Annealing of nylon-1010 under high pressure

Full Paper: A study has been made on the annealing of nylon-1010 under high pressures. Heat treatment of melt-crystallized nylon-1010 was performed at 250degreesC for 30 min in the pressure range 0.7 similar to 2.5 GPa. It was found that the triclinic crystals of virgin nylon-1010 were retained at pressures less than 1.0 GPa or larger than 1.2 GPa. The X-ray diffraction intensity of (100) planes decreased with increasing pressure. The diffraction peaks shifted slightly to higher angles (2theta) relative to the virgin nylon-1010, indicating dense packing of polymer chains at high pressures. The highest melting temperature was 208degreesC for the sample annealed at 1.5 GPa. No extended-chain crystals were formed under the experimental conditions. Crosslinking occurred in the pressure range 1.0 similar to 1.2 GPa. The structure of the crosslinked samples was characterized by means of infrared spectroscopy and X-ray photoelectron spectroscopy. It is concluded that a mechanism of crosslinking via carbodiimide can explain the nature of crosslinking of nylon-1010 annealed at high pressures. The remarkable changes of the structure of annealed nylon-1010 are also discussed in this article.