Quantifying pulsed laser induced damage to grapheme

As an emerging optical material, graphene’s ultrafast dynamics are often probed using pulsed lasers yet the region in which optical damage takes place is largely uncharted. Here, femtosecond laser pulses induced localized damage in single-layer graphene on sapphire. Raman spatial mapping, SEM, and AFM microscopy quantified the damage. The resulting size of the damaged area has a linear correlation with the optical fluence. These results demonstrate local modification of sp2-carbon bonding structures with optical pulse fluences as low as 14 mJ/cm2, an order-of-magnitude lower than measured and theoretical ablation thresholds.

Electronic damage in quartz (c-SiO2) by MeV ion irradiations: Potentiality for optical waveguiding applications

The damage induced on quartz (c-SiO2) by heavy ions (F, O, Br) at MeV energies, where electronic stopping is dominant, has been investigated by RBS/C and optical methods. The two techniques indicate the formation of amorphous layers with an isotropic refractive index (n = 1.475) at fluences around 1014 cm−2 that are associated to electronic mechanisms. The kinetics of the process can be described as the superposition of linear (possibly initial Poisson curve) and sigmoidal (Avrami-type) contributions. The coexistence of the two kinetic regimes may be associated to the differential roles of the amorphous track cores and preamorphous halos. By using ions and energies whose maximum stopping power lies inside the crystal (O at 13 MeV, F at 15 MeV and F at 30 MeV) buried amorphous layer are formed and optical waveguides at the sample surface have been generated.

In-situ optical reflectance characterization of ion beam irradiation damage on crystalline (quartz) and amorphous (silica) SiO2

Outline: • Motivation, aim • Complement waveguide data on silica • Optical data in quartz • Detailed analysis, i.e. both fluence kinetics and resolution • Efficiency of irradiation and analysis, samples, time... • Experimental set-up description • Reflectance procedure • Options: light source (lasers, white light..), detectors, configurations • Results and discussion • Comparative of amorphous and crystalline phases

Non contact inspection of the fatigue damage state of carbon fiber reinforced polymer by optical surface roughness measurements

This work presents the evaluation of a new non-contact technique to assess the fatigue damage state of CFRP structures by measuring surface roughness parameters. Surface roughness and stiffness degradation have been measured in CFRP coupons cycled with constant amplitude loads, and a Pearson?s correlation of 0.79 was obtained between both variables. Results suggest that changes on the surface roughness measured in strategic zones of components made of the evaluated CFRP, could be indicative of the level of damage due to fatigue loads. This methodology could be useful for other FRP due to similarities in the fatigue damage process.

Optical sensing of the fatigue damage state of CFRP under realistic aeronautical load sequences

We present an optical sensing methodology to estimate the fatigue damage state of structures made of carbon fiber reinforced polymer (CFRP), by measuring variations on the surface roughness. Variable amplitude loads (VAL), which represent realistic loads during aeronautical missions of fighter aircraft (FALSTAFF) have been applied to coupons until failure. Stiffness degradation and surface roughness variations have been measured during the life of the coupons obtaining a Pearson correlation of 0.75 between both variables. The data were compared with a previous study for Constant Amplitude Load (CAL) obtaining similar results. Conclusions suggest that the surface roughness measured in strategic zones is a useful technique for structural health monitoring of CFRP structures, and that it is independent of the type of load applied. Surface roughness can be measured in the field by optical techniques such as speckle, confocal perfilometers and interferometry, among others.

Damage tolerance of cold drawn ferritic-austenitic stainless steels wires for prestressed concrete

Damage tolerance of high strength cold-drawn ferritic–austenitic stainless steel wires is assessed by means of tensile fracture tests of cracked wires. The fatigue crack is transversally propagated from the wire surface. The damage tolerance curve of the wires results from the empirical failure load when given as a function of crack depth. As a consequence of cold drawing, the wire microstructure is orientated along its longitudinal axis and anisotropic fracture behaviour is found at macrostructural level at the tensile failure of the cracked specimens. An in situ optical technique known as video image correlation VIC-2D is used to get an insight into this failure mechanism by tensile testing transversally fatigue cracked plane specimens extracted from the cold-drawn wires. Finally, the experimentally obtained damage tolerance curve of the cold-drawn ferritic–austenitic stainless steel wires is compared with that of an elementary plastic collapse model and existing data of two types of high strength eutectoid steel currently used as prestressing steel for concrete.