A vibrational spectroscopic study of the so-called ‘healing’ mineral papagoite CaCuAlSi2O6(OH)3

Papagoite is a silicate mineral named after an American Indian tribe and was used as a healing mineral. Papagoite CaCuAlSi2O6(OH)3 is a hydroxy mixed anion compound with both silicate and hydroxyl anions in the formula. The structural characterization of the mineral papagoite remains incomplete. Papagoite is a four-membered ring silicate with Cu2+ in square planar coordination. The intense sharp Raman band at 1053 cm−1 is assigned to the ν1 (A 1g) symmetric stretching vibration of the SiO4 units. The splitting of the ν3 vibrational mode offers support to the concept that the SiO4 tetrahedron in papagoite is strongly distorted. A very intense Raman band observed at 630 cm−1 with a shoulder at 644 cm−1 is assigned to the ν4 vibrational modes. Intense Raman bands at 419 and 460 cm−1 are attributed to the ν2 bending modes. Intense Raman bands at 3545 and 3573 cm−1 are assigned to the stretching vibrations of the OH units. Low-intensity Raman bands at 3368 and 3453 cm−1 are assigned to water stretching modes. It is suggested that the formula of papagoite is more likely to be CaCuAlSi2O6(OH)3 · xH2O. Hence, vibrational spectroscopy has been used to characterize the molecular structure of papagoite.

Raman spectroscopic study of the mineral shattuckite Cu5(SiO3)4(OH)2

Shattuckite Cu5(SiO3)4(OH)2 is a copper hydroxy silicate and is commonly known as a ‘healing’ mineral. Three shattuckite mineral samples from three different origins were analysed by Raman spectroscopy. Some Raman bands are common in the spectra of the minerals. Raman bands at around 890, 1058 and 1102 are described as the ν3 –SiO3 antisymmetric stretching vibrations. The Raman band at 670 cm-1 is assigned to the ν4 bending modes of the -SiO3 units and the band at around 785 cm-1is due to Si-O-Si chain stretching mode. Raman (and infrared) spectroscopy proves that water is in the molecular structure of shattuckite; thus the formula is better written as Cu5(SiO3)4(OH)2•xH2O.

Vibrational spectroscopic study of the copper silicate mineral kinoite Ca2Cu2Si3O10(OH)4

Kinoite Ca2Cu2Si3O10(OH)4 is a mineral named after a Jesuit missionary. Raman and infrared spectroscopy have been used to characterise the structure of the mineral. The Raman spectrum is characterised by an intense sharp band at 847 cm-1 assigned to the ν1 (A1g) symmetric stretching vibration. Intense sharp bands at 951, 994 and 1000 cm-1 are assigned to the ν3 (Eu, A2u, B1g) SiO4 antisymmetric stretching vibrations. Multiple ν2 SiO4 vibrational modes indicate strong distortion of the SiO4 tetrahedra. Multiple CaO and CuO stretching bands are observed. Raman spectroscopy confirmed by infrared spectroscopy clearly shows that hydroxyl units are involved in the kinoite structure. Based upon the infrared spectra, it is proposed that water is also involved in the kinoite structure. Based upon vibrational spectroscopy, the formula of kinoite is defined as Ca2Cu2Si3O10(OH)4•xH2O.

Vibrational spectroscopy and solubility study of the mineral stringhamite CaCuSiO4•H2O

Stringhamite CaCuSiO4·H2O is a hydrated calcium copper silicate and is commonly known as a significant ‘healing’ mineral and is potentially a semi-precious jewel. Stringhamite is a neosilicate with Cu2+ in square planar coordination. Vibrational spectroscopy has been used to characterise the molecular structure of stringhamite. The intense sharp Raman band at 956 cm−1 is assigned to the ν1 (A1g) symmetric stretching vibration. Raman bands at 980, 997, 1061 cm−1 are assigned to the ν3 (A2u, B1g) antisymmetric stretching vibrations. Splitting of the ν3 vibrational mode supports the concept that the stringhamite SiO4 tetrahedron is strongly distorted. The intense bands at 505 and 519 cm−1 and at 570 cm−1 are assigned to the ν2 and ν4 vibrational modes. The question arises as to whether the mineral stringhamite can actually function as a healing mineral. An estimation of the solubility product at pH < 5 shows that the cupric ion can be released. The copper ion is a very powerful antibiological agent and thus the mineral stringhamite may well function as a healing mineral.

