Nanohardness and contact angle of Si wafers implanted with N and C and Al alloy with N by plasma ion implantation

Surfaces of silicon wafers implanted with N and C, respectively, and aluminum 5052 implanted with N alone by plasma immersion ion implantation WHO were probed by a nanoindentor and analyzed by the contact-angle method to provide information on surface nanohardness and wettability. Silicon nitride and silicon carbide are important ceramic materials for microelectronics, especially for high-temperature applications. These compounds can be synthesized by high-dose ion implantation. The nanohardness of a silicon sample implanted with 12-keV nitrogen PIII (with 3 X 10(17) cm(-2) dose) increased by 10% compared to the unimplanted sample, in layers deeper than the regions where the formation of the Si,N, compound occurred. A factor of 2.5 increase in hardness was obtained for C-implanted Si wafer at 35 keV (with 6 X 10(17) cm(-2) dose), again deeper than the SiC-rich layer, Both compounds are in the amorphous state and their hardness is much lower than that of the crystalline compounds, which require an annealing process after ion implantation. In the same targets, the contact angle increased by 65% and 35% for N- and C-implanted samples, respectively. Compared to the Si target, the nitrogen PIII-irradiated Al 5052 (wish 15 keV) showed negligible change in its hydrophobic character after ion implantation. Its near-surface nanohardness measurement showed a slight increase for doses of 1 X 10(17) cm(-2). We have been searching for an AlN layer of the order of 1000 A thick, using such a low-energy PIII process, but oxide formation during processing has precluded its synthesis. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Nanohardness of a Ti thin film and its interface deposited by an electron beam on a 304 SS substrate

The results of nanohardness measurements at a film surface and film-substrate interface are presented and discussed. An electron beam device was used to deposit a Ti film on a 304 stainless steel (304 SS) substrate. The diluted interface was obtained by thermal activated atomic diffusion. The. Ti film and Ti film-304 SS interface were analyzed by energy dispersive spectrometry and were observed using atomic force microscopy. The nanohardness of the Ti film-304 SS system was measured by a nanoindentation technique. The results showed the Ti film-304 SS interface had a higher hardness value than the Ti film and 304 SS substrate. The Ti film surface had a lower hardness due to the presence of a TiO2 thin layer.

Study of the surface hardness and modulus of elasticity of conventional and microwave-cured acrylic resins

The aim of this study was to evaluate the following acrylic resins: Clássico®, QC-20® and Lucitone®, recommended specifically for thermal polymerization, and Acron MC® and VIPI-WAVE®, made for polymerization by microwave energy. The resins were evaluated regarding their surface nanohardness and modulus of elasticity, while varying the polymerization time recommended by the manufacturer. They were also compared as to the presence of water absorbed by the samples. The technique used was nanoindentation, using the Nano Indenter XP®, MTS. According to an intra-group analysis, when using the polymerization time recommended by the manufacturer, a variation of 0.14 to 0.23 GPa for nanohardness and 2.61 to 3.73 GPa for modulus of elasticity was observed for the thermally polymerized resins. The variation for the resins made for polymerization by microwave energy was 0.15 to 0.22 GPa for nanohardness and 2.94 to 3.73 GPa for modulus of elasticity. The conclusion was that the Classico® resin presented higher nanohardness and higher modulus of elasticity values when compared to those of the same group, while Acron MC® presented the highest values for the same characteristics when compared to those of the same group. The water absorption evaluation showed that all the thermal polymerization resins, except for Lucitone®, presented significant nanohardness differences when submitted to dehydration or rehydration, while only Acron MC® presented no significant differences when submitted to a double polymerization time. Regarding the modulus of elasticity, it was observed that all the tested materials and products, except for Lucitone®, showed a significant increase in modulus of elasticity when submitted to a lack of hydration.

