Physicochemical Properties of Methacrylate Resin-based Root Canal Sealers

Introduction: This study assessed in vitro the physicochemical properties of 2 methacrylate resin-based sealers (Epiphany SE and Hybrid Root SEAL), comparing the results with a well-established epoxy resin-based sealer (AH Plus). Methods: Five samples of each material were used for each test (setting time, flow, radiopacity, dimensional change after setting, and solubility) according to American National Standards Institute/American Dental Association (ANSI/ADA) Specification 57. The samples were assigned to 3 groups: I, AH Plus; II, Epiphany SE; and III, Hybrid Root SEAL. The distilled and deionized water used at the solubility test was submitted to atomic absorption spectrometry to observe the presence of Ca2+, K+, Ni2+, and Zn2+ ions. In addition, the surface morphology of the specimens was analyzed by means of scanning electron microscopy (SEM). Statistical analysis was performed by using one-way analysis of variance and Tukey-Kramer test (P < .05). Results: Flow, radiopacity, and solubility of all sealers were in accordance with ANSI/ADA. The setting time of Hybrid Root SEAL did not agree with ANSUADA requirements. The dimensional change of all sealers was greater than the values considered acceptable by ANSI/ADA. The spectrometry analysis showed significant Ca2+ ions release for AH Plus. In SEM analysis, Hybrid Root SEAL presented spherical monomers with inferior size than AH Plus and Epiphany SE. Conclusions: It might be concluded that physicochemical properties of the tested sealers conformed to ANSI/ADA (2000) standardization, except for the setting time of Hybrid Root SEAL and the dimensional change of all sealers, which did not fulfill the ANSI/ADA requirements. (J Endod 2010;36:1531-1536)

Push-out strength of methacrylate resin-based sealers to root canal walls

P>Aim To assess the push-out strength of Epiphany SE, Epiphany and Hybrid Root SEAL to the dentine walls of root canals. Methodology Sixty roots of canines were prepared and distributed to six groups (n = 10) according to the filling material: GI - Epiphany SE, GII - Epiphany primer and sealer, GIII - Epiphany primer, sealer and resinous solvent, GIV - Clearfil DC Bond and Epiphany sealer, GV - Clearfil, Epiphany sealer and solvent and GVI - Hybrid Root SEAL. Resilon cones were used in all groups. Roots were sectioned transversally to obtain three slices from each third. One slice was subjected to the push-out test (MPa), and results were analysed by anova and Tukey`s test (P < 0.05). The other two slices were prepared for scanning electron microscopy (SEM). Failure mode was also analysed. Results A statistically significant difference (P < 0.05) occurred between Hybrid Root SEAL (5.27 +/- 2.07) and the other materials, GI (0.40 +/- 0.23), GII (0.78 +/- 0.45), GIII (0.57 +/- 0.28), GIV (0.40 +/- 0.24) and GV (0.50 +/- 0.41), which did not differ significantly from each other (P > 0.05). Adhesive failures predominated in groups I, II, IV and V, whilst mixed and cohesive failures were the most frequent in groups III and VI, respectively. There were gaps in the adhesive interface of GI and GII, continuity areas of the filling material with dentine in GIV and GV and good adaptation of the interface of GVI. Conclusion Hybrid Root SEAL had greater push-out strength to root canal dentine than Epiphany SE and Epiphany. The use of primer, solvent and adhesive system did not influence the adhesion of Epiphany.

Solubility of Epiphany Endodontic Sealer Prepared with Resinous Solvent

Purpose: To evaluate in vitro the solubility of the Epiphany endodontic filling material Epiphany (Pentron Clinical Technologies, Wallingford, CT) prepared with its resinous solvent. Methods: The specimens were prepared in the following experimental conditions: (1) GI, epiphany without photoactivation; (2) GII, Epiphany prepared with resinous solvent without photoactivation; (3) Gill, Epiphany followed by photoactivation; and (4) GIV, Epiphany prepared with resinous solvent followed by photoactivation. Ten specimens of each group were obtained from Teflon molds with 80% reduction in volume of the specimen`s dimensions based on American National Standard Institute/American Dental Association (ANSI/ADA) Specification No. 57. The samples were weighted and immersed in distilled water for 7 days. After this period, they were removed, dried, and weighed again. Solubility was calculated by using samples weight loss (%). The immersion liquid was evaluated through atomic absorption spectrometry. Results: The sealers without photoactivation were statistically similar (p > 0.05) between themselves (GI = 6.93% and GII = 6.39%) and different from the uncured sealers, which were statistically different between themselves (p < 0.05) (GIII = 3.56% and GIV = 0.47%). Only the Epiphany sealer prepared with resinous solvent followed by photoactivation presented solubility values within ANSI/ADA requirements, liberating the following amounts of ions: 114.43 mu g of Ca(2+)/mL, 2.4 mu g of Mg(2+)/mL, 0.33 mu g of Fe(2+)/mL, 0.11 mu 4g of Zn(2+)/mL, 1.31 mu g of Ni(2+)/mL, and 7.1 mu g of Na(+)/mL. Conclusion: The association of resinous solvent to the Epiphany sealer followed by photoactivation resulted in a filling material with low solubility and expressive liberation of calcium ions. (J Endod 2009;35:715-718)

