Estimating thermal performance of cool colored paints

The purpose of this study is to investigate the thermal performance of cool colored acrylic paints containing infrared reflective pigments in comparison to conventional colored acrylic paints of similar colors (white, brown and yellow) applied on sheets of corrugated fiber cement roofing. Evaluated properties are: color according to ASTM D 2244-89, the UV/VIS/NIR reflectance according to ASTM E 90396, and thermal performance by exposure to infrared radiation emitted from a lamp with the measurement of surface temperatures of the specimens with thermocouples connected to a data logging system. Results demonstrated that the cool colored paint formulations produced significantly higher NIR reflectance than conventional paints of similar colors, and that the surface temperatures were more than 10 degrees C lower than those of conventional paints when exposed to infrared radiation. The study shows that cool paints enhance thermal comfort inside buildings, which can reduce air conditioning costs. (C) 2009 Elsevier B.V. All rights reserved.

Is it possible to remove polymeric nanoparticles from aqueous paints during the activated sludge treatment?

The market for emulsion polymers (latexes) is large and growing at the expense of other manufacturing processes that emit higher amounts of volatile organic solvents. The paint industry is not an exception and solvent-borne paints have been gradually substituted by aqueous paints. In their life-cycle, much of the aqueous paint used for architectural or decorative purposes will eventually be discharged into wastewater treatment facilities, where its polymeric nanoparticles (mainly acrylic and styrene-acrylic) can work as xenobiotics to the microbial communities present in activated sludge. It is well established that these materials are biocompatible at macroscopic scale. But is their behaviour the same at nanoscale? What happens to the polymeric nanoparticles during the activated sludge process? Do nanoparticles agregate and are discharged together with the sludge or remain in emulsion? How do microorganisms interact with these nanoparticles? Are nanoparticles degradated by them? Are they adsorbed? Are these nanoparticles toxic to the microbial community? To study the influence of these xenobiotics in the activated sludge process, an emulsion of cross-linked poly(butyl methacrylate) nanoparticles of ca. 50 nm diameter was produced and used as model compound. Activated sludge from a wastewater treatment plant was tested by the OCDE’s respiration inhibition test using several concentrations of PBMA nanoparticles. Particle aggregation was followed by Dynamic Light Scattering and microorganism surfaces were observed by Atomic Force Microscopy. Using sequential batch reactors (SBRs) and continuous reactors, both inoculated with activated sludge, the consumption of carbon, ammonia, nitrite and nitrate was monitored and compared, in the presence and absence of nanoparticles. No particles were detected in all treated waters by Dynamic Light Scattering. This can either mean that microorganisms can efficiently remove all polymer nanoparticles or that nanoparticles tend to aggregate and be naturally removed by precipitation. Nevertheless respiration inhibition tests demonstrated that microorganisms consume more oxygen in the presence of nanoparticles, which suggests a stress situation. It was also observed a slight decrease in the efficiency of nitrification in the presence of nanoparticles. AFM images showed that while the morphology of some organisms remained the same both in the presence and absence of nanoparticles, others assumed a rough surface with hilly like shapes of ca. 50 nm when exposed to nanoparticles. Nanoparticles are thus likely to be either incorporated or adsorbed at the surface of some organisms, increasing the overall respiration rate and decreasing nitrification efficiency. Thus, despite its biocompatibility at macroscopic scale, PBMA is likely to be no longer innocuous at nanoscale.

The study of lead white oil paints: a molecular approach to the whites of Amadeo de Souza-Cardoso

Dissertação apresentada na Faculdade de Ciências e Tecnologia da Universidade Nova de Lisboa para obtenção do grau de Mestre em Conservação e Restauro

The application of chemometrics on Infrared and Raman spectra as a tool for the forensic analysis of paints

