Subcutaneous connective tissue response to primary root canal filling materials

This study evaluated the response of the subcutaneous connective tissue of BALB/c mice to root filling materials indicated for primary teeth: zinc oxide/eugenol cement (ZOE), Calen paste thickened with zinc oxide (Calen/ZO) and Sealapex sealer. The mice (n=102) received polyethylene tube implants with the materials, thereby forming 11 groups, as follows: I, II, III: Calen/ZO for 7, 21 and 63 days, respectively; IV, V, VI: Sealapex for 7, 21 and 63 days, respectively; VII, VIII, IX: ZOE for 7, 21 and 63 days, respectively; X and XI: empty tube for 7 and 21 days, respectively. The biopsied tissues were submitted to histological analysis (descriptive analysis and semi-quantitative analysis using a scoring system for collagen fiber formation, tissue thickness and inflammatory infiltrate). A quantitative analysis was performed by measuring the area and thickness of the granulomatous reactionary tissue (GRT). Data were analyzed by Kruskal-Wallis, ANOVA and Tukey's post-hoc tests (?=0.05). There was no significant difference (p>0.05) among the materials with respect to collagen fiber formation or GRT thickness. However, Calen/ZO produced the least severe inflammatory infiltrate (p<0.05). The area of the GRT was significantly smaller (p<0.05) for Calen/ZO and Sealapex. In conclusion, Calen/ZO presented the best tissue reaction, followed by Sealapex and ZOE.

Histopathological evaluation of root canal filling materials for primary teeth

This study aimed to assess the response of apical and periapical tissues of dogs' teeth after root canal filling with different materials. Forty roots from dogs' premolars were prepared biomechanically and assigned to 4 groups filled with: Group I: commercial calcium hydroxide and polyethylene glycol-based paste (Calen®) thickened with zinc oxide; Group II: paste composed of iodoform, Rifocort® and camphorated paramonochlorophenol; Group III: zinc oxide-eugenol cement; Group IV: sterile saline. After 30 days, the samples were subjected to histological processing. The histopathological findings revealed that in Groups I and IV the apical and periapical regions exhibited normal appearance, with large number of fibers and cells and no resorption of mineralized tissues. In Group II, mild inflammatory infiltrate and mild edema were observed, with discrete fibrogenesis and bone resorption. Group III showed altered periapical region and thickened periodontal ligament with presence of inflammatory cells and edema. It may be concluded that the Calen paste thickened with zinc oxide yielded the best tissue response, being the most indicated material for root canal filling of primary teeth with pulp vitality.

Periapical repair after root canal filling with different root canal sealers

The aim of this study was to evaluate periapical repair after root canal filling with different endodontic sealers. Sixty-four root canals from dog´s teeth were filled, divided into 4 groups (n=16). Root canals were instrumented with K-type files and irrigated with 1% sodium hypochlorite solution. Root canals were filled in the same session by active lateral condensation of the cones and sealers: Intrafill, AH Plus, Roeko Seal and Resilon/Epiphany System. After 90 days, the animals were euthanized and the tissues to be evaluated were processed and stained with hematoxylin and eosin. For histopathological analysis, the following parameters were evaluated: inflammatory process, mineralized tissue resorption, and apical mineralized tissue deposition. Histopathological analysis demonstrated that Intrafill had less favorable results in terms of apical and periapical repair, compared to the other sealers (p<0.05). AH Plus, Roeko Seal, and Epiphany sealers had similar and satisfactory results (p>0.05). In conclusion, AH Plus and the materials Roeko Seal and Epiphany are good options for clinical use in Endodontics.

Antibacterial activity of root canal filling materials for primary teeth: zinc oxide and eugenol cement, Calen paste thickened with zinc oxide, Sealapex and EndoREZ

This study evaluated in vitro the antibacterial activity of 4 root canal filling materials for primary teeth - zinc oxide and eugenol cement (ZOE), Calen paste thickened with zinc oxide (Calen/ZO), Sealapex sealer and EndoREZ sealer - against 5 bacterial strains commonly found in endodontic infections (Kocuria rhizophila, Enterococcus faecalis, Streptococcus mutans, Escherichia coli and Staphylococcus aureus) using the agar diffusion test (agar-well technique). Calen paste, 1% chlorhexidine digluconate (CHX) and distilled water served as controls. Seven wells per dish were made at equidistant points and immediately filled with the test and control materials. After incubation of the plates at 37oC for 24 h, the diameter of the zones of bacterial growth inhibition produced around the wells was measured (in mm) with a digital caliper under reflected light. Data were analyzed statistically by analysis of variance and Tukey's post-hoc test (?=0.05). There were statistically significant differences (p<0.0001) among the zones of bacterial growth inhibition produced by the different materials against all target microorganisms. K. rhizophila was inhibited more effectively (p<0.05) by ZOE, while Calen/ZO had its highest antibacterial activity against E. faecalis (p<0.05). S. mutans was inhibited by Calen/ZO, Sealapex and ZOE in the same intensity (p>0.05). E. coli was inhibited more effectively (p<0.05) by ZOE, followed by Calen/ZO and Sealapex. Calen/ZO and ZOE were equally effective (p>0.05) against S. aureus, while Sealapex had the lowest antibacterial efficacy (p<0.05) against this microorganism. EndoREZ presented antibacterial activity only against K. rhizophila and S. aureus. The Calen paste and Calen/ZO produced larger zones of inhibition than 1% CHX when the marker microorganism was E faecalis. In conclusion, the in vitro antibacterial activity of the 4 root canal filling materials for primary teeth against bacterial strains commonly found in endodontic infections can be presented in a decreasing order of efficacy as follows: ZOE>Calen/ZO>Sealapex>EndoREZ.

