Demonstration of (In, Ga)N/GaN Core-Shell Micro Light-Emitting Diodes Grown by Molecular Beam Epitaxy on Ordered MOVPE GaN Pillars

This work reports on the growth of (In, Ga)N core−shell micro pillars by plasma-assisted molecular beam epitaxy using an ordered array of GaN cores grown by metal organic vapor phase epitaxy as a template. Upon (In, Ga)N growth, core−shell structures with emission at around 3.0 eV are formed. Further, the fabrication of a core−shell pin structure is demonstrated.

Diseño y síntesis de materiales nanoestructurados basados en aluminatos de estroncio con propiedades fotoluminiscentes

Durante la última década, se han llevado acabo numeroso estudios sobre la síntesis de materiales fotoluminiscentes sub-micrónicos, en gran medida, al amplio número de aplicaciones que demandan este tipo de materiales. En concreto dentro de los materiales fosforescentes o también denominados materiales con una prolongada persistencia de la luminiscencia, los estudios se han enfocado en la matriz de SrAl2O4 dopada con Europio (Eu2+) y Disprosio (Dy3+) dado que tiene mayor estabilidad y persistencia de la fosforescencia con respecto a otras matrices. Estos materiales se emplean mayoritariamente en pinturas luminiscentes, tintas, señalización de seguridad pública, cerámicas, relojes, textiles y juguetes fosforescentes. Dado al amplio campo de aplicación de los SrAl2O4:Eu, Dy, se han investigado múltiples rutas de síntesis como la ruta sol-gel, la síntesis hidrotermal, la síntesis por combustión, la síntesis láser y la síntesis en estado sólido con el fin de desarrollar un método eficiente y que sea fácilmente escalable. Sin embargo, en la actualidad el método que se emplea para el procesamiento a nivel industrial de los materiales basados en aluminato de estroncio es la síntesis por estado sólido, que requiere de temperaturas de entre 1300 a 1900oC y largos tiempos de procesamiento. Además el material obtenido tiene un tamaño de partícula de 20 a 100 μm; siendo este tamaño restrictivo para el empleo de este tipo de material en determinadas aplicaciones. Por tanto, el objetivo de este trabajo es el desarrollo de nuevas estrategias que solventen las actuales limitaciones. Dentro de este marco se plantean una serie de objetivos específicos: Estudio de los parámetros que gobiernan los procesos de reducción del tamaño de partícula mediante molienda y su relación en la respuesta fotoluminiscente. Estudio de la síntesis por combustión de SrAl2O4:Eu, Dy, evaluando el efecto de la temperatura y la cantidad de combustible (urea) en el proceso para la obtención de partículas cristalinas minimizando la presencia de fases secundarias. Desarrollo de nuevas rutas de síntesis de SrAl2O4:Eu, Dy empleando el método de sales fundidas. Determinación de los mecanismos de reacción en presencia de la sal fundida en función de los parámetros de proceso que comprende la relación de sales y reactivos, la naturaleza de la alúmina y su tamaño, la temperatura y atmósfera de tratamiento. Mejora de la eficiencia de los procesos de síntesis para obtener productos con propiedades finales óptimas en procesos factibles industrialmente para su transferencia tecnológica. Es este trabajo han sido evaluados los efectos de diferentes procesos de molienda para la reducción del tamaño de partícula del material de SrAl2O4:Eu, Dy comercial. En el proceso de molienda en medio húmedo por atrición se observa la alteración de la estructura cristalina del material debido a la reacción de hidrólisis generada incluso empleando como medio líquido etanol absoluto. Con el fin de solventar las desventajas de la molienda en medio húmedo se llevo a cabo un estudio de la molturación en seco del material. La molturación en seco de alta energía reduce significativamente el tamaño medio de partícula. Sin embargo, procesos de molienda superiores a una duración de 10 minutos ocasionan un aumento del estado de aglomeración de las partículas y disminuyen drásticamente la respuesta fotoluminiscente del material. Por tanto, se lleva a cabo un proceso de molienda en seco de baja energía. Mediante este método se consigue reducir el tamaño medio de partícula, d50=2.8 μm, y se mejora la homogeneidad de la distribución del tamaño de partícula evitando la amorfización del material. A partir de los resultados obtenidos mediante difracción de rayos X y microscopia electrónica de barrido se infiere que la disminución de la intensidad de la fotoluminiscencia después de la molienda en seco de alta energía con respecto al material inicial se debe principalmente a la reducción del tamaño de cristalito. Se observan menores variaciones en la intensidad de la fotoluminiscencia cuando se emplea un método de molienda de baja de energía ya que en estos procesos se preserva el dominio cristalino y se reduce la amorfización significativamente. Estos resultados corroboran que la intensidad de la fotoluminiscencia y la persistencia de la luminiscencia de los materiales de SrAl2O4:Eu2+, Dy3+ dependen extrínsecamente de la morfología de las partículas, del tamaño de