Bond Strength of Epiphany Sealer Prepared with Resinous Solvent

This study evaluated in vitro the bond strength of Epiphany sealer prepared with resinous solvent of Epiphany system (Thinning resin) by using a push-out test. Forty maxillary canines were sectioned transversally below the cementoenamel junction to provide 4-mm-thick dentin disks that were centered in aluminum rings and embedded in acrylic resin. Root canals were prepared with tapered diamond bur. Intraradicular dentin was treated with 1% NaOCl for 30 minutes, 17% ethylenediaminetetraacetic acid for 5 minutes, and flushed with distilled water for 1 minute. The specimens were randomly distributed into 4 groups (n = 10) according to the filling material: GI, Epiphany without photoactivation; GII, Epiphany prepared with solvent without photoactivation; Gill, Epiphany followed by photoactivation; and GIV, Epiphany prepared with solvent followed by photoactivation. After the setting time, the specimens were submitted to the push-out test. The highest mean value (14.91 +/- 2.82 MPa) was obtained with Epiphany prepared with solvent followed by photoactivation (GIV), which was statistically different (P < .01) from the other groups. Groups I (8.15 +/- 2.47 MPa), II (9.46 +/- 2.38 MPa), and III (9.80 +/- 2.51 MPa) had inferior bond strength values and were statistically similar among themselves (P > .01). The resinous solvent of Epiphany system increased the bond strength of Epiphany sealer to dentin walls when followed by photoactivation. (J Endod 2009;35: 251-255)

Variability of physicochemical properties of an epoxy resin sealer taken from different parts of the same tube

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Epiphany root canal sealer prepared with resinous solvent is irritating to rat subcutaneous tissues

Objective: This study assessed the biocompatibility of the Epiphany endodontic sealer prepared with resinous solvent of Epiphany system (Thinning resin) in rat subcutaneous tissues. Study Design: Polyethylene tubes were filled with the sealer and 4 groups were established: GI, Epiphany prepared with 1 drop of resinous solvent (RS); GII, Epiphany prepared with 1 drop of RS and photoactivated; GIII, Epiphany associated with self-etch primer and prepared with 1 drop of RS; GIV, Epiphany associated with self-etch primer, prepared with 1 drop of RS and photoactivated. The filled tubes were implanted into 4 different regions of the dorsum of 20 adult male rats. Results: After 7, 14 and 21 days, all groups presented a moderate to severe chronic inflammation, necrosis and foreign-body giant cells. At 42 days, although the intensity of chronic inflammatory reaction decreased, the other features still were observed. Conclusion: The Epiphany sealer prepared with the RS was irritating to rat subcutaneous tissues.

Variability of physicochemical properties of an epoxy resin sealer taken from different parts of the same tube

Baldi JV, Bernardes RA, Duarte MAH, Ordinola-Zapata R, Cavenago BC, Moraes JCS, de Moraes IG. Variability of physicochemical properties of an epoxy resin sealer taken from different parts of the same tube. International Endodontic Journal,similar to 45, 915920, 2012. Abstract Aim To analyse several physicochemical properties of AH Plus (Dentsply DeTrey, Konstanz, Germany), including setting time, flow, radiopacity and the degree of conversion (DC); and to correlate the results with the source of the material: from the beginning, middle or end of the tubes in which they were supplied. Methodology Three experimental groups were established for each property investigated. Group 1 corresponded to material taken from the beginning of tubes A and B; Group 2 corresponded to material taken from the middle of each tube; and group 3 corresponded to that from the end of each tube. The setting time, flow and radiopacity were studied according to American National Standards Institute/American Dental Association (ANSI/ADA) Specification 57. DC was determined from infrared spectra, which were recorded at 1-h intervals for the first 6 h; then, at 2-h intervals for the next 14 h; then, at 24 and 30 h. Data were analysed statistically by analysis of variance (anova), TukeyKramer, KruskalWallis and Dunn tests, with a significance level of 5%. Results Group 1 had a significantly longer setting time (2303 +/- 1058 min) (P < 0.05). Group 3 had the lowest flowability (30.0 +/- 0.7 mm) and the highest radiopacity (14.85 +/- 1.8 mm Al) (P < 0.05). No differences were found for the DC test (P > 0.05). Conclusion The results suggest that segregation occurs between the organic and inorganic components of AH Plus sealer, thereby changing the setting time, flow and radiopacity.