The aim of this work is to evaluate the capabilities and limitations of chemometric methods and other mathematical treatments applied on spectroscopic data and more specifically on paint samples. The uniqueness of the spectroscopic data comes from the fact that they are multivariate - a few thousands variables - and highly correlated. Statistical methods are used to study and discriminate samples. A collection of 34 red paint samples was measured by Infrared and Raman spectroscopy. Data pretreatment and variable selection demonstrated that the use of Standard Normal Variate (SNV), together with removal of the noisy variables by a selection of the wavelengths from 650 to 1830 cm−1 and 2730-3600 cm−1, provided the optimal results for infrared analysis. Principal component analysis (PCA) and hierarchical clusters analysis (HCA) were then used as exploratory techniques to provide evidence of structure in the data, cluster, or detect outliers. With the FTIR spectra, the Principal Components (PCs) correspond to binder types and the presence/absence of calcium carbonate. 83% of the total variance is explained by the four first PCs. As for the Raman spectra, we observe six different clusters corresponding to the different pigment compositions when plotting the first two PCs, which account for 37% and 20% respectively of the total variance. In conclusion, the use of chemometrics for the forensic analysis of paints provides a valuable tool for objective decision-making, a reduction of the possible classification errors, and a better efficiency, having robust results with time saving data treatments.

Survey on batch-to-batch variation in spray paints: a collaborative study

This study represents the most extensive analysis of batch-to-batch variations in spray paint samples to date. The survey was performed as a collaborative project of the ENFSI (European Network of Forensic Science Institutes) Paint and Glass Working Group (EPG) and involved 11 laboratories. Several studies have already shown that paint samples of similar color but from different manufacturers can usually be differentiated using an appropriate analytical sequence. The discrimination of paints from the same manufacturer and color (batch-to-batch variations) is of great interest and these data are seldom found in the literature. This survey concerns the analysis of batches from different color groups (white, papaya (special shade of orange), red and black) with a wide range of analytical techniques and leads to the following conclusions. Colored batch samples are more likely to be differentiated since their pigment composition is more complex (pigment mixtures, added pigments) and therefore subject to variations. These variations may occur during the paint production but may also occur when checking the paint shade in quality control processes. For these samples, techniques aimed at color/pigment(s) characterization (optical microscopy, microspectrophotometry (MSP), Raman spectroscopy) provide better discrimination than techniques aimed at the organic (binder) or inorganic composition (fourier transform infrared spectroscopy (FTIR) or elemental analysis (SEM - scanning electron microscopy and XRF - X-ray fluorescence)). White samples contain mainly titanium dioxide as a pigment and the main differentiation is based on the binder composition (Csingle bondH stretches) detected either by FTIR or Raman. The inorganic composition (elemental analysis) also provides some discrimination. Black samples contain mainly carbon black as a pigment and are problematic with most of the spectroscopic techniques. In this case, pyrolysis-GC/MS represents the best technique to detect differences. Globally, Py-GC/MS may show a high potential of discrimination on all samples but the results are highly dependent on the specific instrumental conditions used. Finally, the discrimination of samples when data was interpreted visually as compared to statistically using principal component analysis (PCA) yielded very similar results. PCA increases sensitivity and could perform better on specific samples, but one first has to ensure that all non-informative variation (baseline deviation) is eliminated by applying correct pre-treatments. Statistical treatments can be used on a large data set and, when combined with an expert's opinion, will provide more objective criteria for decision making.

Raman analysis of multilayer automotive paints in forensic science: measurement variability and depth profile?

The aim of this work is to study the influence of several analytical parameters on the variability of Raman spectra of paint samples. In the present study, microtome thin section and direct (no preparation) analysis are considered as sample preparation. In order to evaluate their influence on the measures, an experimental design such as 'fractional full factorial' with seven factors (including the sampling process) is applied, for a total of 32 experiments representing 160 measures. Once the influence of sample preparation highlighted, a depth profile of a paint sample is carried out by changing the focusing plane in order to measure the colored layer under a clearcoat. This is undertaken in order to avoid sample preparation such a microtome sectioning. Finally, chemometric treatments such as principal component analysis are applied to the resulting spectra. The findings of this study indicate the importance of sample preparation, or more specifically, the surface roughness, on the variability of the measurements on a same sample. Moreover, the depth profile experiment highlights the influence of the refractive index of the upper layer (clearcoat) when measuring through a transparent layer.

A simple model to describe the thixotropic behavior of paints.