partícula, el tamaño de grano, los defectos superficiales e intrínsecamente del tamaño de cristalito. Siendo las características intrínsecas las que dominan con respecto a las extrínsecas y por tanto tienen mayor relevancia en la respuesta fotoluminiscente. Mediante síntesis por combustión se obtuvieron láminas nanoestructuradas de SrAl2O4:Eu, Dy de ≤1 μm de espesor. La cantidad de combustible, urea, en la reacción influye significativamente en la formación de determinadas fases cristalinas. Para la síntesis del material de SrAl2O4:Eu, Dy es necesario incluir un contenido de urea mayor que el estequiométrico (siendo m=1 la relación estequiométrica). La incorporación de un exceso de urea (m>1) requiere de la presencia de un agente oxidante interno, HNO3, para que la reacción tenga lugar. El empleo de un mayor contenido de urea como combustible permite una quelación efectiva de los cationes en el sistema y la creación de las condiciones reductoras para obtener un material de mayor cristalinidad y con mejores propiedades fotoluminiscentes. El material de SrAl2O4:Eu, Dy sintetizado a una temperatura de ignición de 600oC tiene un tamaño medio 5-25 μm con un espesor de ≤1 μm. Mediante procesos de molturación en seco de baja energía es posible disminuir el tamaño medio de partícula ≈2 μm y homogenizar la distribución del tamaño de partícula pero hay un deterioro asociado de la respuesta luminiscente. Sin embargo, se puede mejorar la respuesta fotoluminiscente empleando un tratamiento térmico posterior a 900oC N2-H2 durante 1 hora que no supone un aumento del tamaño de partícula pero si permite aumentar el tamaño de cristalito y la reducción del Eu3+ a Eu2+. Con respecto a la respuesta fotoluminiscente, se obtiene valores de la intensidad de la fotoluminiscencia entre un 35%-21% con respecto a la intensidad de un material comercial de referencia. Además la intensidad inicial del decaimiento de la fosforescencia es un 20% de la intensidad del material de referencia. Por tanto, teniendo en cuenta estos resultados, es necesario explorar otros métodos de síntesis para la obtención de los materiales bajo estudio. Por esta razón, en este trabajo se desarrollo una ruta de síntesis novedosa para sintetizar SrAl2O4:Eu, Dy mediante el método de sales fundidas para la obtención de materiales de gran cristalinidad con tamaños de cristalito del orden nanométrico. Se empleo como sal fundente la mezcla eutéctica de NaCl y KCl, denominada (NaCl-KCl)e. La principal ventaja de la incorporación de la mezcla es el incremento la reactividad del sistema, reduciendo la temperatura de formación del SrAl2O4 y la duración del tratamiento térmico en comparación con la síntesis en estado sólido. La formación del SrAl2O4 es favorecida ya que se aumenta la difusión de los cationes de Sr2+ en el medio líquido. Se emplearon diferentes tipos de Al2O3 para evaluar el papel del tamaño de partícula y su naturaleza en la reacción asistida por sales fundidas y por tanto en la morfología y propiedades del producto final. Se obtuvieron partículas de morfología pseudo-esférica de tamaño ≤0.5 μm al emplear como alúmina precursora partículas sub-micrónicas ( 0.5 μm Al2O3, 0.1 μm Al2 O3 y γ-Al2O3). El mecanismo de reacción que tiene lugar se asocia a procesos de disolución-precipitación que dominan al emplear partículas de alúmina pequeñas y reactivas. Mientras al emplear una alúmina de 6 μm Al2O3 prevalecen los procesos de crecimiento cristalino siguiendo un patrón o plantilla debido a la menor reactividad del sistema. La nucleación y crecimiento de nanocristales de SrAl2O4:Eu, Dy se genera sobre la superficie de la alúmina que actúa como soporte. De esta forma se desarrolla una estructura del tipo coraza-núcleo («core-shell» en inglés) donde la superficie externa está formada por los cristales fosforescentes de SrAl2O4 y el núcleo está formado por alúmina. Las partículas obtenidas tienen una respuesta fotoluminiscente diferente en función de la morfología final obtenida. La optimización de la relación Al2O3/SrO del material de SrAl2O4:Eu, Dy sintetizado a partir de la alúmina de 6 μm permite reducir las fases secundarias y la concentración de dopantes manteniendo la respuesta fotoluminiscente. Comparativamente con un material comercial de SrAl2O4:Eu, Dy de referencia, se han alcanzado valores de la intensidad de la emisión de hasta el 90% y de la intensidad inicial de las curvas de decaimiento de la luminiscencia de un 60% para el material sintetizado por sales fundidas que tiene un tamaño medio ≤ 10μm. Por otra parte, es necesario tener en cuenta que el SrAl2O4 tiene dos polimorfos, la fase monoclínica que es estable a temperaturas inferiores a 650oC y la fase hexagonal, fase de alta temperatura, estable a temperaturas superiores de 650oC. Se ha determinado que fase monoclínica presenta propiedades luminiscentes, sin embargo existen discordancias a cerca de las propiedades luminiscentes de la fase hexagonal. Mediante la síntesis por sales fundidas es posible estabilizar la fase hexagonal empleando como alúmina precursora γ-Al2O3 