Vibrational spectroscopic study of the copper silicate mineral ajoite (K,Na)Cu7AlSi9O24(OH)6•3H2O

Ajoite (K,Na)Cu7AlSi9O24(OH)6•3H2O is a mineral named after the Ajo district of Arizona. Raman and infrared spectroscopy were used to characterise the molecular structure of ajoite. The structure of the mineral shows disorder which is reflected in the difficulty of obtaining quality Raman spectra. The Raman spectrum is characterised by a broad spectral profile with a band at 1048 cm-1 assigned to the ν1 (A1g) symmetric stretching vibration. Strong bands at 962, 1015 and 1139 cm-1 are assigned to the ν3 SiO4 antisymmetric stretching vibrations. Multiple ν4 SiO4 vibrational modes indicate strong distortion of the SiO4 tetrahedra. Multiple AlO and CuO stretching bands are observed. Raman spectroscopy and confirmed by infrared spectroscopy clearly shows that hydroxyl units are involved in the ajoite structure. Based upon the infrared spectra, water is involved in the ajoite structure, probably as zeolitic water.

Mineral trioxide aggregate repair of lateral root perforations

This study was conducted to observe the healing process of intentional lateral root perforation repaired with mineral trioxide aggregate (MTA). Forty-eight root canals of dogs' teeth were instrumented and filled. After partial removal of the filling, an intentional perforation was made with a bur in the lateral area of the root. The perforations were repaired with MTA or Sealapex (control group). Histological analysis occurred 30 and 180 days after treatment. Results showed no inflammation and deposition of cementum over MTA in the majority of the specimens. In the 180-day period, Sealapex exhibited chronic inflammation in all the specimens and slight deposition of cementum over the material in only three cases. In conclusion, MTA exhibited better results than the control group. Copyright © 2001 by The American Association of Endodontists.

Whelanite Ca5Cu2(OH)2CO3,Si6O17•4H2O – A vibrational spectroscopic study

Whelanite Ca5Cu2(OH)2CO3,Si6O17•4H2O is a hydrated hydroxy mixed anion compound with both silicate and carbonate anions in the formula. The structural characterisation of the mineral whelanite remains incomplete. Whelanite is probably a neosilicate with Cu2+ in square planar coordination. Two Raman bands at 1070 and 1094 cm-1 are assigned to the ν1 symmetric stretching modes of the CO32- units. The observation of two symmetric stretching modes supports the concept of two non-equivalent CO32- units in the whelanite structure. The intense sharp Raman band at 1006 cm-1 is assigned to the ν1 (A1g) symmetric stretching vibration of the Si6O17 units. The splitting of the ν3 vibrational mode offers support to the concept that the SiO4 tetrahedron in whelanite is strongly distorted. A very intense Raman band observed at 666 cm-1 with a shoulder at 697 cm-1 is assigned to the ν4 vibrational modes. Intense Raman bands at 3534, 3556, 3550 and 3595 cm-1 are assigned to the stretching vibrations of the OH units. Low intensity Raman bands at 2910, 3187 and 3453 cm-1 are assigned to water stretching modes. Thus, vibrational spectroscopy has been used to characterise the molecular structure of whelanite. Whelanite is a mineral that could be conceived as a healing mineral

A vibrational spectroscopic study of planchéite Cu8Si8O22(OH)4•H2O

Planchéite Cu8Si8O22(OH)4•H2O is a hydrated copper hydroxy silicate. The objective of this work is to use Raman and infrared spectroscopy to determine the molecular structure of planchéite. Raman bands of planchéite at around 1048, 1081 and 1127 are described as the ν1 –SiO3 symmetric stretching vibrations; Raman bands at 828, 906 are attributed to the ν3 –SiO3 antisymmetric stretching vibrations. The Raman band at 699 cm-1 is assigned to the ν4 bending modes of the -SiO3 units. The intense Raman band at 3479 cm-1 is ascribed to the stretching vibration of the OH units. The Raman band at 3250 cm-1 is evidence for water in the structure. A comparison of the spectra of planchéite with that of shattuckite and chrysocolla.

