Controlled electronic transport in single-walled carbon nanotube networks : selecting electron hopping and chemical doping mechanisms

The electronic transport in both intrinsic and acid-treated single-walled carbon nanotube networks containing more than 90% semiconducting nanotubes is investigated using temperature-dependent resistance measurements. The semiconducting behavior observed in the intrinsic network is attributed to the three-dimensional electron hopping mechanism. In contrast, the chemical doping mechanism in the acid-treated network is found to be responsible for the revealed metal-like linear resistivity dependence in a broad temperature range. This effective method to control the electrical conductivity of single-walled carbon nanotube networks is promising for future nanoscale electronics, thermometry, and bolometry. © 2010 American Institute of Physics.

Electron hopping i eui-xsrxfeO3 and ndi-xsrxcOO3

Mössbauer and electrical resistivity measurements on Eu1–xSrxFeO3(0.0 < x[less-than-or-eq] 0.4) show the presence of a time-averaged electron configuration of Fe in these solids at T > TN. Variable range hopping arising from Anderson localization seems to occur at T < TN indicating that the electron hopping time in this regime is likely to be greater than 10–7 s. Mössbauer studies on Nd1–xSrxCoO3 show that in the Anderson localization regime, the hopping time is greater than 10–7 s in this system as well.

Electron flow through cytochrome P450

The cytochromes P450 (P450s) are a remarkable class of heme enzymes that catalyze the metabolism of xenobiotics and the biosynthesis of signaling molecules. Controlled electron flow into the thiolate-ligated heme active site allows P450s to activate molecular oxygen and hydroxylate aliphatic C–H bonds via the formation of high-valent metal-oxo intermediates (compounds I and II). Due to the reactive nature and short lifetimes of these intermediates, many of the fundamental steps in catalysis have not been observed directly. The Gray group and others have developed photochemical methods, known as “flash-quench,” for triggering electron transfer (ET) and generating redox intermediates in proteins in the absence of native ET partners. Photo-triggering affords a high degree of temporal precision for the gating of an ET event; the initial ET and subsequent reactions can be monitored on the nanosecond-to-second timescale using transient absorption (TA) spectroscopies. Chapter 1 catalogues critical aspects of P450 structure and mechanism, including the native pathway for formation of compound I, and outlines the development of photochemical processes that can be used to artificially trigger ET in proteins. Chapters 2 and 3 describe the development of these photochemical methods to establish electronic communication between a photosensitizer and the buried P450 heme. Chapter 2 describes the design and characterization of a Ru-P450-BM3 conjugate containing a ruthenium photosensitizer covalently tethered to the P450 surface, and nanosecond-to-second kinetics of the photo-triggered ET event are presented. By analyzing data at multiple wavelengths, we have identified the formation of multiple ET intermediates, including the catalytically relevant compound II; this intermediate is generated by oxidation of a bound water molecule in the ferric resting state enzyme. The work in Chapter 3 probes the role of a tryptophan residue situated between the photosensitizer and heme in the aforementioned Ru-P450 BM3 conjugate. Replacement of this tryptophan with histidine does not perturb the P450 structure, yet it completely eliminates the ET reactivity described in Chapter 2. The presence of an analogous tryptophan in Ru-P450 CYP119 conjugates also is necessary for observing oxidative ET, but the yield of heme oxidation is lower. Chapter 4 offers a basic description of the theoretical underpinnings required to analyze ET. Single-step ET theory is first presented, followed by extensions to multistep ET: electron “hopping.” The generation of “hopping maps” and use of a hopping map program to analyze the rate advantage of hopping over single-step ET is described, beginning with an established rhenium-tryptophan-azurin hopping system. This ET analysis is then applied to the Ru-tryptophan-P450 systems described in Chapter 2; this strongly supports the presence of hopping in Ru-P450 conjugates. Chapter 5 explores the implementation of flash-quench and other phototriggered methods to examine the native reductive ET and gas binding events that activate molecular oxygen. In particular, TA kinetics that demonstrate heme reduction on the microsecond timescale for four Ru-P450 conjugates are presented. In addition, we implement laser flash-photolysis of P450 ferrous–CO to study the rates of CO rebinding in the thermophilic P450 CYP119 at variable temperature. Chapter 6 describes the development and implementation of air-sensitive potentiometric redox titrations to determine the solution reduction potentials of a series of P450 BM3 mutants, which were designed for non-native cyclopropanation of styrene in vivo. An important conclusion from this work is that substitution of the axial cysteine for serine shifts the wild type reduction potential positive by 130 mV, facilitating reduction by biological redox cofactors in the presence of poorly-bound substrates. While this mutation abolishes oxygenation activity, these mutants are capable of catalyzing the cyclopropanation of styrene, even within the confines of an E. coli cell. Four appendices are also provided, including photochemical heme oxidation in ruthenium-modified nitric oxide synthase (Appendix A), general protocols (Appendix B), Chapter-specific notes (Appendix C) and Matlab scripts used for data analysis (Appendix D).