Influence of the length of remaining root canal filling and post space preparation on the coronal leakage of Enterococcus faecalis

This study evaluated the sealing ability of different lengths of remaining root canal filling and post space preparation against coronal leakage of Enterococcus faecalis. Forty-one roots of maxillary incisors were biomechanically prepared, maintaining standardized canal diameter at the middle and coronal thirds. The roots were autoclaved and all subsequent steps were undertaken in a laminar flow chamber. The canals of 33 roots were obturated with AH Plus sealer and gutta-percha. The root canal fillings were reduced to 3 predetermined lengths (n=11): G1=6 mm, G2=4 mm and G3=2 mm. The remaining roots served as positive and negative controls. Bacterial leakage test apparatuses were fabricated with the roots attached to Eppendorf tubes keeping 2 mm of apex submerged in BHI in glass flasks. The specimens received an E. faecalis inoculum of 1 x 107 cfu/mL every 3 days and were observed for bacterial leakage daily during 60 days. Data were submitted to ANOVA, Tukey's test and Fisher's test. At 60 days, G1 (6 mm) and G2 (4 mm) presented statistically similar results (p>0.05) (54.4% of specimens with bacterial leakage) and both groups differed significantly (p<0.01) from G3 (2 mm), which presented 100% of specimens with E. faecalis leakage. It may be concluded that the shortest endodontic obturation remnant leaked considerably more than the other lengths, although none of the tested conditions avoids coronal leakage of E. faecalis.

Apical limit of root canal filling and its relationship with success on endodontic treatment of a mandibular molar: 11-year follow-up

Objective. This article discusses the relationship between apical limit of root canal filling and success on endodontic treatment of a mandibular molar. Study design. A mandibular right first molar with vital pulp was endodontically treated, and 3 years later periapical lesions on mesial and distal roots were detected. The canals were retreated and obturated to the same levels as in the previous treatment. Results. An 8-year radiographic follow-up showed repair of the periapical lesions on both roots. Conclusions. Results suggest that the apical limit of obturation seems to have no influence in the repair of periapical tissues in mandibular molars. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2011; 112: e48-e50)

Biocompatibility Evaluation of Epiphany/Resilon Root Canal Filling System in Subcutaneous Tissue of Rats

Introduction: The purpose of this study was to evaluate the biocompatibility of the root canal filling system Epiphany/Resilon in connective tissue of rats. Methods: Fifteen rats were used, separated into 3 groups in accordance with its period of death (7, 21, 42 days). Four filled dentin tubes were implanted with the tested materials as follows: ERSP group, Epiphany/Resilon with Self-etch Primer; ER group, Epiphany/Resilon without primer; EG group, Endofill/gutta-percha points; and ET group, empty tube. After 7, 21, and 42 days, animals were killed, obtaining 5 samples per group. A grade from I-IV was used to graduate the inflammatory reaction. Results: Results showed that Epiphany/Resilon (ERSP and ER groups) induced a slight (II) inflammatory reaction after 42 days. However, in ER group, in which the self-etch primer was not applied, severe (IV) to moderate (III) inflammatory reactions were observed between 7 and 21 days. When compared with the EG and ET groups, it was observed that these groups presented tissue reaction ranging from slight (II, 7 and 21 days) to no inflammation (I, 42 days). Conclusions: Epiphany/Resilon root canal filling system presented satisfactory tissue reaction. It was biocompatible when tested in connective tissue of rats. (J Endod 2010;36:110-114)

Histopathological evaluation of root canal filling materials for primary teeth

This study aimed to assess the response of apical and periapical tissues of dogs¿ teeth after root canal filling with different materials. Forty roots from dogs¿ premolars were prepared biomechanically and assigned to 4 groups filled with: Group I: commercial calcium hydroxide and polyethylene glycol-based paste (Calen®) thickened with zinc oxide; Group II: paste composed of iodoform, Rifocort® and camphorated amonochlorophenol; Group III: zinc oxide-eugenol cement; Group IV: sterile saline. After 30 days, the samples were subjected to histological processing. The histopathological findings revealed that in Groups I and IV the apical and periapical regions exhibited normal appearance, with large number of fibers and cells and no resorption of mineralized tissues. In Group II, mild inflammatory infiltrate and mild edema were observed, with discrete fibrogenesis and bone resorption. Group III showed altered periapical region and thickened periodontal ligament with presence of inflammatory cells and edema. It may be concluded that the Calen paste thickened with zinc oxide yielded the best tissue response, being the most indicated material for root canal filling of primary teeth with pulp vitality.