Size and habit of mineral particles in bone and mineralized callus during bone healing in sheep

Bone healing is known to occur through the successive formation and resorption of various tissues with different structural and mechanical properties. To get a better insight into this sequence of events, we used environmental scanning electron microscopy (ESEM) together with scanning small-angle X-ray scattering (sSAXS) to reveal the size and orientation of bone mineral particles within the regenerating callus tissues at different healing stages (2, 3, 6, and 9 weeks). Sections of 200 µm were cut from embedded blocks of midshaft tibial samples in a sheep osteotomy model with an external fixator. Regions of interest on the medial side of the proximal fragment were chosen to be the periosteal callus, middle callus, intercortical callus, and cortex. Mean thickness (T parameter), degree of alignment (ρ parameter), and predominant orientation (ψ parameter) of mineral particles were deduced from resulting sSAXS patterns with a spatial resolution of 200 µm. 2D maps of T and ρ overlapping with ESEM images revealed that the callus formation occurred in two waves of bone formation, whereby a highly disordered mineralized tissue was deposited first, followed by a bony tissue with more lamellar appearance in the ESEM and where the mineral particles were more aligned, as revealed by sSAXS. As a consequence, degree of alignment and mineral particle size within the callus increased with healing time, whereas at any given moment there were structural gradients, for example, from periosteal toward the middle callus.

Spatial and temporal variations of mechanical properties and mineral content of the external callus during bone healing

After bone fracture, various cellular activities lead to the formation of different tissue types, which form the basis for the process of secondary bone healing. Although these tissues have been quantified by histology, their material properties are not well understood. Thus, the aim of this study is to correlate the spatial and temporal variations in the mineral content and the nanoindentation modulus of the callus formed via intramembranous ossification over the course of bone healing. Midshaft tibial samples from a sheep osteotomy model at time points of 2, 3, 6 and 9 weeks were employed. PMMA embedded blocks were used for quantitative back scattered electron imaging and nanoindentation of the newly formed periosteal callus near the cortex. The resulting indentation modulus maps show the heterogeneity in the modulus in the selected regions of the callus. The indentation modulus of the embedded callus is about 6 GPa at the early stage. At later stages of mineralization, the average indentation modulus reaches 14 GPa. There is a slight decrease in average indentation modulus in regions distant to the cortex, probably due to remodelling of the peripheral callus. The spatial and temporal distribution of mineral content in the callus tissue also illustrates the ongoing remodelling process observed from histological analysis. Most interestingly the average indentation modulus, even at 9 weeks, remains as low as 13 GPa, which is roughly 60% of that for cortical sheep bone. The decreased indentation modulus in the callus compared to cortex is due to the lower average mineral content and may be perhaps also due to the properties of the organic matrix which might be different from normal bone.

Healing process of dog dental pulp after pulpotomy and pulp covering with mineral trioxide aggregate or Portland cement.

Considering several reports about the similarity between the chemical compositions of the mineral trioxide aggregate (MTA) and Portland cement (PC), the subject of this investigation was to analyze the behavior of dog dental pulp after pulpotomy and direct pulp protection with these materials. After pulpotomy, the pulp stumps of 26 roots of dog teeth were protected with MTA or PC. Sixty days after treatment, the animal was sacrificed and the specimens removed and prepared for histomorphological analysis. There was a complete tubular hard tissue bridge in almost all specimens. In conclusion, MTA and PC show similar comparative results when used in direct pulp protection after pulpotomy.