Polaron hopping in olivine phosphates studied by nuclear resonant scattering

Valence fluctuations of Fe²⁺ and Fe³⁺ were studied in a solid solution of Li_xFePO₄ by nuclear resonant forward scattering of synchrotron x rays while the sample was heated in a diamond-anvil pressure cell. The spectra acquired at different temperatures and pressures were analyzed for the frequencies of valence changes using the Blume-Tjon model of a system with a fluctuating Hamil- tonian. These frequencies were analyzed to obtain activation energies and an activation volume for polaron hopping. There was a large suppression of hopping frequency with pressure, giving an anomalously large activation volume. This large, positive value is typical of ion diffusion, which indicates correlated motions of polarons, and Li⁺ ions that alter the dynamics of both.

In a parallel study of Na_xFePO₄, the interplay between sodium ordering and electron mobility was investigated using a combination of synchrotron x-ray diffraction and nuclear resonant scattering. Conventional Mossbauer spectra were collected while the sample was heated in a resistive furnace. An analysis of the temperature evolution of the spectral shapes was used to identify the onset of fast electron hopping and determine the polaron hopping rate. Synchrotron x-ray diffraction measurements were carried out in the same temperature range. Reitveld analysis of the diffraction patterns was used to determine the temperature of sodium redistribution on the lattice. The diffraction analysis also provides new information about the phase stability of the system. The temperature evolution of the iron site occupancies from the Mossbauer measurements, combined with the synchrotron diffraction results give strong evidence for a relationship between the onset of fast electron dynamics and the redistribution of sodium in the lattice.

Measurements of activation barriers for polaron hopping gave fundamental insights about the correlation between electronic carriers and mobile ions. This work established that polaron-ion interactions can alter the local dynamics of electron and ion transport. These types of coupled processes may be common in many materials used for battery electrodes, and new details concerning the influence of polaron-ion interactions on the charge dynamics are relevant to optimizing their electrochemical performance.

Fast hole surface conduction observed for indoline sensitizer dyes immobilized at fluorine-doped tin oxide - TiO2 surfaces

The indoline dyes D102, D131, D149, and D205 have been characterized when adsorved on fluorine-doped tin oxide (FTO) and TiO2 electrode surfaces. Adsorption from 50:50 acetonitrile - tert-butanol onto flourine-doped tin oxide (FTO) allows approximate Langmuirian binding constants of 6.5 x 10(4), 2.01 x 10(3), 2.0 x 10(4), and 1.5 x 10(4) mol-1 dm3, respectively, to be determined. Voltammetric data obtained in acetonitrile/0.1 M NBu4PF6 indicate reversible on-electron oxidation at Emid = 0.94, 0.91, 0.88, and 0.88 V vs Ag/AgCI(3 M KCI), respectively, with dye aggregation (at high coverage) causing additional peak features at more positive potentials. Slow chemical degradation processes and electron transfer catalysis for iodine oxidation were observed for all four oxidezed indolinium cations. When adsorbed onto TiO2 nanoparticle films (ca. 9nm particle diameter and ca.3/um thickness of FTO0, reversible voltammetric responses with Emid = 1.08, 1.156, 0.92 and 0.95 V vs Ag/AgCI(3 M KCI), respectively, suggest exceptionally fast hole hopping diffusion (with Dapp > 5 x 10(-9) m2 s-1) for adsorbed layers of four indoline dyes, presumably due to pie-pie stacking in surface aggregates. Slow dye degradation is shown to affect charge transport via electron hopping. Spectrelectrochemical data for the adsorbed indoline dyes on FTO-TiO2 revealed a red-shift of absorption peaks after oxidation and the presence of a strong charge transfer band in the near-IR region. The implications of the indoline dye reactivity and fast hole mobility for solar cell devices are discussed.