Tratamento termoquímico do titânio auxiliado por plasma de ar - N2 - O2

Discs were grade II cp Ti oxynitride by plasma of Ar - N2 - O2 using different proportions of individual gases. These ratios were established from analysis of optical emission spectroscopy (OES) of plasma species. The proportions that resulted in species whose spectra showed an abrupt change of light intensity were chosen for this study. Nanohardness tests revealed that there was a correlation between the intensity of N2 + species with the hardness, because the treatments where they had a higher intensity, obtained a higher value nanohardness, although the crystalline phases have remained unchanged. With respect to topography, it was observed that in general, the surface roughness is related to the intensities of plasma species, because they may have different values depending on the behavior of the species. Images obtained by optical microscopy revealed a surface with grains of different colors to optical reflectance showed a peak of reflection in the red area. Measures the contact angle and surface tension showed hydrophilic properties and hydrophilic with little variation of polar and dispersive components of surface tension

Propriedades tribomecânicas de superfícies de titânio carbonitretadas por plasma

Interstitial compounds of titanium have been mainly studied due to the large range of properties acquired when C, N, O and H atoms are added. In this work, surfaces of TiCxNy were produced by thermochemical treatments assisted by plasma with different proportions of Ar + N2 + CH4 gas mixture. The Ar gas flow was fixed in 4 sccm, varying only N2 and CH4 gas flows. During the thermochemical treatment, the plasma was monitored by Optical Emission Spectroscopy (OES) for the investigation of the influence of active species. After treatments, C and N concentration profile, crystalline and amorphous phases were analyzed by Nuclear Reaction (NRA). Besides tribomechanical properties of the Ti surface were studied through the nanohardness measurements and friction coefficient determination. The worn areas were evaluated by profilometry and Scanning Electronic Microscope (SEM) in order to verify the wear mechanism present in each material. It has been seen which the properties like nanohardness and friction coefficient have strong relation with luminous intensity of species of the plasma, suggesting a using of this characteristic as a parameter of process

Diagnóstico das espécies ativas do plasma usado em tratamentos termoquímicos do titânio

Plasma diagnostics by Optical Emission Spectroscopy were performed for electrical discharge in three gas mixture respecting the combinations z N2 y Ar x H2, z N2 y Ar x O2 e z N2 y Ar x CH4, in which the indexes z and y systematically vary from 1 to 4 and x varies from 0 to 4, every one has dimension SCCM, resulting in 80 combinations. From the all obtained spectrums, the species CH (387,1 nm), N2+ (391,4 nm), Hβ (486,1 nm), Hα (656,3 nm), Ar (750,4 nm), O (777,4 nm) e O (842,6 nm) were analyzed because of their abundance and importance on the kinetic of reaction from the plasma to surface, besides their high dependences on the gases flows. Particularly interesting z, y and x combinations were chosen in order to study the influence of active species on the surface modification during the thermochemical treatment. From the mixtures N2 Ar O2 e N2 Ar CH4 were chosen three peculiar proportions which presented luminous intensity profile with unexpected maximum or minimum values, denominated as plasma anomaly. Those plasma concentrations were utilized as atmosphere of titanium treatment maintaining constant the control parameters pressure and temperature. It has been verified a relation among luminous intensity associated to N2+ and roughness, nanohardness and O atoms diffusion into the crystalline lattice of treated titanium and it has been seen which those properties becomes more intense precisely in the higher points found in the optical profile associated to the N2+ specie. Those parameters were verified for the mixture which involved O2 gas. For the mixture which involves CH4 gas, the relation was determinate by roughness, number of nitrogen and carbon atoms diffused into the titanium structure which presented direct proportionality with the luminous intensity referent to the N2+ and CH. It has been yet studied the formation of TiCN phases on the surface which presented to be essentially directly proportional to the increasing of the CH specie and inversely proportional to the increasing of the specie N2+

Nanomechanical properties of biochemically modified dentin bonded interfaces

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influência do tratamento dentinário com Clorexidina, Ácido Hialurônico ou Vitamina C na resistência adesiva e propriedades mecânicas da camada híbrida

Pós-graduação em Odontologia Restauradora - ICT

Light-curing Time and Aging Effects on the Nanomechanical Properties of Methacrylate- and Silorane-based Restorations

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Preventing erosion with novel agents

