Effect of air-particle abrasion protocols on the biaxial flexural strength, surface characteristics and phase transformation of zirconia after cyclic loading

This study evaluated the effect of air-particle abrasion protocols on the biaxial flexural strength, surface characteristics and phase transformation of zirconia after cyclic loading. Disc-shaped zirconia specimens (Ø: 15mm, thickness: 1.2mm) (N=32) were submitted to one of the air-particle abrasion protocols (n=8 per group): (a) 50μm Al2O3 particles, (b) 110μm Al2O3 particles coated with silica (Rocatec Plus), (c) 30μm Al2O3 particles coated with silica (CoJet Sand) for 20s at 2.8bar pressure. Control group received no air-abrasion. All specimens were initially cyclic loaded (×20,000, 50N, 1Hz) in water at 37°C and then subjected to biaxial flexural strength testing where the conditioned surface was under tension. Zirconia surfaces were characterized and roughness was measured with 3D surface profilometer. Phase transformation from tetragonal to monoclinic was determined by Raman spectroscopy. The relative amount of transformed monoclinic zirconia (FM) and transformed zone depth (TZD) were measured using XRD. The data (MPa) were analyzed using ANOVA, Tukey's tests and Weibull modulus (m) were calculated for each group (95% CI). The biaxial flexural strength (MPa) of CoJet treated group (1266.3±158A) was not significantly different than that of Rocatec Plus group (1179±216.4A,B) but was significantly higher than the other groups (Control: 942.3±74.6C; 50μm Al2O3: 915.2±185.7B,C). Weibull modulus was higher for control (m=13.79) than those of other groups (m=4.95, m=5.64, m=9.13 for group a, b and c, respectively). Surface roughness (Ra) was the highest with 50μm Al2O3 (0.261μm) than those of other groups (0.15-0.195μm). After all air-abrasion protocols, FM increased (15.02%-19.25%) compared to control group (11.12%). TZD also showed increase after air-abrasion protocols (0.83-1.07μm) compared to control group (0.59μm). Air-abrasion protocols increased the roughness and monoclinic phase but in turn abrasion with 30μm Al2O3 particles coated with silica has increased the biaxial flexural strength of the tested zirconia. © 2013 Elsevier Ltd.

Air-particle abrasion on zirconia ceramic using different protocols: Effects on biaxial flexural strength after cyclic loading, phase transformation and surface topography

This study evaluated the effect of different air-particle abrasion protocols on the biaxial flexural strength and structural stability of zirconia ceramics. Zirconia ceramic specimens (ISO 6872) (Lava, 3M ESPE) were obtained (N=336). The specimens (N=118, n=20 per group) were randomly assigned to one of the air-abrasion protocols: Gr1: Control (as-sintered); Gr2: 50 μm Al2O3 (2.5 bar); Gr3: 50 μm Al2O3 (3.5 bar); Gr4: 110 μm Al2O3(2.5 bar); Gr5: 110 μm Al2O3 (3.5 bar); Gr6: 30 μm SiO2 (2.5 bar) (CoJet); Gr7: 30 μm SiO2(3.5 bar); Gr8: 110 μm SiO2 (2.5 bar) (Rocatec Plus); and Gr9: 110 μm SiO2 (3.5 bar) (duration: 20 s, distance: 10 mm). While half of the specimens were tested immediately, the other half was subjected to cyclic loading in water (100,000 cycles; 50 N, 4 Hz, 37 °°C) prior to biaxial flexural strength test (ISO 6872). Phase transformation (t→m), relative amount of transformed monoclinic zirconia (FM), transformed zone depth (TZD) and surface roughness were measured. Particle type (p=0.2746), pressure (p=0.5084) and cyclic loading (p=0.1610) did not influence the flexural strength. Except for the air-abraded group with 110 μm Al2O3 at 3.5 bar, all air-abrasion protocols increased the biaxial flexural strength (MPa) (Controlnon-aged: 1030±153, Controlaged: 1138±138; Experimentalnon-aged: 1307±184-1554±124; Experimentalaged: 1308±118-1451±135) in both non-aged and aged conditions, respectively. Surface roughness (Ra) was the highest with 110 μm Al2O3(0.84 μm. FM values ranged from 0% to 27.21%, higher value for the Rocatec Plus (110 μm SiO2) and 110 μm Al2O3 groups at 3.5 bar pressure. TZD ranged between 0 and 1.43 μm, with the highest values for Rocatec Plus and 110 μm Al2O3 groups at 3.5 bar pressure. © 2013 Elsevier Ltd.