y un exceso de Al2O3 (Al2O3/SrO:2). La estabilización de la fase hexagonal a temperatura ambiente se produce cuando el tamaño de los cristales de SrAl2O4 es ≤20 nm. Además se observó que la fase hexagonal presenta respuesta fotoluminiscente. El diseño de materiales de SrAl2O4:Eu,Dy nanoestructurados permite modular la morfología del material y por tanto la intensidad de la de la fotoluminiscencia y la persistencia de la luminiscencia. La disminución de los materiales precursores, la temperatura y el tiempo de tratamiento significa la reducción de los costes económicos del material. De ahí la viabilidad de los materiales de SrAl2O4:Eu,Dy obtenidos mediante los procesos de síntesis propuestos en esta memoria de tesis para su posterior escalado industrial. ABSTRACT The synthesis of sub-micron photoluminescent particles has been widely studied during the past decade because of the promising industrial applications of these materials. A large number of matrices has been developed, being SrAl2O4 host doped with europium (Eu2+) and dysprosium (Dy3+) the most extensively studied, because of its better stability and long-lasting luminescence. These functional inorganic materials have a wide field of application in persistent luminous paints, inks and ceramics. Large attention has been paid to the development of an efficient method of preparation of SrAl2O4 powders, including solgel method, hydrothermal synthesis, laser synthesis, combustion synthesis and solid state reaction. Many of these techniques are not compatible with large-scale production and with the principles of sustainability. Moreover, industrial processing of highly crystalline powders usually requires high synthesis temperatures, typically between 1300 a 1900oC, with long processing times, especially for solid state reaction. As a result, the average particle size is typically within the 20-100 μm range. This large particle size is limiting for current applications that demand sub-micron particles. Therefore, the objective of this work is to develop new approaches to overcome these limitations. Within this frame, it is necessary to undertake the following purposes: To study the parameters that govern the particle size reduction by milling and their relation with the photoluminescence properties. To obtain SrAl2O4:Eu, Dy by combustion synthesis, assessing the effect of the temperature and the amount of fuel (urea) to synthesize highly crystalline particles minimizing the presence of secondary phases. To develop new synthesis methods to obtain SrAl2O4:Eu, Dy powders. The molten salt synthesis has been proposed. As the method is a novel route, the reaction mechanism should be determine as a function of the salt mixture, the ratio of the salt, the kind of Al2O3 and their particle size and the temperature and the atmosphere of the thermal treatment. To improve the efficiency of the synthesis process to obtain SrAl2O4:Eu, Dy powders with optimal final properties and easily scalable. On the basis of decreasing the particle size by using commercial product SrAl2O4:Eu2+, Dy3+ as raw material, the effects of different milling methods have been evaluated. Wet milling can significantly alter the structure of the material through hydrolysis reaction even in ethanol media. For overcoming the drawbacks of wet milling, a dry milling-based processes are studied. High energy dry milling process allows a great reduction of the particle size, however milling times above 10 min produce agglomeration and accelerates the decrease of the photoluminescence feature. To solve these issues the low energy dry milling process proposed effectively reduces the particle size to d50=2.8 μm, and improves the homogeneity avoiding the amorphization in comparison with previous methods. The X-ray diffraction and scanning electron microscope characterization allow to infer that the large variations in PL (Photoluminescence) values by high energy milling process are a consequence mainly of the crystallite size reduction. The lesser variation in PL values by low energy milling proces is related to the coherent crystalline domain preservation and the unnoticeable amorphization. These results corroborate that the photoluminescence intensity and the persistent luminescence of the SrAl2O4:Eu2+, Dy3+ powders depend extrinsically on the morphology of the particles such as particle size, grain size, surface damage and intrinsically on the crystallinity (crystallite size); being the intrinsically effects the ones that have a significant influence on the photoluminescent response. By combustion method, nanostructured SrAl2O4:Eu2+, Dy3+ sheets with a thickness ≤1 μm have been obtained. The amount of fuel (urea) in the reaction has an important influence on the phase composition; urea contents larger than the stoichiometric one require the presence of an oxidant agent such as HNO3 to complete the reaction. A higher amount of urea (excess of urea: denoted m>1, being m=1 the stoichiometric composition) including an oxidizing agent produces SrAl2O4:Eu2+,Dy3+ particles with