Objectives: This in vitro study aimed to investigate the protective effect of four commercial novel agents against erosion. Methods: Ninety human molars were distributed into 9 groups, and after incubation in human saliva for 2 h, a pellicle was formed. Subsequently, the specimens were submitted to demineralization (orange juice, pH 3.6, 3 min) and remineralization (paste slurry containing one of the tested novel agents, 3 min) cycles, two times per day, for 4 days. The tested agents were: (1) DenShield Tooth; active ingredient: 7.5% W/W NovaMin® (calcium sodium phosphosilicate); (2) Nanosensitive hca; active ingredient: 7.5% W/W NovaMin®; (3) GC Tooth Mousse; active ingredient: 10% Recaldent™ (CPP-ACP); (4) GC MI Paste Plus; active ingredients: 10% Recaldent™, 900 ppm fluoride. Two experimental procedures were performed: in procedure 1, the tested agents were applied prior to the erosive attack, and in procedure 2 after the erosive attack. A control group receiving no prophylactic treatment was included. Surface nanohardness (SNH) of enamel specimens was measured after pellicle formation and after completion of daily cyclic treatment. Results: SNH significantly decreased at the end of the experiment for all groups (p < 0.05). In both procedures, there was no statistically significant difference between the control group and those treated with paste slurries (p > 0.05). In addition, the changes in SNH (ΔSNH = SNHbaseline − SNHfinal) did not show statistically significant difference between both procedures (p > 0.05). Conclusion: Tooth erosion cannot be prevented or repaired by these novel agents, regardless of fluoride content.

The impact of ocean acidification and warming on the skeletal mechanical properties of the sea urchin Paracentrotus lividus from laboratory and field observations

Increased atmospheric CO2 concentration is leading to changes in the carbonate chemistry and the temperature of the ocean. The impact of these processes on marine organisms will depend on their ability to cope with those changes, particularly the maintenance of calcium carbonate structures. Both a laboratory experiment (long-term exposure to decreased pH and increased temperature) and collections of individuals from natural environments characterized by low pH levels (individuals from intertidal pools and around a CO2 seep) were here coupled to comprehensively study the impact of near-future conditions of pH and temperature on the mechanical properties of the skeleton of the euechinoid sea urchin Paracentrotus lividus. To assess skeletal mechanical properties, we characterized the fracture force, Young's modulus, second moment of area, material nanohardness, and specific Young's modulus of sea urchin test plates. None of these parameters were significantly affected by low pH and/or increased temperature in the laboratory experiment and by low pH only in the individuals chronically exposed to lowered pH from the CO2 seeps. In tidal pools, the fracture force was higher and the Young's modulus lower in ambital plates of individuals from the rock pool characterized by the largest pH variations but also a dominance of calcifying algae, which might explain some of the variation. Thus, decreases of pH to levels expected for 2100 did not directly alter the mechanical properties of the test of P. lividus. Since the maintenance of test integrity is a question of survival for sea urchins and since weakened tests would increase the sea urchins' risk of predation, our findings indicate that the decreasing seawater pH and increasing seawater temperature expected for the end of the century should not represent an immediate threat to sea urchins vulnerability

Comportamento em desgaste por erosão cavitação, erosão - corrosão e em ensaios de microesclerometria linear instrumentada de um aço inoxidável martensítico AISI 410 nitretado a plasma em baixa temperatura, utilizando a tecnologia de tela ativa.

Amostras de um aço inoxidável martensítico AISI 410 temperado e revenido foram nitretadas a plasma em baixa temperatura usando o tratamento de nitretação plasma DC e a nitretação a plasma com tela ativa. Ambos os tratamentos foram realizados a 400 °C, utilizando mistura gasosa de 75 % de nitrogênio e 25 % de hidrogênio durante 20 horas e 400 Pa de pressão. As amostras de aço AISI 410 temperado e revenido foram caracterizadas antes e depois dos tratamentos termoquímicos, usando as técnicas de microscopia óptica, microscopia eletrônica de varredura, medidas de microdureza, difração de raios X e medidas de teor de nitrogênio em função da distância à superfície por espectrometria WDSX de raios X. A resistência à erosão por cavitação do aço AISI 410 nitretado DC e com tela ativa foi avaliada segundo a norma ASTM G32 (1998). Os ensaios de erosão, de erosão - corrosão e de esclerometria linear instrumentada segundo norma ASTM C1624 (2005) somente foram realizados no aço AISI 410 nitretado com tela ativa. Ensaios de nanoindentação instrumentada forma utilizados para medir a dureza (H) e o módulo de elasticidade reduzido (E*) e calcular as relações H/E* e H3/E*2 e a recuperação elástica (We), utilizando o método proposto por Oliver e Pharr. Ambos os tratamentos produziram camadas nitretadas de espessura homogênea constituídas por martensita expandida supersaturada em nitrogênio e nitretos de ferro com durezas superiores a 1200 HV, porém, a nitretação DC produziu maior quantidade de nitretos de ferro do que o tratamento de tela ativa. Os resultados de erosão por cavitação do aço nitretado DC mostraram que a precipitação de nitretos de ferro é prejudicial para a resistência à cavitação já que reduziu drasticamente o período de incubação e aumentou a taxa de perda de massa nos estágios iniciais do ensaio; entretanto, depois da remoção desses nitretos de ferro, a camada nitretada formada somente por martensita expandida resistiu bem ao dano por cavitação. Já no caso do aço nitretado com tela ativa, a resistência à erosão por cavitação aumentou 27 vezes quando comparada com o aço AISI 410 sem nitretar, fato atribuído à pequena fração volumétrica e ao menor tamanho dos nitretos de ferro presente na camada nitretada, às maiores relações H/E* e H3/E*2 e à alta recuperação elástica da martensita expandida. A remoção de massa ocorreu, principalmente, pela formação de crateras e de destacamento de material da superfície dos grãos por fratura frágil sem evidente deformação plástica. As perdas de massa acumulada mostradas pelo aço nitretado foram menores do que aquelas do aço AISI 410 nos ensaios de erosão e de erosão corrosão. O aço nitretado apresentou uma diminuição nas taxas de desgaste em ambos os ensaios de aproximadamente 50 % quando comparadas com o aço AISI 410. O mecanismo de remoção de material foi predominantemente dúctil, mesmo com o grande aumento na dureza. Os resultados de esclerometria linear instrumentada mostraram que a formação de martensita expandida possibilitou uma diminuição considerável do coeficiente de atrito em relação ao observado no caso do aço AISI 410 sem nitretar. O valor de carga crítica de falha foi de 14 N. O mecanismo de falha operante no aço nitretado foi trincamento por tensão.

