Effect of drying methods on the structure and catalytic combustion activity of Mn-substituted hexaaluminate catalysts

Conventional oven drying (COD) and supercritical drying (SCD) methods were applied to the preparation of Mn-substituted hexaaluminate (BaMnA(11)O(19-alpha)) catalysts. The effect of drying methods on phase composition, specific surface area, pore structure and combustion activity of the samples was investigated. The samples obtained by SCD have higher surface area, narrower pore size distribution, and higher combustion activity than those obtained by COD.

Preparation of Mn substituted La-hexaaluminate catalysts by using supercritical drying

LaMnxAl12-xO19 catalysts were prepared from NH4OH and metal nitrates solutions. Supercritical drying (SCD) and conventional oven drying (CD) methods were used to extract the water in the hydrogel. The effects of drying methods on properties of the catalysts were investigated by means of TEM, N-2-adsorption, thermogravimetry (TG)-differential thermal analysis (DTA) and X-ray diffraction. SCD method is beneficial to maintain high surface area and improving catalytic activity for methane combustion of the catalyst. The specific surface area and pore volume of LaMn1Al11O19 catalyst prepared by SCD method are 28 m(2)/g and 0.23 cm(3)/g, respectively, and the ignition of methane could be carried out at 450degreesC. However, those of the CD catalyst prepared from the same precursor are 15 m(2)/g, 0.11 cm(3)/g and 530 degreesC, respectively. Suitable Mn content (0 less than or equal to x less than or equal to 2) could promote the formation of LaMnAl11O19 hexaaluminate, while further addition of Mn (2 less than or equal to x less than or equal to 6) cause the formation of LaMnO3. (C) 2003 Elsevier B.V All rights reserved.

Synthesis and high-pressure sintering of lanthanum magnesium hexaaluminate

Lanthanum magnesium hexaaluminate is a very important ceramic material for high temperature applications. In this paper lanthanum magnesium hexaaluminate has been synthesized directly by solid-state reaction. The forming mechanism was investigated by XRD. The SEM photographs show that the prepared powders are made of hexagonal plates. These powders can be well sintered at the high temperature (1600 degrees C) under the high pressure (4.5 GPa), and the relative density reaches 94.8%.

Laser glazing of lanthanum magnesium hexaaluminate

Lanthanum magnesium hexaalumminate (LMA) is an important candidate for thermal barrier coatings due to its thermal stability and low thermal conductivity. On the other hand, laser glazing method can potentially make thermal barrier coatings impermeable, resistant to corrosion on the surface and porous at bulk. LMA powder was synthesized at 1600 degrees C by solid-state reaction, pressed into tablet and laser glazed with a 5-kW continuous wave CO2 laser.

An Electron-Microscopic Investigation Of Oxides Related To Beta-Alumina

High resolution electron microscopic (HREM) investigation of potassiumbeta-alumina and the related gallate and ferrite has revealed that whereas the aluminate and gallate are highly disordered, consisting of random sequence ofbeta andbetaPrime units, the ferrite is more ordered. The aluminate and gallate are sensitive to electron beam irradiation exhibiting beam-induced damage similar to sodiumbetaPrime-alumina. Significantly, the ferrite is beamstable, the difference in behaviour amongst these related oxides arising from the different mechanisms by which alkali metal nonstoichiometry is accommodated. Barium hexaaluminate and hexaferrite are both highly ordered; specimens prepared by the barium borate flux method exhibit a new radic3a×radic3a superstructure of the hexagonal magnetoplumbite cell.

Barium hexaferrite (M-phase) exhibiting superstructure

Barium hexaferrite (M-phase) prepared by the flux method is found to exhibit \checkmark 3 \ut \times \checkmark 3 \ut superstructure similar to barium hexaaluminate.

