Improved GaN-based HEMT performance by nanocrystalline diamond capping

As a wide-bandgap semiconductor, gallium nitride (GaN) is an attractive material for next-generation power devices. To date, the capabilities of GaN-based high electron mobility transistors (HEMTs) have been limited by self-heating effects (drain current decreases due to phonon scattering-induced carrier velocity reductions at high drain fields). Despite awareness of this, attempts to mitigate thermal impairment have been limited due to the difficulties involved with placing high thermal conductivity materials close to heat sources in the device. Heat spreading schemes have involved growth of AIGaN/GaN on single crystal or CVD diamond, or capping of fullyprocessed HEMTs using nanocrystalline diamond (NCD). All approaches have suffered from reduced HEMT performance or limited substrate size. Recently, a "gate after diamond" approach has been successfully demonstrated to improve the thermal budget of the process by depositing NCD before the thermally sensitive Schottky gate and also to enable large-area diamond implementation.

Sputter optimization of AlN on diamond substrates for high frequency SAW resonators

The AlN/diamond structure is an attractive combination for SAW devices and its application at high frequencies. In this work, the synthesis of AlN thin films by reactive sputtering has been optimized on diamond substrates in order to process high frequency devices. Polished microcrystalline and as-grown nanocrystalline diamond substrates have been used to deposit AlN of different thickness under equal sputtering conditions. For the smoother substrates, the FWHM of the rocking curve of the (002) AlN peak varies from 3.8° to 2.7° with increasing power. SAW one port resonators have been fabricated on these films, whose electrical characterization (in terms of S11 parameters) is reported.

Fabrication of high frequency SAW resonators using AlN/Diamond/Si technology

The synthesis of AlN on diamond is a great challenge, not only because of the between an AlN/diamond interface, but also because of the high surface roughness of the diamond layers [8, 9]. In the case of microcrystalline diamond, the last problem was solved by polishing. However, polishing nanocrystalline diamond is not straightforward. For the diamond synthesis by CVD, silicon was used as a substrate. The diamond/Si interface presents a smoother diamond than the diamond/air interface. This paper reports on the fabrication of high frequency SAW resonators using AlN/Diamond/Si technology.

Optimization of AlN thin layers on diamond substrates for high frequency SAW resonators

AlN/diamond heterostructures are very promising for high frequency surface acoustic wave (SAW) resonators. In their design, the thickness of the piezoelectric film is one of the key parameters. On the other hand, the film material quality and, hence, the device performance, also depend on that thickness. In this work, polished microcrystalline diamond substrates have been used to deposit AlN films by reactive sputtering, from 150 nm up to 3 μm thick. A high degree of the c-axis orientation has been obtained in all cases. SAW one port resonators at high frequency have been fabricated on these films with a proper combination of the film thickness and transducer size.

Determination of a refractive index and an extinction coefficient of standard production of CVD-graphene

The refractive index and extinction coefficient of chemical vapour deposition grown graphene are determined by ellipsometry analysis. Graphene films were grown on copper substrates and transferred as both monolayers and bilayers onto SiO2/Si substrates by using standard manufacturing procedures. The chemical nature and thickness of residual debris formed after the transfer process were elucidated using photoelectron spectroscopy. The real layered structure so deduced has been used instead of the nominal one as the input in the ellipsometry analysis of monolayer and bilayer graphene, transferred onto both native and thermal silicon oxide. The effect of these contamination layers on the optical properties of the stacked structure is noticeable both in the visible and the ultraviolet spectral regions, thus masking the graphene optical response. Finally, the use of heat treatment under a nitrogen atmosphere of the graphene-based stacked structures, as a method to reduce the water content of the sample, and its effect on the optical response of both graphene and the residual debris layer are presented. The Lorentz-Drude model proposed for the optical response of graphene fits fairly well the experimental ellipsometric data for all the analysed graphene-based stacked structures.