persistent luminescence due to the effective chelation of the cations and the creation of suitable atmospheric conditions to reduce the Eu3+ to Eu2+. Therefore, optimizing the synthesis parameters in combustion synthesis by using a higher amount of urea and an internal oxidizing agent allows to complete the reaction. The amount of secondary phases can be significantly reduced and the photoluminescence response can be enhanced. This situation is attributed to a higher energy that improves the crystallinity of the powders. The powders obtained have a particle size c.a. 5-25 μm with a thickness ≤1 μm and require relatively low ignition temperatures (600oC). It is possible to reduce the particle size by a low energy dry milling but this process implies the decrease of the photoluminescent response. However, a post-thermal treatment in a reducing atmosphere allows the improvement of the properties due to the increment of crystallinity and the reduction of Eu3+ to Eu2+. Compared with the powder resulted from solid state method (commercial reference: average particle size, 20 μm and heterogeneous particle size distribution) the emission intensity of the powder prepared by combustion method achieve the values between 35% to 21% of the reference powder intensity. Moreover, the initial intensity of the decay curve is 20% of the intensity of the reference powder. Taking in account these results, it is necessary to explore other methods to synthesize the powders For that reason, an original synthetic route has been developed in this study: the molten salt assisted process to obtain highly crystalline SrAl2O4 powders with nanometric sized crystallites. The molten salt was composed of a mixture of NaCl and KCl using a 0.5:0.5 molar ratio (eutectic mixture hereafter abbreviated as (NaCl-KCl)e). The main advantages of salt addition is the increase of the reaction rate, the significant reduction of the synthesis temperature and the duration of the thermal treatment in comparison with classic solid state method. The SrAl2O4 formation is promoted due to the high mobility of the Sr2+ cations in the liquid medium. Different kinds of Al2O3 have been employed to evaluate the role of the size and the nature of this precursor on the kinetics of reaction, on the morphology and the final properties of the product. The SrAl2O4:Eu2+, Dy3+ powders have pseudo-spherical morphology and particle size ≤0.5 μm when a sub-micron Al2O3 ( 0.5 μm Al2O3, 0.1 μm Al2O3 and γ-Al2O3) has been used. This can be attributed to a higher reactivity in the system and the dominance of dissolution-precipitation mechanism. However, the use of larger alumina (6 μm Al2O3) modifies the reaction pathway leading to a different reaction evolution. More specifically, the growth of SrAl2O4 sub-micron particles on the surface of hexagonal platelets of 6μm Al2O3 is promoted. The particles retain the shape of the original Al2O3 and this formation process can be attributed to a «core-shell» mechanism. The particles obtained exhibit different photoluminescent response as a function of the final morphology of the powder. Therefore, through this study, it has been elucidated the reaction mechanisms of SrAl2O4 formation assisted by (NaCl-KCl)e that are governed by the diffusion of SrCO3 and the reactivity of the alumina particles. Optimizing the Al2O3/SrO ratio of the SrAl2O4:Eu, Dy powders synthesized with 6 μm Al2O3 as a precursor, the secondary phases and the concentration of dopant needed can be reduced keeping the photoluminescent response of the synthesized powder. Compared with the commercial reference powder, up to 90% of the emission intensity of the reference powder has been achieved for the powder prepared by molten salt method using 6μm Al2O3 as alumina precursor. Concerning the initial intensity of the decay curve, 60% of the initial intensity of the reference powder has been obtained. Additionally, it is necessary to take into account that SrAl2O4 has two polymorphs: monoclinic symmetry that is stable at temperatures below 650oC and hexagonal symmetry that is stable above this temperature. Monoclinic phase shows luminescent properties. However, there is no clear agreement on the emission of the hexagonal structure. By molten salt, it is possible to stabilize the hexagonal phase of SrAl2O4 employing an excess of Al2O3 (Al2O3/SrO: 2) and γ-Al2O3 as a precursor. The existence of nanometric crystalline domains with lower size (≤20 nm) allows the stabilization of the hexagonal phase. Moreover, it has been evidenced that the hexagonal polymorph exhibits photoluminescent response. To sum up, the design of nanostructured SrAl2O4:Eu2+, Dy3+ materials allows to obtain different morphologies and as consequence different photoluminescent responses. The reduction of temperature, duration of the thermal treatment and the precursors materials needed imply the decrease of the economic cost of the material. Therefore, the viability, suitability and scalability of the synthesis strategy developed in this work to process SrAl2O4:Eu2+, Dy3+ are demonstrated.

