Osteogenesis at implants without primary bone contact - An experimental study in dogs

Aim: To evaluate the healing at implants with a moderately rough surface placed and stabilized in recipient sites of dimensions deeper and larger than that of the implants to avoid any contact between parent bone and the implant.Material & methods: In six Labrador dogs, premolars and first molars were extracted bilaterally in the mandible. After 3 months of healing, mucoperiosteal full-thickness flaps were elevated and the premolar area of the alveolar bony crest was selected. Three recipient sites were prepared to place three implants. One implant was used as control. The other two were placed in recipient sites which left a circumferentially and periapical prepared defect of 0.7 mm (small) and 1.2 mm (large), respectively. All implants were stabilized with passive fixation plates to maintain the implants stable and without any contact with the implant bed. After 3 months of submerged healing, the animals were sacrificed. Ground sections were prepared and analyzed histomorphometrically.Results: The BIC% was 5.3% and 0.3% for implants placed in small and large defect sites, respectively, whereas it was 46.1% for control implants. The differences were statistically significant. The width of the residual defects was 0.4 and 0.5 mm at the small and large defects, respectively. An approximately 0.09 mm layer of dense connective tissue (DCT) rich in fibers and fibroblast-like cells was observed adherent to the implant surfaces. The percentage of implant surface covered by DCT was 92.8% and 95.6% at the small and large defects, respectively.Conclusion: Osseointegration was observed at the test sites, and the dimensions of the defects influenced the outcomes. However, the degree of osseointegration at both small and large defects was very low compared with the control sites.

Deproteinized bovine bone mineral particles and osseointegration of implants without primary bone contact: An experimental study in dogs

Objectives: To evaluate the influence on osseointegration of Deproteinized bovine bone mineral (DBBM) particles used to fill defects of at least 1 mm around implants having no primary contact with bone. Material and methods: Premolars and first molars were extracted bilaterally from the mandible of six Labrador dogs. After 3 months of healing, mucoperiosteal full-thickness flaps were elevated, and one recipient site was prepared in the molar region of each hemi-mandible to place implants. These were installed with a deliberate circumferential and periapical space to the bone walls of 1.2 mm. All implants were stabilized with passive fixation plates to maintain the implants in situ and without any contact with the implant bed. The control sites were left to be filled with coagulum, while at the test sites, the residual gap was filled with DBBM. After 3 months of submerged healing, the animals were sacrificed. Ground sections were prepared and analyzed histomorphometrically. Results: Mineralized bone-to-implant contact was 4.0% and 3.9% for control and test sites, respectively. The width of the residual defects was 0.48 mm and 0.88 mm at the control and test sites, respectively. The percentage of implant surface covered by a layer of dense connective tissue of 0.12 mm of width on average was 84.9% and 88.5% at the control and test sites, respectively. Conclusion: A minor and not predictable degree of contact or distance osteogenesis was obtained on the implant surface when primary contact of the implant surface with the implant bed had deliberately been avoided. DBBM grafting of the artificial gap did not favor osseointegration. Neither did it enhance the ability to bridge the gap with newly formed bone in an artificial defect wider than 1 mm. © 2013 John Wiley & Sons A/S.

Predicting the pathogen of diabetic toe osteomyelitis by two consecutive ulcer cultures with bone contact

In this study, we investigate the accuracy of two consecutive ulcer cultures with bone contact compared to bone biopsy for the diagnosis of diabetic toe osteomyelitis. The same nurse and orthopaedic surgeon obtained all samples: sample A-1: bone contact swabbing through the ulcer; sample A-2: a second culture swabbing from the bone surface within 24 h; sample B: surgical bone biopsy in the operating theatre. The kappa statistic measure between samples A-1 and A-2 (bone contact swabs) indicated 82.35% agreement. The sensitivity, specificity, positive and negative predictive values of the two samples A compared to B were 96%, 79%, 92% and 88%, respectively, for the causative pathogen. These results were similar with prior antibiotic treatment, discordant bone surface swabs or with monomicrobial infections. As a conclusion, two consecutive diabetic toe cultures with bone contact accurately predict the pathogen of diabetic toe osteomyelitis in 90% of cases.

