Structural Investigations on the Compositional Anomalies in Lanthanum Zirconate System Synthesized by Coprecipitation Method

The study set out to investigate the compositional inconsistency in lanthanum zirconate system revealed the presence of nonstoichiometry in lanthanum zirconate powders when synthesized by coprecipitation route. X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM) investigations confirmed the depletion of La3+ ions in the system. Analysis using Vegard's law showed the La/Zr mole ratio in the sample to be around 0.45. An extra step of ultrasonication, introduced during the washing stage followed by the coprecipitation reaction, ensured the formation of stoichiometric La2Zr2O7. Noteworthy is also the difference between crystal sizes in the samples prepared by with and without ultrasonication step. This difference has been explained in light of the formation of individual nuclei and their scope of growth within the precipitate core. The differential scanning calorimetry (DSC) analyses revealed that optimum pH for the synthesis of La2Zr2O7 is about 11. The ultrasonication step was pivotal in assuring consistency in mixing and composition for the lanthanum zirconate powders.

Studies on state and structure of noble metals in electrocatalyst made by coprecipitation method

The electrocatalysts of Pt/C, PtRu/C and Ru/C were prepared by the impregnation method. The facet characterization, the dispersion and the particle size for the catalysts were determined by means of X-ray diffraction and transmission electron microscopy. X-ray photoelectron spectroscopy was also used to analyze the state and the valency of the noble metals. The results show that the particle size was in nanometer range and the binary metals have come into being an alloy. The platinum in the catalysts existed in zero valency. The valency of the ruthenium on the surface is different from that in the body, while the ruthenium on the surface existed in oxide-form. PtRu/C and Pt/C are of good activity to the electrooxidation of hydrogen except Ru/C. PtRu/C is more tolerant of CO than Pt/C, and CO is only adsorbed on Pt.

Preparation of bioactive glass ceramic nanoparticles by combination of sol-gel and coprecipitation method

SiO2-CaO-P2O5 ternary bioactive glass ceramic nanoparticles were prepared via the combination of sol-gel and coprecipitation processes. Precursors of silicon and calcium were hydrolyzed in acidic solution and gelated in alkaline condition together with ammonium dibasic phosphate. Gel particles were separated by centrifugation, followed by freeze drying, and calcination procedure to obtain the bioactive glass ceramic nanoparticles. The investigation of the influence of synthesis temperature on the nanopartilce's properties showed that the reaction temperature played an important role in the crystallinity of nanoparticle. The glass ceramic particles synthesized at 55 degrees C included about 15% crystalline phase, while at 25 degrees C and 40 degrees C the entire amorphous nanopowder could be obtained.

Structural refinement, growth process, photoluminescence and photocatalytic properties of (Ba1-xPr2x/3)WO4 crystals synthesized by the coprecipitation method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural refinement, growth process, photoluminescence and photocatalytic properties of (Ba1-xPr2x/3)WO4 crystals synthesized by the coprecipitation method

Barium praseodymium tungstate (Ba1-xPr2x/3)WO4 crystals with (x = 0, 0.01, and 0.02) were prepared by the coprecipitation method. These crystals were structurally characterized by X-ray diffraction (XRD), Rietveld refinements, Fourier-transform Raman (FT-Raman) and Fourier-transform infrared (FT-IR) spectroscopies. The shape and size of these crystals were observed by field emission scanning electron microcopy (FE-SEM). Their optical properties were investigated by ultraviolet visible (UV-vis) absorption and photoluminescence (PL) measurements. Moreover, we have studied the photocatalytic (PC) activity of crystals for degradation of rhodamine B (RhB) dye. XRD patterns, Rietveld refinements data, FT-Raman and FT-IR spectroscopies indicate that all crystals exhibit a tetragonal structure without deleterious phases. FT-Raman spectra exhibited 13 Raman-active modes in a range from 50 to 1000 cm(-1), while FT-IR spectra have 8 infrared active modes in a range from 200 to 1050 cm(-1). FE-SEM images showed different shapes (bonbon-, spindle-, rice-and flake-like) as well as a reduction in the crystal size with an increase in Pr3+ ions. A possible growth process was proposed for these crystals. UV-vis absorption measurements revealed a decrease in optical band gap values with an increase of Pr3+ into the matrix. An intense green PL emission was noted for (Ba1-xPr2x/3)WO4 crystals (x = 0), while crystals with (x = 0.01 and 0.02) produced a reduction in the wide band PL emission and the narrow band PL emission which is related to f-f transitions from Pr3+ ions. High photocatalytic efficiency was verified for the bonbon-like BaWO4 crystals as a catalyst in the degradation of the RhB dye after 25 min under UV-light. Finally, we discuss possible mechanisms for PL and PC properties of these crystals.

