Fretting wear behaviour of hydroxyapatite-titanium composites in simulated body fluid, supplemented with 5 g l(-1) bovine serum albumin

Damaged articulating joints can be repaired or replaced with synthetic biomaterials, which can release wear debris due to articulation, leading to the osteolysis. In a recent work, it has been shown that it is possible to achieve a better combination of flexural strength/fracture toughness as well as in vitro bioactivity and cytocompatibility properties in spark plasma sintered hydroxyapatite-titanium (HA-Ti) composites. Although hydroxyapatite and titanium are well documented for their good biocompatibility, nanosized hydroxyapatite (HA) and titanium (Ti) particles can cause severe toxicity to cells. In order to address this issue, fretting wear study of HA-Ti composites under dry and wet (1x SBF, supplemented with 5 g l(-1) bovine serum albumin (BSA)) condition was performed to assess the wear resistance as well as wear debris formation, in vitro. The experimental results reveal one order of magnitude lower wear rate for HA-10 wt% Ti (7.5 x 10(-5) mm(3) N-1 m(-1)) composite than monolithic HA (3.9 x 10(-4) mm(3) N-1 m(-1)) in simulated body fluid. The difference in the tribological properties has been analyzed in the light of phase assemblages and mechanical properties. Overall, the results suggest the potential use of HA-Ti composites over existing HA-based biocomposites in orthopedic as well as dental applications.

Effect of surface roughness of Ti, Zr, and TiZr on apatite precipitation from simulated body fluid

Some of the critical properties for a successful orthopedic or dental implant material are its biocompatibility and bioactivity. Pure titanium (Ti) and zirconium (Zr) are widely accepted as biocompatible metals, due to their non-toxicity. While the bioactivity of Ti and some Ti alloys has been extensively investigated, there is still insufficient data for Zr and titanium-zirconium (TiZr) alloys. In the present study, the bioactivity, that is, the apatite forming ability on the alkali and heat treated surfaces of Ti, Zr, and TiZr alloy in simulated body fluid (SBF), was studied. In particular, the effect of the surface roughness characteristics on the bioactivity was evaluated for the first time. The results indicate that the pretreated Ti, Zr and TiZr alloy could form apatite coating on their surfaces. It should be noted that the surface roughness also critically affected the bioactivity of these pretreated metallic samples. A surface morphology with an average roughness of approximately 0.6 microm led to the fastest apatite formation on the metal surfaces. This apatite layer on the metal surface is expected to bond to the surrounding bones directly after implantation.

Control of biodegradation of a Mg alloy in simulated body fluid

Mg alloy AZ31 is an attractive candidate for coronary artery stents, as it possesses excellent biocompatibility in human body and good mechanical properties. However, AZ31 magnesium alloys generally have poor corrosion resistance in the body environment. This paper reports on the early stages of an investigation into the corrosion mechanism and the morphology of corrosion of AZ31 in simulated body fluid (SBF). The investigation will also consider ways of improving corrosion resistance of this alloy in SBF through the use of ionic liquids. The results to date have shown that AZ31 suffers severe localized pitting corrosion in SBF. The pits mainly develop adjacent to the Al-Mn intermetallic second phase in the α matrix. Energy Dispersive X-Ray Spectroscopy results revealed the presence of Mg, O, Ca, and P in the layer of corrosion product. Treatment of the AZ31 alloy prior to corrosion testing in SBF with the ionic liquid trimethyl (butyl) phosphonium diphenyl phosphate (P1444DPP) produced some increase in the corrosion resistance of the alloy.

Ionic liquid pretreatment as a means to control the corrosion behavior of magnesium alloys in simulated body fluid

Recently, the use of magnesium alloys as metallic implant materials for biodegradable coronary artery stents has been steadily growing in interest. However, AZ31 magnesium alloys present poor corrosion resistance in the body environment. This work reports on the use of a treatment with low-toxicity IL Trimethyl (butyl) phosphonium diphenyl phosphate P₁₄₄₄DPP, which provides corrosion protection for magnesium alloy AZ31 in simulated body fluid (SBF). Before IL treatment, surface was cleaned by HNO₃ and H₃PO₄ acid pickling solution. The effect of ionic liquid treatment on the corrosion performance of magnesium alloys AZ31in simulated body fluid has been investigated by electrochemical tests and the observation of surface morphology. The results show that this IL treatment succeeded in increasing the corrosion resistance of AZ31 when exposed to SBF.