Macroporous Scaffolds for Bone Engineering. Studies on Cell Culture and Ectopic Bone Formation

Bone engineering is a rapidly developing area of reconstructive medicine where bone inducing factors and/or cells are combined with a scaffold material to regenerate the structure and function of the original tissue. The aim of this study was to compare the suitability of different macroporous scaffold types for bone engineering applications. The two scaffold categories studied were a) the mechanically strong and stable titanium fiber meshes and b) the elastic and biodegradable porous polymers. Furthermore, bioactive modifications were applied to these basic scaffold types, and their effect on the osteogenic responses was evaluated in cell culture and ectopic bone formation studies. The osteogenic phenotype of cultured cell-scaffold constructs was heightened with a sol-gel derived titania coating, but not with a mixed titania-silica coating. The latter coating also resulted in delayed ectopic bone formation in bone marrow stromal cell seeded scaffolds. However, the better bone contact in early implantation times and more even bone tissue distribution at later times indicated enhanced osteoconductivity of both the coated scaffold types. Overall, the most promising bone engineering results were obtained with titania coated fiber meshes. Elastic and biodegradable poly(ε-caprolactone/D,L-lactide) based scaffolds were also developed in this study. The degradation rates of the scaffolds in vitro were governed by the hydrophilicity of the polymer matrix, and the porous architecture was controlled by the amount and type of porogen used. A continuous phase macroporosity was obtained using a novel CaCl2 • 6H2O porogen. Dynamic culture conditions increased cell invasion, but decreased cell numbers and osteogenicity, within the scaffolds. Osteogenic differentiation in static cultures and ectopic bone formation in cell seeded scaffolds were enhanced in composites, with 30 wt-% of bioactive glass filler.

Osteoconductivity of modified fluorcanasite glass-ceramics for bone tissue augmentation and repair

Modified fluorcanasite glasses were fabricated by either altering the molar ratios of Na(2)O and CaO or by adding P(2)O(5) to the parent stoichiometric glass compositions. Glasses were converted to glass-ceramics by a controlled two-stage heat treatment process. Rods (2 mm x 4 mm) were produced using the conventional lost-wax casting technique. Osteoconductive 45S5 bioglass was used as a reference material. Biocompatibility and osteoconductivity were investigated by implantation into healing defects (2 mm) in the midshaft of rabbit femora. Tissue response was investigated using conventional histology and scanning electron microscopy. Histological and histomorphometric evaluation of specimens after 12 weeks implantation showed significantly more bone contact with the surface of 45S5 bioglass implants when compared with other test materials. When the bone contact for each material was compared between experimental time points, the Glass-Ceramic 2 (CaO rich) group showed significant difference (p = 0.027) at 4 weeks, but no direct contact at 12 weeks. Histology and backscattered electron photomicrographs showed that modified fluorcanasite glass-ceramic implants had greater osteoconductivity than the parent stoichiometric composition. Of the new materials, fluorcanasite glass-ceramic implants modified by the addition of P(2)O(5) showed the greatest stimulation of new mineralized bone tissue formation adjacent to the implants after 4 and 12 weeks implantation. (C) 2010 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 94A: 760-768, 2010

Bone Formation Following Implantation of Titanium Sponge Rods into Humeral Osteotomies in Dogs: A Histological and Histometrical Study

Background: Titanium (Ti) is widely proven to enhance bone contact and growth on its surface. It is expected that bone defects could benefit from Ti to promote healing and to increase strength of the implanted area. Purpose: The present study aimed at comparing the potential of porous Ti sponge rods with synthetic hydroxyapatite (HA) for the healing of bone defects in a canine model. Material and Methods: Six mongrel dogs were submitted to three trephined osteotomies of 6.0 x 4.0 mm in one humerus and after 2 months another three osteotomies were performed in the contralateral humerus. A total of 36 defects were randomly filled either with Ti foam, particulate HA, or coagulum (control). The six animals were killed 4 months after the first surgery for histological and histometrical analysis. Results: The Ti-foam surface was frequently found in intimate contact with new bone especially at the defect walls. Control sites showed higher amounts of newly formed bone at 2 months - Ti (p = 0.000) and HA (p = 0.009) - and 4 months when compared with Ti (p = 0.001). Differently from HA, the Ti foam was densely distributed across the defect area which rendered less space for bone growth in the latter`s sites. The use of Ti foams or HA resulted in similar amounts of bone formation in both time intervals. Nevertheless, the presence of a Ti-foam rod preserved defect`s marginal bone height as compared with control groups. Also, the Ti-foam group showed a more mature bone pattern at 4 months than HA sites. Conclusion: The Ti foam exhibited good biocompatibility, and its application resulted in improved maintenance of bone height compared with control sites. The Ti foam in a rod design exhibited bone ingrowth properties suitable for further exploration in other experimental situations.

