Caries Resistance of Lased Human Root Surface with 10.6 mu m CO(2) Laser-Thermal, Morphological, and Microhardness Analysis

Although the cariostatic effects of CO(2) laser on enamel have been shown, its effects on root surface demineralization remains uncertain. The objectives of this in vitro research was to establish safe parameters for a pulsed 10.6 mu m CO(2) laser and to evaluate its effect on morphological features of the root surface, as well as on the reduction of root demineralization. Ninety-five human root surfaces were randomly divided into five groups: G1-No treatment (control); G2-2.5 J/cm(2); G3-4.0 J/cm(2); G4-5.0 J/cm(2); and G5-6.0 J/cm(2). Intrapulpal temperature was evaluated during root surface irradiation by a thermocouple and morphological changes were evaluated by SEM. After the surface treatment, the specimens were submitted to a 7-day pH-cycling model. Subsequently, the cross-sectional Knoop microhardness values were measured. For all irradiated groups, intrapulpal temperature changes were less than 1.5 degrees C. Scanning electron microscopy images indicated that fluences as low as 4.0 J/cm(2) were sufficient to induce morphological changes in the root surface. Additionally, for fluences reaching or exceeding 4.0 J/cm(2), laser-induced inhibitory effects on root surface demineralization were observed. It was concluded that laser energy density in the range of 4.0 to 6.0 J/cm(2) could be applied to a dental root to reduce demineralization of this surface without compromising pulp vitality.

Quantitative analysis of mineral content in enamel using laboratory microtomography and microhardness analysis. - art. no. 631823

This study evaluates laboratory microtomography and microhardness analysis for quantifying the mineral content of bovine enamel. Fifty enamel blocks were submitted individually for 5 days to a pH-cycling model at 37 degrees C and remained in the remineralizing solution for 2 days. The blocks were treated twice daily for 1 min with NaF dentifrices (Placebo, 275, 550, 1,100 mu g F/g and Crest (R)) diluted in deionized water. Surface microhardness changes (%SMH) and mineral loss (Delta Z) were then calculated. Laboratory microtomography was also used to measure total mineral lost (LMM). Pearson's correlation (p < 0.05) was used to determine the relationship between different methods of analysis and dose-response between treatments. Dentifrice fluoride concentration and %SMH and Delta Z were correlated (p < 0.05). There was a positive relationship (p < 0.05) when comparing LMM vs. Delta Z; a negative relationship (p < 0.05) was found for %SMH vs. LMM and %SMH vs. Delta Z. Therefore, both mineral quantification techniques provide adequate precision for studying the bovine enamel-pH-cycling demineralization/remineralization model.

Quantitative analysis of mineral content in enamel using synchrotron microtomography and microhardness analysis. - art. no. 631824

Synchrotron microtomography is a tool to quantify the mineralization of dental tissues as well as microhardness analysis, since they provide adequate precision and contrast sensitivity. This study evaluates synchrotron microtomography and microhardness analysis for quantifying the mineral content of bovine enamel. Fifty enamel blocks were submitted individually for 5 days to a pH-cycling model at 37 degrees C and remained in the remineralizing solution for 2 days. The blocks were treated twice daily for 1 min with NaF dentifrices (Placebo, 275, 550, 1,100 mu g F/g and Crest (R)) diluted in deionized water. Surface microhardness changes (%SMH) and mineral loss (Delta Z) were then calculated. Synchrotron microtomography was also used to measure total mineral lost (SMM). Pearson's correlation (p < 0.05) was used to determine the relationship between different methods of analysis and dose-response between treatments. Dentifrice fluoride concentration and %SMH and Delta Z were correlated (p < 0.05). There was a positive relationship (p < 0.05) when comparing SMM vs. Delta Z; a negative relationship (p < 0.05) was found for %SMH vs. SMM and %SMH vs. Delta Z. Based on the results of this study, it was possible to conclude that synchrotron microtomography provides the best spatial resolution and contrast sensitivity for quantifying mineral gradients.