Effect of platelet-rich plasma on the healing of intrabony defects treated with an anorganic bovine bone mineral: a pilot study

BACKGROUND: Periodontal therapy using the combination of platelet-rich plasma (PRP) and different grafting materials has been suggested as a modality to enhance the outcome of regenerative surgery. In most clinical studies, a barrier membrane was used to cover the defects, and thus, the effects of PRP may have been masked by the effects of the barrier. The data from controlled clinical studies evaluating the effect of regenerative therapy using various grafting materials with or without PRP are still limited. The purpose of this study was to clinically compare the healing of intrabony defects treated with either a combination of an anorganic bovine bone mineral (ABBM) and PRP to those obtained with ABBM alone. METHODS: Thirty patients with advanced chronic periodontal disease and displaying one intrabony defect were randomly treated with PRP + ABBM or ABBM alone. The following clinical parameters were evaluated at baseline and 1 year after treatment: plaque index (PI), gingival index (GI), bleeding on probing (BOP), probing depth (PD), gingival recession (GR), and clinical attachment level (CAL). The primary outcome variable was CAL. RESULTS: No statistical significant differences in any of the investigated parameters between the two groups were observed at baseline. Healing was uneventful in all patients. In the PRP + ABBM group, mean PD decreased from 8.6 +/- 1.8 mm to 3.4 +/- 1.4 mm (P <0.001) and mean CAL changed from 9.9 +/- 1.7 mm to 5.3 +/- 1.8 mm (P <0.001). In the ABBM group, mean PD decreased from 8.5 +/- 2.0 mm to 3.2 +/- 1.3 mm (P <0.001) and mean CAL changed from 9.6 +/- 1.9 mm to 4.9 +/- 1.5 mm (P <0.001). CAL gains >or=3 mm were measured in 80% (12 of 15 defects) of cases treated with PRP + ABBM and in 87% (13 of 15 defects) of cases treated with ABBM alone. No statistically significant differences in any of the investigated parameters were observed between the two groups at the 1-year reevaluation. CONCLUSIONS: Within the limits of the present study, it can be concluded that 1) at 1 year after regenerative surgery with PRP + ABBM and ABBM alone, significant PD reductions and CAL gains were found, and 2) the use of PRP failed to improve the results obtained with ABBM alone.

Five-year results evaluating the effects of platelet-rich plasma on the healing of intrabony defects treated with enamel matrix derivative and natural bone mineral

BACKGROUND Regenerative periodontal surgery using the combination of enamel matrix derivative (EMD) and natural bone mineral (NBM) with and without addition of platelet-rich plasma (PRP) has been shown to result in substantial clinical improvements, but the long-term effects of this combination are unknown. METHODS The goal of this study was to evaluate the long-term (5-year) outcomes after regenerative surgery of deep intrabony defects with either EMD + NBM + PRP or EMD + NBM. Twenty-four patients were included. In each patient, one intrabony defect was randomly treated with either EMD + NBM + PRP or EMD + NBM. Clinical parameters were evaluated at baseline and 1 and 5 years after treatment. The primary outcome variable was clinical attachment level (CAL). RESULTS The sites treated with EMD + NBM + PRP demonstrated a mean CAL change from 10.5 ± 1.6 to 6.0 ± 1.7 mm (P <0.001) at 1 year and 6.2 ± 1.5 mm (P <0.001) at 5 years. EMD + NBM-treated defects showed a mean CAL change from 10.6 ± 1.7 to 6.1 ± 1.5 mm (P <0.001) at 1 year and 6.3 ± 1.4 mm (P <0.001) at 5 years. At 1 year, a CAL gain of ≥4 mm was measured in 83% (10 of 12) of the defects treated with EMD + NBM + PRP and in 100% (all 12) of the defects treated with EMD + NBM. Compared to baseline, in both groups at 5 years, a CAL gain of ≥4 mm was measured in 75% (nine of 12 in each group) of the defects. Four sites in the EMD + PRP + NBM group lost 1 mm of the CAL gained at 1 year. In the EMD + NBM group, one defect lost 2 mm and four other defects lost 1 mm of the CAL gained at 1 year. No statistically significant differences in any of the investigated parameters were observed between the two groups. CONCLUSIONS Within their limits, the present results indicate that: 1) the clinical outcomes obtained with both treatments can be maintained up to a period of 5 years; and 2) the use of PRP does not appear to improve the results obtained with EMD + NBM.