Osteoconductivity of modified fluorcanasite glass-ceramics for bone tissue augmentation and repair

Modified fluorcanasite glasses were fabricated by either altering the molar ratios of Na 2O and CaO or by adding P 2O 5 to the parent stoichiometric glass compositions. Glasses were converted to glass-ceramics by a controlled two-stage heat treatment process. Rods (2 mm x 4 mm) were produced using the conventional lost-wax casting technique. Osteoconductive 45S5 bioglass was used as a reference material. Biocompatibility and osteoconductivity were investigated by implantation into healing defects (2 mm) in the midshaft of rabbit femora. Tissue response was investigated using conventional histology and scanning electron microscopy. Histological and histomorphometric evaluation of specimens after 12 weeks implantation showed significantly more bone contact with the surface of 45S5 bioglass implants when compared with other test materials. When the bone contact for each material was compared between experimental time points, the Glass-Ceramic 2 (CaO rich) group showed significant difference (p = 0.027) at 4 weeks, but no direct contact at 12 weeks. Histology and backscattered electron photomicrographs showed that modified fluorcanasite glass-ceramic implants had greater osteoconductivity than the parent stoichiometric composition. Of the new materials, fluorcanasite glass-ceramic implants modified by the addition of P 2O 5 showed the greatest stimulation of new mineralized bone tissue formation adjacent to the implants after 4 and 12 weeks implantation. © 2010 Wiley Periodicals, Inc.

Comparisons between Bio-Oss® and Straumann® Bone Ceramic in immediate and staged implant placement in dogs mandible bone defects

Objective: To compare immediate and staged approach implant placement in circumferential defects treated with deproteinized bovine bone mineral (DBBM); hidroxyapatite/tricalcium phosphate (HA/TP); autogenous bone (Ab); and coagulum (Cg); upon implant stability, osseointegration and alveolar crest maintenance. Materials and methods: Six dogs underwent extractions of lower premolars, bilaterally. Twelve weeks later four bone defects (6 mm wide/4 mm long) were drilled at one side and randomly filled with DBBM; HA/TP; Ab; and Cg, respectively, and left to heal (staged approach). Eight weeks later one implant (Osseospeed™, AstraTech) was placed in experimental sites. At the same session four defects were drilled on contra-lateral side and implants were inserted immediately after biomaterials grafting (immediate approach). Animals were euthanized 8 weeks later. Implant stability was measured by resonance frequency analysis (RFA) at installation and after sacrifice. Ground sections were prepared for bone contact (BIC); bone area (BA); distance implant shoulder-bone crest (IS-C); distance implant shoulder first bone contact (IS-B); and areas occupied by soft tissue. Results: The BA and BIC were superior in the staged approach. The Cg exhibited higher BIC and BA as compared with other materials at the total implant body (P = 0.004 and 0.012, respectively). The DBBM, HA/TP and Ab groups rendered similar BA and BIC. The immediate approach resulted in less crest resorption compared to staged approach. The biomaterials did not affect the IS-C and IS-B measurements. Particles area tended to be higher in DBBM group than HA/TP (P = 0.15), while soft tissue infiltrate was higher in DBBM group when used in the immediate approach (P = 0.04). The RFA indicated gain in stability in the staged approach (P = 0.002). The correlation test between RFA vs. BIC and BA demonstrated inferior stability for DBBM group in immediate approach (P = 0.01). Conclusions: Implants placed in healed defects resulted in better stability as a consequence of higher BIC and BA. The Cg alone rendered increased BIC compared to other materials in both approaches. Immediate approach should be preferable to staged approach in terms of alveolar crest maintenance. The BIC and BA values did not vary between micro and macro-threads in this experimental model. Implants installed in sites filled with DBBM in immediate approach were less stable. © 2011 John Wiley & Sons A/S.

Histologic and histometric evaluation of calvarial autogenous bone graft in reconstruction of atrophyc maxilla for dental implants

The calvarial bone is highlighted as a good donor area for large reconstructions of atrophic jaw for subsequent rehabilitation with implant-supported prosthesis. The aim of this study was to observe and measure through histological and histometric evaluation, the cellular events that occur at the interface of union from onlay parietal bone graft on the maxilla of 10 patients, after a period of 6 months of incorporation. The biopsies were performed at the time of installation of osseointegrated implants. The bone contact area represented 78.75% and connective contact 21.25%. The region of connective union between the bone graft to the maxillae presented new bone formation (41.26%), marrow bone (36.06%), osteoid tissue (15.86%) and connective tissue (6.80%). All samples had good graft incorporation to the receptor bed with osteogenic activity and absence of inflammatory cells.