Tailoring the Optical Properties of Silica Irradiated with Swift Heavy Ions

Irradiation with swift heavy ions (SHI), roughly defined as those having atomic masses larger than 15 and energies exceeding 1 MeV/amu, may lead to significant modification of the irradiated material in a nanometric region around the (straight) ion trajectory (i.e., latent tracks). In the case of amorphous silica it has been reported that SHI irradiation originates nano-tracks of either higher density than the virgin material (for low electronic stopping powers, Se < 7 keV/nm) [1] or having a low-density core and a dense shell (Se > 12 keV/nm) [2]. The intermediate region has not been studied in detail but we will show in this work that essentially no changes in density occur in this zone. An interesting effect of the compaction is that the refractive index is increased with respect to that of the surroundings. In the first Se region it is clear that track overlapping leads to continuous amorphous layers that present a significant contrast with respect to the pristine substrate and this has been used to produce optical waveguides. The optical effects of intermediate and high stopping powers, on the other hand, are largely unknown so far. In this work we have studied theoretically (molecular dynamics and optical simulations) and experimentally (irradiation with SHI and optical characterization) the dependence of the macroscopic optical properties (i.e., the refractive index of the effective medium, n_EMA) on the electronic stopping power of the incoming ions. Our results show that the refractive index of the irradiated silica is not increased in the intermediate region, as expected; however, the core-shell tracks of the high-Se region produce a quite effective enhancement of n_EMA that could prove attractive for the fabrication of optical waveguides at ultralow fluences (as low as 1E11 cm^-2). 1. J. Manzano, J. Olivares, F. Agulló-López, M. L. Crespillo, A. Moroño, and E. Hodgson, "Optical waveguides obtained by swift-ion irradiation on silica (a-SiO2)," Nucl. Instrum. Meth. B 268, 3147-3150 (2010). 2. P. Kluth, C. S. Schnohr, O. H. Pakarinen, F. Djurabekova, D. J. Sprouster, R. Giulian, M. C. Ridgway, A. P. Byrne, C. Trautmann, D. J. Cookson, K. Nordlund, and M. Toulemonde, "Fine structure in swift heavy ion tracks in amorphous SiO2," Phys. Rev. Lett. 101, 175503 (2008).

Advances on MBE selective area growth of III-nitride nanostructures: from nanoLEDs to pseudo substrates

The aim of this work is to provide an overview on the recent advances in the selective area growth (SAG) of (In)GaN nanostructures by plasma assisted molecular beam epitaxy, focusing on their potential as building blocks for next generation LEDs. The first three sections deal with the basic growth mechanisms of GaN SAG and the emission control in the entire ultraviolet to infrared range, including approaches for white light emission, using InGaN disks and thick segments on axial nanocolumns. SAG of axial nanostructures is eveloped on both GaN/sapphire templates and GaN-buffered Si(111). As an alternative to axial nanocolumns, section 4 reports on the growth and characterization of InGaN/GaN core-shell structures on an ordered array of top-down patterned GaN microrods. Finally, section 5 reports on the SAG of GaN, with and without InGaN insertion, on semi-polar (11-22) and non-polar (11-20) templates. Upon SAG the high defect density present in the templates is strongly reduced as indicated by a dramatic improvement of the optical properties. In the case of SAG on nonpolar (11-22) templates, the formation of nanostructures with a low aspect ratio took place allowing for the fabrication of high-quality, non-polar GaN pseudo-templates by coalescence of these nanostructures.

