Anodic-oxide-induced interdiffusion in GaAs/AlGaAs quantum wells

Enhancement of interdiffusion in GaAs/AlGaAs quantum wells due to anodic oxides was studied. Photoluminescence, transmission electron microscopy, and quantum well modeling were used to understand the effects of intermixing on the quantum well shape. Residual water in the oxide was found to increase the intermixing, though it was not the prime cause for intermixing. Injection of defects such as group III vacancies or interstitials was considered to be a driving force for the intermixing. Different current densities used in the experimental range to create anodic oxides had little effect on the intermixing. ©1998 American Institute of Physics.

Interdiffusion at Sb/Ge interfaces induced in thin multilayer films by nanosecond laser irradiation

Thin films consisting of 3 or 4 Sb and Ge alternating layers are irradiated with single nanosecond laser pulses (12 ns, 193 nm). Real time reflectivity (RTR) measurements are performed during irradiation, and Rutherford backscattering spectrometry (RBS) is used to obtain the concentration depth profiles before and after irradiation. Interdiffusion of the elements takes place at the layer interfaces within the liquid phase. The reflectivity transients allow to determine the laser energy thresholds both to induce and to saturate the process being both thresholds dependent on the multilayer configuration. It is found that the energy threshold to initiate the process is lower when Sb is at the surface while the saturation is reached at lower energy densities in those configurations with thinner layers.

Strain relaxation and stress-driven interdiffusion in InAsInGaAsInP nanowires

The authors have investigated strain relaxation in InAsInGaAsInP nanowires (NW's). Transmission electron microscopy images show an additional stress field attributed to compositional modulation in the ternary layer, which disrupts NW formation and drives Ga interdiffusion into InAs, according to grazing incidence x-Ray diffraction under anomalous scattering conditions. The strain profile along the NW, however, is not significantly affected when interdiffusion is considered. Results show that the InAs NW energetic stability is preserved with the introduction of ternary buffer layer in the structure. © 2007 American Institute of Physics.

Evaluation of three different adhesive systems using a bacterial method to develop secondary caries in vitro

Purpose: To assess the effects of three different dental adhesive systems on the formation of secondary root caries, in vitro, with a standardized interfacial gap in a filled cavity model. Methods: 40 sound human molars were selected and randomly assigned to four experimental groups: Clearfil SE Bond (CSEB), Xeno III (X-III), Scotchbond Multi-Purpose Plus (SBMP) and negative control (NC) without an adhesive system. After the standardized Class V cavity preparations on the buccal and lingual surfaces, restorations were placed with resin composite (Filtek Z250) using a standardized interfacial gap, using a 3 x 2 mm piece of 50 mu m metal matrix. The teeth were sterilized with gamma irradiation and exposed to a cariogenic challenge using a bacterial system with Streptococcus mutans. Depth and extension of wall lesions formed and the depth of outer lesions were measured by software coupled with light microscopy. Results: For wall lesion extension the ANOVA test showed differences between groups except between X-HI and SBMP (P= 0.294). The Tukey`s test of confidence intervals indicated smaller values for the CSEB group than for the others. For wall lesion depth the CSEB group also presented the smallest mean values of wall lesion depth when compared to the others (P< 0.0001) for all comparisons using Tukey`s test. Regarding outer lesion depth, all adhesives showed statistically similar behavior. SEM evaluation of the morphologic appearance of caries lesions confirmed the statistical results showing small caries lesion development for cavities restored with CSEB adhesive system, which may suggest that this adhesive system interdiffusion zone promoted a good interaction with subjacent dentin protecting the dental tissues from recurrent caries. (Am J Dent 2010;23:93-97).

Stability of wet versus dry bonding with different solvent-based adhesives

Objective. To evaluate the effects of surface moisture (wet or dry) and storage (24h or 3 months) on the microtensile bond strength (BS) of resin/dentin bonds mediated by two water/ethanol based adhesives Single Bond, 3M-ESPE, (SB) and Opti Bond Solo Plus, Kerr, (OB), and two acetone-based adhesives, One Step, Bisco, (OS) and Prime&Bond NT, Caulk/Dentsply, (PB). Materials and methods. Flat dentin surfaces were polished with 600-grit SiC paper, etched with 35% phosphoric acid for 15 s and rinsed for 20 s. Half the surface was maintained moist and the other half was air-dried for 30 s. Each adhesive was applied simultaneously to both halves, left undisturbed for 30 s and light-cured. Four-mm resin build-ups were constructed incrementally. After storage in water at 37 degrees C for 24h, slabs were produced by transversal sectioning and trimmed to an hourglass shape (0.8 mm 2). Half of the specimens were tested in tension at 0.6 mm/min immediately after trimming and the other half after 3 months of water storage. Data were analyzed by two-way ANOVA and SNK for each material. Results. Both moisture and storage affected BS to dentin, and was material- dependent. Dry, bonding affected mostly the acetone-based adhesives. Larger reductions in bond strength were associated with dry bonding after 3 months of water storage. Significance. Wet bonding resulted in more stable bonds over 3 months of water storage for most of the materials tested. (C) 2007 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Perpendicular magnetic anisotropy in chemically disordered FePd-FeV(100) alloy thin films

