The effect of synthesis temperature on the formation of hydrotalcites in Bayer liquor : a vibrational spectroscopic analysis

The seawater neutralisation process is currently used in the Alumina industry to reduce the pH and dissolved metal concentrations in bauxite refinery residues, through the precipitation of Mg, Al, and Ca hydroxide and carbonate minerals. This neutralisation method is very similar to the co-precipitation method used to synthesise hydrotalcite (Mg6Al2(OH)16CO3•4H2O). This study looks at the effect of temperature on the type of precipitates that form from the seawater neutralisation process of Bayer liquor. The Bayer precipitates have been characterised by a variety of techniques, including X-ray diffraction, Raman spectroscopy and infrared spectroscopy. The mineralogical composition of Bayer precipitates largely includes hydrotalcite, hydromagnesite, and calcium carbonate species. XRD determined that Bayer hydrotalcites that are synthesised at 55 °C have a larger interlayer distance, indicating more anions are removed from Bayer liquor. Vibrational spectroscopic techniques have identified an increase in hydrogen bond strength for precipitates formed at 55 °C, suggesting the formation of a more stable Bayer hydrotalcite. Raman spectroscopy identified the intercalation of sulfate and carbonate anions into Bayer hydrotalcites using these synthesis conditions.

Thermal decomposition of Bayer precipitates formed at varying temperatures

Bayer hydrotalcites prepared using the seawater neutralisation (SWN) process of Bayer liquors are characterised using X-ray diffraction and thermal analysis techniques. The Bayer hydrotalcites are synthesised at four different temperatures (0, 25, 55, 75 °C) to determine the effect on the thermal stability of the hydrotalcite structure, and to identify other precipitates that form at these temperatures. The interlayer distance increased with increasing synthesis temperature, up to 55 °C, and then decreased by 0.14 Å for Bayer hydrotalcites prepared at 75 °C. The three mineralogical phases identified in this investigation are; 1) Bayer hydrotalcite, 2), calcium carbonate species, and 3) hydromagnesite. The DTG curve can be separated into four decomposition steps; 1) the removal of adsorbed water and free interlayer water in hydrotalcite (30 – 230 °C), 2) the dehydroxylation of hydrotalcite and the decarbonation of hydrotalcite (250 – 400 °C), 3) the decarbonation of hydromagnesite (400 – 550 °C), and 4) the decarbonation of aragonite (550 – 650 °C).

Settling behaviours of low alumina/caustic ratios during seawater neutralisation of Bayer liquor

Factors that affect the settleability of seawater neutralised bauxite refinery residues are poorly understood, in particular, the settleability of precipitates in the absence of red mud and those formed with different alumina/caustic (AC) ratios. The influence of temperature, AC ratio, caustic concentration and the volumetric ratio of seawater on the settleability of seawater neutralisation precipitates and their respective compositions and stabilities have been determined. An array of techniques have been used to determine the composition and stability of precipitates and include pH, conductivity, inductively coupled plasma optical emission spectroscopy, infrared spectroscopy and X-ray diffraction. Temperature has been shown to have a significant influence on the settleability and calcium carbonate phase distributions in precipitates, as well as the overall stability of the precipitates. More complex phase compositions have also been found for Bayer liquors with lower AC ratios. The caustic concentration and temperature of the reaction have the greatest influence on the settling efficiency of the precipitates. Assessments on the chemical stability of the precipitates, precipitate settleability and discharge water quality have been made. In addition, productivity and environmental impacts caused by changes in precipitate settleability have also been considered.

Determination of sodium oxalate in Bayer liquor using flow-analysis incorporating an anion exchange column and tris(2,2`-bipyridyl)ruthenium(II) chemiluminescence detection

Semi-automated flow injection instrumentation, incorporating a small anion exchange column coupled with tris(2,2′-bipyridyl)ruthenium(II) (Ru(bipy)₃²⁺) chemiluminescence detection, was configured and utilised to develop rapid methodology for the determination of sodium oxalate in Bayer liquors. The elimination of both negative and positive interferences from aluminium(III) and, as yet, unknown concomitant organic species, respectively are discussed. The robustness of the methodology was considerably enhanced by using the temporally stable form of the chemiluminescence reagent, tris(2,2′-bipyridyl)ruthenium(III) perchlorate in dry acetonitrile. Real Bayer process samples were analysed and the results obtained compared well with those performed using standard methods within industrial laboratories.

Effect of increased temperature on erosion-corrosion under turbulent conditions in Bayer liquor

A study of the behaviour of mild steel in synthetic Bayer liquor at 25 °C and 95 °C showed that turbulent conditions had a small effect on the anodic currents at 25 °C, but caused large increases in currents at 95 °C. This may be due to the increased solubility of magnetite at the higher temperature.

