Polycrystalline diamond thin film as wide bandgap material: the optoelectronic behaviour and the relationship with the structure

In this work metal - Microwave Plasma CVD diamond Schottky devices were studied. The current density vs. applied voltage reveals rectification ratios up to 10(4) at \ +/- 2V \. Under illumination an inversion and increase of the rectification is observed. The carrier density is 10(15) cm(-3) and the ideality factors near 1.5. The dark current vs. temperature shows that below 150 K the bulk transport is controlled by a hopping process with a density of defects of 10(16) cm(-3). For higher temperatures an extrinsic ionisation with activation energy of 0.3 eV takes place. The correlation with the polycrystalline nature of the samples is focused.

Charge transport in poly(3-methylthiophene) schottky barrier diodes

Schottky-barrier devices were formed from electropolymerised films of poly (3-methylthiophene) (PMeT). Thermal annealing of a partially undoped film led to diodes with rectification ratios as high as 5900 at 1 V and 50,000 at 2.5 V and ideality factors slightly above 2. The temperature dependence of ac loss tangent and forward currents are identical suggesting that bulk effects dominate device behaviour event at very low forward voltages. Below 250 K forward currents are essentially independent of temperature. Preliminary TSC measurements show the presence of at least two trapping levels in the devices. © 1993.