Characterization of ZnO Nanorods Grown on GaN Using Aqueous Solution Method

Uniformly distributed ZnO nanorods with diameter 70-100 nm and 1-2μm long have been successfully grown at low temperatures on GaN by using the inexpensive aqueous solution method. The formation of the ZnO nanorods and the growth parameters are controlled by reactant concentration, temperature and pH. No catalyst is required. The XRD studies show that the ZnO nanorods are single crystals and that they grow along the c axis of the crystal plane. The room temperature photoluminescence measurements have shown ultraviolet peaks at 388nm with high intensity, which are comparable to those found in high quality ZnO films. The mechanism of the nanorod growth in the aqueous solution is proposed. The dependence of the ZnO nanorods on the growth parameters was also investigated. While changing the growth temperature from 60°C to 150°C, the morphology of the ZnO nanorods changed from sharp tip (needle shape) to flat tip (rod shape). These kinds of structure are useful in laser and field emission application.

Growth and Characterization of LiCoO₂ Thin Films for Microbatteries

LiCoO₂thin films have been grown by pulsed laser deposition on stainless steel and SiO₂/Si substrates. The film deposited at 600°C in an oxygen partial pressure of 100mTorr shows an excellent crystallinity, stoichiometry and no impurity phase present. Microstructure and surface morphology of thin films were examined using a scanning electron microscope. The electrochemical properties of the thin films were studied with cyclic voltammetry and galvanostatic charge-discharge techniques in the potential range 3.0-4.2 V. The initial discharge capacity of the LiCoO2 thin films deposited on the stainless steel and SiO₂/Si substrates reached 23 and 27 µAh/cm², respectively.