Use of Composition-Graded Bi-Electrolyte Cells for Thermodynamic Studies on Lanthanum Aluminates

Innovative bi-electrolyte solid-state cells incorporating single crystal CaF2 and composition-graded solid electrolyte (LaF3) y (CaF2) 1-y (y = 0 to 0.32) were used for measurement of the standard Gibbs energy of formation of hexagonal La0.885Al11.782O19 and cubic LaAlO3 from component binary oxides La2O3 and alpha-Al2O3 in the temperature range from 875 to 1175 K. The cells were designed based on experimentally verified relevant phase relations in the systems La2O3-Al2O3LaF3 and CaF2-LaF3. The results can be summarized as: 5.891 alpha-Al2O3 + 0.4425 La2O3 (A-rare earth)-> La0.885Al11.782O19 (hex), Delta G(f(ox))(degrees)(+/- 2005)/Jmol(-1) = -80982 + 7.313(T/K); 1/2 La2O3 (A-rare earth) + 1/2 a-Al2O3 -> LaAlO3 (cubic), Delta G(f(ox))(degrees)(+/- 2100)/Jmol(-1) = -59810 + 4.51(T/K). Electron probe microanalysis was used to ascertain the non-stoichiometric range of the hexaaluminate phase. The results are critically analyzed in the light of earlier electrochemical measurements. Several imperfections in the electrochemical cells used by former investigators are identified. Data obtained in the study for LaAlO3 are consistent with calorimetric enthalpy of formation and entropy derived from heat capacity data. Estimated are the standard entropy and the standard enthalpy of formation from elements of hexagonal La0.885Al11.782O19 and rhombohedral LaAlO3 at 298.15 K. c 2014 The Electrochemical Society. All rights reserved.

Failure of the plasma-sprayed coating of lanthanum hexaluminate

Lanthanum magnesium hexaluminate (LaMgAl11O19, LMA) is an attractive material for thermal barrier coatings (TBCs), and the failure of its coating was studied in this work by thermal cycling, X-ray diffraction, dilatometric measurement and thermal gravimetric-differential thermal analysis. The dilatometric measurement indicates that even though the bulk material of LMA has a higher sintering-resistance than the typical TBC material, i.e. yttria-stabilized zirconia (YSZ), the plasma sprayed coating of LMA has two serious contractions due to the re-crystallization of LMA and phase transitions of alumina.

Sintering-resistant hollow fibers of LaMgAl11O19 prepared by electrospinning

Lanthanum magnesium hexaaluminate (LMA) is very important ceramic material for catalytic combustion of natural gas. The sintering-resistant hollow fibers of LMA with diameters ranging from 1 to 3 mu m were fabricated from alcoholic solutions containing polyvinyl pyrrolidone (PVP) and aqueous solution of lanthanum, magnesium and aluminum nitrates. The interaction between PVP and nitrates were studied by X-ray diffraction and Fourier transmission-infrared spectroscopy. The forming mechanism of hollow fibers and the sintering ability of hollow LaMgAl11O19 fibers were discussed.

Thermal-shock resistance of LnMgAl(11)O(19) (Ln = La, Nd, Sm, Gd) with magnetoplumbite structure

Lanthanide hexaaluminates including LaMgAl11O19, NdMgAl11O19, SmMgAl11O19 and GdMgAl11O19 were synthesized via Sol-Gel method. Due to the anisotropic crystal growth, these oxides crystallize in the form of platelets and the platelet thickness increases with the decrease of rare-earth ionic radius. It was observed that the thermal-shock resistances of LaMgAl11O19, NdMgAl11O19 and SmMgAl11O19 oxides were superior to 8YSZ as proved by water quenching tests. In addition, the thinner the platelet. the more interstices are retained in the sintered specimen, and the better thermal-shock resistance the oxide has. Based on SEM images, it can be seen that the SmMgAl11O19 sample exhibits a mixture of the intergranular and transgranular fracture after thermal cycling failure.

Studies of methane reforming with carbon dioxide over LaNiAl11O19

A new type of the catalyst, LaNiAl11O19, for the methane reforming with carbon dioxide was synthesized and evaluated. LaNiAl11O19 has a hexaaluminate structure and can keep large surface and heat resistance against sintering at high reaction temperature. As compared with La2O3-Ni/SrAl12O19, in the CH4 + CO2 reaction, LaNiAl11O19 catalyst displays a higher catalytic activity, lower coking amount and excellent sintering resistance of Ni particle, due to its stable structure.