Bond strength of a pit-and-fissure sealant associated to etch-and-rinse and self-etching adhesive systems to saliva-contaminated enamel: individual vs. simultaneous light curing

This study evaluated in vitro the shear bond strength (SBS) of a resin-based pit-and-fissure sealant [Fluroshield (F), Dentsply/Caulk] associated with either an etch-and-rinse [Adper Single Bond 2 (SB), 3M/ESPE] or a self-etching adhesive system [Clearfil S3 Bond (S3), Kuraray Co., Ltd.] to saliva-contaminated enamel, comparing two curing protocols: individual light curing of the adhesive system and the sealant or simultaneous curing of both materials. Mesial and distal enamel surfaces from 45 sound third molars were randomly assigned to 6 groups (n=15), according to the bonding technique: I - F was applied to 37% phosphoric acid etched enamel. The other groups were contaminated with fresh human saliva (0.01 mL; 10 s) after acid etching: II - SB and F were light cured separately; III - SB and F were light cured together; IV - S3 and F were light cured separately; V - S3 and F were light cured simultaneously; VI - F was applied to saliva-contaminated, acid-etched enamel without an intermediate bonding agent layer. SBS was tested to failure in a universal testing machine at 0.5 mm/min. Data were analyzed by one-way ANOVA and Fisher's test (α=0.05).The debonded specimens were examined with a stereomicroscope to assess the failure modes. Three representative specimens from each group were observed under scanning electron microscopy for a qualitative analysis. Mean SBS in MPa were: I-12.28 (±4.29); II-8.57 (±3.19); III-7.97 (±2.16); IV-12.56 (±3.11); V-11.45 (±3.77); and VI-7.47 (±1.99). In conclusion, individual or simultaneous curing of the intermediate bonding agent layer and the resin sealant did not seem to affect bond strength to saliva-contaminated enamel. S3/F presented significantly higher SBS than the that of the groups treated with SB etch-and-rinse adhesive system and similar SBS to that of the control group, in which the sealant was applied under ideal dry, noncontaminated conditions.

Influence of sodium hypochlorite and edta on the microtensile bond strength of a self-etching adhesive system

Chemical substances used during biomechanical preparation of root canals can alter the composition of dentin surface and affect the interaction with restorative materials. OBJECTIVE: The purpose of this study was to evaluate the microtensile bond strength (µTBS) of a self-etching adhesive system to dentin irrigated with sodium hypochlorite (NaOCl) and ethylenediaminetetraacetic acid (EDTA). MATERIAL AND METHODS: Thirty human third molars were sectioned 3 mm below the occlusal surface, polished with 600- to 1200-grit silicon carbide papers, and randomly divided into 3 groups: G1 (control): no irrigating solution; G2: 1% NaOCl; and G3: 1% NaOCl followed by the application of 17% EDTA. The specimens received the self-etching adhesive system (XENO III - Dentsply), restored with microhybrid composite resin (Z250 - 3M ESPE), sectioned and trimmed to create 4 hourglass-shaped slabs of each tooth. The slabs were tested in microtensile strength in a universal testing machine (Emic DL 2000) at a crosshead speed of 0.5 mm/min until fracture. The results were analyzed statistically by ANOVA and Newman-Keuls test. RESULTS: Mean µTBS values and standard deviations in MPa were: G1 = 11.89 ± 4.22; G2 = 19.41 ± 5.32; G3 = 11.34 ± 4.73. 1% NaOCl increased the adhesive resistance significantly (p<0.001/F=22.5763). The application of 1% NaOCl/17% EDTA resulted in statistically similar µTBS to the control group. CONCLUSIONS: None of the irrigants affected negatively the µTBS of XENO III to dentin. The use of 1% NaOCl alone resulted in higher bond strength than the other treatments. The combination of 1% NaOCl and 17% EDTA produced similar bond strength to that of untreated dentin.