The synthesis and spectroscopic characterisation of hydrotalcite formed from aluminate solutions

Raman spectroscopy has been used to characterise nine hydrotalcites prepared from aluminate and magnesium solutions (magnesium chloride and seawater). The aluminate hydrotalcites are proposed to have the following formula Mg6Al2(OH)16(CO32-).xH2O, Mg6Al2(OH)16(CO32-,SO42-).xH2O, and Mg6Al2(OH)16(SO42-).xH2O. The synthesis of these hydrotalcites using seawater results in the intercalation of sulfate anions into the hydrotalcite interlayer. The spectra have been used to assess the molecular assembly of the cations and anions in the hydrotalcite structures. The spectra have been conveniently subdivided into spectral features based upon the carbonate anion, the hydroxyl units and water units. This investigation has shown the ideal conditions to form hydrotalcite from aluminate solutions is at pH 14 using magnesium chloride. Changes in synthesis conditions resulted in the formation of impurity products aragonite, thenardite, and gypsum.

An examination of the applicability of hydrotalcite for removing oxalate anions from Bayer process solutions

Hydrotalcite and thermally activated hydrotalcites were examined for their potential as methods for the removal of oxalate anions from Bayer Process liquors. Hydrotalcite was prepared and characterised by a number of methods, including X-ray diffraction, thermogravimetric analysis, nitrogen adsorption analysis and vibrational spectroscopy. Thermally activated hydrotalcites were prepared by a low temperature method and characterised using X-ray diffraction, nitrogen adsorption analysis and vibrational spectroscopy. Oxalate intercalated hydrotalcite was prepared by two methods and analysed with X-ray diffraction and for the first time thermogravimetric analysis, Raman spectroscopy and infrared emission spectroscopy. The adsorption of oxalate anions by hydrotalcite and thermally activated hydrotalcite was tested in a range of solutions using both batch and kinetic adsorption models.

Thermal analysis of hydrotalcite synthesised from aluminate solutions

The aluminate hydrotalcites are proposed to have either of the following formulas: Mg4Al2(OH)12(CO3 2-)·xH2O or Mg4Al2(OH)12(CO3 2-, SO4 2-)·xH2O. A pure hydrotalcite phase forms when magnesium chloride and aluminate solns. are mixed at a 1:1 volumetric ratio at pH 14. The synthesis of the aluminate hydrotalcites using seawater results in the formation of an impurity phase bayerite. Two decompn. steps have been identified for the aluminate hydrotalcites: (1) removal of interlayer water (230 °C) and (2) simultaneous dehydroxylation and decarbonation (330 °C).

Stability of hydrotalcites formed from Bayer refinery environmental control processes

Bauxite refinery residues (red mud) are derived from the Bayer process by the digestion of crushed bauxite in concentrated sodium hydroxide at elevated temperatures and pressures. This slurry residue, if untreated, is unsuitable for discharge directly into the environment and is usually stored in tailing dams. The liquid portion has the potential for discharge, but requires pre-treatment before this can occur. The seawater neutralisation treatment facilitates a significant reduction in pH and dissolved metal concentrations, through the precipitation of hydrotalcite-like compounds and some other Mg, Ca, and Al hydroxide and carbonate minerals. The hydrotalcite-like compounds, precipitated during seawater neutralisation, also remove a range of transition metals, oxy-anions and other anionic species through a combination of intercalation and adsorption reactions: smaller anions are intercalated into the hydrotalcite matrix, while larger molecules are adsorbed on the particle surfaces. A phenomenon known as ‘reversion’ can occur if the seawater neutralisation process is not properly controlled. Reversion causes an increase in the pH and dissolved impurity levels of the neutralised effluent, rendering it unsuitable for discharge. It is believed that slow dissolution of components of the red mud residue and compounds formed during the neutralisation process are responsible for reversion. This investigation looked at characterising natural hydrotalcite (Mg6Al2(OH)16(CO3)∙4H2O) and ‘Bayer’ hydrotalcite (synthesised using the seawater neutralisation process) using a variety of techniques including X-ray diffraction, infrared and Raman spectroscopy, and thermogravimetric analysis. This investigation showed that Bayer hydrotalcite is comprised of a mixture of 3:1 and 4:1 hydrotalcite structures and exhibited similar chemical characteristic to the 4:1 synthetic hydrotalcite. Hydrotalcite formed from the seawater neutralisation of Bauxite refinery residues has been found not to cause reversion. Other components in red mud were investigated to determine the cause of reversion and this investigation found three components that contributed to reversion: 1) tricalcium aluminate, 2) hydrocalumite and 3) calcium hydroxide. Increasing the amount of magnesium in the neutralisation process has been found to be successful in reducing reversion.

Preventing industrial scale using bauxite refinery residues

An Australian green power (AGP) company produces energy from burning biomass from the sugar industry and recycled wood waste, however alkali in biomass is released into a recirculating stream that forms a scale as it becomes more concentrated. This investigation has shown that the addition of Bayer liquor (alumina waste residue) successfully removes scale-forming species from the recirculating stream and thus has the potential to reduce the rate of scaling. Characterisation of the scale and Bayer precipitates has been performed using X-ray diffraction (XRD), infrared spectroscopy (IR) and inductively coupled plasma optical emission spectroscopy (ICP-OES).

