In vitro cytotoxicity of binary TI alloys for bone implants

Interest in using titanium (Ti) alloys as load-bearing implant materials has increased due to their high strength to weight ratio, lower elastic modulus, and superior biocompatibility and enhanced corrosion resistance compared to conventional metals such as stainless steel and Co-Cr alloys. In the present study, the in vitro cytotoxicity of five binary titanium alloys, Ti15Ta, Ti15Nb, Ti15Zr, Ti15Sn and Ti15Mo, was assessed using human osteosarcoma cell line, SaOS-2 cells. The Cell proliferation and viability were determined, and cell adhesion and morphology on the surfaces of the binary Ti alloys after cell culture were observed by SEM. Results indicated that the Ti binary alloys of Ti15Ta, Ti15Nb and Ti15Zr exhibited the same level of excellent biocompatibility; Ti15Sn alloy exhibited a moderate biocompatibility while Ti15Mo alloy exhibited a moderate cytotoxicity. The SaOS-2 osteoblast-like cells had flattened and spread across the surfaces of the Ti15Ta, Ti15Nb, Ti15Zr and Ti15Sn groups; however, the cell shapes on the Ti15Mo alloy was shrinking and unhealthy. These results indicated that the Mo contents should be limited to a certain level in the design and development of new Ti alloys for implant material applications.

Diffusion of oxygen in some binary Ti-Based alloys used as biomaterials

Ti and its alloys are widely used as biomaterials. Their main properties are excellent corrosion resistance, relatively low elastic modulus, high specific strength, and good biocompatibility. The development of new Ti alloys with properties favorable for use in the human body is desired. To this end, Ti alloys with Mo, Nb, Zr, and Ta are being developed, because these elements do not cause cytotoxicity. The presence of interstitial elements (such as oxygen and nitrogen) induces strong changes in the elastic properties of the material, which leads to hardening or softening of the alloy. By means of anelastic spectroscopy, we are able to obtain information on the diffusion of these interstitial elements present in the crystalline lattice. In this paper, the effect of oxygen on the anelastic properties of some binary Ti-based alloys was analyzed with anelastic spectroscopy. The diffusion coefficients, pre-exponential factors, and activation energies were calculated for oxygen and nitrogen in these alloys.

pGreen : a versatile and flexible binary Ti vector for Agrobacterium-mediated plant transformation

Binary Ti vectors are the plasmid vectors of choice in Agrobacterium-mediated plant transformation protocols. The pGreen series of binary Ti vectors are configured for ease-of-use and to meet the demands of a wide range of transformation procedures for many plant species. This plasmid system allows any arrangement of selectable marker and reporter gene at the right and left T-DNA borders without compromising the choice of restriction sites for cloning, since the pGreen cloning sites are based on the well-known pBluescript general vector plasmids. Its size and copy number in Escherichia coli offers increased efficiencies in routine in vitro recombination procedures. pGreen can replicate in Agrobacterium only if another plasmid, pSoup, is co-resident in the same strain. pSoup provides replication functions in trans for pGreen. The removal of RepA and Mob functions has enabled the size of pGreen to be kept to a minimum. Versions of pGreen have been used to transform several plant species with the same efficiencies as other binary Ti vectors. Information on the pGreen plasmid system is supplemented by an Internet site (http://www.pgreen.ac.uk) through which comprehensive information, protocols, order forms and lists of different pGreen marker gene permutations can be found.

A guide to Agrobacterium binary Ti vectors

Agrobacterium-based plasmid vectors allow the transformation of a wide range of plant species by capitalizing on a natural bacterial system to introduce DNA into the nuclear genome of plants. It is often a complex task to consider fully all the possible plasmid vectors and Agrobacterium strains available, and it can thus be difficult to take full advantage of these research tools. This practical guide is a survey of the many binary Ti plasmid vectors and Agrobacterium strains available, and aims to help researchers to make an informed decision about the system that is best suited to their needs...

Study of texture evolution in metastable beta-Ti alloy as a function of strain path and its effect on alpha transformation texture

Texture evolution in a low cost beta titanium alloy was studied for different modes of rolling and heat treatments. The alloy was cold rolled by unidirectional and multi-step cross rolling. The cold rolled material was either aged directly or recrystallized and then aged. The evolution of texture in alpha and beta phases were studied. The rolling texture of beta phase that is characterized by the gamma fiber is stronger for MSCR than UDR; while the trend is reversed on recrystallization. The mode of rolling affects alpha transformation texture on aging with smaller alpha lath size and stronger alpha texture in UDR than in MSCR. The defect structure in beta phase influences the evolution of a texture on aging. A stronger defect structure in beta phase leads to variant selection with the rolled samples showing fewer variants than the recrystallized samples.