In vivo Dentin Microhardness beneath a Calcium-Phosphate Cement

A minimally invasive caries-removal technique preserves potentially repairable, caries-affected dentin. Mineral-releasing cements may promote remineralization of soft residual dentin. This study evaluated the in vivo remineralization capacity of resin-based calcium-phosphate cement (Ca-PO(4)) used for indirect pulp-capping. Permanent carious and sound teeth indicated for extraction were excavated and restored either with or without the Ca-PO(4) base (control), followed by adhesive restoration. Study teeth were extracted after 3 months, followed by sectioning and in vitro microhardness analysis of the cavity floor to 115-mu m depth. Caries-affected dentin that received acid conditioning prior to Ca-PO(4) basing showed significantly increased Knoop hardness near the cavity floor. The non-etched group presented results similar to those of the non-treated group. Acid etching prior to cement application increased microhardness of residual dentin near the interface after 3 months in situ.

Effect of weathering and thickness on the superficial microhardness of acrylic resin and ocular button

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effects of bleaching with carbamide peroxide gels on microhardness of restoration materials

The objective of this in vitro study was to quantitatively assess the effects of bleaching with 10 and 15% carbamide peroxide (CP) on restoration materials by performing superficial microhardness analysis. Acrylic cylindrical containers (4 x 2 mm) were filled with the following restoration products: Charisma (Heraues Kulzer, Vila Santa Catarina, São Paulo, Brazil), Durafill VS (Heraeus Kulzer), Vitremer (3M, Sumaré, São Paulo, Brazil), Dyract (Dentsply, Petrópolis, Rio de Janeiro, Brazil), and Permite C (SDI, São Pauio, São Paulo, Brazil). Sixty samples were prepared of each restoration material. Twenty samples received bleaching treatment with 10% CP, 20 samples received bleaching treatment with 15% CP, and 20 samples were kept submerged in artificial saliva, which was replaced daily. The treatment consisted of immersion of the specimens in 1 cm3 of CP at 10 and 15% for 6 hours per day during 3 weeks, whereupon the test specimens were washed, dried, and kept immersed in artificial saliva for 18 hours. Then the test and control specimens were analyzed using a microhardness gauge. The Knoop Hardness Number (KHN) was taken for each test and control specimen at five different locations by applying a 25 g force for 20 seconds. The values obtained were transformed into KHNs and the mean was calculated. The data were submitted to statistical analysis by analysis of variance and Tukey test, p < .05. The means/standard deviations were as follows: Charisma: CP 10% 38.52/4.08, CP 15% 34.31/6.13, saliva 37.36/4.48; Durafill VS: CP 10% 18.65/1.65, CP 15% 19.38/2.23, saliva 18.27/1.43; Dyract AP: CP 10% 30.26/2.81, CP 15% 28.64/5.44, saliva 33.88/3.46; Vitremer: CP 10% 28.15/3.04, CP 15% 17.40/3.11, saliva 40.93/4.18; and Permite C: CP 10% 183.50/27.09, CP 15% 159.45/5.78, saliva 215.80/26.15. A decrease in microhardness was observed for the materials Dyract AP, Vitremer, and Permite C after treatment with CP at 10 and 15%, whereas no effect on either of the two composites (Charisma and Durafill) was verified. CLINICAL SIGNIFICANCE: The application of the carbamide peroxide gels at 10 and 15% did not alter the microhardness of the composite resins Charisma and Durafill. In situ and clinical studies are necessary to enable one to conclude that the reduction in microhardness of the materials effectively results in clinical harm to the restorations.

Short-term in situ/ex vivo study of the anticariogenic potential of a resin-modified glass-ionomer cement associated with adhesive systems

Objective: As resin-modified glass-ionomer cement (RMGIC) is an adhesive material, its association to dentin bonding agents (DBAs) was previously proposed. This study investigated the adjunctive behavior of an RMGIC with etch-and-rinse bonding systems under in situ/ex vivo cariogenic challenge. Method and Materials: Bovine enamel blocks (3 3 2 mm) were randomly assigned to group VP, Vitremer + its own primer (3M ESPE); group VSB, Vitremer + Single Bond (3M ESPE); and group VPB, Vitremer + Prime & Bond 2.1 (Dentsply). Two blocks of each group were randomly placed in an acrylic palatal appliance, so each appliance included six blocks. Volunteers (n = 10) wore these appliances according to given instructions to promote a sucrose challenge eight times/day for 15 days. After this period, the blocks were removed from the devices and cleaned, and demineralization was assessed through longitudinal microhardness analysis (Knoop indenter, 25 g/5 s). Data were submitted to three-way ANOVA and Tukey test (P < .05). Results: No treatment was able to completely avoid demineralization. All materials showed a statistically significant difference in mineral loss when the microhardness on the outer enamel was compared with deeper regions (P < .05). Conclusion: Association of the tested RMGICs with etch-and-rinse DBAs did not seem to be more beneficial against caries than the conventional treatment with RMGIC. (Quintessence Int 2010; 41: e192-e199)