We find that the use of V(100) buffer layers on MgO(001) substrates for the epitaxy of FePd binary alloys yields to the formation at intermediate and high deposition temperatures of a FePd¿FeV mixed phase due to strong V diffusion accompanied by a loss of layer continuity and strong increase of its mosaic spread. Contrary to what is usually found in this kind of systems, these mixed phase structures exhibit perpendicular magnetic anisotropy (PMA) which is not correlated with the presence of chemical order, almost totally absent in all the fabricated structures, even at deposition temperatures where it is usually obtained with other buffer layers. Thus the observed PMA can be ascribed to the V interdiffusion and the formation of a FeV alloy, being the global sample saturation magnetization also reduced.

Surface studies of some metallic thin films by optical methods

The thesis aims to present the results of experimental investigations on the changes of optical properties of metallic thin films due to heating. The parameters which are measured are reflectivity, refractive indices and the ellipsometric quantities V and A . The materials used in the studies are metals like Silver, Aluminium and Copper. By applying the optical method the interdiffusion taking place in multilayer ‘films of Aluminium and Silver has also been studied. Special interest has been taken to reveal the mechanisms of the hillock growth and surface roughness caused by heating and their relation with the stress in the film

Thermoset matrix reinforced with sisal fibers: Effect of the cure cycle on the properties of the biobased composite

Thermoset phenolic composites reinforced with sisal fibers were prepared to optimize the cure step. In the present study, processing parameters such as pressure, temperature, and time interval were varied to control the vaporization of the water generated as a byproduct during the crosslinking reaction. These molecules can vaporize forming voids, which in turn affect the final material properties. The set of results on impact strength revealed that the application of higher pressure before the gel point of the phenolic matrix produced composites with better properties. The SEM images showed that the cure cycle corresponding to the application of higher values of molding pressure at the gel point of the phenolic resin led to the reduction of voids in the matrix. In addition, the increase in the molding pressure during the cure step increased the resin interdiffusion. Better filling of the fiber channels decreased the possibility of water molecules diffusing through the internal spaces of the fibers. These molecules then diffused mainly through the bulk of the thermoset matrix, which led to a decrease in the water diffusion coefficient (D) at all three temperatures (25, 55 and 70 degrees C) considered in the experiments. (C) 2009 Elsevier Ltd. All rights reserved.

The influence of temperature of three adhesive systems on bonding to ground enamel

This study evaluated the microtensile bond strength test (mu T), micromorphology of resin-enamel interface (RET) and etching patterns (EP) promoted by the etch-and-rinse adhesive, Prime&Bond NT (PB), and two self-etching adhesives, Clearfil SE Bond (SE) and Adper Prompt L-Pop (APR), to ground bovine enamel surfaces' when applied at temperatures of 5 degrees C (C), 40 degrees C (H) and 20 degrees C (R). Materials and Methods. Sixty-three bovine incisors were randomly divided into nine experimental groups (n=7) according to adhesive systems and temperatures. The buccal enamel surfaces were flattened with 600-grit SiC paper and abraded with a diamond bur under water-cooling. The adhesive systems were applied according to the manufacturer's instructions. After the restorative procedures, the specimens were sectioned into five slabs. Four slabs were prepared for mu T and one for interface analysis. For etching pattern analysis, the remaining 16 bovine enamel fragments were used (n=2). The adhesives were applied and the surfaces were rinsed with organic solvents after application. The specimens for RET and EP analysis were prepared for SEM analysis. Results. No significant differences among the adhesives were found at R temperature. However, at 5 degrees C, PB and APR presented lower bond strength than SE. At H temperature, higher bond strength was observed for PB than for APR and SE. At C and H temperature, formation of the interdiffusion zone was impaired and the treated enamel surfaces presented an undefined EP.