Silylation of layered double hydroxides via an induced hydrolysis method

A series of layered double hydroxides (LDHs) based composites were synthesized by using induced hydrolysis silylation method (IHS), surfactant precursor method, in-situ coprecipitation method, and direct silylation method. Their structures, morphologies, bonding modes and thermal stabilities can be readily adjusted by changing the parameters during preparation and drying processing of the LDHs. The characterization results show that the direct silylation reaction cannot occur between the dried LDHs and 3-aminopropyltriethoxysilane (APS) in an ethanol medium. However, the condensation reaction can proceed with heating process between adsorbed APS and LDHs plates. While using wet state substrates with and without surfactant and ethanol as the solvent, the silylation process can be induced by hydrolysis of APS on the surface of LDHs plates. Surfactants improve the hydrophobicity of the LDHs during the process of nucleation and crystallization, resulting in fluffy shaped crystals; meanwhile, they occupy the surface –OH positions and leave less “free –OH” available for the silylation reaction, favoring formation of silylated products with a higher population in the hydrolyzed bidentate (T2) and tridentate (T3) bonding forms. These bonding characteristics lead to spherical aggregates and tightly bonded particles. All silylated products show higher thermal stability than those of pristine LDHs.

Bulk manufacture of YBCO powders by coprecipitation

This work presents an assessment of the coprecipitation technique for the reliable production of high-temperature superconducting (HTS) copper-oxide powders in quantities scaled up to 1 kg. This process affords precise control of cation stoichiometry (< 4% relative), occurs rapidly (almost instantaneously) and can be suitably developed for large-scale (e.g. tonne) manufacture of HTS materials. The process is based upon a simple control of the chemistry of the cation solution and precipitation with oxalic acid. This coprecipitation method is applicable to all copper-oxides and has been demonstrated in this work using over thirty separate experiments for the following compositions: YBa2Cu3O7-δ, Y2BaCuO5 and YBa2Cu4O8. The precursor powders formed via this coprecipitation process are fine-grained (∼ 5-10 nm), chemically homogeneous at the nanometer scale and reactive, Conversion to phase-pure HTS powders can therefore occur in minutes at appropriate firing temperatures. © 1995.

Use of hydrotalcites for the removal of toxic anions from aqueous solutions

The removal of toxic anions has been achieved using hydrotalcite via two methods: (1) coprecipitation and (2) thermal activation. Hydrotalcite formed via the coprecipitation method, using solutions containing arsenate and vanadate up to pH 10, are able to remove more than 95% of the toxic anions (0.2 M) from solution. The removal of toxic anions in solutions with a pH of >10 reduces the removal uptake percentage to 75%. Raman spectroscopy observed multiple A1 stretching modes of V−O and As−O at 930 and 810 cm−1, assigned to vanadate and arsenate, respectively. Analysis of the intensity and position of the A1 stretching modes helped to identify the vanadate and arsenate specie intercalated into the hydrotalcite structure. It has been determined that 3:1 hydrotalcite structure predominantly intercalate anions into the interlayer region, while the 2:1 and 4:1 hydrotalcite structures shows a large portion of anions being removed from solution by adsorption processes. Treatment of carbonate solutions (0.2 M) containing arsenate and vanadate (0.2 M) three times with thermally activated hydrotalcite has been shown to remove 76% and 81% of the toxic anions, respectively. Thermally activated hydrotalcite with a Mg:Al ratio of 2:1, 3:1, and 4:1 have all been shown to remove 95% of arsenate and vanadate (25 ppm). At increased concentrations of arsenate and vanadate, the removal uptake percentage decreased significantly, except for the 4:1 thermally activated hydrotalcite. Thermally activated Bayer hydrotalcite has also been shown to be highly effective in the removal of arsenate and vanadate. The thermal activation of the solid residue component (red mud) removes 30% of anions from solution (100 ppm of both anions), while seawater-neutralized red mud removes 70%. The formation of hydrotalcite during the seawater neutralization process removes anions via two mechanisms, rather than one observed for thermally activated red mud.