We propose a simple rheological model to describe the thixotropic behavior of paints, since the classical hysteresis area, which is usually used, is not enough to evaluate thixotropy. The model is based on the assumption that viscosity is a direct measure of the structural level of the paint. The model depends on two equations: the Cross-Carreau equation to describe the equilibrium viscosity and a second order kinetic equation to express the time dependence of viscosity. Two characteristic thixotropic times are differentiated: one for the net structure breakdown, which is defined as a power law function of shear rate, and an other for the net structure buildup, which is not dependent on the shear rate. The knowledge of both kinetic processes can be used to improve the quality and applicability of paints. Five representative commercial protective marine paints are tested. They are based on chlorinated rubber, acrylic, alkyd, vinyl, and epoxy resins. The temperature dependence of the rheological behavior is also studied with the temperature ranging from 5 ºC to 35 ºC. It is found that the paints exhibit both shear thinning and thixotropic behavior. The model fits satisfactorily the thixotropy of the studied paints. It is also able to predict the thixotropy dependence on temperature. Both viscosity and the degree of thixotropy increase as the temperature decreases.

Forensic aspects of the weathering and ageing of spray paints

This paper presents a preliminary study on the degradation of spray paint samples, illustrated by Optical, FTIR and Raman measurements. As opposed to automotive paints which are specifically designed for improved outdoor exposure and protected using hindered amine light absorbers (HALS) and ultra-violet absorbers (UVA), the spray paints on their side are much simpler in composition and very likely to suffer more from joint effects of solar radiation, temperature and humidity. Six different spray paint were exposed to outdoor UV-radiation for a total period of three months and both FTIR and Raman measurements were taken systematically during this time. These results were later compared to an artificial degradation using a climate chamber. For infrared spectroscopy, degradation curves were plotted using the photo-oxidation index (POI), and could be successfully approximated with a logarithmic fitting (R2 > 0.8). The degradation can appear after the first few days of exposure and be important until 2 months, where it stabilizes and follow a more linear trend afterwards. One advantage is that the degradation products appeared almost exclusively at the far end (∼3000 cm−1) of mid-infrared spectra, and that the fingerprint region of the spectra remained stable over the studied period of time. Raman results suggest that the pigments on the other side, are much more stable and have not shown any sign of degradation over the time of this study. Considering the forensic implications of this environmental degradation, care should be taken when comparing samples if weathering is an option (e.g. an exposed graffiti compared to the paint from a fresh spray paint can). Degradation issues should be kept in mind as they may induce significant differences between paint samples of common origin.

Receipt from W.J. McCalla, Groceries, Hardware, Paints and Oils, St. Catharines

Receipt from W.J. McCalla, Groceries, Hardware, Paints and Oils, St. Catharines for groceries and cutlery, March 21, 1887.

Controlling ivy attachment to wall surfaces by applying paints, metal meshes and sheets

Growing ivy around buildings has benefits. However, ivy potentially damages buildings which limit its use. Options for preventing ivy attachment were investigated to provide ivy management alternatives. Indoor and outdoor experiments were conducted, where metals (Cu, Zn) and anti-graffiti paints were applied to model wall panels. Metal treatments, in both indoor and outdoor experiments, fully prevented ivy attachment. For Hedera helix, silane-based anti-graffiti paint prevented attachment in the laboratory and required under half the peak detachment force necessary to detach the control in the outdoor experiment. In conclusion, metals and silane-based paint are management possibilities for ivy attachment around buildings.

Application of non-isothermal cure kinetics on the interaction of poly(ethylene terephthalate) - Alkyd resin paints

Samples of paint (P), reused PET (PET-R) and paint/PET-R mixtures (PPET-R) were evaluated using DSC to verify their physical-chemical properties and thermal behavior. Films from paints and PPET-R are visually similar. It was possible to establish that the maximum amount of PET-R that can be added to paint without significantly altering its filming properties is 2%. The cure process (80-203°C) was identified through DSC curves. The kinetic parameters, activation energy (E a) and Arrhenius parameters (A) for the samples containing 0.5 to 1% of PET-R, were calculated using the Flynn-Wall-Ozawa isoconversional method. It was observed that for greater amounts of PET-R added, there is a decrease in the E a values for the cure process. A Kinetic compensation effect (KCE), represented by the equation InA=-2.70+0.31E a was observed for all the samples. The most suitable kinetic model to describe this cure process is the autocatalytic Šesták-Berggreen, model applied to heterogeneous systems. © 2007 Springer Science+Business Media, LLC.