Corrosion behaviour of pure magnesium in a simulated body fluid

The corrosion behaviour of pure magnesium in Hank's simulated body fluid (SBF) was investigated. It was found that the polarization of Mg in the SBF solution was similar to that in a NaCl aqueous solution. However, AC impedance analysis suggested that the detailed dissolution steps involved in the corrosion of Mg in the SBF could be different in terms of their rates or contributions to corrosion damage of Mg. Moreover, the corrosion rate of Mg in the SBF solution was found to be increasing with time and significant hydrogen evolution and alkalization of the SBF solution resulting from corrosion of Mg were measured in the study. The results suggested that after some proper measures are taken to retard corrosion reaction, Mg can be successfully employed as a degradable and absorbable implant material.

In-vitro study of the spontaneous calcification of PHEMA-based hydrogels in simulated body fluid

In-vitro calcification of poly(2-hydroxyethyl methacrylate) (PHEMA)-based hydrogels in simulated body fluid (SBF) under a steady/batch system without agitation or stirring the solutions has been investigated. It was noted that the formation of calcium phosphate (CaP) deposits primarily proceeded through spontaneous precipitation. The CaP deposits were found both on the surface and inside the hydrogels. It appears that the effect of chemical structure or reducing the relative number of oxygen atoms in the copolymers on the degree of calcification was only important at the early stage of calcification. The morphology of the CaP deposits was observed to be spherical aggregates with a thickness of the CaP layer less than 0.5 mu m. Additionally, the CaP deposits were found to be poorly crystalline or to have nano-size crystals, or to exist mostly as an amorphous phase. Characterization of the CaP phases in the deposits revealed that the deposits were comprised mainly of whitlockite [Ca9MgH(PO4)(7)] type apatite and DCPD (CaHPO4 center dot 2H(2)O) as the precursors of hydroxyapatite [Ca-10(PO4)(6)(OH)(2)]. The presence of carbonate in the deposits was also detected during the calcification of PHEMA based hydrogels in SBF solution.

Effect of equal channel angular extrusion on wear and corrosion behavior of the orthopedic Ti-13Nb-13Zr alloy in simulated body fluid

We report investigations on the texture, corrosion and wear behavior of ultra-fine grained (UFG) Ti-13Nb-Zr alloy, processed by equal channel angular extrusion (ECAE) technique, for biomedical applications. The microstructure obtained was characterized by X-ray line profile analysis, scanning electron microscope (SEM) and electron back scattered diffraction (EBSD). We focus on the corrosion resistance and the fretting behavior, the main considerations for such biomaterials, in simulated body fluid. To this end. potentiodynamic polarization tests were carried out to evaluate the corrosion behavior of the UFG alloy in Hanks solution at 37 degrees C. The fretting wear behavior was carried out against bearing steel in the same conditions. The roughness of the samples was also measured to examine the effect of topography on the wear behavior of the samples. Our results showed that the ECAE process increases noticeably the performance of the alloy as orthopedic implant. Although no significant difference was observed in the fretting wear behavior, the corrosion resistance of the UFG alloy was found to be higher than the non-treated material. (c) 2012 Elsevier B.V. All rights reserved.

Evaluation of Corrosion Fatigue Behaviour of Laser-welded NiTi Alloys using Bending Rotation Fatigue Test in Simulated Body Fluid

Shape memory NiTi alloys have been used extensively for medical device applications such as orthopedic, dental, vascular and cardiovascular devices on account of their unique shape memory effect (SME) and super-elasticity (SE). Laser welding is found to be the most suitable method used to fabricate NiTi-based medical components. However, the performance of laser-welded NiTi alloys under corrosive environments is not fully understood and a specific focus on understanding the corrosion fatigue behaviour is not evident in the literature. This study reveals a comparison of corrosion fatigue behaviour of laser-welded and bare NiTi alloys using bending rotation fatigue (BRF) test which was integrated with a specifically designed corrosion cell. The testing environment was Hanks’ solution (simulated body fluid) at 37.5oC. Electrochemical impedance spectroscopic (EIS) measurement was carried out to monitor the change of corrosion resistance at different periods during the BRF test. Experiments indicate that the laser-welded NiTi alloy would be more susceptible to the corrosion fatigue attack than the bare NiTi alloy. This finding can serve as a benchmark for the product designers and engineers to determine the factor of safety of NiTi medical devices fabricated using laser welding.