Probing second harmonic components of pH-sensitive Redox processes in a mesoporous TiO2-Nafion film electrode with Fourier-transformed large-amplitude sinusoidally modulated voltammetry

Electrochemical processes in mesoporous TiO2-Nafion thin films deposited on indium tin oxide (ITO) electrodes are inherently complex and affected by capacitance, Ohmic iR-drop, RC-time constant phenomena, and by potential and pH-dependent conductivity. In this study, large-amplitude sinusoidally modulated voltammetry (LASMV) is employed to provide access to almost purely Faradaic-based current data from second harmonic components, as well as capacitance and potential domain information from the fundamental harmonic for mesoporous TiO2-Nafion film electrodes. The LASMV response has been investigated with and without an immobilized one-electron redox system, ferrocenylmethyltrimethylammonium+. Results clearly demonstrate that the electron transfer associated with the immobilized ferrocene derivative follows two independent pathways i) electron hopping within the Nafion network and ii) conduction through the TiO2 backbone. The pH effect on the voltammetric response for the TiO2 reduction pathway (ii) can be clearly identified in the 2nd harmonic LASMV response with the diffusion controlled ferrocene response (i) acting as a pH independent reference. Application of second harmonic data derived from LASMV measurement, because of the minimal contribution from capacitance currents, may lead to reference-free pH sensing with systems like that found for ferrocene derivatives.

Structural, Magnetic, and Electrical Properties of Microwave-Sintered Cr3+-Doped Sr Hexaferrites

SrCrxFe12-xO19 (x = 0.0, 0.1, 0.3, 0.5, 0.7, 0.9) hexaferrites were prepared by a microwave-hydrothermal method and subsequently sintered at 950 degrees C for 90 min using the microwave sintering method. The results show that, with increasing Cr3+ content, the lattice parameters changed anisotropically. The average grain sizes of sintered samples were in the range of 280 nm to 660 nm. The saturation magnetization systematically decreased with increasing Cr3+ doping, but the coercivity values increased. The electrical resistivity (log rho) decreased linearly with increasing temperature up to a certain temperature known as the transition temperature (T-c), and T-c decreased with further increase (x>0.5) of the Cr3+ content. This decrease in log rho and the activation energy (E-g) is due to electron hopping and occupancy of doped ions at different lattice sites. We found that the dielectric constant and dielectric loss for all the samples decreased with the Cr3+ content. The structural, magnetic, and electrical properties of Cr3+-doped SrFe12O19 hexaferrites have thus been investigated.

A study of the electrochemical characteristics of the Co(salen)-Nafion modified electrode

A Co(salen)-Nafion modified electrode was prepared by immersing a glassy carbon electrode coated with the Nafion film into the aqueous solution with saturated Co(salen), The modified electrode showed a stable electrochemical reaction of Co(salen) at about 0 V(vs, SCE), The result of XPS indicated the valence of cobalt in Co(salen) changes from +2 before to +3 after Co(salen) enters the Nafion film, It is due to forming axis coordination of cobalt with sulfonic group in Nafion film, It was found that the mode of electron transfer in Co(salen)-Nafion modified electrode was controlled by physical diffusion and electron hopping, It was also found that the modified electrode could catalyze the reduction of O-2 to H2O2. The real catalyst may be the adduct of Co-I(salen) and O-2.

