microcracked quartz. The rapid reactive aggregates were deeply studied in a previous research (Víctor Daniel Lanza’s Thesis) also carried out in CEDEX. In this research, a detailed description of the components involved in the rapid alkali-silica reaction was given. Also, a fast method to detect them in the laboratory was developed. The research of the present PhD Thesis is focused in the slow-reactive aggregates, much less studied. The state of the art has shown some gaps in the knowledge about this reaction, mainly the absence of a reliable method to detect slow-reactive aggregates. On one side, there is no systematic and quantitative petrographic test for these aggregates. On the other side, the accelerated mortar bar test has been proved to be effective to detect rapid reactive aggregates but the standard limits fail in the detection of the slowreactive aggregates. In recent investigations it has been proposed extending the test until 90 days, but this period is considered too long. In this research, aggregates taken from affected structures have been used in the test, so their reactivity has been shown in practice. With the aim of increasing the number of samples aggregates from quarries have been also used. A method to stain alkali-silica gels has been applied to mortar bars, thereby quantifying the volume of gel generated inside. This volume has been related to the expansion of the bars, both for rapid for slow reactive aggregates, establishing similarities and differences. The quantification of the gel volume, applied to concrete cores extracted from affected structures, could be an important tool in mathematical models to predict the future behaviour of the structures affected by the alkali-silica reaction. The staining method has been also used to develop a method to detect slow reactive aggregates, based on the optimised Gel-Pat test, obtaining results in 14 days. This represents a major improvement compared to the actual methods (accelerated mortar bar test) which give an indicative value of reactivity at 56 days, and a final result at 90 days.

An eco-friendly way to fire retardant flexible polyurethane foam: layer-by-layer assembly of fully bio-based substances

The objective of the present study is to develop fully renewable and environmentally benign techniques for improving the fire safety of flexible polyurethane foams (PUFs). A multilayered coating made from cationic chitosan (CS) and anionic alginate (AL) was deposited on PUFs through layer-by-layer assembly. This coating system exhibits a slight influence on the thermal stability of PUF, but significantly improves the char formation during combustion. Cone calorimetry reveals that 10 CS-AL bilayers (only 5.7% of the foams weight) lead to a 66% and 11% reduction in peak heat release rate and total heat release, respectively, compared with those of the uncoated control. The notable decreased fire hazards of PUF are attributed to the CS-AL coatings being beneficial to form an insulating protective layer on the surface of burning materials that inhibits the oxygen and heat permeation and slows down the flammable gases in the vapor phase, and thereby improves the flame resistance. This water-based, environmentally benign natural coating will stimulate further efforts in improving fire safety for a variety of polymer substrates.