Corrosion Fatigue Behaviour of Laser-welded Shape Memory NiTi Wires in a Simulated Body Fluid

Corrosion fatigue is a fracture process as a consequence of synergistic interactions between the material structure, corrosive environment and cyclic loads/strains. It is difficult to be detected and can cause unexpected failure of engineering components in use. This study reveals a comparison of corrosion fatigue behaviour of laser-welded and bare NiTi wires using bending rotation fatigue (BRF) test coupled with a specifically-designed corrosion cell. The testing medium was Hanks’ solution (simulated body fluid) at 37.5 oC. Electrochemical impedance spectroscopic (EIS) measurement was carried out to monitor the change of corrosion resistance of sample during the BRF test at different periods of time. Experiments indicate that the laser-welded NiTi wire would be more susceptible to the corrosion fatigue attack than the bare NiTi wire. This study can serve as a benchmark for the product designers and engineers to understand the corrosion fatigue behaviour of the NiTi laser weld joint and determine the fatigue life safety factor for NiTi medical devices/implants involving laser welding in the fabrication process.

In situ impedance spectroscopy study of the electrochemical corrosion of Ti and Ti-6Al-4V in simulated body fluid at 25 degrees C and 37 degrees C

The corrosion resistance of Ti and Ti-6Al-4V was investigated through electrochemical impedance spectroscopy, EIS, potentiodynamic polarisation curves and UV-Vis spectrophotometry. The tests were done in Hank solution at 25 degrees C and 37 degrees C. The EIS measurements were done at the open circuit potential at specific immersion times. An increase of the resistance as a function of the immersion time was observed, for Ti (at 25 degrees C and 37 degrees C), and for Ti-6Al-4V (at 25 degrees C), which was interpreted as the formation and growth of a passive film on the metallic surfaces. (C) 2009 Elsevier Ltd. All rights reserved.

In vitro behavior of human osteoblast-like cells (SaOS2) cultured on surface modified titanium and titanium–zirconium alloy

In this study, titanium (Ti) and titanium-zirconium (TiZr) alloy samples fabricated through powder metallurgy were surface modified by alkali-heat treatment and calcium (Ca)-ion-deposition. The alteration of the surface morphology and the chemistry of the Ti and TiZr after surface modification were examined. The bioactivity of the Ti and TiZr alloys after the surface modification was demonstrated. Subsequently, the cytocompatibility of the surface modified Ti and TiZr was evaluated via in vitro cell culture using human osteoblast-like cells (SaOS2). The cellular attachment, adhesion and proliferation after cell culture for 14 days were characterized by scanning electron microscopy (SEM) and MTT assay. The relationship between surface morphology and chemical composition of the surface modified Ti and TiZr and cellular responses was investigated. Results indicated that the surface-modified Ti and TiZr alloys exhibited excellent in vitro cytocompatibility together with satisfactory bioactivity. Since osteoblast adhesion and proliferation are essential prerequisites for a successful implant in vivo, these results provide evidence that Ti and TiZr alloys after appropriate surface modification are promising biomaterials for hard tissue replacement.

Influence of calcium ion deposition on apatite-inducing ability of porous titanium for biomedical applications

In the present study, the influence of calcium ion deposition on the apatite-inducing ability of porous titanium(Ti) was investigated in a modified simulated body fluid (m-SBF). Calcium hydroxide (Ca(OH)₂) solutions with five degrees of saturation were used to hydrothermally deposit Ca ions on porous Ti with a porosity of 80%. Apatite-inducing ability of the Ca-ion-deposited porous Ti was evaluated by soaking them in m-SBF for up to 14 days. Scanning electron microscopy (SEM) and X-ray diffractometry (XRD) confirmed that a thin layer of calcium titanate (CaTiO₃)/calcium oxide (CaO) mixture with a nanostructured porous network was produced on porous Ti substrates after hydrothermal treatment at 200 °C for 8 h. X-ray photoelectron spectroscopy results demonstrated that the content of the Ca ions deposited on Ti and the thickness of the CaTiO₃/CaO layer increased with increasing saturation degree of the Ca(OH)₂ solution. The thickest (over 10 nm) CaTiO₃/CaO layer with the highest Ca content was achieved on the Ti treated in an oversaturated Ca(OH)₂ solution (0.2 M). SEM, XRD, transmission electron microscopy and Fourier transformed infrared spectroscopy analysis indicated that the porous Ti samples deposited with the highest content of Ca ions exhibited the best apatite-inducing ability, producing a dense and complete carbonated apatite coating after a 14 day soaking in m-SBF. The present study illustrated the validity of using Ca ion deposition as a pre-treatment to endow desirable apatite-inducing ability of porous Ti for bone tissue engineering applications.

