Effect of Fe impurity on the optical loss of Nd-doped phosphate laser glass

The optical loss coefficient at 1053-nm wavelength, influenced by Fe ions in N31-type Nd-doped phosphate laser glass, was determined precisely and analyzed in detail. It is found that the optical loss coefficient per unit of Fe concentration (cm^(-1)/ppmw) increases with Fe concentration in the range of 0---300 ppmw, but it approaches a constant as the Fe concentration is larger than 300 ppmw. Such a concentration effect is due to a shift in the redox equilibrium between Fe3+ and Fe2+ ions in the glass. The effect of oxygen pressure, temperature, and variable valence states of other metal ions in glass samples on the optical loss is also discussed.

Er3+ and Yb3+ codoped phosphate laser glass for high power flashlamp pumping

A novel Vb(3+)-Er-(3+) codoped phosphate glass for high power flashlamp pumping and high repetition rate laser at 1.54 mu m, designated EAT5-2, is developed. The weight-loss rate of is 1.3 x 10(-5) gcm(-2) h(-1) in boiling water, which is comparable to Kigre's QX-Er glass. Some spectroscopic parameters are analysed by Judd-Ofelt theory and McCumber theory The emission cross section is calculated to be 0.73 x 10(-20) cm(2). The thermo-mechanical properties of EAT5-2 are modified after an ion-exchange chemical strengthening process in a KNO3/NaNO3 molten salt bath. The thresholds for optical damage from the flashlamp pumping are tested on glass rods. A repetition rate of 15 Hz is achieved for chemically strengthened glass. The laser experimental results at. 1.54 mu m from flashlamp pumping are also reported.

High Er3+ concentration low refractive index fluorophosphate glass for evanescent wave optical amplifiers

This is about the first reported laser glass with very low no, high Er3+ concentration and no quenching. In this work, a series of high Er3+ concentration (10.6-12.2 x 10(20) ions/cm(3)), low refractive index (n(1550) < 1.47) and relatively high fluorescence lifetime (6.8-12.6 ms) fluorophosphate glasses were made. A cw-pumping evanescent wave optical amplifier experiment was performed with it, and a relative gain of around 2dB at 1550 nm wavelength was achieved while the noise level was almost unchanged. To our knowledge, this is the first successful relative gain in evanescent wave optical amplifiers (EWOA) demonstrated with cw pumping. It is a valuable study of specially designed fluorophosphate glass suitable for EWOA communication experiment. (C) 2008 Elsevier B.V. All rights reserved.

1.5 GHz picosecond pulse generation from a monolithic waveguide laser with a graphene-film saturable output coupler

We fabricate a saturable absorber mirror by coating a graphenefilm on an output coupler mirror. This is then used to obtain Q-switched mode-locking from a diode-pumped linear cavity channel waveguide laser inscribed in Ytterbium-doped Bismuthate Glass. The laser produces 1.06 ps pulses at ∼1039 nm, with a 1.5 GHz repetition rate, 48% slope efficiency and 202 mW average output power. This performance is due to the combination of the graphene saturable absorber and the high quality optical waveguides in the laser glass. © 2013 Optical Society of America.

Comparative Histopathological Analysis of Human Pulps after Class I Cavity Preparation with a High-Speed Air-Turbine Handpiece or Er:YAG Laser

The purpose of this study was to comparatively evaluate the response of human pulps after cavity preparation with different devices. Deep class I cavities were prepared in sound mandibular premolars using either a high-speed air-turbine handpiece (Group 1) or an Er: YAG laser (Group 2). Following total acid etching and the application of an adhesive system, all cavities were restored with composite resin. Fifteen days after the clinical procedure, the teeth were extracted and processed for analysis under optical microscopy. In Group 1 in which the average for the remaining dentin thickness (RDT) between the cavity floor and the coronal pulp was 909.5 mu m, a discrete inflammatory response occurred in only one specimen with an RDT of 214 mu m. However, tissue disorganization occurred in most specimens. In Group 2 (average RDT = 935.2 mu m), the discrete inflammatory pulp response was observed in only one specimen (average RDT = 413 mu m). It may be concluded that the high-speed air-turbine handpiece caused greater structural alterations in the pulp, although without inducing inflammatory processes.

Plasma assisted femtosecond laser inscription in dielectrics

Principles of the femtosecond fabrication of the optoelectronic components in glass are explained and illustrated by examples of the in-bulk writing. The results of the experimental investigation of the dependence of the induced index change on the pulse energy and the numerical modelling of the corresponding laser-glass interaction are presented. The distribution of the plasma density is simulated that may bridge the gap between the models of the pulse propagation and the induced permanent refractive index change. © 2006 American Institute of Physics.

