Obtenção de pós de tântalo metálico a partir da redução aluminotérmica com ignição a plasma

Metallic tantalum has a high commercial value due to intrinsic properties like excellent ductility, corrosion resistance, high melt and boiling points and good electrical and thermal conductivities. Nowadays, it is mostly used in the manufacture of capacitors, due to excellent dielectric properties of its oxides. In the nature, tantalum occurs in the form of oxide and it is extracted mainly from tantalite-columbite ores. The tantalum is usually produced by the reduction of its oxide, using reductants like carbon, silicon, calcium, magnesium and aluminum. Among these techniques, the aluminothermic reduction has been used as the industrial method to produce niobium, tantalum and their alloys, due to the easy removal of the Al and Al2O3 of the system, easing further refining. In conventional aluminothermic reduction an electrical resistance is used to trigger the reaction. This reaction self-propagates for all the volume of material. In this work, we have developed a novel technique of aluminothermic reduction that uses the hydrogen plasma to trigger the reaction. The results obtained by XRD, SEM and EDS show that is possible to obtain a compound rich in tantalum through this technique of aluminothermic reduction in the plasma reactor

Obtenção de pós de tântalo metálico a partir da redução aluminotérmica com ignição a plasma

Metallic tantalum has a high commercial value due to intrinsic properties like excellent ductility, corrosion resistance, high melt and boiling points and good electrical and thermal conductivities. Nowadays, it is mostly used in the manufacture of capacitors, due to excellent dielectric properties of its oxides. In the nature, tantalum occurs in the form of oxide and it is extracted mainly from tantalite-columbite ores. The tantalum is usually produced by the reduction of its oxide, using reductants like carbon, silicon, calcium, magnesium and aluminum. Among these techniques, the aluminothermic reduction has been used as the industrial method to produce niobium, tantalum and their alloys, due to the easy removal of the Al and Al2O3 of the system, easing further refining. In conventional aluminothermic reduction an electrical resistance is used to trigger the reaction. This reaction self-propagates for all the volume of material. In this work, we have developed a novel technique of aluminothermic reduction that uses the hydrogen plasma to trigger the reaction. The results obtained by XRD, SEM and EDS show that is possible to obtain a compound rich in tantalum through this technique of aluminothermic reduction in the plasma reactor

Redução aluminotérmica do óxido de tântalo usando uma tocha de plasma como ignitor

In this work was used a plasma torch of non transferred arc with argon as work gas, using a power supply with maximum DC current of 250 A and voltage of 30 V to activate the plasma and keep it switched on. The flame temperature was characterized by optical emission spectroscopy, through Boltzmann-plot-method. The torch has been used like igniter in the aluminothermic reduction of the mixture tantalum oxide and aluminum, seeking to obtain metallic tantalum. In heating of the reagents only one particle will be considered to study interactions between plasma-particle, seeking to determinate its fusion and residence time. The early powders were characterized by laser granulometry, scanning electron microscopy (SEM) and X-ray diffraction analysis. The final product of this reaction was characterized by SEM and X-ray diffraction. Crystallite size was calculated by the Scherrer equation and microdeformation was determined using Willamsom-Hall graph. With Rietveld method was possible to quantify the percentile in weight of the products obtained in the aluminothermic reaction. Semi-quantitative chemical analysis (EDS) confirmed the presence of metallic tantalum and Al2O3 as products of the reduction. As was waited the particle size of the metallic tantalum produced, presents values in nanometric scale due the short cooling time of those particles during the process

Redução aluminotérmica do óxido de tântalo usando uma tocha de plasma como ignitor

In this work was used a plasma torch of non transferred arc with argon as work gas, using a power supply with maximum DC current of 250 A and voltage of 30 V to activate the plasma and keep it switched on. The flame temperature was characterized by optical emission spectroscopy, through Boltzmann-plot-method. The torch has been used like igniter in the aluminothermic reduction of the mixture tantalum oxide and aluminum, seeking to obtain metallic tantalum. In heating of the reagents only one particle will be considered to study interactions between plasma-particle, seeking to determinate its fusion and residence time. The early powders were characterized by laser granulometry, scanning electron microscopy (SEM) and X-ray diffraction analysis. The final product of this reaction was characterized by SEM and X-ray diffraction. Crystallite size was calculated by the Scherrer equation and microdeformation was determined using Willamsom-Hall graph. With Rietveld method was possible to quantify the percentile in weight of the products obtained in the aluminothermic reaction. Semi-quantitative chemical analysis (EDS) confirmed the presence of metallic tantalum and Al2O3 as products of the reduction. As was waited the particle size of the metallic tantalum produced, presents values in nanometric scale due the short cooling time of those particles during the process