Evaluation of epoxy resin sealer after three root canal filling techniques by confocal laser scanning microscopy

The aim of this study was to evaluate the penetration of endodontic sealer into the dentin tubules, the integrity of the sealer layer perimeter, and the sealer area at the apical third after different filling techniques by confocal laser scanning microscopy (CLSM). Forty-five mandibular premolars were mechanically prepared with ProTaper files, until F5 file. Thereafter, they were filled with an epoxy-resin sealer (AH Plus) mixed with Rhodamine B dye (0.1% proportion) and allocated in three groups: Group 1, single master cone; Group 2, cold lateral compaction; and Group 3, Thermafil. For confocal laser scanning microscopy analysis, the specimens were transversely sectioned at 4 mm from the apex. The images at x10 and x40 were analyzed by Imagetool 3.0 software. Significant differences were not found among the three experimental groups according the dentin-impregnate area by the sealer (P = 0.68) and between the sealer and root canal perimeter (P = 0.18). However, root canal filling techniques were significantly different when apical sealer areas were compared (P = 0.001). Thermafil group showed smaller sealer areas (8.09%) while cold lateral compaction and gutta-percha master cone showed similar areas (17.37 and 21.18%, respectively). The dentin-impregnated area was not dependent on the root canal filling technique. Single master cone, cold lateral condensation and Thermafil techniques presented integrity of the sealer perimeter close to 100% and Thermafil resulted in a significantly thinner sealer layer. Microsc. Res. Tech. 75:12771280, 2012. (C) 2012 Wiley Periodicals, Inc.

Six-month evaluation of a resin/dentin interface created by methacrylate and silorane-based materials

Objectives: This study aimed to compare the micro-tensile bond strength of methacrylate resin systems to a silorane-based restorative system on dentin after 24 hours and six months water storage. Material and Methods: The restorative systems Adper Single Bond 2/Filtek Z350 (ASB), Clearfil SE Bond/Z350 (CF), Adper SE Plus/Z350 (ASEP) and P90 Adhesive System/Filtek P90 (P90) were applied on flat dentin surfaces of 20 third molars (n=5). The restored teeth were sectioned perpendicularly to the bonding interface to obtain sticks (0.8 mm2) to be tested after 24 hours (24 h) and 6 months (6 m) of water storage, in a universal testing machine at 0.5 mm/min. The data was analyzed via two-way Analysis of Variance/Bonferroni post hoc tests at 5% global significance. Results: Overall outcomes did not indicate a statistical difference for the resin systems (p=0.26) nor time (p=0.62). No interaction between material × time was detected (p=0.28). Mean standard-deviation in MPa at 24 h and 6 m were: ASB 31.38 (4.53) and 30.06 (1.95), CF 34.26 (3.47) and 32.75 (4.18), ASEP 29.54 (4.14) and 33.47 (2.47), P90 30.27 (2.03) and 31.34 (2.19). Conclusions: The silorane-based system showed a similar performance to methacrylate-based materials on dentin. All systems were stable in terms of bond strength up to 6 month of water storage.

Effect Of Daily Use Of An Enzymatic Denture Cleanser On Candida Albicans Biofilms Formed On Polyamide And Poly(methyl Methacrylate) Resins: An In Vitro Study.

Candida biofilms on denture surfaces are substantially reduced after a single immersion in denture cleanser. However, whether this effect is maintained when dentures are immersed in cleanser daily is unclear. The purpose of this study was to evaluate the effect of the daily use of enzymatic cleanser on Candida albicans biofilms on denture base materials. The surfaces of polyamide and poly(methyl methacrylate) resin specimens (n=54) were standardized and divided into 12 groups (n=9 per group), according to study factors (material type, treatment type, and periods of treatment). Candida albicans biofilms were allowed to form over 72 hours, after which the specimens were treated with enzymatic cleanser once daily for 1, 4, or 7 days. Thereafter, residual biofilm was ultrasonically removed and analyzed for viable cells (colony forming units/mm(2)) and enzymatic activity (phospholipase, aspartyl-protease, and hemolysin). Factors that interfered with the response variables were analyzed by 3-way ANOVA with the Holm-Sidak multiple comparison method (α=.05). Polyamide resin presented more viable cells of Candida albicans (P<.001) for both the evaluated treatment types and periods. Although enzymatic cleansing significantly (P<.001) reduced viable cells, daily use did not maintain this reduction (P<.001). Phospholipase activity significantly increased with time (P<.001) for both materials and treatments. However, poly(methyl methacrylate) based resin (P<.001) and enzymatic cleansing treatment (P<.001) contributed to lower phospholipase activity. Aspartyl-protease and hemolysin activities were not influenced by study factors (P>.05). Although daily use of an enzymatic cleanser reduced the number of viable cells and phospholipase activity, this treatment was not effective against residual biofilm over time.

