A scanning electronic microscopy study of the action of different desensitizing agents on bovine dentin

This study sought to use scanning electronic microscopy (SEM) to evaluate the dentinal tubule occlusion potential of different desensitizing agents. Ten slices of bovine dentin were divided into six fragments, cleaned (using ultrasound), and etched for 15 seconds with a 35% phosphoric acid solution. All but one of the groups received a different desensitizing agent; the sixth group served as a control and received no additional treatment. After the agents were applied, the dentin specimens were analyzed by SEM and scores were assigned based on the extent of tubular obliteration. Only three agents demonstrated tubular sealing that was significantly different from that of the control group.

Clinical Efficiency of Low-Level Diode Laser in Reducing Dentin Hypersensitivity

Dentin hipersensitivity (DH) is a relatively common clinical condition, especially in periodontal patients after treatment. In this study it was evaluated 28 teeth who presented dentin hypersensitivity. The teeth were subjected to clinical and radiographic exams and were divided into groups following the treatment and the time of examination after application proposed: GI: PO 3% (Potassium Oxalate-group control)/Baseline; GII: PO 3%/3 days after first session; GIII: PO 3%/6 days; GIV: PO 3%/30 days; GV: PO 3%/60 days; GVI: PO 3%/90 days; GVII: Laser (Low-level diode laser with 110 mW/cm(2))/Baseline; GVIII: Laser/7 days after first session; GIX: Laser/14 days; GX: Laser/30 days; GXI: Laser/60 days; and GXII: Laser/90 days. The groups I-VI, the teeth were subjected to 3 applications (GI-GIII) of desensitizing agent at regular intervals of seven days. The Groups VII-XI, each tooth was subjected to three applications (GVII GIX) in three different points (mesial, meddle and distal surfaces) with an interval of 72 h. The time of application in each point was of 33 s and the patients from both groups were followed up to 90 days. The nonparametric test Friedman (alpha = 0.05) was applied and the test of Mann Whitney (alpha = 0.05) was used to compare the time of examination between groups. The application of Laser was effective 6 days after first session and to PO was 30 days. It was observed that both treatments were effective for the reduction of dentin hypersensitivity, however the laser presented better effectiveness.

Effects of cement-curing mode and light-curing unit on the bond durability of ceramic cemented to dentin

The aim of this study was to evaluate the effects of different light-curing units and resin cement curing types on the bond durability of a feldspathic ceramic bonded to dentin. The crowns of 40 human molars were sectioned, exposing the dentin. Forty ceramic blocks of VITA VM7 were produced according to the manufacturer's recommendations. The ceramic surface was etched with 10% hydrofluoric acid/60s and silanized. The dentin was treated with37% phosphoric acid/15s, and the adhesive was applied. The ceramic blocks were divided and cemented to dentin according to resin cement/RC curing type(dual-and photocured), light-curing unit (halogen light/QTH and LED), and storage conditions (dry and storage/150 days + 12,000 cycles/thermocycling). All blocks were stored in distilled water (37°C/24h) and sectioned (n = 10): G1-QTH + RC Photo, G2-QTH + RC Dual, G3-LED + RC Photo, G4-LED + RC Dual. Groups G5, G6, G7, and G8 were obtained exactly as G1 through G4, respectively, and then stored and thermocycled. Microtensile bond strength tests were performed (EMIC), and data were statistically analyzed by ANOVA and Tukey's test (5%). The bond strength values (MPa) were: G1-12.95 (6.40)ab; G2-12.02 (4.59)ab; G3-13.09 (5.62)ab; G4-15.96 (6.32)a; G5-6.22 (5.90)c; G6-9.48 (5.99)bc; G7-12.78 (11.30)ab; and G8-8.34 (5.98)bc. The same superscript letters indicate no significant differences. Different light-curing units affected the bond strength betweenceramic cemented to dentin when the photocured cement was used, and only after aging (LED>QTH). There was no difference between the effects of dual-and photo-cured resin-luting agents on the microtensile bond strength of the cement used in this study.

Avaliação in vivo e in vitro de diferentes protocolos no tratamento da hipersensibilidade dentinária cervical