Do the origins of primary teeth affect the bond strength of a self-etching adhesive system to dentin?

The aim of this in vitro study was to evaluate the tensile bond strength of a self-etching adhesive system to three different dentinal substrates. Primary molar teeth that had been recently exfoliated (RE), with unknown time of exfoliation (UT), and extracted due to prolonged retention (PR) were used for this investigation. Ten primary molar teeth of each group were cut in the middle following the mesio-distal direction, creating a total of twenty specimens per group. The specimens were included in acrylic resin and had a flat dentin surface exposed. The self-etching adhesive system was applied to this surface and a 3-millimeter high cone with diameter of 2 mm in the adhesion area was constructed using composite resin. The specimens were stored in distilled water at 37ºC for 24 hours. Fifteen specimens of each substrate were used for the tensile bond test (n = 15) and 5 had the interface analyzed by scanning electron microscopy (SEM). The data was examined by one-way ANOVA and presented no significant differences between groups (p = 0.5787). The mean values obtained for RE, UT and PR were 18.39 ± 9.70, 19.41 ± 7.80, and 23.30 ± 9.37 MPa, respectively. Any dentinal substrates of primary teeth studied are safe for tensile bond strength tests with adhesive systems.

Micromorphology of Resin-Dentin Interfaces Using One-Bottle Etch&Rinse and Self-Etching Adhesive Systems on Laser-Treated Dentin Surfaces: A Confocal Laser Scanning Microscope Analysis

Background and Objectives: This study evaluated the hybrid layer (HL) morphology created by three adhesive systems (AS) on dentin surfaces treated with Er:YAG laser using two irradiation parameters. Study Design: Occlusal flat dentin surfaces of 36 human third molars were assigned into nine groups (n = 4) according to the following ASs: one bottle etch&rinse Single Bond Plus (3M ESPE), two-step Clearfil Protect Bond (Kuraray), and all-in-one S3 Bond (Kuraray) self-etching, which were labeled with rhodamine B or fluorescein isothiocyanate dextran and were applied to dentin surfaces that were irradiated with Er:YAG laser at either 120 (38.7 J/cm(2)) or 200 mJ/pulse (64.5 J/cm(2)), or were applied to untreated dentin surfaces (control group). The ASs were light-activated following MI and the bonded surfaces were restored with resin composite Z250 (3M ESPE). After 24 hours of storage in vegetable oil, the restored teeth were vertically, serially sectioned into 1-mm thick slabs, which had the adhesive interfaces analyzed with confocal laser microscope (CLSM-LSM 510 Meta). CLSM images were recorded in the fluorescent mode from three different regions along each bonded interface. Results: Non-uniform HL was created on laser-irradiated dentin surfaces regardless of laser irradiation protocol for all AS, while regular and uniform HL was observed in the control groups. ""Stretch mark""-like red lines were found within the HL as a result of resin infiltration into dentin microfissures, which were predominantly observed in 200 mJ/pulse groups regardless of AS. Poor resin infiltration into peritubular dentin was observed in most regions of adhesive interfaces created by all ASs on laser-irradiated dentin, resulting in thin resin tags with neither funnel-shaped morphology nor lateral resin projections. Conclusion: Laser irradiation of dentin surfaces at 120 or 200 mJ/pulse resulted in morphological changes in HL and resin tags for all ASs evaluated in the study. Lasers Surg. Med. 42:662-670, 2010. (C) 2010 Wiley-Liss, Inc.