Multiphoton-excited upconversion luminescence of Nd : YVO4

Fluorescence spectra of Nd: YVO4 under excitation of a continuous wave (CW) diode laser and a femtosecond laser at 800nm were investigated. It was found that Nd: YVO4 shows different upconversion and downconversion luminescencent behaviors when excited by the diode laser and the femtosecond laser. The dependence of the upconversion luminescence intensity on the pump power of the femtosecond laser was discussed. The populations of the upper energy levels for upconversion and downconversion luminescence were calculated based on the Bloch equations. The calculations agree well with the experimental results. (c) 2007 Optical Society of America.

磷酸盐激光玻璃聚（CH3）2Si（OC2H5）2防潮膜

以（CH3）2Si（OC2H5）2为前驱体，采用溶胶-凝胶与有机合成相结合的方法，制得稳定性良好的涂膜液。采用旋转涂膜法在掺钕磷酸盐激光玻璃棒端面涂制防潮膜，膜层固化后透过率达96．5％，获得的膜层表面粗糙度优良，均方根表面粗糙度（RMS）为1．659nm，平均粗糙度（RA）平均为1．321nm；在激光波长1053nm，脉冲宽度1 ns条件下膜层的激光破坏闽值可达10～14 J／cm^2。经过“神光Ⅱ”高功率激光器物理实验运行，膜层使用期为五年，并且已经在我国“神光Ⅲ”原型装置上试用。

磷酸盐激光玻璃的化学机械抛光

从磷酸盐激光玻璃的成分和结构出发,分析了其化学机械抛光(CMP)机制。通过实验验证了磷酸盐激光玻璃对抛光液pH值具有较强的选择性,在微酸性和中性条件下磷酸盐激光玻璃具有较高的抛光效率,在抛光液中添加pH值调节添加剂会保持抛光环境的酸碱性从而影响抛光效率和抛光质量。通过对pH值和抛光剂浓度的控制获得了均方根(RMS)优于0.6 nm的磷酸盐激光玻璃的超光滑表面。

固着磨料加工工艺对磷酸盐钕玻璃亚表面缺陷的影响

散粒磨料研磨与固着磨料研磨是光学研磨加工过程中的两种主要手段,但两者材料去除的机制不同。目前针对高功率固体激光装置中的主要工作物质——磷酸盐激光钕玻璃的亚表面缺陷(SSD)研究相对较少,因此在实验的基础上,通过系统地研究固着磨料对磷酸盐激光钕玻璃的研磨工艺过程,分析了多种因素,如磨料粒径、载荷大小、机床转速,以及结合剂材料与冷却液等对钕玻璃亚表面缺陷形成的影响,并与散粒磨料研磨工艺所产生的亚表面缺陷进行了比较,对关键工艺参数进行定量,为高质量钕玻璃制造工艺的选型以及进一步优化亚表面缺陷提供了重要的参考数据。

磷酸盐钕玻璃表面/亚表面损伤特性实验研究

系统地研究了光学研磨过程中,磨料粒径、载荷大小以及机床转速对钕玻璃表面及亚表面损伤的影响。结果表明,机床转速和载荷基本不改变材料表面粗糙度,而较大载荷或较低机床转速产生较大的亚表面缺陷,表面粗糙度和亚表面缺陷缺陷深度基本与最大磨料粒径呈正比,载荷增倍使亚表面缺陷与表面粗糙度的常数比值增加0.05。研究结果为钕玻璃加工工艺改进提供了参考依据。

侧面抽运板条激光介质动态热畸变测量方法

研究了基于干涉测量激光介质热畸变的原理,利用CCD摄像机记录干涉条纹并通过计算机图像处理,来测量板条激光介质动态热畸变的方法。对采集得到的干涉条纹进行图像处理,提出了一种简单快速提取条纹中心的算法。通过分析、计算干涉条纹的移动,得到抽运过程中板条激光介质的动态热畸变情况,为动态补偿激光介质热效应提供了可能。实验采用了N31磷酸盐激光玻璃作样品,得到了加热过程中激光玻璃内部的温度分布,误差约为3%,验证了该测量方法的可行性。

氟磷酸盐玻璃的应用研究进展

氟磷酸盐玻璃系统南于其特殊的光学性能和优良的机做与热学性能一直是特种光学玻璃材料领域的一个研究热点。总结了氟磷酸盐玻璃的分类及玻璃组分与其结构的关系，综述了氟磷玻璃在光学器件、高能高功率激光玻璃、光纤激光器、光纤放大器及上转换发光基质材料等领域上的应用，并对其未来的发展进行了展望。