Evolution of recrystallization during and following hot deformation

Recrystallization of austenite during and following hot deformation has been studied in detail in a type 304 austenitic stainless steel. Furthermore, the effect of second phase on the softening process of austenite has been investigated using a 2205 duplex stainless steel. The mechanical and microstructural features have been compared for dynamic and post deformation recrystallization.

Microstructural features of rolled mg-3Al-1Zn

The microstructures of hot- and cold-rolled Mg-3Al-1Zn (AZ31) are examined using scanning electron and optical microscopy. It is shown that the microstructures following multipass hot rolling and annealing are more uniform than those formed by heavy single pass rolling and annealing. The importance of twins in producing intragranular recrystallization is evident, although the most dominant nucleation site is grain boundaries. The cold-rolled structure after a rolling reduction of 15 pct is dominated by the presence of deformation twins. Twin trace analysis suggests that approximately two thirds of the twins are a form of “c-axis compression” twin. A number of “c-axis tension” twins were also observed and additional in-situ scanning electron microscopy experiments were performed to confirm earlier observations that suggest these twins can form after deformation, during unloading.

Microstructural development during hot working of Mg-3AI-1Zn

he microstructural evolution is examined during the hot compression of magnesium alloy AZ31 for both wrought and as-cast initial microstructures. The influences of strain, temperature, and strain rate on the dynamically recrystallized microstructures are assessed. Both the percentage dynamic recrysallization (DRX) and the dynamically recrystallized grain size were found to be sensitive to the initial microstructure and the applied deformation conditions. Lower Z conditions (lower strain rates and higher temperatures) yield larger dynamically recrystallized grain sizes and increased percentages of DRX, as expected. The rate with which the percentage DRX increases for the as-cast material is considerably lower than for the wrought material. Also, in the as-cast samples, the percentage DRX does not continue to increase toward complete DRX with decreasing Z. These observations may be attributed to the deformation becoming localized in the DRX fraction of the material. Also, the dynamically recrystallized grain size is generally larger in as-cast material than in wrought material, which may be attributed to DRX related to twins and the inhomogeneity of deformation. Orientation maps of the as-cast material (from electron backscattering diffraction (EBSD) data) reveal evidence of discontinuous DRX (DDRX) and DRX related to twins as predominant mechanisms, with some manifestation of continuous DRX (CDRX) and particle-stimulated nucleation (PSN).

Evolution of hot working stress and microstructure of Mg-3Al-1Zn

The deformation behaviour of magnesium alloy AZ31 was examined. The work found that dynamic recrystallisation operates during hot deformation. The influence that different process variables have on this mechanism were quantified. The optimisation of dynamic recrystallisation allows magnesium alloys to be formed into products more easily whilst developing enhanced final properties.

Microscale modelling of AISI 304 behaviour during hot deformation

This project aimed to model the microstructure evolution during and following hot deformation using a cellular automaton approach. The flow curves, softening kinetics and final microstructures were used as the input data for the post-deformation simulation to elucidate the effect of dynamic recrystallization on the post-deformation softening.

Study of the deformation behaviour of austenite via model alloys

This study compared two potential model alloys, 304 stainless steel and Ni-30wt.%Fe, to study the behaviour of austenite during the thermo-mechanical processing of steel. The deformation behaviour as well as the textural and microstructural evolution was characterised in detail over a wide range of deformation conditions.

Effects of copper vapor laser radiation on the root canal wall of human teeth: A scanning electron microscope study

Objective: The aim of this study is to analyze the effects of copper vapor laser radiation on the radicular wall of human teeth. Materials and Methods: Immediately after the crowns of 10 human uniradicular teeth were cut along the cement-enamel junction, a chemical-surgical preparation of the radicular canals was completed. Then the roots were longitudinally sectioned to allow for irradiation of the surfaces of the dentin walls of the root canals. The hemi-roots were separated into two groups: one (control) with five hemi-roots that were not irradiated, and another (experimental) with 15 hemi-roots divided into three subgroups that were submitted to the following exposure times: 0.02,0.05, and 0.1 s. A copper vapor laser (510.6 nm) with a total average power of 6.5 W in green emission, frequency of 16.000 Hz, and pulse duration of 30 ns was used. Results: The results obtained by scanning electron microscope analysis showed the appearance of a cavity in the region of laser beam impact, with melting, recrystallization, and cracking on the edges of the dentin of the cavity due to heat diffusion. Conclusions: We determined that the copper vapor laser produces significant morphologic changes in the radicular wall of human teeth when using the parameters in this study. However, further research should be done to establish parameters that are compatible with dental structure in order to eliminate thermal damages. © Mary Ann Liebert, Inc.