Influence of Blood Contamination on Bond Strength of a Self-etching Adhesive to Dental Tissues

Purpose: The aim of this study was to detect the influence of (1) storage period of heparinized blood, (2) type of blood and presence of contaminant, (3) application mode of cleansing agents, and (4) efficacy of cleansing agents on contaminated enamel and dentin during the adhesion process of a one-step adhesive system. Materials and Methods: One hundred four human molars were sectioned into halves along the long axis for enamel and dentin tests. Heparinized and fresh blood were obtained from the same donor, applied and dried to maintain a layer of dry blood on the top of samples. The cleansing agents used were hydrogen peroxide, anionic detergent, and antiseptic solution. A one-step adhesive system (Clearfil S3 Bond) was applied on the dental surface, and composite resin cylinders were built up using Tygon tubing molds. After 24 h, the mu SBS test (1 mm/min) and fracture analysis were performed. Results: There was no statistically significant difference in bond strength values regarding the storage period of heparinized blood and the types of blood. Groups without contamination presented higher bond strengths than contaminated groups. The application mode of the cleansing agents had no influence on bond strength results. There was no statistically significant difference among cleansing agents and they were as effective as a water stream in counteracting the effect of blood contamination. Conclusion: Heparinized blood can be used as a contaminant for up to one week, and it is a reliable procedure to standardize the contaminant. The cleansing agents can be used without friction. A water stream is sufficient to remove blood contamination from dental tissues, before the application of a one-step adhesive system.

Erbium, chromium : yttrium scandium gallium garnet laser for caries removal: influence on bonding of a self-etching adhesive system

This study evaluated the influence of the dental substrates obtained after the use of different caries removal techniques on bonding of a self-etching system. Forty, extracted, carious, human molars were ground to expose flat surfaces containing caries-infected dentine surrounded by sound dentine. The caries lesions of the specimens were removed or not (control-G1) either by round steel burs and water-cooled, low speed, handpiece (G2), or by irradiation with an erbium, chromium:yttrium scandium gallium garnet (Er,Cr:YSGG) laser (2W, 20 Hz, 35.38 J/cm(2), fiber G4 handpiece with 0.2826 mm(2), non-contact mode at a 2 mm distance, 70% air/20% water-G3) or using a chemo-mechanical method (Carisolv-G4). Caries-infected, caries-affected and sound dentines were submitted to a bonding system followed by construction of a resin-based composite crown. Hour-glass shaped samples were obtained and submitted to a micro-tensile bond test. The bond strength data were compared by analysis of variance (ANOVA), complemented by Tukey`s test (P <= 0.05). The samples of sound dentine presented higher bond strengths than did samples of caries-affected dentine, except for the groups treated with the Er,Cr:YSGG laser. The highest bond strengths were observed with the sound dentine treated with burs and Carisolv. The bond strengths to caries-affected dentine were similar in all groups. Additionally, bonding to caries-affected dentine of the Er,Cr:YSGG laser and Carisolv groups was similar to bonding to caries-infected dentine. Thus, caries-affected dentine is not an adequate substrate for adhesion. Moreover, amongst the caries removal methods tested, the Er,Cr:YSGG laser irradiation was the poorest in providing a substrate for bonding with the tested self-etching system.

Direct pulp capping with a self-etching adhesive system: Histopathologic evaluation in dogs` teeth

Objective. This study evaluated histopathologically the response of pulp and periradicular tissues after pulp capping with an all-in-one self-etching adhesive system in dogs` teeth. Study design. Forty teeth of 4 dogs were assigned to 3 groups according to the pulp capping material: G1 (n = 20): self-etching adhesive system; G2 (n = 10): Ca(OH)(2); G3 (n = 10): zinc oxide-eugenol. The animals were killed 7 and 70 days after pulp capping. The pieces containing the pulp-capped teeth were removed and processed for histologic analysis. Results. At 7 days, no dentin bridge formation was observed; G1 and G3 exhibited inflammatory pulpal alterations, whereas G2 presented only mild inflammatory infiltrate in the pulp tissue adjacent to the capping material, the remainder being intact. At 70 days, no specimen in G1 or G3 presented dentin bridge formation. The remaining pulp tissue exhibited severe inflammatory alterations and areas of necrosis. In G2, all specimens showed dentin bridge formation and absence of inflammation and mineralized tissue resorption. No bacteria were identified using Brown and Brenn staining techniques in all 3 groups at any observation period. Conclusion. According to the conditions of this study, direct pulp capping with the self-etching adhesive system did not allow pulp tissue repair and failed histopathologically in 100% of the cases. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2009; 108: e34-e40)