Photo-induced transformations in chalcogenide nanocomposite layers

Investigations of photo-induced structural transformations (PST) and related changes of optical parameters in amorphous chalcogenide layers were further developed towards the establishment of their dependence on the compositional modulation of the material at nanoscale-dimensions (similar to3-10 nm) and possible improvement of optical recording parameters as well. Besides the known amorphous-amorphous PST, photo-stimulated interdiffusion and crystallization in multilayer structures were found as a useful method for amplitude-phase optical relief formation. The last two types of PST were influenced by size restrictions and efficiently operated by the composition and by the modulation period of the layered nanocomposite. Experimental evidences were obtained in Se-, AsSe-, Se0.4Te0.6-containing layered or quasi zero-dimensional structures based on As2S3 or SiOx and MgF2 matrix. Comparison was made with As2S3- and GeS2-based multicomponent layers, containing Se, Te and Ga. (C) 2004 Elsevier B.V. All rights reserved.

Optical recording in Se(Te)/As2S3 multilayers

The development of Te containing nanoscaled, compositionally modulated Te/As2S3 multilayer structures enables the realisation of optical recording in real time with a CW He-Ne laser illumination (lambda=633 nm) with improved recording parameters in comparison with known Se/As2S3 structures. It is established that the efficiency of the recording process depends on the light stimulated interdiffusion and thickness of sub-layers.

Photo-induced transformations in chalcogenide composite layers

Investigations of photo-induced structural transformations (PST) and related changes of optical parameters in the light-sensitive amorphous chalcogenides were extended to composite layers, which consist of a wide band-gap material and an active material, Se60Te40 with a smaller band gap. Photo-stimulated interdiffusion and/or crystallization in layered Se0.6Tc0.4/As0.6Se0.94 and Se0.6Te0.4/SiOx were investigated with respect to their dependence on the compositional modulation of the multilayer at scale-dimensions (similar to3-10nm). It was established that PST due to the interdiffusion and crystallization can be efficiently operated by the composition of the adjacent layers of the multilayer which results in the change of the transformation rate and of the optical relief type (positive or negative). The comparison with a single Se0.6Te0.4 layer and with the known data for amorphous-Se/As2S3 multilayers supports the advantages of composite layers for amplitude-phase optical recording. (C) 2004 Published by Elsevier B.V.

Preparation, microstructural and electrical characterization of SrTiO3 thin films prepared by chemical route

Polycrystalline SrTiO3 thin films having a cubic perovskite structure were prepared at different temperatures by the polymeric precursor method on platinum-coated silicon substrate. Crystalline films with uniform composition and thickness were prepared by spin-coating and the post-deposition heat treatment was carried out at different temperatures. The film showed good structural, dielectric, and insulating properties, Scanning electron microscopy (SEM) micrographs showed no occurrence of interdiffusion between the bottom electrode (platinum) and the film during post-annealing, indicating a stable interface between the SrTiO3 and the bottom electrode. The dielectric constant and dissipation factor at a frequency of 100 kHz were 250 and 0.01, respectively, for a 360 nm thick film annealed at 600 degreesC. The capacitance versus applied voltage characteristics showed that the capacitance was almost independent of the applied voltage. The I-V characteristics were ohmic in low fields and a Schottky emission and/or Poole-Frenkel emission were postulated in high fields. Room temperature leakage current density was found to be in the order of 10(-7) A/cm(2) for a 360 nm thick film in an applied electric field of about 100 kV/cm. The charge storage density of 36 fC/mum(2) was obtained in an applied electric field of about 100 kV/cm. (C) 2001 Published by Elsevier B.V. Ltd. All rights reserved.

Tensile bond strength of self-etching versus total-etching adhesive systems under different dentinal substrate conditions

The use of acid etchants to produce surface demineralization and collagen network exposure, allowing adhesive monomers interdiffusion and consequently the formation of a hybrid layer, has been considered the most efficient mechanism of dentin bonding. The aim of this study was to compare the tensile bond strength to dentin of three adhesive systems, two self-etching ones (Clearfil SE Bond - CSEB and One Up Bond F - OUBF) and one total-etching one (Single Bond - SB), under three dentinal substrate conditions (wet, dry and re-wet). Ninety human, freshly extracted third molars were sectioned at the occlusal surface to remove enamel and to form a flat dentin wall. The specimens were restored with composite resin (Filtek Z250) and submitted to tensile bond strength testing (TBS) in an MTS 810. The data were submitted to two-way ANOVA and Tukey's test (p = 0.05). Wet dentin presented the highest TBS values for SB and CSEB. Dry dentin and re-wet produced significantly lower TBS values when using SB. OUBF was not affected by the different conditions of the dentin substrate, producing similar TBS values regardless of the surface pretreatments.