Solid state amorphization in binary Ti---Ni, Ti---Cu and ternary Ti---Ni---Cu system by mechanical alloying

An amorphous phase has been synthesized by mechanical alloying in a planetary mill over a nickel content range of 10�70 at.% in the Ti---Ni system and a copper content range of 10�50 at.% in the Ti---Cu system. In the case of ternary Ti---Ni---Cu alloys the glass-forming composition range has been found to be given by x = 10�20 for Ti60Ni40 ? xCux, x = 10 � 30 for Ti50Ni50 ? xCux and x = 10 � 40 for Ti40Ni60 ? xCux alloys. The difficulty in the amorphization of copper-rich compositions is explained in the light of enthalpy composition diagrams calculated for the ternary solid solution and the amorphous phase.

Processing-microstructure-yield strength correlation in a near beta Ti alloy, Ti-5Al-5Mo-5V-3Cr

A combined set of thermo-mechanical steps recommended for high strength beta Ti alloy are homogenization, deformation, recrystallization, annealing and ageing steps in sequence. Recrystallization carried out above or below beta transus temperature generates either beta annealed (lath type morphology of alpha) or bimodal (lath+globular morphology of alpha) microstructure. Through variations in heat treatment parameters at these processing steps, wide ranges of length scales of features have been generated in both types of microstructures in a near beta Ti alloy, Ti-5Al-5Mo-5V-3Cr (Ti-5553). 0.2% Yield strength (YS) has been correlated to various microstructural features and associated heat treatment parameters. Relative importance of microstructural features in influencing YS has been identified. Process parameters at different steps have been identified and recommended for attaining different levels of YS for this near beta Ti alloy. (C) 2014 Elsevier B.V. All rights reserved.

Resputtering Effect on Nanocrystalline Ni-Ti Alloy Films

We report on the effect of resputtering on the properties of nanocrystalline Ni-Ti alloy thin films deposited using co-sputtering of Ni and Ti targets. In order to facilitate the formation of nanocrystalline phases, films were deposited at room temperature and 573 K (300 A degrees C) with substrate bias voltage of -100 V. The influence of substrate material on the composition, surface topography microstructure, and phase formations of nanocrystalline Ni-Ti thin films was also systematically investigated. The preferential resputtering of Ti adatoms was lesser for Ni-Ti films deposited on quartz substrate owing to high surface roughness of 4.87 nm compared to roughness value of 1.27 nm for Si(100) substrate.

The diffusion of Co⠶溩 Zrâ â Tiâ â alloy /|nS. Kumar. -- 260 St Catharines [Ont.] : Dept. of Physics, Brock University,

The diffusion of Co60 in the body centered cubic beta phase of a ZrSOTi SO alloy has been studied at 900°, 1200°, and 1440°C. The results confirm earlier unpublished data obtained by Kidson17 • The temperature dependence of the diffusion coefficient is unusual and suggests that at least two and possibly three mechanisms may be operative Annealing of the specimen in the high B.C.C. region prior to the deposition of the tracer results in a large reduction in the diffusion coefficient. The possible significance of this effect is discussed in terms of rapid transport along dislocation network.

Anelastic spectroscopy in a Ti alloy used as biomaterial

Ti and its alloys have been used thoroughly in the production of prostheses and dental implants due to their properties, such as high corrosion resistance, low elasticity modulus and high mechanical strength/density relation. Among the Ti-based alloys, the Ti-35Nb-7Zr-5Ta (TNZT) is one that presents the smallest elasticity modulus, making it an excellent alternative to be used as a biomaterial. In this paper, mechanical spectroscopy measurements were made in TNZT alloys containing several quantities of oxygen and nitrogen in solid solution. Mechanical spectroscopy measurements were made by using a torsion pendulum, operating at an oscillation frequency in the interval 4-30 Hz, temperature in the range 100-700 K, heating rate of about 1 K/min and vacuum lower than 10(-5) Torr. Complex relaxation structures and a reduction in the elasticity modulus were observed for the heat-treated and doped samples. The observed peaks were associated with the interactions of interstitial atoms and the alloy elements. (C) 2009 Elsevier B.V. All rights reserved.