Hybrid layer thickness and resin tag length of a self-etching adhesive bonded to sound dentin

Objectives: the purpose of this study is to employ optical microscopy to measure the thickness of the hybrid layer and the penetration (tags) of an aggressive self-etching adhesive system into sound dentin.Methods: occtusat cavities were prepared in 40 extracted human posterior teeth. The prepared teeth were randomly assigned to four experimental groups with 10 specimens each. The self-etching adhesive system Adper Prompt L-Pop was applied to the dentin surface as follows: Group 1: cavosurface enamel was etched for 60 s and dentin for 20 s with 35% phosphoric acid get, immediately followed by application of the self -etching adhesive with a brush to the entire cavity for 15 s; Groups 2, 3, and 4: no pre-etching was performed, and the self -etching adhesive was applied to both enamel and dentin for 15, 30 and 45 s, respectively. After curing, the cavities were fitted with composite resin Fittek Z250. Afterwards, the teeth were decalcified and the restorations were carefully removed for later embedding in paraffin. The specimens were serially sectioned at 6 mu m of thickness and sequentially mounted in glass slides. These sections were stained with Brown and Brenn staining for posterior analysis and measurement of the hybrid layer and resin tags on a tight microscope with a micrometric ocular 40/075. The results were submitted to analysis of variance at the 5% level.Results: whenever there was significance, the Tukey test was applied at the 5% level. The specimens receiving application of acid etching before the selfetching. adhesive displayed a larger thickness of the hybrid layer; on the other hand, specimens receiving only application of the self -etching adhesive on dentin for 15, 30 and 45 s exhibited similar thickness of the hybrid layer. As regards the resin tags, no statistically significant differences could be found between the study groups.Conclusions: it could be concluded that the increase in the time of application of the self-etching adhesive Adper Prompt L-Pop did not significantly influence the formation and thickness of hybrid layer, as well as its penetration into the sound dentin surface. (c) 2005 Elsevier Ltd. All rights reserved.

Transdentinal diffusion and cytotoxicity of self-etching adhesive systems

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Influence of human dentine on the antibacterial activity of self-etching adhesive systems against cariogenic bacteria

Objectives: The incorporation of antibacterial agents into adhesive systems has been proposed to eliminate residual bacteria from dentine. This study used the agar diffusion method to evaluate the antibacterial activity of Clearfil Protect Bond (CPB), Clearfil SE Bond (CSEB), Clearfil Tri-S Bond (C3SB) and Xeno-III (XIII) self-etching adhesive systems, with or without light-activation, against cariogenic bacteria, and to assess the influence of human dentine on the antibacterial activity of these materials.Methods: An aliquot of 10 mu l per material (and individual components) were pipetted onto paper and dentine discs distributed in Petri dishes containing bacterial culture in BHI agar. Positive control was 0.2% chlorhexidine digluconate (CHX).Results: After incubation, the adhesive components of CPB and CSEB, liquid A of XIII and C3SB did not present antibacterial activity when applied to paper discs. The non-light-activated CPB primer + adhesive promoted the greatest inhibition of Streptococcus mutans (p < 0.05), whereas with light-activation, there was no significant difference between primer + adhesive and primer alone. For Lactobacillus acidophilus, CPB primer presented the greatest antibacterial activity in both light-activation conditions (p < 0.05). Regarding the dentine discs, only CHX promoted an inhibitory effect, though less intense than on paper discs (p < 0.05). CHX presented greater antibacterial activity against S. mutans than against L. acidophilus (p < 0.05).Conclusions: Light-activation significantly reduced the antibacterial activity of the self-etching adhesive systems; MDPB incorporation contributed to the effect of adhesive systems against cariogenic bacteria; the components eluted from the adhesive systems were not capable to diffuse through 400 mu m-thick dentine disc to exert their antibacterial activity against cariogenic bacteria. (C) 2008 Elsevier Ltd. All rights reserved.

