High-temperature electron-hole liquid and dynamics of Fermi excitons in a In0.65Al0.35As/Al0.4Ga0.6As quantum dot array

State-filling effects of the exciton in a In0.65Al0.35As/Al0.4Ga0.6As quantum dot array are observed by quantum dot array photolumineseence at a sample temperature of 77 K. The exciton emission at low excitation density is dominated by the radiative recombination of the states in the s shell and at high excitation density the emission mainly results from the radiative recombination of the exciton state in the p shell. The spectral interval between the states in the s and p shells is about 30-40 mcV. The time resolved photoluminescence shows that the decay time of exciton states in the p shell is longer than that of exciton states in the s shell, and the emission intensity of the exciton state in the p shell is superlinearly dependent on excitation density. Furthermore, electron-hole liquid in the quantum dot array is observed at 77 K, which is a much higher temperature than that in bulk. The emission peak of the. recombination, of electron-hole liquid has an about 200 meV redshift from the exciton fluorescence. Two excitation density-dependent emission peaks at 1.56 and 1.59 eV are observed, respectively, which result from quantum confinement effects in QDs. The emission intensity of electron-hole liquid is directly proportional to the cubic of excitation densities and its decay time decreases significantly at the high excitation density.

Persistent Photoconductivity in n-type GaN

The persistent photoconductivity（PPC） phenomena in n-type GaN Films grown by metalorganic chemical vapor deposition（MOCVD） have been studied. After using some testing and analysis methods, such as the double crystal X-ray diffraction（DCXRD）, the photolumineseence（PL） spectra, etc, it is found that the issue which influences PPC in n-type GaN is not relative to the dislocations and yellow band （YB）, and is caused by the doping level of Si most likely.

Photoluminescence characterization of 1.3 mu m In(Ga)As/GaAs islands grown by molecular beam epitaxy

1.3 mum wavelength In(Ga)As/GaAs nanometer scale islands grown by molecular beam epitaxy (MBE) were characterized by photoluminescence (PL) and atomic force microscopy (AFM) measurements. It is shown that inhomogeneous broadening of optical emission due to fluctuation of the In0.5Ga0.5As islands both in size and in compositions can be effectively suppressed by introducing a AlAs layer and a strain reduction In0.2Ga0.8As layer overgrown on top of the islands, 1.3mum emission wavelength with narrower line-width less than 20meV at room temperature was obtained.