Bone response to loaded implants with non-matching implant-abutment diameters in the canine mandible

BACKGROUND: One way to evaluate various implant restorations is to measure the amount of bone change that occurs at the crestal bone. The objective of this study was to histologically evaluate the alveolar bone change around a bone-level, non-matching implant-abutment diameter configuration that incorporated a horizontal offset and a Morse taper internal connection. METHODS: The study design included extraction of all mandibular premolars and first molars in five canines. After 3 months, 12 dental implants were placed at three levels in each dog: even with the alveolar crest, 1 mm above the alveolar crest, and 1 mm below the alveolar crest. The implants were submerged on one side of the mandible. On the other side, healing abutments were exposed to the oral cavity (non-submerged). Gold crowns were attached 2 months after implant placement. The dogs were sacrificed 6 months postloading, and specimens were processed for histologic and histometric analyses. RESULTS: Evaluation of the specimens indicated that the marginal bone remained near the top of the implants under submerged and non-submerged conditions. The amount of bone change for submerged implants placed even with, 1 mm below, and 1 mm above the alveolar crest was -0.34, -1.29, and 0.04 mm, respectively (negative values indicate bone loss). For non-submerged implants, the respective values were -0.38, -1.13, and 0.19 mm. For submerged and non-submerged implants, there were significant differences in the amount of bone change among the three groups (P <0.05). The percentage of bone-to-implant contact for submerged implants was 73.3%, 71.8%, and 71.5%. For non-submerged implants, the respective numbers were 73.2%, 74.5%, and 76%. No significant differences occurred with regard to the percentage of bone contact. CONCLUSIONS: Minimal histologic bone loss occurred when dental implants with non-matching implant-abutment diameters were placed at the bone crest and were loaded for 6 months in the canine. The bone loss was significantly less (five- to six-fold) than that reported for bone-level implants with matching implant-abutment diameters (butt-joint connections).

Radiographic bone level changes of implant-supported restorations in edentulous and partially dentate patients: 5-year results.

PURPOSE To evaluate and compare crestal bone level changes and peri-implant status of implant-supported reconstructions in edentulous and partially dentate patients after a minimum of 5 years of loading. MATERIALS AND METHODS All patients who received a self-tapping implant with a microstructured surface during the years 2003 and 2004 at the Department of Prosthodontics, University of Bern, were included in this study. The implant restorations comprised fixed and removable prostheses for partially and completely edentulous patients. Radiographs were taken immediately after surgery, at impression making, and 1 and 5 years after loading. Crestal bone level (BIC) was measured from the implant shoulder to the first bone contact, and changes were calculated over time (ΔBIC). The associations between pocket depth, bleeding on probing (BOP), and ΔBIC were assessed. RESULTS Sixty-one implants were placed in 20 patients (mean age, 62 ± 7 years). At the 5-year follow-up, 19 patients with 58 implants were available. Implant survival was 98.4% (one early failure; one patient died). The average ΔBIC between surgery and 5-year follow-up was 1.5 ± 0.9 mm and 1.1 ± 0.6 mm for edentulous and partially dentate patients, respectively. Most bone resorption (50%, 0.7 mm) occurred during the first 3 months (osseointegration) and within the first year of loading (21%, 0.3 mm). Mean annual bone loss during the 5 years of loading was < 0.12 mm. Mean pocket depth was 2.6 ± 0.7 mm. Seventeen percent of the implant sites displayed BOP; the frequency was significantly higher in women. None of the variables were significantly associated with crestal bone loss. CONCLUSION Crestal bone loss after 5 years was within the normal range, without a significant difference between edentulous and partially dentate patients. In the short term, this implant system can be used successfully for various prosthetic indications.