Self assembled and ordered group III nitride nanocolumnar structures for light emitting applications

El objetivo de este trabajo es un estudio profundo del crecimiento selectivo de nanoestructuras de InGaN por epitaxia de haces moleculares asistido por plasma, concentrandose en el potencial de estas estructuras como bloques constituyentes en LEDs de nueva generación. Varias aproximaciones al problema son discutidas; desde estructuras axiales InGaN/GaN, a estructuras core-shell, o nanoestructuras crecidas en sustratos con orientaciones menos convencionales (semi polar y no polar). La primera sección revisa los aspectos básicos del crecimiento auto-ensamblado de nanocolumnas de GaN en sustratos de Si(111). Su morfología y propiedades ópticas son comparadas con las de capas compactas de GaN sobre Si(111). En el caso de las columnas auto-ensambladas de InGaN sobre Si(111), se presentan resultados sobre el efecto de la temperatura de crecimiento en la incorporación de In. Por último, se discute la inclusión de nanodiscos de InGaN en las nanocolumnas de GaN. La segunda sección revisa los mecanismos básicos del crecimiento ordenado de nanoestructuras basadas en GaN, sobre templates de GaN/zafiro. Aumentando la relación III/V localmente, se observan cambios morfológicos; desde islas piramidales, a nanocolumnas de GaN terminadas en planos semipolares, y finalmente, a nanocolumnas finalizadas en planos c polares. Al crecer nanodiscos de InGaN insertados en las nanocolumnas de GaN, las diferentes morfologias mencionadas dan lugar a diferentes propiedades ópticas de los nanodiscos, debido al diferente carácter (semi polar o polar) de los planos cristalinos involucrados. La tercera sección recoge experimentos acerca de los efectos que la temperatura de crecimiento y la razón In/Ga tienen en la morfología y emisión de nanocolumnas ordenadas de InGaN crecidas sobre templates GaN/zafiro. En el rango de temperaturas entre 650 y 750 C, la incorporacion de In puede modificarse bien por la temperatura de crecimiento, o por la razón In/Ga. Controlar estos factores permite la optimización de la longitud de onda de emisión de las nanocolumnas de InGaN. En el caso particular de la generación de luz blanca, se han seguidos dos aproximaciones. En la primera, se obtiene emisión amarilla-blanca a temperatura ambiente de nanoestructuras donde la región de InGaN consiste en un gradiente de composiciones de In, que se ha obtenido a partir de un gradiente de temperatura durante el crecimiento. En la segunda, el apilamiento de segmentos emitiendo en azul, verde y rojo, consiguiendo la integración monolítica de estas estructuras en cada una de las nanocolumnas individuales, da lugar a emisores ordenados con un amplio espectro de emisión. En esta última aproximación, la forma espectral puede controlarse con la longitud (duración del crecimiento) de cada uno de los segmentos de InGaN. Más adelante, se presenta el crecimiento ordenado, por epitaxia de haces moleculares, de arrays de nanocolumnas que son diodos InGaN/GaN cada una de ellas, emitiendo en azul (441 nm), verde (502 nm) y amarillo (568 nm). La zona activa del dispositivo consiste en una sección de InGaN, de composición constante nominalmente y longitud entre 250 y 500 nm, y libre de defectos extendidos en contraste con capas compactas de InGaN de similares composiciones y espesores. Los espectros de electroluminiscencia muestran un muy pequeño desplazamiento al azul al aumentar la corriente inyectada (desplazamiento casi inexistente en el caso del dispositivo amarillo), y emisiones ligeramente más anchas que en el caso del estado del arte en pozos cuánticos de InGaN. A continuación, se presenta y discute el crecimiento ordenado de nanocolumnas de In(Ga)N/GaN en sustratos de Si(111). Nanocolumnas ordenadas emitiendo desde el ultravioleta (3.2 eV) al infrarrojo (0.78 eV) se crecieron sobre sustratos de Si(111) utilizando una capa compacta (“buffer”) de GaN. La morfología y eficiencia de emisión de las nanocolumnas emitiendo en el rango espectral verde pueden ser mejoradas ajustando las relaciones In/Ga y III/N, y una eficiencia cuántica interna del 30% se deriva de las medidas de fotoluminiscencia en nanocolumnas optimizadas. En la siguiente sección de este trabajo se presenta en detalle el mecanismo tras el crecimiento ordenado de nanocolumnas de InGaN/GaN emitiendo en el verde, y sus propiedades ópticas. Nanocolumnas de InGaN/GaN con secciones largas de InGaN (330-830 nm) se crecieron tanto en sustratos GaN/zafiro como GaN/Si(111). Se encuentra que la morfología y la distribución espacial del In dentro de las nanocolumnas dependen de las relaciones III/N e In/Ga locales en el frente de crecimiento de las nanocolumnas. La dispersión en el contenido de In entre diferentes nanocolumnas dentro de la misma muestra es despreciable, como indica las casi identicas formas espectrales de la catodoluminiscencia de una sola nanocolumna y del conjunto de ellas. Para las nanocolumnas de InGaN/GaN crecidas sobre GaN/Si(111) y emitiendo en el rango espectral verde, la eficiencia cuántica interna aumenta hasta el 30% al disminuir la