Revestimentos a base de Ta/Al2O3 produzidos por aspersão térmica sobre substrato metálico

Metal substrates were coated by thermal spraying plasma torch, they were positioned at a distance of 4 and 5 cm from the nozzle exit of the plasma jet. The starting materials were used for deposition of tantalum oxide powder and aluminium. These two materials were mixed and ground into high-energy mill, then immersed in the torch for the production of alumina coating infused with particles of tantalum with nano and micrometric size. The spraying equipment used is a plasma torch arc not transferred, which operating in the range of 250 A and 80 V, was able to produce enough heat to ignite aluminothermic between Ta2O5 and aluminum. Upon reaching the plasma jet, the mixing powders react with the heat of the blaze, which provides sufficient energy for melting aluminum particles. This energy is transferred through mechanisms of self-propagating to the oxide, beginning a reduction reaction, which then hits on the surface of the substrate and forms a coating on which a composite is formed by a junction metal - ceramic (Ta +Al2O3). The phases and quantification of each were obtained respectively by X-ray diffraction and the Rietveld method. Morphology by scanning electron microscopy and chemical analysis by energy dispersive spectroscopy EDS. It was also performed measurements of the substrate roughness, Vickers microhardness measurements in sprays and determination of the electron temperature of the plasma jet by optical emission spectroscopy EEO. The results confirmed the expectation generated around the end product of spraying the mixture Ta2O5 + Al, both in the formation of nano-sized particles and in their final form. The electron excitation temperature was consistent with the purpose of work, in addition, the thermodynamic temperature was efficient for the reduction process of Ta2O5. The electron excitation temperature showed values of 3000, 4500 and 8000 K for flows10, 20 and 30 l / min respectively, these values were taken at the nozzle exit of the plasma jet. The thermodynamic temperature around 1200 ° C, was effective in the reduction process of Ta2O5

Revestimentos a base de Ta/Al2O3 produzidos por aspersão térmica sobre substrato metálico

Metal substrates were coated by thermal spraying plasma torch, they were positioned at a distance of 4 and 5 cm from the nozzle exit of the plasma jet. The starting materials were used for deposition of tantalum oxide powder and aluminium. These two materials were mixed and ground into high-energy mill, then immersed in the torch for the production of alumina coating infused with particles of tantalum with nano and micrometric size. The spraying equipment used is a plasma torch arc not transferred, which operating in the range of 250 A and 80 V, was able to produce enough heat to ignite aluminothermic between Ta2O5 and aluminum. Upon reaching the plasma jet, the mixing powders react with the heat of the blaze, which provides sufficient energy for melting aluminum particles. This energy is transferred through mechanisms of self-propagating to the oxide, beginning a reduction reaction, which then hits on the surface of the substrate and forms a coating on which a composite is formed by a junction metal - ceramic (Ta +Al2O3). The phases and quantification of each were obtained respectively by X-ray diffraction and the Rietveld method. Morphology by scanning electron microscopy and chemical analysis by energy dispersive spectroscopy EDS. It was also performed measurements of the substrate roughness, Vickers microhardness measurements in sprays and determination of the electron temperature of the plasma jet by optical emission spectroscopy EEO. The results confirmed the expectation generated around the end product of spraying the mixture Ta2O5 + Al, both in the formation of nano-sized particles and in their final form. The electron excitation temperature was consistent with the purpose of work, in addition, the thermodynamic temperature was efficient for the reduction process of Ta2O5. The electron excitation temperature showed values of 3000, 4500 and 8000 K for flows10, 20 and 30 l / min respectively, these values were taken at the nozzle exit of the plasma jet. The thermodynamic temperature around 1200 ° C, was effective in the reduction process of Ta2O5

