Inorganic Photovoltaics - Planar and Nanostructured Devices

Since its invention in the 1950s, semiconductor solar cell technology has evolved in great leaps and bounds. Solar power is now being considered as a serious leading contender for replacing fossil fuel based power generation. This article reviews the evolution and current state, and potential areas of near future research focus, of leading inorganic materials based solar cells, including bulk crystalline, amorphous thin-films, and nanomaterials based solar cells. Bulk crystalline silicon solar cells continue to dominate the solar power market, and continued efforts at device fabrication improvements, and device topology advancements are discussed. III-V compound semiconductor materials on c-Si for solar power generation are also reviewed. Developments in thin-film based solar cells are reviewed, with a focus on amorphous silicon, copper zinc tin sulfide, cadmium telluride, as well as nanostructured Cadmium telluride. Recent developments in the use of nano-materials for solar power generation, including silicon and gallium arsenide nanowires, are also reviewed.

Improved modeling of photoluminescent and electroluminescent coupling in multijunction solar cells

The performance of tandem stacks of Group III?V multijunction solar cells continues to improve rapidly, both through improved performance of the individual cells in the stack and throughi ncrease in the number of stacked cells. As the radiative efficiency of these individual cells increases, radiative coupling between the stacked cells becomes an increasingly important factor not only in cell design, but also in accurate efficiency measurement and in determining performance of cells and systems under varying spectral conditions in the field. Past modeling has concentrated on electroluminescent coupling between the cells, although photoluminescent coupling is shown to be important for cells operating near their maximum power point voltage or below or when junction defect recombination is significant. Extension of earlier models i sproposed to allow this non-negligible component of luminescent coupling to be included. Therefined model is validated by measurement of the closely related external emission from both single and double junction cells.

Correlation among Growth Conditions, Morphology, and Optical Properties of Nanocolumnar InGaN/GaN Heterostructures Selectively Grown by Molecular Beam Epitaxy

This work reports on the selective area growth mechanism of green-emitting InGaN/GaN nanocolumns. The evolution of the morphology of the InGaN segment is found to depend critically on the nominal III/V ratio as well as the diameter of the GaN section. In addition, the In distribution inside the InGaN segment is found to depend on the local III/V and In/Ga ratios.

Internal quantum efficiency of III-nitride quantum dot superlattices grown by plasma-assisted molecular-beam epitaxy

We present a study of the optical properties of GaN/AlN and InGaN/GaN quantum dot (QD) superlattices grown via plasma-assisted molecular-beam epitaxy, as compared to their quantum well (QW) counterparts. The three-dimensional/two-dimensional nature of the structures has been verified using atomic force microscopy and transmission electron microscopy. The QD superlattices present higher internal quantum efficiency as compared to the respective QWs as a result of the three-dimensional carrier localization in the islands. In the QW samples, photoluminescence (PL) measurements point out a certain degree of carrier localization due to structural defects or thickness fluctuations, which is more pronounced in InGaN/GaN QWs due to alloy inhomogeneity. In the case of the QD stacks, carrier localization on potential fluctuations with a spatial extension smaller than the QD size is observed only for the InGaN QD-sample with the highest In content (peak emission around 2.76 eV). These results confirm the efficiency of the QD three-dimensional confinement in circumventing the potential fluctuations related to structural defects or alloy inhomogeneity. PL excitation measurements demonstrate efficient carrier transfer from the wetting layer to the QDs in the GaN/AlN system, even for low QD densities (~1010 cm-3). In the case of InGaN/GaN QDs, transport losses in the GaN barriers cannot be discarded, but an upper limit to these losses of 15% is deduced from PL measurements as a function of the excitation wavelength.

Substrate nanopatterning by e-beam lithography to growth ordered arrays of III-nitride nanodetectors, white light emitters, and solar cells

III-nitride nanorods have attracted much scientific interest during the last decade because of their unique optical and electrical properties [1,2]. The high crystal quality and the absence of extended defects make them ideal candidates for the fabrication of high efficiency opto-electronic devices such as nano-photodetectors, light-emitting diodes, and solar cells [1-3]. Nitride nanorods are commonly grown in the self-assembled mode by plasma-assisted molecular beam epitaxy (MBE) [4]. However, self-assembled nanorods are characterized by inhomogeneous heights and diameters, which render the device processing very difficult and negatively affect the electronic transport properties of the final device. For this reason, the selective area growth (SAG) mode has been proposed, where the nanorods preferentially grow with high order on pre-defined sites on a pre-patterned substrate

Oxygen photo-adsorption related quenching of photoluminescence in group-III nitride nanocolumns

GaN and InGaN nanocolumns of various compositions are studied by room-temperature photoluminescence (PL) under different ambient conditions. GaN nanocolumns exhibit a reversible quenching upon exposure to air under constant UV excitation, following a t−1/2 time dependence and resulting in a total reduction of intensity by 85–90%, as compared to PL measured in vacuum, with no spectral change. This effect is not observed when exposing the samples to pure nitrogen. We attribute this effect to photoabsorption and photodesorption of oxygen that modifies the surface potential bending. InGaN nanocolumns, under the same experimental conditions do not show the same quenching features: The high-energy part of the broad PL line is not modified by exposure to air, whereas a lower-energy part, which does quench by 80–90%, can now be distinguished. We discuss the different behaviors in terms of carrier localization and possible composition or strain gradients in the InGaN nanocolumns.

Advances on MBE selective area growth of III-nitride nanostructures: from nanoLEDs to pseudo substrates

The aim of this work is to provide an overview on the recent advances in the selective area growth (SAG) of (In)GaN nanostructures by plasma assisted molecular beam epitaxy, focusing on their potential as building blocks for next generation LEDs. The first three sections deal with the basic growth mechanisms of GaN SAG and the emission control in the entire ultraviolet to infrared range, including approaches for white light emission, using InGaN disks and thick segments on axial nanocolumns. SAG of axial nanostructures is eveloped on both GaN/sapphire templates and GaN-buffered Si(111). As an alternative to axial nanocolumns, section 4 reports on the growth and characterization of InGaN/GaN core-shell structures on an ordered array of top-down patterned GaN microrods. Finally, section 5 reports on the SAG of GaN, with and without InGaN insertion, on semi-polar (11-22) and non-polar (11-20) templates. Upon SAG the high defect density present in the templates is strongly reduced as indicated by a dramatic improvement of the optical properties. In the case of SAG on nonpolar (11-22) templates, the formation of nanostructures with a low aspect ratio took place allowing for the fabrication of high-quality, non-polar GaN pseudo-templates by coalescence of these nanostructures.