temperatura de crecimiento y aumentar el nitrógeno activo. Este comportamiento se debe probablemente a la formación de estados altamente localizados, como indica la particular evolución de la energía de fotoluminiscencia con la temperatura (ausencia de “s-shape”) en muestras con una alta eficiencia cuántica interna. Por otro lado, no se ha encontrado la misma dependencia entre condiciones de crecimiento y efiencia cuántica interna en las nanoestructuras InGaN/GaN crecidas en GaN/zafiro, donde la máxima eficiencia encontrada ha sido de 3.7%. Como alternativa a las nanoestructuras axiales de InGaN/GaN, la sección 4 presenta resultados sobre el crecimiento y caracterización de estructuras core-shell de InGaN/GaN, re-crecidas sobre arrays de micropilares de GaN fabricados por ataque de un template GaN/zafiro (aproximación top-down). El crecimiento de InGaN/GaN es conformal, con componentes axiales y radiales en el crecimiento, que dan lugar a la estructuras core-shell con claras facetas hexagonales. El crecimiento radial (shell) se ve confirmado por medidas de catodoluminiscencia con resolución espacial efectuadas en un microscopio electrónico de barrido, asi como por medidas de microscopía de transmisión de electrones. Más adelante, el crecimiento de micro-pilares core-shell de InGaN se realizó en pilares GaN (cores) crecidos selectivamente por epitaxia de metal-orgánicos en fase vapor. Con el crecimiento de InGaN se forman estructuras core-shell con emisión alrededor de 3 eV. Medidas de catodoluminiscencia resuelta espacialmente indican un aumento en el contenido de indio del shell en dirección a la parte superior del pilar, que se manifiesta en un desplazamiento de la emisión de 3.2 eV en la parte inferior, a 3.0 eV en la parte superior del shell. Este desplazamiento está relacionado con variaciones locales de la razón III/V en las facetas laterales. Finalmente, se demuestra la fabricación de una estructura pin basada en estos pilares core-shell. Medidas de electroluminiscencia resuelta espacialmente, realizadas en pilares individuales, confirman que la electroluminiscencia proveniente del shell de InGaN (diodo lateral) está alrededor de 3.0 eV, mientras que la emisión desde la parte superior del pilar (diodo axial) está alrededor de 2.3 eV. Para finalizar, se presentan resultados sobre el crecimiento ordenado de GaN, con y sin inserciones de InGaN, en templates semi polares (GaN(11-22)/zafiro) y no polares (GaN(11-20)/zafiro). Tras el crecimiento ordenado, gran parte de los defectos presentes en los templates originales se ven reducidos, manifestándose en una gran mejora de las propiedades ópticas. En el caso de crecimiento selectivo sobre templates con orientación GaN(11-22), no polar, la formación de nanoestructuras con una particular morfología (baja relación entre crecimiento perpedicular frente a paralelo al plano) permite, a partir de la coalescencia de estas nanoestructuras, la fabricación de pseudo-templates no polares de GaN de alta calidad. ABSTRACT The aim of this work is to gain insight into the selective area growth of InGaN nanostructures by plasma assisted molecular beam epitaxy, focusing on their potential as building blocks for next generation LEDs. Several nanocolumn-based approaches such as standard axial InGaN/GaN structures, InGaN/GaN core-shell structures, or InGaN/GaN nanostructures grown on semi- and non-polar substrates are discussed. The first section reviews the basics of the self-assembled growth of GaN nanocolumns on Si(111). Morphology differences and optical properties are compared to those of GaN layer grown directly on Si(111). The effects of the growth temperature on the In incorporation in self-assembled InGaN nanocolumns grown on Si(111) is described. The second section reviews the basic growth mechanisms of selectively grown GaNbased nanostructures on c-plane GaN/sapphire templates. By increasing the local III/V ratio morphological changes from pyramidal islands, to GaN nanocolumns with top semi-polar planes, and further to GaN nanocolumns with top polar c-planes are observed. When growing InGaN nano-disks embedded into the GaN nanocolumns, the different morphologies mentioned lead to different optical properties, due to the semipolar and polar nature of the crystal planes involved. The third section reports on the effect of the growth temperature and In/Ga ratio on the morphology and light emission characteristics of ordered InGaN nanocolumns grown on c-plane GaN/sapphire templates. Within the growth temperature range of 650 to 750oC the In incorporation can be modified either by the growth temperature, or the In/Ga ratio. Control of these factors allows the optimization of the InGaN nanocolumns light emission wavelength. In order to achieve white light emission two approaches are used. First yellow-white light emission can be obtained at room temperature from nanostructures where the InGaN region is composition-graded by using temperature gradients during growth. In a second approach the stacking of red, green and blue emitting segments was used to achieve the monolithic integration of these structures in