SOFT TISSUE INTEGRATION IN THE NECK AREA OF TITANIUM IMPLANTS - AN ANIMAL TRIAL

Dental implant materials are required to enable good apposition of bone and soft tissues. They must show sufficient resistance to chemical, physical and biological stress in the oral cavity to achieve good long-term outcomes. A critical issue is the apposition of the soft tissues, as they have provided a quasi-physiological closure of oral cavity. The present experiment was performed to study the peri-implant tissue response to non-submerged (1-stage) implant installation procedures. Two different implants types (NobelBiocare, NobelReplace (R) Tapered Groovy 4.3 x 10 mm and Replace (R) Select Tapered TiU RP 4.3 x 10 mm) were inserted into the right and left sides of 8 domestic pigs (Sus scrofa domestica) mandibles, between canines and premolars and immediately provided with a ceramic crown. Primary implant stability was determined using ressonance frequency analysis. Soft tissue parameters were assessed: sulcus depth (SDI) and junctional epithelium (JE). Following 70 days of healing, jaw sections were processed for histology and histomorphometric examination. Undecalcified histological sections demonstrated osseointegration with direct bone contact. The soft tissue parameters revealed no significant differences between the two implant types. The peri-implant soft tissues appear to behave similarly in both implant types.

Optimising the design and manufacture of a customised, prescription fit, Maxillo-facial prosthesis

This thesis is a continuation of the Enterprise-Ireland Research Innovation Fund (RIF) Project entitled’ "Design and Manufacturing of Customised Maxillo-Facial Prostheses" The primary objective of this Internal Research Development Program (IRDP) project was to investigate two fundamental design changes 1 To incorporate the over-denture abutments directly into the implant. 2 To remove the restraining wings by the addition of screws, which affix the. implant to the dense material of the jawbone. The prosthetic was redesigned using the ANSYS Finite Element Analysis software program and analysed to* • Reduce the internal von Mises stress distribution The new prosthetic had a -63.63 % lower von Mises stress distribution when compared with the original prosthetic. • Examine the screw preload effects. A maximum relative displacement of 22 6 * lO^mm between the bone and screw was determined, which is well below the critical threshold of micromotion which prevents osseointegration • Investigate the prosthetic-bone contact interface. Three models of the screw, prosthesis, and bone, were studied. (Axisymmetnc, quarter volume, and full volume), a recommended preload torque of 0 32 Nm was applied to the prosthetic and a maximum von Mises stress of 1.988 MPa was predicted • Study the overdenture removal forces. This analysis could not be completed because the correct plastic multilinear properties of the denture material could not be established The redesigned prosthetic was successfully manufactured on a 3-axis milling machine with an indexing system The prosthetic was examined for dimensional quality and strength The research established the feasibility of the new design and associated manufacturing method.

Tibio-talar arthrodesis with long anterograde nail after complex open fracture-dislocation of the ankle : P17

Introduction: Posttraumatic painful osteoarthritis of the ankle joint after fracture-dislocation often has to be treated with arthrodesis. In the presence of major soft tissue lesions and important bone loss the technique to achieve arthrodesis has to be well chosen in order to prevent hardware failure, infection of bulky implants or non-union. Methods: We present the case of a 53 year-old biker suffering of a fracture-dislocation of the ankle associated with a mayor degloving injury of the heel. After initial immobilization of the lesion by external fixation in Spain the patient was transferred to our hospital for further treatment. The degloving injury of the heel with MRSA infection was initially treated by repeated débridement, changing of the configuration of the Ex Fix and antibiotic therapy with favourable outcome. Because of the bony lesions reconstruction of the ankle-joint was juged not to be an option and arthrodesis was planned. Due to bad soft-tissue situation standard open fixtion with plate and/or screws was not wanted but an option for intramedullary nailing was taken. However the use of a standard retrograde arthrodesis nail comes with two problems: 1) Risk of infection of the heel-part of the calaneus/nail in an unstable soft tissue situation with protruding nail. And 2) talo-calcaneal arthrodesis of an initially healthy subtalar joint. Given the situation of an unstable plantar/heel flap it was decided to perform anklearthrodesis by means of an anterograde nail with static fixation in the talus and in the proximal tibia. Results:This operation was performed with minimal opening at the ankle-site in order to remove the remaining cartilage and improve direct bone to bone contact. Arthrodesis was achieved by means of an anterograde T2 Stryker tibial nail.One year after the anterograde nailing the patient walks without pain for up to 4 hours with a heel of good quality and arthrodesis is achieved. Conclusion: Tibiotalar arthrodesis in the presence of mayor soft tissue lesions and bone loss can be successfully achieved with antegrade nailing.

Avaliação da osseointegração promovida por implantes jateados por Al2O3: análises histológica e histométrica em cães