Delocalization of a hole in van der Waals clusters: Ionization potential of rare-gas and small Hg_n clusters

The size dependence of the ionization potential I_p(n) of van der Waals (vdW) bound clusters has been calculated by using a model Hamiltonian, which includes electron hopping, vdW interactions, and charge-dipole interactions. The charge-density and dipole-density distributions for both neutral and ionized n-atom clusters are determined self-consistently. The competition between the polarization energy of the neutral atoms surrounding a partially localized hole and the tendency toward hole delocalization in the ionized clusters is found to dominate the size dependence of I_p(n). To test our theory, we culculate I_p(Xe_n) and I_p(Kr_n) for n \le 300. Good quantitative agreement with experiment is obtained. The theory is also applied to calculate I_p(Hg_n). Comparison with experiments suggests that in Hg_n^+ clusters with n \le 20 the positive charge is mainly distributed within a trimer which is situated at the center of the cluster and which polarizes the n - 3 surrounding neutral atoms.

Correlation of reactivity with structural factors in a series of Fe(II) substituted cobalt ferrites

A series of powdered cobalt ferrites, CoxFe3-xO4 with 0.66 <= x< 1.00 containing different amounts of Fe-II, were synthesized by a mild procedure, and their Fe and Co site occupancies and structural characteristics were explored using X-ray anomalous scattering and the Rietveld refinement method. The dissolution kinetics, measured in 0.1 M oxalic acid aqueous solution at 70 degrees C, indicate in all cases the operation of a contracting volume rate law. The specific rates increased with the Fell content following approximately a second-order polynomial expression. This result suggests that the transfer of Fe-III controls the dissolution rate, and that the leaching of a first layer of ions Co-II and Fe-II leaves exposed a surface enriched in slower dissolving octahedral Fe-III ions. Within this model, inner vicinal lattice Fe-II accelerates the rate of Fe-III transfer via internal electron hopping. A chain mechanism, involving successive electron transfers, fits the data very well. (C) 2006 Elsevier B.V. All rights reserved.

Electrical characterization of SnO2 : Sb ultrathin films obtained by controlled thickness deposition

A representative study is reported on the electrical properties of SnO2: Sb. ultrathin films (thickness of 40-70 nm) produced by a deposition method based on aqueous colloidal suspensions of 3-5 nm crystalline oxides. The results revealed the films' electrical behavior in a range of 10-300 K, showing a strong dependence on dopant incorporation, with minimum resistivity values in 10 mol % of Sb content. All the samples displayed semiconductor behavior, but the transport mechanism showed a strong dependence on thickness, making it difficult to fit it to well-known models. In thicker films, the mechanism proved to be an intermediary system, with thermally activated and hopping features. Electron hopping was estimated in the range of 0.4-1.9 nm, i.e., in the same order as the particle size. (c) 2007 American Institute of Physics.

