Foaming properties of a peptide designed to form stimuli-responsive interfacial films

We have designed an amphipathic peptide, AM1, that can self-assemble at the air-water interface to form an interfacial ensemble capable of switching between a mechanically strong cohesive film state and a mobile detergent state in response to changes in the solution conditions. The mechanical properties of the AM1 ensemble in the cohesive film state are qualitatively equivalent to the protein beta-LG, while in the mobile detergent state they are equivalent to the low molecular weight surfactant, SDS. In this work the foaming properties of AM1 are compared to those of beta-LG and SDS at the same weight concentration and it is found that AM1 adsorbs rapidly to the interface, initially forming a dense foam like that formed by SDS and superior to beta-LG. In addition, under solution conditions where interfacially adsorbed AM1 forms a cohesive film state the foam stability is high, comparable to beta-LG. However when the interfacially adsorbed AM1 forms a foam under detergent-state conditions, the foam stability is poor. We have achieved control of foam stability through the design of a peptide that exhibits stimuli-responsive changes in the extent of intermolecular interactions between peptide molecules adsorbed at the air water interface. These results illustrate the exciting potential of peptide surfactants to form a new class of stimuli-responsive foaming agents.

Utilização intracoágulo de espuma fibrinolítica - preparação, caracterização e atividade in vitro de uma espuma de estreptoquinase e proposta de uma nova abordagem terapêutica

Foam was developed as a novel vehicle for streptokinase with the purpose of increasing the contact time and area between the fibrinolytic and the target thrombus, which would lead to a greater therapeutic efficacy at lower doses, decreasing the drug s potential to cause bleeding. Fibrinolytic foams were prepared using CO2 and human albumin (at different v:v ratios), as the gas and liquid phases, respectively, and streptokinase at a low total dose (100,000 IU) was used as fibrinolytic agent conveyed in 1 mL of foam and in isotonic saline solution. The foams were characterized as foam stability and apparent viscosity. The thrombolytic effect of the streptokinase foam was determined in vitro as thrombus lysis and the results were compared to those of a fibrinolytic solution (prepared using the same dose of streptokinase) and foam without the fibrinolytic. In vitro tests were conducted using fresh clots were weighed and placed in test tubes kept at 37 ° C. All the samples were injected intrathrombus using a multiperforated catheter. The results showed that both foam stability and apparent viscosity increased with the increase in the CO2:albumin solution ratio and therefore, the ratio of 3:1 was used for the incorporation of streptokinase. The results of thrombus lysis showed that the streptokinase foam presented the highest thrombolytic activity (44.78 ± 9.97%) when compared to those of the streptokinase solution (32.07 ± 3.41%) and the foam without the drug (19.2 ± 7.19%). We conclude that fibrinolytic foam showed statistically significant results regarding the enhancement of the lytic activity of streptokinase compared to the effect of the prepared saline solution, thus it can be a promising alternative in the treatment of thrombosis. However, in vivo studies are needed in order to corroborate the results obtained in vitro

Desidratação de polpa de manga em leito de espuma com e sem intermitência térmica

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Glass foam of macroporosity using glass waste and sodium hydroxide as the foaming agent

Glass foams using float glass waste and sodium hydroxide were produced. The influence of the sodium hydroxide amount in the foam formulation was studied. Titanium dioxide was used as a strengthening agent. The variations of temperature, heating rate and sintering time were investigated during the synthesis process. Open porosity was estimated using mercury porosimetry. The morphology of the glass foams was evaluated using scanning electron microscopy, phase formation was studied using X-ray diffraction, and chemical composition was estimated using X-ray fluorescence. As a result, glass foams with macroporosity were obtained. Since the glass foams used glass waste as reactant, the results suggest the development of an alternative route for glass recycling. © 2012 Elsevier Ltd and Techna Group S.r.l.