Synthesis and enhanced green photoluminescence emission from BCT ZnS nanocrystals

Body-centered-tetragonal (BCT) ZnS nanocrystals have been synthesized, for the first time to the best of our knowledge, by using the chemical coprecipitation method at higher synthesis temperatures of 65 and 95 degrees C. It is confirmed from X-ray diffraction (XRD) studies that in the high-temperature-synthesized samples, cubic and BCT phases coexist, in contrast to the room-temperature-synthesized sample, which consists of only cubic phase with sizes of the particles lying between 2 and 3 nm. The sizes of BCT phase nanocrystals are bigger than those of cubic phase of ZnS. The presence of BCT phase of ZnS in the samples is increased from 40 to 90% when the temperature of synthesis is increased from 65 to 95 degrees C. The nanocrystalline nature and UV-Vis absorption characteristics of the prepared samples have been studied with a transmission electron microscope (TEM) and a UV-Visible pectrophotometer, respectively. The room-temperature-synthesized ZnS sample shows photoluminescence (PL) emission in the blue region with multiple peaks, whereas the high-temperature-synthesized samples show PL emissions in the visible region. The Gaussian fittings of the measured PL spectra shows that three PL peaks at 429, 477, and 525 nm are appeared in the 65 degrees C sample and two peaks at 491 and 540 nm appear in the 95 degrees C sample with the enhanced PL intensity of the green peak at 540 nm. (C) 2010 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim

Characterization of coprecipitated ferroelectric Bi2 VO5·5

Fine powders of orthorhombic bismuth vandate (Bi2VO5.5) have been synthesized by coprecipitation method. Powder X-ray diffraction and electron microscopic techniques have been used to characterize these samples. The formation of the monophasic Bi2VO5.5 was confirmed. The compacted powders sintered at 1070 K have been characterized for their dielectric properties as a function of both temperature (300-900 K) and frequency (100 Hz-10 MHz) and found to be superior to those obtained by the conventional solid-state reaction route.

Estudo de catalisadores modelo à base de CeO2-ZrO2 dopado com cobre para controle de emissões de NOx

Convencionalmente, metais nobres são empregados como metais ativos em catalisadores automotivos, mas o uso de cobre vem sendo estudado pelo fato de promover sítios ativos para adsorção química e redução de NOx. Diante deste contexto, esta dissertação visa testar novas formulações de catalisadores, com foco em seu desempenho na reação de redução do NO pelo CO e sua seletividade a N2. Foram avaliados o método de adição de cobre no preparo e os teores de cobre utilizados na preparação. Os métodos de adição utilizados foram impregnação a seco (IS), reação em estado sólido (RS) e coprecipitação (CO). Os teores de cobre estudados ficaram entre 0,36 e 6,9% (m/m). Além disso, foi estudado o impacto no desempenho do catalisador após envelhecimento térmico a 950C por 12h. Foram empregadas as seguintes técnicas de caracterização textural e físico-química como espectrometria de absorção atômica, fisissorção de N2, difração de raios X, espectroscopia Raman e redução a temperatura programada. Os catalisadores também foram avaliados na reação de redução do NO pelo CO. A análise textural indicou que o método de coprecipitação levou a características texturais diferentes dos outros catalisadores. Análises de DRX mostraram a formação de CuO cristalino para teores iguais ou superiores a 3,3% (m/m) de cobre. As análises de Redução a Temperatura Programada (RTP) indicaram que ocorreu uma forte interação na interface entre o suporte e as espécies de cobre dispersas, acompanhada da diminuição da temperatura de redução do CuO e da redução parcial da céria em temperaturas mais baixas. Os testes catalíticos mostraram um melhor desempenho dos catalisadores (IS) que apresentaram conversões mais elevadas em menores temperaturas. Com relação ao envelhecimento, observou-se uma diminuição significativa da eficiência dos catalisadores. Uma comparação com catalisadores à base de metal nobre mostrou um bom desempenho dos catalisadores à base de cobre, com a vantagem destes apresentarem emissão de N2O restrita a baixas temperaturas