Visoelastic studies on thermoplastic polyurethane nanocomposites using a nano-hardness tester

The viscoelastic behaviour of a range of polyurethane thermoplastic elastomer montmorillonite nanocomposites has been studied using a nanohardness tester. For softer Shore hardness 80A materials, the introduction of the organo-clay increased the creep strain obtained while the nano-indentor was held at constant load. The increase in creep strain was greatest for materials containing an organo-clay modified with a more hydrophilic quaternary alkylammonium surfactant and with higher loadings of the hydrophilic organo-clay. This suggested the effect might be due to a plasticising effect of the excess surfactant. For the harder Shore hardness 55D materials, the addition of the organo-clays produced only a small decrease in the creep strain, probably due to the interconnected hard domains in this material.

Tratamento termoquímico do titânio auxiliado por plasma de ar - N2 - O2

Discs were grade II cp Ti oxynitride by plasma of Ar - N2 - O2 using different proportions of individual gases. These ratios were established from analysis of optical emission spectroscopy (OES) of plasma species. The proportions that resulted in species whose spectra showed an abrupt change of light intensity were chosen for this study. Nanohardness tests revealed that there was a correlation between the intensity of N2 + species with the hardness, because the treatments where they had a higher intensity, obtained a higher value nanohardness, although the crystalline phases have remained unchanged. With respect to topography, it was observed that in general, the surface roughness is related to the intensities of plasma species, because they may have different values depending on the behavior of the species. Images obtained by optical microscopy revealed a surface with grains of different colors to optical reflectance showed a peak of reflection in the red area. Measures the contact angle and surface tension showed hydrophilic properties and hydrophilic with little variation of polar and dispersive components of surface tension

Propriedades tribomecânicas de superfícies de titânio carbonitretadas por plasma

Interstitial compounds of titanium have been mainly studied due to the large range of properties acquired when C, N, O and H atoms are added. In this work, surfaces of TiCxNy were produced by thermochemical treatments assisted by plasma with different proportions of Ar + N2 + CH4 gas mixture. The Ar gas flow was fixed in 4 sccm, varying only N2 and CH4 gas flows. During the thermochemical treatment, the plasma was monitored by Optical Emission Spectroscopy (OES) for the investigation of the influence of active species. After treatments, C and N concentration profile, crystalline and amorphous phases were analyzed by Nuclear Reaction (NRA). Besides tribomechanical properties of the Ti surface were studied through the nanohardness measurements and friction coefficient determination. The worn areas were evaluated by profilometry and Scanning Electronic Microscope (SEM) in order to verify the wear mechanism present in each material. It has been seen which the properties like nanohardness and friction coefficient have strong relation with luminous intensity of species of the plasma, suggesting a using of this characteristic as a parameter of process