one single InGaN nanocolumn leading to ordered broad spectrum emitters. With this approach, the spectral shape can be controlled by changing the thickness of the respective InGaN segments. Furthermore the growth of ordered arrays of InGaN/GaN nanocolumnar light emitting diodes by molecular beam epitaxy, emitting in the blue (441 nm), green (502 nm), and yellow (568 nm) spectral range is reported. The device active region, consisting of a nanocolumnar InGaN section of nominally constant composition and 250 to 500 nm length, is free of extended defects, which is in strong contrast to InGaN layers (planar) of similar composition and thickness. Electroluminescence spectra show a very small blue shift with increasing current, (almost negligible in the yellow device) and line widths slightly broader than those of state-of-the-art InGaN quantum wells. Next the selective area growth of In(Ga)N/GaN nanocolumns on Si(111) substrates is discussed. Ordered In(Ga)N/GaN nanocolumns emitting from ultraviolet (3.2 eV) to infrared (0.78 eV) were then grown on top of GaN-buffered Si substrates. The morphology and the emission efficiency of the In(Ga)N/GaN nanocolumns emitting in the green could be substantially improved by tuning the In/Ga and total III/N ratios, where an estimated internal quantum efficiency of 30 % was derived from photoluminescence data. In the next section, this work presents a study on the selective area growth mechanisms of green-emitting InGaN/GaN nanocolumns and their optical properties. InGaN/GaN nanocolumns with long InGaN sections (330-830nm) were grown on GaN/sapphire and GaN-buffered Si(111). The nanocolumn’s morphology and spatial indium distribution is found to depend on the local group (III)/N and In/Ga ratios at the nanocolumn’s top. A negligible spread of the average indium incorporation among different nanostructures is found as indicated by similar shapes of the cathodoluminescence spectra taken from single nanocolumns and ensembles of nanocolumns. For InGaN/GaN nanocolumns grown on GaN-buffered Si(111), all emitting in the green spectral range, the internal quantum efficiency increases up to 30% when decreasing growth temperature and increasing active nitrogen. This behavior is likely due to the formation of highly localized states, as indicated by the absence of a complete s-shape behavior of the PL peak position with temperature (up to room temperature) in samples with high internal quantum efficiency. On the other hand, no dependence of the internal quantum efficiency on the growth conditions is found for InGaN/GaN nanostructures grown on GaN/sapphire, where the maximum achieved efficiency is 3.7%. As alternative to axial InGaN/GaN nanostructures, section 4 reports on the growth and characterization of InGaN/GaN core-shell structures on an ordered array of top-down patterned GaN microrods etched from a GaN/sapphire template. Growth of InGaN/GaN is conformal, with axial and radial growth components leading to core-shell structures with clear hexagonal facets. The radial InGaN growth (shell) is confirmed by spatially resolved cathodoluminescence performed in a scanning electron microscopy as well as in scanning transmission electron microscopy. Furthermore the growth of InGaN core-shell micro pillars using an ordered array of GaN cores grown by metal organic vapor phase epitaxy as a template is demonstrated. Upon InGaN overgrowth core-shell structures with emission at around 3.0 eV are formed. With spatially resolved cathodoluminescence, an increasing In content towards the pillar top is found to be present in the InGaN shell, as indicated by a shift of CL peak position from 3.2 eV at the shell bottom to 3.0 eV at the shell top. This shift is related to variations of the local III/V ratio at the side facets. Further, the successful fabrication of a core-shell pin diode structure is demonstrated. Spatially resolved electroluminescence measurements performed on individual micro LEDs, confirm emission from the InGaN shell (lateral diode) at around 3.0 eV, as well as from the pillar top facet (axial diode) at around 2.3 eV. Finally, this work reports on the selective area growth of GaN, with and without InGaN insertion, on semi-polar (11-22) and non-polar (11-20) templates. Upon SAG the high defect density present in the GaN templates is strongly reduced as indicated by TEM and a dramatic improvement of the optical properties. In case of SAG on non-polar (11-22) templates the formation of nanostructures with a low aspect ratio took place allowing for the fabrication of high-quality, non-polar GaN pseudo-templates by coalescence of the nanostructures.

Stopping of α particles from the core in corona plasmas

In the laser fusion reactor design, the protection of first wall and the final optics from high energy ions is the key issue. So, it is necessary to predict the precise energy spectra of ions.In the previous reactor designs, the ion energy spectra were provided by the classical ion transport codes. However, this poster shows that the α particle spectrum is significantly modified by the anomalous process in ablated plasmas.