Surface transformation hardening of carbon steel with high power fiber laser

This study investigated the surface hardening of steels via experimental tests using a multi-kilowatt fiber laser as the laser source. The influence of laser power and laser power density on the hardening effect was investigated. The microhardness analysis of various laser hardened steels was done. A thermodynamic model was developed to evaluate the thermal process of the surface treatment of a wide thin steel plate with a Gaussian laser beam. The effect of laser linear oscillation hardening (LLOS) of steel was examined. An as-rolled ferritic-pearlitic steel and a tempered martensitic steel with 0.37 wt% C content were hardened under various laser power levels and laser power densities. The optimum power density that produced the maximum hardness was found to be dependent on the laser power. The effect of laser power density on the produced hardness was revealed. The surface hardness, hardened depth and required laser power density were compared between the samples. Fiber laser was briefly compared with high power diode laser in hardening medium-carbon steel. Microhardness (HV0.01) test was done on seven different laser hardened steels, including rolled steel, quenched and tempered steel, soft annealed alloyed steel and conventionally through-hardened steel consisting of different carbon and alloy contents. The surface hardness and hardened depth were compared among the samples. The effect of grain size on surface hardness of ferritic-pearlitic steel and pearlitic-cementite steel was evaluated. In-grain indentation was done to measure the hardness of pearlitic and cementite structures. The macrohardness of the base material was found to be related to the microhardness of the softer phase structure. The measured microhardness values were compared with the conventional macrohardness (HV5) results. A thermodynamic model was developed to calculate the temperature cycle, Ac1 and Ac3 boundaries, homogenization time and cooling rate. The equations were numerically solved with an error of less than 10-8. The temperature distributions for various thicknesses were compared under different laser traverse speed. The lag of the was verified by experiments done on six different steels. The calculated thermal cycle and hardened depth were compared with measured data. Correction coefficients were applied to the model for AISI 4340 steel. AISI 4340 steel was hardened by laser linear oscillation hardening (LLOS). Equations were derived to calculate the overlapped width of adjacent tracks and the number of overlapped scans in the center of the scanned track. The effect of oscillation frequency on the hardened depth was investigated by microscopic evaluation and hardness measurement. The homogeneity of hardness and hardened depth with different processing parameters were investigated. The hardness profiles were compared with the results obtained with conventional single-track hardening. LLOS was proved to be well suitable for surface hardening in a relatively large rectangular area with considerable depth of hardening. Compared with conventional single-track scanning, LLOS produced notably smaller hardened depths while at 40 and 100 Hz LLOS resulted in higher hardness within a depth of about 0.6 mm.