Raman spectroscopy of gallium based hydrotalcites of formula Mg6Ga2(CO3)(OH)16•4H2O

Insight into the unique structure of hydrotalcites has been obtained using Raman spectroscopy. Gallium containing hydrotalcites of formula Mg4Ga2(CO3)(OH)12•4H2O (2:1 Ga-HT) to Mg8Ga2(CO3)(OH)20•4H2O (4:1 Ga-HT) have been successfully synthesised and characterized by X-ray diffraction and Raman spectroscopy. The d(003) spacing varied from 7.83 Å for the 2:1 hydrotalcite to 8.15 Å for the 3:1 gallium containing hydrotalcite. Raman spectroscopy complemented with selected infrared data has been used to characterise the synthesised gallium containing hydrotalcites of formula Mg6Ga2(CO3)(OH)16•4H2O. Raman bands observed at around 1046, 1048 and 1058 cm-1 were attributed to the symmetric stretching modes of the (CO32-) units. Multiple ν3 CO32- antisymmetric stretching modes are found at around 1346, 1378, 1446, 1464 and 1494 cm-1. The splitting of this mode indicates the carbonate anion is in a perturbed state. Raman bands observed at 710 and 717 cm-1 assigned to the ν4 (CO32-) modes support the concept of multiple carbonate species in the interlayer.

Removing organic impurities from bayer process liquors

A process for treating a Bayer liquor by wet oxidn. to oxidize org. contaminants in the Bayer liquor in which the wet oxidn. process is conducted in the presence of a mixed Ce/Mn oxide. The catalyst may have nano-sized grains, and be supported on a mesoporous oxide support. The catalyst may also contain a platinum group metal. [on SciFinder(R)]

Implication of calcium hydroxide in the seawater neutralisation of bauxite refinery liquors

Tricalcium aluminate, hydrocalumite and residual lime have been identified as reversion contributing compounds after the seawater neutralisation of bauxite refinery residues. The formation of these compounds during the neutralisation process is dependent on the concentration of residual lime, pH and aluminate concentrations in the residue slurry. Therefore, the effect of calcium hydroxide (CaOH2) in bauxite refinery liquors was analysed and the degree of reversion monitored. This investigation found that the dissolution of tricalcium aluminate, hydrocalumite and CaOH2 caused reversion and continued to increase the pH of the neutralised residue until a state of equilibrium was reached at a solution pH of 10.5. The dissolution mechanism for each compound has been described and used to demonstrate the implications that this has on reversion in seawater neutralised Bayer liquor. This investigation describes the limiting factors for the dissolution and formation of these trigger compounds as well as confirming the formation of Bayer hydrotalcite (mixture of Mg6Al2(OH)16(CO32-,SO42-)•xH2O and Mg8Al2(OH)12(CO32-,SO42-)•xH2O) as the primary mechanism for reducing reversion during the neutralisation process. This knowledge then allowed for a simple but effective method (addition of magnesium chloride or increased seawater to Bayer liquor ratio) to be devised to reduce reversion occurring after the neutralisation of Bayer liquors. Both methods utilise the formation of Bayer hydrotalcite to permanently (stable in neutralised residue) remove hydroxyl (OH-) and aluminate (Al(OH)4-) ions from solution.

Solution chemistry impacts on the seawater neutralisation process: Benefits of nanofiltered seawater and reverse osmosis brine

It is well known that the neutralisation of Bayer liquor with seawater causes the precipitation of stable alkaline products and a reduction in pH and dissolved metal concentrations in the effluent. However, there is limited information available on solution chemistry effects on the stability and reaction kinetics of these precipitates. This investigation shows the influence of reactive species (magnesium and calcium) in seawater on precipitate stabilities and volumetric efficiencies during the neutralisation of bauxite refinery residues. Correlations between synthetic seawater solutions and real samples of seawater (filtered seawater, nanofiltered seawater and reverse osmosis brine) have been made. These investigations have been used to confirm that alternative seawater sources can be used to increase the productivity potential of the neutralisation process with minimal implications on the composition and stability of precipitates formed. The volume efficiency of the neutralisation process using synthetic analogues has been shown to be almost directly proportional with the concentration of magnesium. This was further confirmed in the nanofiltered seawater and reverse osmosis brine that showed increases in the efficiency of neutralisation by factors of 3 and 2 compared to seawater, which corresponds with relatively the same increase in the concentration of magnesium in these alternative seawater sources. An assessment of the chemical stability of the precipitates, volumetric efficiency, and discharge water quality have been determined using numerous techniques that include pH, conductivity, inductively coupled plasma optical emission spectroscopy, infrared spectroscopy, thermogravimetric analysis coupled to mass spectrometry and X-ray diffraction. Correlations between synthetic solution compositions and alternative seawater sources have been used to determine if alternative seawater sources are potential substitutes for seawater based on improvements in productivity, implementation costs, savings to operations and environmental benefits.