Fabrication and spectral properties of Nd3+-doped yttrium lanthanum oxide transparent ceramics

Transparent 1 at% Nd3+:Y1.9La0.1O3 ceramics were fabricated with nanopowders prepared by carbonate coprecipitation method. The powder compacts were sintered in H-2 atmosphere at 1550 degrees C for 30 h. The Nd3+:Y1.9La0.1O3 ceramics display uniform grains of about 50 mu m and high transparency. The highest transmittance of the ceramics reaches 67%. The strongest absorption peak is in the wavelength of 820 nm with absorption cross section of 2.48 x 10(-20) cm(2). The absorption is still high at LD wavelength 806 nm with absorption cross section of 1.78 x 10(-20) cm(2) and broad full width at half maximum (FWHM) of about 6.3 nm. The strongest emission peak was centered at 1078 nm with large stimulated emission cross section of 9.63 x 10(-20) cm(2) and broad FWHM of about 7.8 nm. The broad absorption and emission bandwidth of Nd3+:y(1.9)La(0.1)O(3) transparent ceramics are favorable to achieve the miniaturized LD pumping apparatus and ultrashort modelocked pulse laser output, respectively. (c) 2007 Elsevier B.V. All rights reserved.

Optical and magnetic properties of ZnS nanoparticles doped with Mn2+

ZnS:Mn nanoparticles of the cubic zinc blende structure with the average sizes of about 3 nm were synthesized using a coprecipitation method and their optical and magnetic properties were investigated. Two emission bands were observed in doped nanoparitcles and attributed to the defect-related emission of ZnS and the Mn2+ emission, respectively. With the increase of Mn2+ concentration, the luminescence intensities of these two emission bands increased and the ZnS emission band shifted to lower energy. Based on the luminescence excitation spectra of Mn2+, the 3d(5) level structure of Mn2+ in ZnS nanoparticles is similar to that in bulk ZnS:Mn, regardless of Mn2+ concentration. Magnetic measurements showed that all the samples exhibit paramagnetic behavior and no antiferromagnetic interaction between Mn2+ ions exists, which are in contrast to bulk ZnS:Mn. (c) 2005 Elsevier B.V. All rights reserved.

Porous ZnAl2O4 spinel nanorods doped with Eu3+: synthesis and photoluminescence

Eu3+-doped zinc aluminate (ZnAl2O4) nanorods with a spinel structure were successfully synthesized via an annealing transformation of layered precursors obtained by a homogeneous coprecipitation method combined with surfactant assembly. These spinel nanorods, which consist of much finer nanofibres together with large quantities of irregular mesopores and which possess a large surface area of 93.2 m(2) g(-1) and a relatively narrow pore size distribution in the range of 6 - 20 nm, are an ideal optical host for Eu3+ luminescent centres. In this nanostructure, rather disordered surroundings induce the typical electric-dipole emission (D-5(0) --> F-7(2)) of Eu3+ to predominate and broaden.

Uniaxial anisotropy and novel magnetic behaviors of CoFe2O4 nanoparticles prepared in a magnetic field

CoFe2O4 nanoparticles prepared by chemical coprecipitation method in a magnetic field exhibit novel magnetic properties. The average particle diameter was about 2 nm and larger depending on the post annealing temperature. Magnetization measurements indicate that smaller nanoparticles are superparamagnetic above their respective blocking temperatures. In the blocked state, these nanoparticles exhibit interesting behaviors in the magnetic hysteresis measurements. Constricted, or wasp waisted with extremely narrow waist, hysteresis curves have been observed in the magnetization versus field sweeps. For larger nanoparticles, the room temperature hysteresis is typical of a ferromagnet with an open loop, but the loop closes at lower temperature. The novel magnetic behavior is attributed to the directional order of Co ions and vacancies in CoFe2O4 established during the coprecipitation of the nanoparticles under an applied field.