Simulação com o código GEANT4 de medida de espessura de revestimento metálico em metal por XRF

Nesta dissertação são apresentados resultados de simulações Monte Carlo de fluorescência de raios X (XRF), utilizando o programa GEANT4, para medidas de espessura de revestimento metálico (Ni e Zn) em base metálica (Fe). As simulações foram feitas para dois tamanhos de espessura para cada metal de revestimento, (5μm e 10μm), com passos de 0,1 μm e 0,001 μm e com 106 histórias. No cálculo da espessura do revestimento foram feitas as aproximações de feixe de raios X monoenegético, com a análise da transmissão apenas da energia do K-alfa e para uma geometria compatível com um sistema real de medição (ARTAX-200). Os resultados mostraram a eficiência da metodologia de simulação e do cálculo da espessura do revestimento, o que permitirá futuros cálculos, inclusive para multirevestimentos metálicos em base metálica.

Medição de espessura de filmes eletrodepositados em suporte metálico por EDXRF

Esse trabalho apresenta a técnica de fluorescência de raios X por dispersão de energia (EDXRF) para calcular a espessura de filmes metálicos finos por ser de custo relativamente baixo, não destrutiva e que permite também uma análise qualitativa e até quantitativa dos elementos do revestimento. As espessuras do Níquel, Zinco e Cromo sobre aço, foram calculadas utilizando cinco procedimentos diferentes e todas as relações matemáticas obtidas foram baseadas na lei de atenuação de Beer-Lambert, que relaciona as intensidades Kα e/ou Kβ e as relações específicas do material (coeficiente de atenuação, μm). Os resultados experimentais para as espessuras do Zinco e Níquel, utilizando somente a intensidade Kα, apresentaram valores próximos dos valores estimados. Quando foi considerada a razão Kα/Kβ, os resultados experimentais divergiram bastante do estimado. Para calcular a espessura do Cromo foi necessário utilizar um método em que as camadas são calculadas separadamente, pois o revestimento de Cromo é composto por múltiplas camadas (Cromo, Cobre e Níquel), Os resultados para a espessura do Cromo foram satisfatórios.

Estudo dos modos de Plasmon em Fibras fracamente guiadas com camadas dielétricas sobre Filme Metálico.

Neste trabalho são analisados os quatro modos de plasmon, ligados simétrico (Sb) e assimétrico (ab), fuga pelo núcleo (ln) e fuga pela cobertura (lc), que se propagam em uma fibra óptica fracamente guiada envolta por um filme metálico. No filme metálico é depositada uma camada dielétrica extra e acima desta, uma outra denominada cobertura. A análise será desenvolvida para filmes metálicos de prata, paládio e ouro. Esta estrutura é muito útil na confecção de sensores ópticos.

Dimensionamento de um pavilhão industrial metálico com fundações indirectas

Trabalho de projecto para obtenção do grau de Mestre em Engenharia Civil na Área de Especialização em Estruturas

Dimensionamento de um edifício metálico de ensacagem a construir numa instalação industrial

Trabalho de Projeto para obtenção do grau de Mestre em Engenharia Civil na Área de Especialização de Estruturas

Optimização da estrutura principal de um armazém metálico

Esta Tese consiste no cálculo estrutural de um pórtico pertencente a um suposto pavilhão instalado na zona Industrial de Matosinhos. Trata-se de um estudo comparativo entre dois tipos de pórticos metálicos que incluem o estudo das várias vertentes de permeabilidade. O objectivo é a optimização da quantidade de aço e betão que satisfaçam os requisitos segundo o REAP e Eurocódigo para a concepção deste pórtico. Posteriormente é feito uma análise crítica aos resultados obtidos.

Síntesis del tetraester metílico del ácido etilendiaminotetraacetico

Tesis (Maestría en Ciencias Químicas con Especialidad en Química Orgánica) UANL

La técnica del procedimiento de soldar por medio del sistema de arco metálico continuo con protección de CO2

UANL

Observación de la ley de Lenz con un imán y un tubo metálico

Resumen tomado de la publicación