An investigation into complex inorganic materials with Mössbauer spectroscopy

Mössbauer Spektroskopie ist ein unverzichtbares Instrument für die Bestimmung von Oxidationszuständen und für die Analyse von lokalen Ordnungsphänomenen von Mössbauer aktiven Atomen. Weil es sich um eine lokale Methode handelt können sowohl kristalline als auch amorphe Materialien untersucht werden. Die Kombination von lokaler Prüfung mit Mössbauer Spektroskopie und globaler Untersuchung z.B. mit Röntgendiffraktometrie ermöglicht die Studie von Ordnungseffekten von statistisch besetzten Positionen in einer geordneten Matrix. Das wurde hier eingesetzt um die lokale Umgebung in zwei Serien von Heuslerverbindungen, Co2-xFe1+xSi and Co2Mn1-xFexAl zu untersuchen. Für die Co2Mn1-xFexAl Serie wurde eine L21 geordnete Phase in einer insgesamt B2 geordneten Probe detektiert. Ein Wechsel von der AlCu2Mn zu der CuHg2Ti Struktur wurde für die Co2-xFe1+xSi Proben gefunden. Die Transformation von einem Glas zu einem keramischen Material wurde mit 119Sn Mössbauer Spektroskopie untersucht. Die höhere Ordnung in der Keramik wurde von einer kleiner werdenden Mössbauerlinienbreite begleitet. Demzufolge geben die Modifikationen der Sn Umgebungen klar die Transformation des gesamten Materials wieder. Ist die lokale Umgebung von unregelmäßig auftretenden Atomen in einer amorphen Matrix von Interesse, sind lokal prüfende Methoden die zuverlässigsten Methoden die zur Verfügung stehen. In dieser Arbeit wurde 119Sn Mössbauer Spektroskopie eingesetzt um die Oxidationszustände, die lokalen Umgebungen und relativen Intensitäten von Zinn Atomen in einer Silikatmatrix zu bestimmen. Modifikationen dieser Parameter als Funktion von Prozess bestimmenden Parametern wie der Sauerstoffpartialdruck, die Temperatur, die Behandlungsdauer und der Abkühlprozess genauso wie der SnO2 Gehalt sind von Interesse, weil durch Reduktions- und Diffusionsprozesse Änderungen des Koordinations- und des Oxidationszustands der Zinnatome auftreten. Da diese Änderungen in der Glasmatrix verursachen, die das fertige Produkt im industriellen Fertigungsprozess ruinieren können sind diese feinen Veränderungen sehr wichtig. Wenigstens zwei Mössbauerlinien korrespondierend mit zwei verschiedenen Umgebungen für Sn2+ und Sn4+ sind für eine Analyse mit ausreichender Qualität notwendig. Durch Vergleich von den bestimmten Hyperfein Parametern mit den Parametern von Modelsubstanzen werden lokale Umgebungen der Zinnatome entworfen. Für Sn2+ werden zwei auf einer trigonalen Pyramide basierende Umgebungen mit variierender Anzahl von bindenden und nicht-bindenden Sauerstoffatomen formuliert. Für Sn4+ wurde eine tetraedrische und eine oktaedrische Umgebung postuliert. Die relativen Intensitäten der vier Mössbauerlinien wurden um ein Diffusions- und Reaktionsmodell zu entwickeln und um einen Satz von Diffusions- und Transferkoeffizienten zu bestimmen eingesetzt. Die bestimmten Diffusionskoeffizienten stimmen mit den Literaturdaten überein. Der Massentransferkoeffizient ist kleiner als der bestimmte Wert, aber immer noch in der gleichen Größenordnung. Im Gegensatz zu den Erwartungen ist der präsentierte Diffusionskoeffizient für Sn4+ bestimmt als der von Sn2+. Das wiederum kann durch Berücksichtigung von Elektronhoppingprozessen erklärt werden.

Microbial nanowires : an electrifying tale

Electromicrobiology has gained momentum in the last ten years with advances in microbial fuel cells and the discovery of microbial nanowires (MNWs). The list of MNWs producing microorganisms is growing and providing intriguing insights into the presence of such microorganisms in diverse environments and the potential roles MNWs can perform. This review discusses the MNWs produced by different microorganisms, including their structure, composition and role in electron transfer through MNWs. Two hypotheses, metallic-like conductivity and an electron hopping model, have been proposed for electron transfer and we present a current understanding of both these hypotheses. MNWs are not only poised to change the way we see microorganisms but may also impact the fields of bioenergy, biogeochemistry and bioremediation, hence their potential applications in these fields are highlighted here.

Insulating phase of a disordered system: Fermi glass versus electron glass

The authors examine the critical divergence of the low-frequency conductivity of the noninteracting Fermi glass and interacting electron glass models of the insulating phase of a disordered system as the metallic phase is approached. Results for the two are found to be rather different, which can be tested experimentally. In particular, for the electron glass, there exists a nonvanishing contribution to the dielectric constants from the low-frequency (hopping) conductivity even at low temperatures, which scales with the high-frequency (optical) contribution, and diverges with the same exponent at the insulator-metal transition.

Intrinsic Electron localization in manganites

We mention here an unusual disorder effect in manganites, namely the ubiquitous hopping behavior for electron transport observed in them over a wide range of doping. We argue that the implied Anderson localization is intrinsic to manganites, because of the existence of polarons in them which are spatially localized, generally at random sites (unless there is polaron ordering). We have developed a microscopic two fluid lb model for manganites, where l denotes lattice site localized l polarons, and b denotes band electrons. Using this, and the self-consistent theory of localization, we show that the occupied b states are Anderson localized in a large range of doping due to the scattering of b electrons from l polarons. Numerical simulations which further include the effect of long range Coulomb interactions support this, as well the existence of a novel polaronic Coulomb glass. A consequence is the inevitable hopping behaviour for electron transport observed in doped insulating manganites.