Bone healing around nanocrystalline hydroxyapatite, deproteinized bovine bone mineral, biphasic calcium phosphate, and autogenous bone in mandibular bone defects.

The individual healing profile of a given bone substitute with respect to osteogenic potential and substitution rate must be considered when selecting adjunctive grafting materials for bone regeneration procedures. In this study, standardized mandibular defects in minipigs were filled with nanocrystalline hydroxyapatite (HA-SiO), deproteinized bovine bone mineral (DBBM), biphasic calcium phosphate (BCP) with a 60/40% HA/β-TCP (BCP 60/40) ratio, or particulate autogenous bone (A) for histological and histomorphometric analysis. At 2 weeks, percent filler amongst the test groups (DBBM (35.65%), HA-SiO (34.47%), followed by BCP 60/40 (23.64%)) was significantly higher than the more rapidly substituted autogenous bone (17.1%). Autogenous bone yielded significantly more new bone (21.81%) over all test groups (4.91%-7.74%) and significantly more osteoid (5.53%) than BCP 60/40 (3%) and DBBM (2.25%). At 8 weeks, percent filler amongst the test groups (DBBM (31.6%), HA-SiO (31.23%), followed by BCP 60/40 (23.65%)) demonstrated a similar pattern and was again significantly higher as compared to autogenous bone (9.29%). Autogenous bone again exhibited statistically significantly greater new bone (55.13%) over HA-SiO (40.62%), BCP 60/40 (40.21%), and DBBM (36.35%). These results suggest that the osteogenic potential of HA-SiO and BCP is inferior when compared to autogenous bone. However, in instances where a low substitution rate is desired to maintain the volume stability of augmented sites, particularly in the esthetic zone, HA-SiO and DBBM may be favored. © 2014 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 103B: 1478-1487, 2015.

The stimulation of healing within a rat calvarial defect by mPCL–TCP/collagen scaffolds loaded with rhBMP-2

Bone morphogenetic proteins (BMPs) have been widely investigated for their clinical use in bone repair and it is known that a suitable carrier matrix to deliver them is essential for optimal bone regeneration within a specific defect site. Fused deposited modeling (FDM) allows for the fabrication of medical grade poly 3-caprolactone/tricalcium phosphate (mPCL–TCP) scaffolds with high reproducibility and tailor designed dimensions. Here we loaded FDM fabricated mPCL–TCP/collagen scaffolds with 5 mg recombinant human (rh)BMP-2 and evaluated bone healing within a rat calvarial critical-sized defect. Using a comprehensive approach, this study assessed the newly regenerated bone employing microcomputed tomography (mCT), histology/histomorphometry, and mechanical assessments. By 15 weeks, mPCL–TCP/collagen/rhBMP-2 defects exhibited complete healing of the calvarium whereas the non- BMP-2-loaded scaffolds showed significant less bone ingrowth, as confirmed by mCT. Histomorphometry revealed significantly increased bone healing amongst the rhBMP-2 groups compared to non-treated scaffolds at 4 and 15 weeks, although the % BV/TV did not indicate complete mineralisation of the entire defect site. Hence, our study confirms that it is important to combine microCt and histomorphometry to be able to study bone regeneration comprehensively in 3D. A significant up-regulation of the osteogenic proteins, type I collagen and osteocalcin, was evident at both time points in rhBMP-2 groups. Although mineral apposition rates at 15 weeks were statistically equivalent amongst treatment groups, microcompression and push-out strengths indicated superior bone quality at 15 weeks for defects treated with mPCL–TCP/collagen/rhBMP-2. Consistently over all modalities, the progression of healing was from empty defect < mPCL–TCP/collagen < mPCL–TCP/collagen/rhBMP-2, providing substantiating data to support the hypothesis that the release of rhBMP-2 from FDM-created mPCL–TCP/collagen scaffolds is a clinically relevant approach to repair and regenerate critically-sized craniofacial bone defects. Crown Copyright 2008 Published by Elsevier Ltd. All rights reserved.