Simulation of the micro-physics of rocks using LSMearth

The particle-based Lattice Solid Model (LSM) was developed to provide a basis to study the physics of rocks and the nonlinear dynamics of earthquakes (MORA and PLACE, 1994; PLACE and MORA, 1999). A new modular and flexible LSM approach has been developed that allows different microphysics to be easily included in or removed from the model. The approach provides a virtual laboratory where numerical experiments can easily be set up and all measurable quantities visualised. The proposed approach provides a means to simulate complex phenomena such as fracturing or localisation processes, and enables the effect of different micro-physics on macroscopic behaviour to be studied. The initial 2-D model is extended to allow three-dimensional simulations to be performed and particles of different sizes to be specified. Numerical bi-axial compression experiments under different confining pressure are used to calibrate the model. By tuning the different microscopic parameters (such as coefficient of friction, microscopic strength and distribution of grain sizes), the macroscopic strength of the material and can be adjusted to be in agreement with laboratory experiments, and the orientation of fractures is consistent with the theoretical value predicted based on Mohr-Coulomb diagram. Simulations indicate that 3-D numerical models have different macroscopic properties than in 2-D and, hence, the model must be recalibrated for 3-D simulations. These numerical experiments illustrate that the new approach is capable of simulating typical rock fracture behaviour. The new model provides a basis to investigate nucleation, rupture and slip pulse propagation in complex fault zones without the previous model limitations of a regular low-level surface geometry and being restricted to two-dimensions.

Repair of segmental bone defects with fiber-reinforced composite: a study of material development and an animal model on rabbits

The Repair of segmental defects in load-bearing long bones is a challenging task because of the diversity of the load affecting the area; axial, bending, shearing and torsional forces all come together to test the stability/integrity of the bone. The natural biomechanical requirements for bone restorative materials include strength to withstand heavy loads, and adaptivity to conform into a biological environment without disturbing or damaging it. Fiber-reinforced composite (FRC) materials have shown promise, as metals and ceramics have been too rigid, and polymers alone are lacking in strength which is needed for restoration. The versatility of the fiber-reinforced composites also allows tailoring of the composite to meet the multitude of bone properties in the skeleton. The attachment and incorporation of a bone substitute to bone has been advanced by different surface modification methods. Most often this is achieved by the creation of surface texture, which allows bone growth, onto the substitute, creating a mechanical interlocking. Another method is to alter the chemical properties of the surface to create bonding with the bone – for example with a hydroxyapatite (HA) or a bioactive glass (BG) coating. A novel fiber-reinforced composite implant material with a porous surface was developed for bone substitution purposes in load-bearing applications. The material’s biomechanical properties were tailored with unidirectional fiber reinforcement to match the strength of cortical bone. To advance bone growth onto the material, an optimal surface porosity was created by a dissolution process, and an addition of bioactive glass to the material was explored. The effects of dissolution and orientation of the fiber reinforcement were also evaluated for bone-bonding purposes. The Biological response to the implant material was evaluated in a cell culture study to assure the safety of the materials combined. To test the material’s properties in a clinical setting, an animal model was used. A critical-size bone defect in a rabbit’s tibia was used to test the material in a load-bearing application, with short- and long-term follow-up, and a histological evaluation of the incorporation to the host bone. The biomechanical results of the study showed that the material is durable and the tailoring of the properties can be reproduced reliably. The Biological response - ex vivo - to the created surface structure favours the attachment and growth of bone cells, with the additional benefit of bioactive glass appearing on the surface. No toxic reactions to possible agents leaching from the material could be detected in the cell culture study when compared to a nontoxic control material. The mechanical interlocking was enhanced - as expected - with the porosity, whereas the reinforcing fibers protruding from the surface of the implant gave additional strength when tested in a bone-bonding model. Animal experiments verified that the material is capable of withstanding load-bearing conditions in prolonged use without breaking of the material or creating stress shielding effects to the host bone. A Histological examination verified the enhanced incorporation to host bone with an abundance of bone growth onto and over the material. This was achieved with minimal tissue reactions to a foreign body. An FRC implant with surface porosity displays potential in the field of reconstructive surgery, especially regarding large bone defects with high demands on strength and shape retention in load-bearing areas or flat bones such as facial / cranial bones. The benefits of modifying the strength of the material and adjusting the surface properties with fiber reinforcement and bone-bonding additives to meet the requirements of different bone qualities are still to be fully discovered.

