Synthesis of NaA zeolite membrane on a ceramic hollow fiber

NaA zeolite membrane was successfully synthesized on a ceramic hollow fiber with an outer diameter of 400 mum, a thickness of 100 mum and an average pore radius of 0.1 mum. The as-synthesized membranes were characterized by XRD, SEM as well as gas permeation. A continuous C NaA zeolite membrane formed after a three-stage synthesis. The membrane thickness was similar to5 mum. Gas permeation data indicated that a relatively high quality NaA zeolite membrane formed on the ceramic hollow fiber support. (C) 2003 Elsevier B.V. All rights reserved.

Microwave-assisted hydrothermal synthesis of hydroxy-sodalite zeolite membrane

A high quality pure hydroxy-sodalite zeolite membrane was successfully synthesized on an alpha-Al2O3 support by a novel microwave-assisted hydrothermal synthesis (MARS) method. Influence of synthesis conditions, such as synthesis time, synthesis procedure, etc., on the formation of hydroxy-sodalite zeolite membrane by MAHS method was studied by X-ray diffraction (XRD), scanning electron microscopy (SEM) and gas permeation measurements. The synthesis of hydroxy-sodalite zeolite membrane by MAHS method only needed 45 min and synthesis was more than 8 times faster than by the conventional hydrothermal synthesis (CHS) method. A pure hydroxy-sodalite zeolite membrane was easily synthesized by MAHS method, while a zeolite membrane, which consisted of NaX zeolite, NaA zeolite and hydroxy-sodalite zeolite, was usually synthesized by CHS method. The effect of preparation procedures had a dramatic impact on the formation of hydroxy-sodalite zeolite membrane and a single-stage synthesis procedure produced a pure hydroxy-sodalite zeolite membrane. The pure hydroxy-sodalite zeolite membrane synthesized by MARS method was found to be well inter-grown and the thickness of the membrane was 6-7 mum. Gas permeation results showed that the hydrogen/n-butane permselectivity of the hydroxy-sodalite zeolite membrane was larger than 1000. (C) 2004 Elsevier Inc. All rights reserved.

Synthesis and gas permeation properties of an NaA zeolite membrane

A high quality NaA zeolite membrane, which shows a H-2/n-C4H10 permselectivity of 106, has been synthesized on a seeded alpha-Al2O3 support by a multistage synthesis method.

Fast formation of NaA zeolite membrane in the microwave field

NaA zeolite membrane was successfully synthesized on the porous alpha-Al2O3 support by microwave heating. The synthesis of NaA zeolite membrane in the microwave field only needs 15 min and the synthesis time is 10 times shorter than that by conventional heating. SEM characterization indicates that the zeolite crystals in the NaA zeolite membrane synthesized by microwave heating are uniform in size; the membrane thickness is about 4 mu m and is thinner than that of the NaA zeolite membrane synthesized by conventional heating. Gas permeation studies indicate that the permeances of the NaA zeolite membrane synthesized by microwave heating are 3-4 times higher than those of the NaA zeolite membrane synthesized by conventional heating, while their permselectivities are comparable.

Synthesis of a high-permeance NaA zeolite membrane by microwave heating

Zeolite membranes with high permeance and separation factors are highly desirable for practical applications. Although, in the past, very good separation factors have been obtained, it has proved difficult to achieve a high permeance. Ken a comparative study of microwave versus conventional heating in the hydrothermal synthesis of NaA zeolite membranes is made. It is demonstrated that membranes prepared by microwave heating have not only a higher permeance but also a considerably shorter synthesis time. These observations are rationalized by examining the mechanism of membrane formation.

Synthesis of NaA zeolite membrane by microwave heating

The synthesis of NaA zeolite membrane on a porous alpha -Al2O3 support by microwave heating (MH) was investigated. The formation of a NaA zeolite membrane was drastically promoted by MH. The synthesis time was reduced from 3 h for conventional heating (CH) to 15 min for MH. Surface seeding cannot only promote the formation of NaA zeolite on the support, but also inhibit the transformation of NaA zeolite into other types of zeolites. The thickness of the NaA zeolite membrane synthesized by MH was about 4 mum, thinner than that of NaA zeolite membrane synthesized by CH. The permeance of NaA zeolite membrane synthesized by MH was four times higher than that of the NaA zeolite membrane synthesized by CH, while their permselectivities were comparable. Multi-stage synthesis resulted in the transformation of NaA zeolite into other types of zeolites, and the perfection of the as-synthesized membrane decreased.

Synthesis and perfection evaluation of NaA zeolite membrane

The synthesis of NaA zeolite membrane on a porous alpha -Al2O3 support from clear solution and the evaluation of the perfection of the as-synthesized membrane by gas permeation were investigated. When an unseeded support was used, the NaA zeolite began to transform into other types of zeolites before a continuous NaA zeolite membrane formed. When the support was coated with nucleation seeds, not only the formation of NaA zeolite on the support surface was accelerated, but also the transformation of NaA zeolite into other types of zeolites was inhibited. A continuous NaA zeolite membrane can be formed. Perfection evaluation indicated that the NaA zeolite membrane with the synthesis time of 3 h showed the best perfection after a one-stage synthesis. The perfection of NaA zeolite membrane can be improved by employing the multi-stage synthesis method. The NaA zeolite membrane with a synthesis time of 2 h after a two-stage synthesis showed the best gas permeation performance, The permselectivity of H-2/n-C4H10 and O-2/N-2 were 19.1 and 1.8, respectively, higher than those of the corresponding Knudsen diffusion selectivity of 5.39 and 0.94, which showed the molecular sieving effect of NaA zeolite. However, the permeation of n-C4H10 also indicated that the NaA zeolite membrane had certain defects, the diameter of which were larger than the NaA zeolite channels. (C) 2001 Elsevier Science B.V. All rights reserved.

Preparation of zeolite-metal composite membrane

A NaA zeolite membrane was synthesized on the surface of the stainless steel stab. The membrane was characterized by XRD and SEM. The membrane was continuous and highly intergrown. The size of NaA zeolite crystals was about 5 similar to 6 mum.