Effect of recrystallization and grain growth on the mechanical properties of an extruded AZ21 Mg alloy

An experimental investigation into the effect of microstructural changes, which occur during post-extrusion annealing of a Mg based AZ21 alloy, on tensile and fatigue properties is conducted. Mechanical properties in the as-cast, as-extruded, and microstructural states that correspond to recovery, recrystallization and grain growth stages of annealing are compared. Results show that these microstructural changes do not alter the yield strength of the alloy markedly whereas significant differences were noted in the ultimate tensile strength as well as ductility. The initiation of abnormal grain growth (or secondary recrystallization) renders the tensile stress-strain response elastic perfectly plastic and results in a large drop in ductility, as high as similar to 60% during intermediate stages of abnormal grain growth, vis-A-vis the ductility of the as-extruded alloy. While the fatigue performance of all the wrought alloys is far superior to as expected, abnormal grain growth leads to a marked decrease in the endurance that of the as-cast alloy, limit. Possible microscopic origins of these are discussed. (C) 2009 Elsevier B.V. All rights reserved.

Effect of stacking fault energy on the dynamic recrystallization during hot working of FCC metals: A study using processing maps

The influence of stacking fault energy (SFE) on the mechanism of dynamic recrystallization (DRX) during hot deformation of FCC metals is examined in the light of results from the power dissipation maps. The DRX domain for high SFE metals like Al and Ni occurred at homologous temperature below 0·7 and strain rates of 0·001 s−1 while for low SFE metals like Cu and Pb the corresponding values are higher than 0·8 and 100 s−1. The peak efficiencies of power dissipation are 50% and below 40% respectively. A simple model which considers the rate of interface formation (nucleation) involving dislocation generation and simultaneous recovery and the rate of interface migration (growth) occurring with the reduction in interface energy as the driving force, has been proposed to account for the effect of SFE on DRX. The calculations reveal that in high SFE metals, interface migration controls DRX while the interface formation is the controlling factor in low SFE metals. In the latter case, the occurrence of flow softening and oscillations could be accounted for by this model.

Processing maps for hot-working of powder metallurgy 1100 Al-10 vol % SiC-particulate metal-matrix composite

The hot-working characteristics of the metal-matrix composite (MMC) Al-10 vol % SiC-particulate (SiCp) powder metallurgy compacts in as-sintered and in hot-extruded conditions were studied using hot compression testing. On the basis of the stress-strain data as a function of temperature and strain rate, processing maps depicting the variation in the efficiency of power dissipation, given by eegr = 2m/(m+1), where m is the strain rate sensitivity of flow stress, have been established and are interpreted on the basis of the dynamic materials model. The as-sintered MMC exhibited a domain of dynamic recrystallization (DRX) with a peak efficiency of about 30% at a temperature of about 500°C and a strain rate of 0.01 s�1. At temperatures below 350°C and in the strain rate range 0.001�0.01 s�1 the MMC exhibited dynamic recovery. The as-sintered MMC was extruded at 500°C using a ram speed of 3 mm s�1 and an extrusion ratio of 10ratio1. A processing map was established on the extruded product, and this map showed that the DRX domain had shifted to lower temperature (450°C) and higher strain rate (1 s�1). The optimum temperature and strain rate combination for powder metallurgy billet conditioning are 500°C and 0.01 s�1, and the secondary metal-working on the extruded product may be done at a higher strain rate of 1 s�1 and a lower temperature of 425°C.

Processing map for controlling microstructure in hot working of hot isostatically pressed powder metallurgy NIMONIC AP-1 superalloy

The hot deformation behavior of hot isostatically pressed (HIP) NIMONIC AP-1 superalloy is characterized using processing maps in the temperature range 950-degrees-C to 1200-degrees-C and strain rate range 0.001 to 100 s-1. The dynamic materials model has been used for developing the processing maps which show the variation of the efficiency of power dissipation given by [2m/(m +1)] with temperature and strain rate, with m being the strain rate sensitivity of flow stress. The processing map revealed a domain of dynamic recrystallization with a peak efficiency of 40 pct at 1125-degrees-C and 0.3 s-1, and these are the optimum parameters for hot working. The microstructure developed under these conditions is free from prior particle boundary (PPB) defects, cracks, or localized shear bands. At 100 s-1 and 1200-degrees-C, the material exhibits inter-crystalline cracking, while at 0.001 s-1, the material shows wedge cracks at 1200-degrees-C and PPB cracking at 1000-degrees-C. Also at strain rates higher than 10 s-1, adiabatic shear bands occur; the limiting conditions for this flow instability are accurately predicted by a continuum criterion based on the principles of irreversible thermodynamics of large plastic flow.