Este estudo possui duas partes distintas: 1. in vivo (randomizado e longitudinal) que teve como objetivo avaliar protocolos de tratamento para hipersensibilidade dentinária com laser de baixa potência (com diferentes dosagens), laser de alta potência e agente dessensibilizante, por um período de 12 e 18 meses; e 2. in vitro que teve como objetivo analisar a perda de estrutura de dois dentifrícios distintos (Colgate Total 12 e Colgate Pró Alívio) e analisar a permeabilidade dentinária dos tratamentos da etapa 01, associados aos dentifrícios, após diferentes ciclos de abrasão. Na parte in vivo, as lesões cervicais não cariosas de 32 voluntários, previamente submetidos aos critérios de elegibilidade ou exclusão, foram divididas em nove grupos (n=10): G1: Gluma Desensitizer (Heraeus Kulzer), G2: Laser de baixa potência com baixa dosagem (Photon Lase, DMC) (três pontos de irradiação vestibulares e um ponto apical: 30 mW, 10 J/cm2, 9 seg por ponto com o comprimento de onda de 810nm). Foram realizadas três sessões com um intervalo de 72 horas), G3: Laser de baixa potência com alta dosagem (um ponto cervical e um ponto apical: 100 mW, 90 J/cm2, 11 seg por ponto com o comprimento de onda de 810nm. Foram realizadas três sessões com um intervalo de 72 horas), G4: Laser de baixa potência com baixa dosagem + Gluma Desensitizer, G5: Laser de baixa potência com alta dosagem + Gluma Desensitizer, G6: Laser de Nd:YAG (Power LaserTM ST6, Lares Research®), em contato com a superfície dental: 1,0W, 10 Hz e 100 mJ, ? 85 J/cm2, com o comprimento de onda de 1064nm, G7: Laser de Nd:YAG + Gluma Desensitizer, G8: Laser de Nd:YAG + Laser de baixa potência com baixa dosagem, G9: Laser de Nd:YAG + Laser de baixa potência com alta dosagem. O nível de sensibilidade de cada voluntário foi avaliado através da escala visual analógica de dor (VAS) com auxílio do ar da seringa tríplice e exploração com sonda após 12 e 18 meses do tratamento. Na parte 02, in vitro, foram utilizados terceiros molares humanos não irrompidos e recém-extraídos. Todos foram limpos e tiveram suas raízes separadas das coroas. As raízes foram seccionadas em quadrados de dentina com dimensões de 4x4x2 mm, os quais foram embutidos em resina Epoxi e devidamente polidos até uma curvatura de 0,3 ?m, analisados em perfilometria ótica. Estes foram imersos em solução de EDTA 17% por 2min para abertura dos túbulos e armazenados em uma solução de Soro Fetal Bovino diluído em salina tamponada com fosfato. Os espécimes foram divididos aleatoriamente em 12 grupos (n=10) G1: Sem tratamento de superfície, sem dentifrício; G2: Nd:YAG/sem dentifrício; G3: Gluma/sem dentifrício; G4: Nd:YAG + Gluma/sem dentifrício; G5: Sem tratamento de superfície/Colgate Total 12; G6: Nd:YAG/Colgate Total 12; G7: Gluma/Colgate Total 12; G8: Nd:YAG + Gluma/Colgate Total 12; G9: Sem tratamento de superfície/Colgate Pró Alívio; G10: Nd:YAG/Colgate Pró Alívio; G11: Gluma/Colgate Pró Alívio; G12: Nd:YAG + Gluma/Colgate Pró Alívio. Em seguida, as superfícies receberam a aplicação de fitas adesivas nas duas margens, mantendo uma área central de teste exposta de 4 x 1 mm, onde foram realizados os tratamentos de superfície e os ciclos de abrasão correspondentes a 1, 7, 30 e 90 dias de escovação (52 ciclos, 210 segundos de contato com o slurry; 361 ciclos, 1470 segundos de contato com o slurry; 1545 ciclos, 6300 segundos de contato com o slurry; 4635 ciclos, 18900 segundos de contato com o slurry, respectivamente). A cada etapa de abrasão, foi realizada análise em Perfilometria Ótica. Para as analises de permeabilidade e Microscopia Eletrônica de Varredura, foram utilizadas amostras circulares de 6 mm de diâmetro e 1 mm de espessura de dentina obtidas das coroas dentais. Estas foram divididas aleatoriamente nos mesmos grupos já descritos anteriormente, sendo que 120 espécimes foram utilizados para permeabilidade (n=10) e 36 para MEV (n=3). Ambas as análises foram realizadas após imersão no EDTA; após tratamentos para a sensibilidade; pós 1 dia, 7 dias, 30 dias e 90 dias de escovação. Após análise estatística pode-se concluir que, in vivo, todos os tratamentos foram eficazes para a redução da hipersensibilidade dentinária. Ainda que o nível da sensibilidade dos pacientes aumentou numericamente, estes não são considerados estatisticamente diferentes a partir de 12 meses. Portanto, até a avaliação de 18 meses, podemos concluir que não houve um aumento na sensibilidade dentinária desde a sua diminuição pós-tratamento. In vitro, pode-se concluir que todos os tratamentos foram capazes de diminuir a permeabilidade dentinária. O dentifrício Total 12 apresentou-se como o mais abrasivo em comparação com o dentifrício Pro Alivio, pois este último promoveu uma perda de estrutura menor, porém ambos não apresentaram aumento na permeabilidade nos tempos de escovação. As microscopias eletrônicas de varredura mostram a formação da smear layer, obliterando os túbulos para ambos os dentifricios. Como conclusão, pode-se afirmar que todos os agentes dessensibilizantes foram efetivos, mesmo apresentando estratégias de ação diferentes. Os dentifrícios são igualmente interessantes para o uso caseiro por ocasionarem oclusão tubular e a associação de tratamentos (caseiro e de consultório) parece ser uma alternativa eficaz no tratamento da hipersensibilidade dentinária.

Influence of desensitizing agents on the microshear bond strength of adhesive systems to dentin.

The aim of this study was to evaluate the effect of desensitizing agents on the micro-shear bond strength of adhesive systems to dentin. Forty bovine teeth were divided into 8 groups (n=5): G1--Single Bond (SB); G2--GH.F + SB; G3-- Desensibilize + SB; G4--essensiv + SB; G5 --ingle Bond 2 (SB2); G6--H.E + SB2; G7--esensibilize + SB2; G8--Dessensiv + SB2. In all of the groups, the desensitizing agents were applied after phosphoric acid etching and before the dentin adhesive application. Z250 composite resin tubes were bonded on the treated surface. After 24 hours, the teeth were tested in a universal machine. Data were submitted to ANOVA and Tukey's test (5%). The results showed that the groups where Desensibilize and Dessensiv were applied exhibited smaller bond strength values.