Determination of the hoop fracture properties of unirradiated hydrogen-charged nuclear fuel cladding from ring compression tests

In this work, a new methodology is devised to obtain the fracture properties of nuclear fuel cladding in the hoop direction. The proposed method combines ring compression tests and a finite element method that includes a damage model based on cohesive crack theory, applied to unirradiated hydrogen-charged ZIRLOTM nuclear fuel cladding. Samples with hydrogen concentrations from 0 to 2000 ppm were tested at 20 �C. Agreement between the finite element simulations and the experimental results is excellent in all cases. The parameters of the cohesive crack model are obtained from the simulations, with the fracture energy and fracture toughness being calculated in turn. The evolution of fracture toughness in the hoop direction with the hydrogen concentration (up to 2000 ppm) is reported for the first time for ZIRLOTM cladding. Additionally, the fracture micromechanisms are examined as a function of the hydrogen concentration. In the as-received samples, the micromechanism is the nucleation, growth and coalescence of voids, whereas in the samples with 2000 ppm, a combination of cuasicleavage and plastic deformation, along with secondary microcracking is observed.

Revisiting the method to obtain the mechanical properties of hydrided fuel cladding in the hoop direction

The method reported in the literature to calculate the stress–strain curve of nuclear fuel cladding from ring tensile test is revisited in this paper and a new alternative is presented. In the former method, two universal curves are introduced under the assumption of small strain. In this paper it is shown that these curves are not universal, but material-dependent if geometric nonlinearity is taken into account. The new method is valid beyond small strains, takes geometric nonlinearity into consideration and does not need universal curves. The stress–strain curves in the hoop direction are determined by combining numerical calculations with experimental results in a convergent loop. To this end, ring tensile tests were performed in unirradiated hydrogen-charged samples. The agreement among the simulations and the experimental results is excellent for the range of concentrations tested (up to 2000 wppm hydrogen). The calculated stress–strain curves show that the mechanical properties do not depend strongly on the hydrogen concentration, and that no noticeable strain hardening occurs. However, ductility decreases with the hydrogen concentration, especially beyond 500 wppm hydrogen. The fractographic results indicate that as-received samples fail in a ductile fashion, whereas quasicleavage is bserved in the hydrogen-charged samples.

TiN-based coatings on fuel cladding tubes for advanced nuclear reactors

Titanium nitride (TiN) thin films are coated on HT-9 and MA957 fuel cladding tubes and bars to explore their mechanical strength, thermal stability, diffusion barrier properties, and thermal conductivity properties. The ultimate goal is to implement TiN as an effective diffusion barrier to prevent the inter-diffusion between the nuclear fuel and the cladding material, and thus lead to a longer lifetime of the cladding tubes. Mechanical tests including hardness and scratch tests for the samples before and after thermal cycle tests show that the films have a high hardness of 28GPa and excellent adhesion properties despite the thermal treatment. Thermal conductivity measurements demonstrate that the thin TiN films have very minimal impact on the overall thermal conductivity of the MA957 and HT-9 substrates, i.e., the thermal conductivity of the uncoated HT-9 and MA957 substrates was 26.25 and 28.44 W m-1 K-1, and that of the coated ones was 26.21 and 28.38W m-1 K-1, respectively. A preliminary Ce diffusion test on the couple of Ce/TiN/HT-9 suggests that TiN has excellent material compatibility and good diffusion barrier properties.

A method for VVER-1000 fuel rearrangement optimization taking into account both fuel cladding durability and burnup

A method for VVER-1000 fuel rearrangement optimization that takes into account both cladding durability and fuel burnup and which is suitable for any regime of normal reactor operation has been established. The main stages involved in solving the problem of fuel rearrangement optimization are discussed in detail. Using the proposed fuel rearrangement efficiency criterion, a simple example VVER-1000 fuel rearrangement optimization problem is solved under deterministic and uncertain conditions. It is shown that the deterministic and robust (in the face of uncertainty) solutions of the rearrangement optimization problem are similar in principle, but the robust solution is, as might be anticipated, more conservative. © 2013 Elsevier B.V.

Crystallography of zirconium hydrides in recrystallized Zircaloy-2 fuel cladding lay electron backscatter diffraction

Precipitation morphology and habit planes of the delta-phase Zr hydrides, which were precipitated within the a-phase matrix grains and along the grain boundaries of recrystallized Zircaloy-2 cladding tube, have been examined by electron backscatter diffraction (EBSD). Radially-oriented hydrides, induced by residual tensile stress, precipitated in the outside region of the cladding, and circumferentially-oriented hydrides in the stress-free middle region of the cladding. The most common crystallographic relationship for both types of the hydrides precipitated at the inter- and intra-granular sites was identical at (0001)(alpha) // {111}(delta), with {1017}(alpha) // {111}(delta) being the occasional exception only for the inter-granular radial hydrides. When tensile stress was loaded, the intra-granular hydrides tended to preferentially precipitate in the grains with circumferential basal pole textures. The inter-granular hydrides tended to preferentially precipitate on the grain faces opposite to tensile axis. The change of prioritization in the precipitation sites for the hydrides due to tensile stress could be explained in terms of the relaxation effect of constrained elastic energy on the terminal solid solubility of hydrogen at hydride precipitation.