Direct pulp capping with a self-etching adhesive system: Histopathologic evaluation in dogs' teeth

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influence of Application Methods of Self-etching Adhesive Systems on Adhesive Bond Strength to Dentin

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effects of Self-Etching Adhesive Systems Used in the Dental Modelling Technique on the Cohesive Strength of Composite Resin

This study evaluated the cohesive strength of composite using self-etching adhesive systems (SE) in the lubrication of instruments between layers of composite. The specimens were made by using a Teflon (R) device. SE were used at the interface to lubricate the instruments: Group 1(G1) - control group, no lubricant was used; Group 2(G2) -Futurabond (R) M; Group 3(G3) - Optibond (R) All-In-One; Group 4(G4) - Clearfil (R) SE Bond; Group 5(G5) - Futurabond (R) NR; Group 6(G6) - Adper (R) SE Plus; Group 7(G7) - One Up Bond (R) F. Specimens were submitted to the tensile test to evaluate the cohesive strength. Data were submitted to the ANOVA and Tukey tests. ANOVA showed a value of p = 0.00. The average means (SD): G2 = 11.33(+/-3.44) a, G3 = 15.36(+/-4.06) ab, G4 = 18.9(+/-4.72) bc, G7 = 19.62(+/-4.46) bc, G5 = 21.02(+/-5.09) bc, G6 = 23.39(+/-4.17) cd, and G1 = 28.49(+/-2.89) d. All SE decreased the cohesive strength of the composite, except for Adper (R) SE Plus.

Influence of Methods of Application of Self-etching Adhesive Systems on Adhesive Bond Strength to Enamel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of the shear bond strength of a composite resin in sound, demineralized and hypermineralized bovine dentin after irradiation with Er:YAG and Nd:YAG lasers, employing a self-etching adhesive system

Background and Objectives. The adhesion of dental materials is important for the success of treatment. The aim of this study is to evaluate the bond strength of a composite resin applied with a self-etching adhesive system in different dentins after irradiation with Er:YAG and Nd:YAG lasers, observing their morphologic pattern using Scanning Electronic Microscopy (SEM). Materials and Methods. The buccal surface of 72 bovine incisors was worn until exposure of medium depth dentin. The specimens were divided into three groups; GI: normal, GII: demineralized and GIII: hypermineralized dentin. These were also divided into two subgroups; A-irradiated for 30 s with Er:YAG laser in noncontact mode at 40 mJ and 6 Hz and B- irradiated for 30 s with Nd:YAG laser in contact mode at 60 mJ and 10 Hz. The adhesive system Clearfil SE. Bond (Kuraray) and composite resin Tetric Ceram (Vivadent) were applied on the irradiated area by the incremental technique. After storage for 24 h in distilled water at 37 degrees C, the specimens were submitted to the shear strength test in a universal testing machine (EMIC) at a crosshead speed of 1.0 mm/min. Other specimens were made to be analyzed by SEM. Results. The results were statistically analyzed by Analysis of Variance and the Tukey test. Regardless of the type of dentin, the bond strength of specimens irradiated with the Nd:YAG laser (8,94 +/- 2,07) was higher compared to specimens irradiated with the Er:YAG laser (7,03 +/- 2,47); the highest bond strength was obtained for the group of hypermineralized dentin irradiated with the Nd:YAG laser. The SEM analysis showed that the Er:YAG laser caused opening of tubules and the Nd:YAG laser produced areas of fusion as well as regions of opening of dentinal tubules. Conclusions. The dentin showed different morphological patterns and the laser promote alterations on their surfaces, influencing the bond strength of the composite resin. (C) 2010 Laser Institute of America.