Microstructures and bond strengths of the calcium phosphate coatings formed on titanium from different simulated body fluids

Calcium phosphate (Ca-P) coatings were deposited on Ti substrates by a biomimetic method from m-SBF and 10× SBF, respectively. Comparative study of microstructures and bond strengths of the Ca-P coatings deposited from those different SBFs was carried out. Effect of the surface roughness of the substrates on the bond strength of the Ca-P coatings was also studied. Scanning electron microscopy (SEM), X-ray diffractometry (XRD), Fourier transformed infrared spectroscopy (FTIR), inductive coupled plasma spectrometry (ICP) and thermogravimetry (TG) were used to characterize the Ca-P coatings. The bond strengths between the coatings and Ti substrates were measured using an adhesive strength test. Results indicated that the ionic concentrations of the SBFs and the surface roughness of the substrate had a significant influence on the formation, morphology and bond strength of the Ca-P precipitates. The induction period of time to deposit a complete Ca-P layer from the m-SBF is much longer, but the Ca-P coating is denser and has higher bond strength than that formed from the 10× SBF. The Ti with a surface roughness of R_a 0.64 µm and R_z 2.81 µm favoures the formation of a compact Ca-P coating from the m-SBF with the highest bond strength of approximately 15.5 MPa.

On corrosion behaviour of magnesium alloy AZ31 in simulated body fluids and influence of ionic liquid pretreatments

This paper reports on the corrosion of Mg alloy AZ31 in simulated body fluid (SBF) using static immersion tests and electrochemical impedance spectroscopy. A preliminary study on the effect of flowing SBF on the corrosion behaviour of AZ31 has also been carried out. Low toxicity ionic liquids (ILs) trimethyl(butyl)phosphonium diphenyl phosphate P1444DPP and trihexyl(tetradecyl)-phosphonium bis-2,4,4trimethylpentyl-phosphinate [P66614][ i(C8) 2PO2] have been used to provide corrosion protection for AZ31 in SBF. Time dependent immersion tests indicate that under static conditions, AZ31 suffers severe localised corrosion in SBF, with pits developing predominantly beside the Al-Mn intermetallic phase in the α matrix. At longer immersion times, the corrosion product eventually precipitates and covers the entire specimen surface. When exposed to SBF under flowing conditions with a shear stress of 0·88 Pa, more uniform corrosion was observed. The optical profilometry results and electrochemical impedance spectroscopy analysis suggest that both P
1444DPP and [P66614][i(C8)2PO2] pretreatments can increase the corrosion resistance of AZ31 in SBF, in particular by decreasing the number of deeper pits found on the alloy surface. Cytotoxic test shows that the presence of the ILs P
1444DPP and [P66614][i(C8)2PO2] in cell culture media slightly inhibits the growth of human coronary artery endothelial cells in comparison with the good cell viability around the treated specimen. A pretreatment with IL is used in order to improve the corrosion resistance of this alloy in SBF. © 2012 Institute of Materials, Minerals and Mining.

Dynamics of the interaction between body fluid and Ti cp: the influence of surface functionalization in the first stages of osseointegration

INTRODUCTION: Regenerative therapies using biomaterials require accurate information on interactions between the implanted material and the human body. To improve the process of bone regeneration it is necessary to obtain a better understanding of the influence of the surfaces on the early stages of osseointegration. This work aims to investigate the dynamic interaction between simulated body fluid (SBF) and titanium surfaces (Ti cp) immediately after their first contact. METHODS: Ti cp samples were passed through physicochemical treatments after immersion in acid solution, alkaline solution and solutions containing TiO2 and Ca2+, to obtain three different surfaces. These were characterized by electron microscopy and free energy estimates. The evaluation of the interaction with SBF was performed by measuring the dynamic contact angles after contacting the surfaces. RESULTS: The effects of SBF wettability were more significant on surfaces according to high energy estimates. A comparative analysis of the three types of surfaces showed that fluid spreading was greater in samples with greater polar components, indicating that the surface nature influences interactions in the early stages of osseointegration. CONCLUSION: The results indicate the influence of polar interactions in the dynamic wettability of the SBF. It is possible that these interactions can also influence cellular viability on surfaces. Based on these results, new experiments are being designed to improve the presented methodology as a tool for the evaluation of biomaterials without the need for in vivo experiments.