Influence of carbide particles on the dynamic recrystallization of as-cast 304 stainless steel: a study using secondary ion mass spectrometric (SIMS) analysis

The domain of dynamic recrystallization (DRX) in as-cast 304 stainless steel material occurs at higher temperatures (1250 degrees C) and lower strain rates (0.001 s(-1)) than in wrought 304 stainless steel (1100 degrees C and 0.01 s(-1)). The above result has been explained earlier on the basis of a simple theoretical DRX model involving the rate of nucleation versus rate of grain boundary migration. The present investigation is aimed at examining experimentally the influence of carbide particles on the DRX of ascast 304 using secondary ion mass spectrometric (SIMS) analysis. Isothermal compression tests at a constant true strain rate have been performed on wrought 304 and as-cast 304 materials in the temperature and strain rate ranges of 1000 to 1250 degrees C and 0.001 to 1 s(-1) respectively. The SIMS analysis carried out on the deformed samples revealed that the large carbides present in the as-cast 304 material strongly influence the DRX process. In as-cast 304 material, the presence of large carbide particles in the microstructure shifts the DRX domain to higher temperature and lower strain rate in comparison with wrought 304 material.

Evolution of texture and grain boundary microstructure in two-phase (α + β) brass during recrystallization

The evolution of texture and microstructure during recrystallization is studied for two-phase copper alloy (Cu–40Zn) with a variation of the initial texture and microstructure (hot rolled and solution treated) as well as the mode of rolling (deformation path: uni-directional rolling and cross rolling). The results of bulk texture have been supported by micro-texture and microstructure studies carried out using electron back scatter diffraction (EBSD). The initial microstructural condition as well as the mode of rolling has been found to alter the recrystallization texture and microstructure. The uni-directionally rolled samples showed a strong Goss and BR {236}385 component while a weaker texture similar to that of rolling evolved for the cross-rolled samples in the α phase on recrystallization. The recrystallization texture of the β phase was similar to that of the rolling texture with discontinuous 101 α and {111} γ fiber with high intensity at {111}101. For a given microstructure, the cross-rolled samples showed a higher fraction of coincident site lattice Σ3 twin boundaries in the α phase. The higher fraction of Σ3 boundaries is explained on the basis of the higher propensity of growth accidents during annealing of the cross-rolled samples. The present investigation demonstrates that change in strain path, as introduced during cross-rolling, could be a viable tool for grain boundary engineering of low SFE fcc materials.

Softening and dynamic recrystallization in magnesium single crystals during c-axis compression

Commercial purity (99.8%) magnesium single crystals were subjected to plane strain compression (PSC) along the c-axis at 200 and 370 degrees C and a constant strain rate of 10(-3) s(-1). Extension was confined to the < 1 1 (2) over bar 0 > direction and the specimens were strained up to a logarithmic true strain of -1. The initial rapid increase in flow stress was followed by significant work softening at different stresses and comparable strains of about -0.05 related to macroscopic twinning events. The microstructure of the specimen after PSC at 200 degrees C was characterized by a high density of {1 0 (1) over bar 1} and {1 0 (1) over bar 3} compression twins, some of which were recrystallized. After PSC at 370 degrees C, completely recrystallized twin bands were the major feature of the observed microstructure. All new grains in these bands retained the same c-axis orientation of their compression twin hosts. The basal plane in these grains was randomly rotated around the c-axis, forming a fiber texture component. The obtained results are discussed with respect to the mechanism of recrystallization, the specific character of the boundaries between new grains and the initial matrix, and the importance of the dynamically recrystallized bands for strain accommodation in these deformed magnesium single crystals. (C) 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Deformation and Recrystallization texture evolution in Nano-crystalline Nickel

Deformation and recrystallization textures in nano-crystalline nickel with average grain size of 20 nm were investigated using X-ray diffraction, electron microscopy and differential scanning calorimetry. The deformation behaviour of nano-crystalline nickel is quite complicated due to intervention of other deformation mechanisms like grain boundary sliding and restoration mechanisms like grain growth and grain rotation to dislocation mediated slip. Recrystallization studies carried out on the deformed nano-crystalline nickel showed that the deformation texture was retained during low temperature annealing (300 degrees C), while at higher temperature (1000 degrees C), the texture got randomised. The exact mechanism of texture formation during deformation and recrystallization has been discussed.