Análise da dentina de dentes decíduos submetidos ao capeamento pulpar indireto

O objetivo do estudo foi avaliar as características da dentina cariada remanescente de molares decíduos quanto à coloração, consistência e microdureza, após um período médio de 3 anos e 8 meses da realização do capeamento pulpar indireto. O estudo clínico constou de 27 dentes que apresentavam lesões cariosas ativas com expressão radiográfica em metade interna de dentina. Aleatoriamente, foi realizado o capeamento pulpar indireto e utilizado como material capeador o hidróxido de cálcio (HC) e o cimento de ionômero de vidro resinoso modificado (CIVRM). As crianças foram acompanhadas através de exames clínicos e radiográficos, e ao longo de um período médio de 3 anos e 8 meses, observou-se um índice de sucesso de 89% para o grupo do HC e de 93% para o CIVRM, não havendo diferença estatisticamente significante entre os dois grupos (p=0,62). Os dentes considerados como sucesso no estudo clínico foram agrupados em um único grupo (grupo teste), que constou de 13 dentes que sofreram esfoliação natural ou exodontia por motivos ortodônticos. Além disso, foram selecionados 15 molares decíduos hígidos (grupo controle positivo) e 15, portadores de lesões cariosas ativas em metade interna de dentina (grupo controle negativo). As amostras do grupo teste tiveram suas respectivas restaurações removidas, a profundidade medida e a dentina remanescente avaliada por um operador calibrado, seguindo critérios descritivos, quanto à consistência e a coloração. Nos dentes do grupo controle positivo, foram realizados preparos cavitários oclusais em até 4 mm de profundidade, enquanto que, no grupo controle negativo, o mesmo operador do estudo clínico realizou a remoção parcial de tecido cariado in vitro. A partir daí, todos os dentes foram preparados para análise de microdureza, que foi realizada por um examinador calibrado, que empregou o princípio de cegamento. Na análise da consistência, todos os dentes do grupo teste (n=13) apresentaram-se endurecidos, enquanto que 9, apresentaram coloração amarela-clara (8 do CIVRM e 1 do HC) e 4, castanho-escura (1 do CIVRM e 3 do HC). Para o teste de microdureza no grupo teste, obteve-se uma média KHN de 40,81 (±16,28) MPa, enquanto que nos grupos controles positivo e negativo, foram alcançados valores médios de 62,73 (±11,24) MPa e 19,15 (±6,99) MPa, respectivamente. A análise estatística mediante o teste ANOVA indicou que houve diferença significativa entre os 3 grupos. Foi constatada a remineralização da dentina de dentes decíduos em que foi realizada a técnica do capeamento pulpar indireto após um período médio de 3 anos e 8 meses, através de critérios clínico (consistência) e laboratorial (análise da microdureza).

Short-term in situ/ex vivo study of the anticariogenic potential of a resin-modified glass-ionomer cement associated with adhesive systems

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Evaluation of light transmission through translucent and opaque posts

Objectives: The transmission of light through translucent posts was observed, and the microhardness of light-cured cement used to secure these posts was evaluated at different depths. Methods: Fifteen single-rooted standard bovine teeth, 16 mm in size, were used. The root canals were prepared using #3 drills Light-Post (five teeth) and Aestheti Post (five teeth) systems (BISCO), with a working-length of 12 mm. In five teeth, translucent posts were cemented (Light-Post #2), while another five teeth received opaque posts (Aestheti Post #2). The roots were painted with black nail varnish to prevent the passage of light through the lateral walls of the roots. The root canals of all the specimens were treated with the All-Bond 2 adhesive system (BISCO) and cemented with light-cured cement (Enforce, Dentsply). All the roots were transversally cut to obtain six specimens 1.5 mm thick. Every two sections corresponded to a specific region of the root (cervical, middle, apical), making it possible to observe the cement microhardness at different levels. The groups (n=10) were defined as: G1: translucent post (TP)/cervical region; G2: TP/middle region; G3: TP/apical region; G4: Opaque post (OP)/cervical region; G5: OP/middle region; G6: PO/apical region. Five root canals were only filled with cement for use as a control (G7). Then, Vickers microhardness analyses were performed. Results: In G3, G5 and G6, the cement was not sufficiently hard to allow for microhardness analysis. When submitted to the ANOVA test, G1 (35.07), G2 (24.28) and G4 (28.64) presented no statistical differences. When the previous groups were compared to G7 (51.00) using the Kruskal-Wallis test, a statistical difference was found. Conclusion: Translucent posts allow cement polymerization up to the middle portion of the root.

Fluoride dose response in pH-cycling models using bovine enamel

The aim of this study was to establish methodologies for verification of the fluoride solution dose-response relationship using bovine enamel and pH-cycling models. Six models of the cariogenic challenge were performed, varying the time of demineralization and pH, time of remineralization, composition of de- and remineralization solutions, frequency and time of application of treatment solutions and pH-cycling duration. For the evaluation of the fluoride effect on caries dynamics, two proposed models provided for improvement in standardization of methods leading to a higher level of precision, demonstrating a dose response between treatments with regard to surface microhardness and Delta Z. For the evaluation of the fluoride effect on enamel remineralization, the addition of fluoride to the de- and remineralization solutions and the reduction of frequency and time of application of fluoride solutions led to a more suitable pH-cycling model. Copyright (C) 2005 S. Karger AG, Basel.

Ação do peróxido de hidrogênio 35% sobre a morfologia do esmalte e sua interferência do processo des-remineralização: estudo in situ

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influência do extrato de araçá (Psidium cattleianum) e aroeira do sertão (Myracrodruon urundeuva) na prevenção à cárie em modelos animais

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)