Setting Time Affects In Vitro Biological Properties of Root Canal Sealers

Introduction: Biocompatibility of root canal sealers is important because of the long-term contact of their eluates and/or degradation products with periapical tissues. The literature still lacks studies about the genotoxic effects of these materials and the influence of setting time on biological properties. The cytotoxicity and genotoxicity of an epoxy resin-based sealer (AH Plus), a single methacrylate-based sealer (EndoRez), and a silicone-based sealer (RoekoSeal) were assessed. Methods: Chinese hamster fibroblasts (V79) were cultured and exposed to different dilutions of extracts from the sealers that were left to set for 0, 12, and 24 hours before contact with culture medium. Cell viability was measured by the methyl-thiazol-diphenyltetrazolium assay. Genotoxicity was assessed by the comet assay. Data were statistically analyzed by Kruskal-Wallis and Dunn tests (P < .05). Results: Root canal sealers were statistically more cytotoxic than the untreated control group, except for the silicon-based sealer. Cell viability ranking was the following (from the most to the least cytotoxic): methacrylate-based > epoxy resin-based > silicone-based. The setting time influenced the epoxy resin-based sealer cytotoxicity (decreased at 12 hours) and the general genotoxicity (increased at 24 hours). DNA damage ranking was the following (from the most to the least genotoxic): methacrylate-based > silicone-based = epoxy resin-based. Conclusions: The setting time had influence on the cytotoxicity of the epoxy resin-based sealer and genotoxicity of all tested sealers. The methacrylate-based sealer was the most cytotoxic, and the silicone-based sealer was not cytotoxic. Genotoxicity was observed for all sealers. © 2013 American Association of Endodontists.

Análise da termoplasticidade e adesividade da guta-percha e resilon

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Infiltração coronária microbiana em canais radiculares obturados pela técnica do cone único com diferentes cimentos endodônticos

With the emergence of new filling materials with different properties and behaviors, the approach of endodontic treatment must be readjusted so that the appropriate result can be achieved. New endodontic sealers include methacrylate resin-based, plant resin-based and the evolution of epoxy-based sealers. This study verified the behavior of new materials that presents controversial results in the literature, about coronal bacterial leakage. That for, 56 single-rooted human teeth were prepared in the direction crown-apex and filled with gutta-percha points with taper of 4% using the single cone technique. Roots were divided randomly into 4 groups according to the sealer (Apexit Plus, AH Plus, EndoREZ and Polifil). After filling, the roots were incorporated in a leakage model, which upper chamber contained a suspension of Streptococcus mutans, and lower chamber a broth, leaving 3 mm of root apical portion immersed. Leakage was assessed for turbidity in lower chamber every day for 60 days. Survival analysis was performed using the nonparametric Kaplan- Meier method (p<0,05). All experimental groups presented leakage during the study’s period, however the maximum time achieve was 22 days. The medium time of leakage was: Apexit Plus 6,3 days, AH Plus 6,3 days and Polifil 5,1 days, but in EndoREZ all specimens infiltrated in the first day, presenting shorter capacity of impermeabilization compared to the other groups. Concluding that none of the sealers tested was able to prevent coronal bacterial leakage

Effects of age condition on the distribution and integrity of inorganic fillers in dental resin composites

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Analysis of four gutta-percha techniques used to fill mesial root canals of mandibular molars

P>Aim To compare the percentage of gutta-percha, sealer and voids and the influence of isthmuses in mesial root canals of mandibular molars filled with different techniques. Methodology Canals in 60 mesial roots of mandibular first molars were prepared with ProTaper instruments to size F2 (size 25, 0.08 taper) and filled using a single-cone, lateral compaction, System B or Thermafil techniques. An epoxy resin sealer was labelled with Rhodamine-B dye to allow analysis under a confocal microscope. The percentage of gutta-percha, sealer and area of voids was calculated at 2, 4 and 6 mm from the apex, using Image Tool 3.0 software. Statistical analysis was performed using nonparametric Kruskal-Wallis and Dunn tests (P < 0.05). The influence of isthmuses on the presence or absence of voids was evaluated using the Fisher test. Results At the 2 mm level, the percentage of gutta-percha, sealer and voids was similar amongst the System B, lateral compaction and single-cone techniques. The single-cone technique revealed significantly less gutta-percha, more sealer and voids in comparison with the Thermafil technique at the 2 and 4 mm level (P < 0.05). The analysis of all sections (2, 4 and 6 mm) revealed that more gutta-percha and less sealer and voids were found in root canals filled with Thermafil and System B techniques (P < 0.05). The Fisher test revealed that the presence of isthmuses increased the occurence of voids in the lateral compaction group only (P < 0.05). Conclusion Gutta-percha, sealer filled area and voids were dependent on the canal-filling technique. The presence of isthmuses may influence the quality of root filling.