Intracanal dressing and root canal filling materials in tooth replantation: a literature review

The prognosis of tooth replantation is usually related to the need of endodontic treatment, which has a direct relationship with the occurrence of root resorptions. Several studies have been undertaken in an attempt to prevent, delay, or treat these complications, which are the main causes of loss of replanted teeth. This literature review examines research evidence on intracanal dressings and root canal filling materials used in cases of tooth replantation. A comprehensive search was performed in the Medline/Pubmed, Bireme and Scielo full-text electronic journal databases to retrieve English-language articles referring to these topics that had been published between 1964 and 2010. Calcium hydroxide (CH) remains the usually recommended choice as an intracanal medicament in replanted teeth; however, there is evidence to support the initial use of a corticosteroid-antibiotic combination such as Ledermix paste to control potential early resorption, prior to the introduction of CH where the beneficial effect in the treatment of progressive root resorption has been well proven. Regarding root filling materials, CH-containing sealers are a good option because of their biological properties. Accurate diagnosis and adequate treatment plan may constitute very complex tasks, particularly in tooth avulsion because several variables are involved. In addition to the technical knowledge and clinical experience directed toward the quality of treatment, patient education may favorably influence the survival of replanted teeth.

Analysis of the healing process in delayed tooth replantation after root canal filling with calcium hydroxide, Sealapex and Endofill: a microscopic study in rats

The major concern in the therapeutics of tooth replantation refers to the occurrence of root resorption and different approaches have been proposed to prevent or treat these complications. The purpose of this study was to evaluate tissue response to delayed replantation of anterior rat teeth treated endodontically using calcium hydroxide, Sealapex, and Endofill without the placement of gutta-percha cones. Thirty rats had their right upper incisor extracted and maintained in dry storage for 60 min. After removal of the dental papilla, enamel organ, pulp tissue, and periodontal ligament remnants, the teeth were immersed in 2% sodium fluoride phosphate acidulated, pH 5.5, for 10 min. The root canals were dried with absorbent paper points and the teeth were assigned to three groups (n = 10) according to the filling material. Group I - calcium hydroxide and propyleneglycol paste, Group II - Sealapex, and Group III - Endofill. The sockets were irrigated with saline and the teeth were replanted. Replacement resorption, inflammatory resorption and ankylosis were observed in all groups. Although the occurrence of inflammatory resorption was less frequent in Group I, there were no statistically significant differences among the groups. It may be concluded that compared to the paste, filling the root canals with Sealapex and Endofill sealers without the placement of gutta-percha cones did not provide better results.

Influence of the type of vehicle and limit of obturation on apical and periapical tissue response in dogs' teeth after root canal filling with mineral trioxide aggregate

The purpose of this study was to investigate the influence of the type of vehicle (distilled water or propyleneglycol) on the response of apical tissues of dogs' teeth after root canal filling with mineral trioxide aggregate (MTA) at two different limits. Forty roots of incisors and premolars of two adult dogs were used. After pulpectomy, the root canals were prepared biomechanically, and the roots had the apical cemental barrier penetrated with a #15 K-file and widened to a #25 K-file. The root canals were assigned to four groups according to the vehicle used for MTA (ProRoot-MTA; Tulsa Dental, Tulsa, OK) preparation and the limit of root canal filling: group 1, filling with MTA/distilled water to the limit of the cemental canal; group 2, overfilling with MTA/distilled water, group 3, filling with MTA/propyleneglycol to the limit of the cemental canal; and group 4, overfilling with MTAlpropyleneglycol. The animals were killed by anesthetic overdose 90 days after endodontic treatment and the anatomic pieces were prepared for histomorphological analysis. The sections were stained with hematoxylin and eosin and Brown and Brenn techniques. The results showed that MTA pastes prepared with either distilled water or propyleneglycol as vehicles had similar biological behavior (p > 0.05); root fillings placed at the cemental canal limit showed better results than the overfillings (p = 0.01), and MTA/propyleneglycol paste was more easily placed into the root canals than MTA/distilled water paste.

Radiopacity evaluation of new root canal filling materials by digitalization of images

The aim of this study was to evaluate the radiopacity of five root canal filling materials (AH Plus, Intrafill, Roeko Seal, Epiphany, and EndoRez). Following the International Organization of Standardization 687612001, five circular specimens (10 X 1 mm) were made from each material. After the material set, radiographs were made using occlusal film and a graduated aluminum step-wedge varying in thickness from 2 to 16 mm. The dental X-ray unit (GE1000) was set at 50 Kvp, 10 mA, 18 pulses/second, and distance of 33.5 cm. The radiographs were digitized, and the radiopacity was compared with the aluminum step-wedge, using WIXWIN-2000 software (Gendex). Data (mm Al) were analyzed using ANOVA and Tukey tests. AH Plus and Epiphany were the most radiopaque materials (9.8 and 8.8 mm Al, respectively), followed by EndoRez (7.2 mm Al). Roeko Seal and Intrafill presented the lowest radiopacity values (5.7 and 6.1 mm Al, respectively). Although the materials evaluated demonstrated different radiopacities, all had values above the minimum recommended by the international Organization of Standardization.