Kylmälaitekoneikon runkorakenteen kehittäminen

Kylmälaitekoneikot ovat kylmäkomponentteja sisältäviä rakenteita, joiden avulla toteutetaan suurten tilojen, kuten elintarvikemyymälöiden sisäilman jäähdytys. Lisäksi koneikkojen avulla jäähdytetään matalampiin lämpötiloihin pienempiä kylmähuoneita. Osa koneikoista ottaa talteen kylmäprosessissa syntyvän lämmön, jota hyödynnetään tilojen lämmityksessä. Tämän diplomityön tavoitteena oli suunnitella ja mitoittaa kahdeksalle eri kylmälaitekoneikolle entistä kustannustehokkaammat runkorakenteet, jotka ovat niin kestäviä, että koneikkoja on mahdollista pinota tilan säästämiseksi kolme päällekkäin. Lisäksi runkorakenteilta vaadittiin helppoa kuljetettavuutta, hyviä kiinnitysominaisuuksia ja korroosionkestävyyttä. Aluksi työssä selvitettiin runkorakenteisiin kohdistuvat vaatimukset, jonka jälkeen materiaalin valinta tehtiin materiaaliin kohdistuvien vaatimusten perusteella. Rakenteiden palkit mitoitettiin tarvittavan taivutusvastuksen ja kiepahduksen mukaan. Pilarit puolestaan mitoitettiin nurjahduksen ja kaksiaksiaalisen taivutustilan perusteella. Tämän jälkeen mitoitettiin eri sauvojen väliset hitsi- ja ruuviliitokset siten, että rakenne hajoaa ylikuormitustilanteessa mahdollisimman turvallisesti. Työssä tehdyt laskelmat varmennettiin elementtimenetelmän avulla ja lopullisille rakenteille tehtiin elementtimenetelmällä vielä ominaistaajuusanalyysejä. Lopuksi työssä suunniteltiin runkorakenteille sopiva korroosionsuojaus.

Monolithic zirconium dioxide as a full contour restorative material: With special emphasis on the optical and mechanical properties

Full contour monolithic zirconia restorations have shown an increased popularity in the dental field over the recent years, owing to its mechanical and acceptable optical properties. However, many features of the restoration are yet to be researched and supported by clinical studies to confirm its place among the other indirect restorative materials This series of in vitro studies aimed at evaluating and comparing the optical and mechanical properties, light cure irradiance, and cement polymerization of multiple monolithic zirconia material at variable thicknesses, environments, treatments, and stabilization. Five different monolithic zirconia materials, four of which were partially stabilized and one fully stabilized were investigated. The optical properties in terms of surface gloss, translucency parameter, and contrast ratio were determined via a reflection spectrophotometer at variable thicknesses, coloring, sintering method, and after immersion in an acidic environment. Light cure irradiance and radiant exposure were quantified through the specimens at variable thicknesses and the degree of conversion of two dual-cure cements was determined via Fourier Transform Infrared spectroscopy. Bi-axial flexural strength was evaluated to compare between the partially and fully stabilized zirconia prepared using different coloring and sintering methods. Surface characterization was performed using a scanning electron microscope and a spinning disk confocal microscope. The surface gloss and translucency of the zirconia investigated were brand and thickness dependent with the translucency values decreasing as the thickness increased. Staining decreased the translucency of the zirconia and enhanced surface gloss as well as the flexural strength of the fully stabilized zirconia but had no effect on partially stabilized zirconia. Immersion in a corrosive acid increased surface gloss and decreased the translucency of some zirconia brands. Zirconia thickness was inversely related to the amount of light irradiance, radiant exposure, and degree of monomer conversion. Type of sintering furnace had no effect on the optical and mechanical properties of zirconia. Monolithic zirconia maybe classified as a semi-translucent material that is well influenced by the thickness, limiting its use in the esthetic zones. Conventional acid-base reaction, autopolymerizing and dual-cure cements are recommended for its cementation. Its desirable mechanical properties give it a high potential as a restoration for posterior teeth. However, close monitoring with controlled clinical studies must be determined before any definite clinical recommendations can be drawn.

Biomechanical Performance of Flexible Intramedullary Nails With End Caps Tested in Distal Segmental Defects of Pediatric Femur Models

Background: Unstable distal femoral fractures in children are challenging lesions with restricted surgical options for adequate stabilization. Elastic nails have become popular for treating femoral shaft fractures, yet they are still challenging for using in distal fractures. The aim of this study was to test whether end caps (CAP) inserted into the nail extremity improved the mechanical stabilization of a segmental defect at the distal femoral metaphyseal-diaphyseal junction created in an artificial pediatric bone model. Methods: Two 3.5-mm titanium elastic nails (TEN) were introduced intramedullary into pediatric femur models, and a 7.0-mm-thick segmental defect was created at the distal diaphyseal-metaphyseal junction. Nondestructive 4-point bending, axial-bending, and torsion tests were conducted. After this, the end caps were inserted into the external tips of the nails and then screwed into the bone cortex. The mechanical tests were repeated. Stiffness, displacement, and torque were analyzed using the Wilcoxon nonparametric test for paired samples. Results: In the combined axial-bending tests, the TEN + CAP combination was 8.75% stiffer than nails alone (P < 0.01); in torsion tests, the TEN + CAP was 14% stiffer than nails alone (P < 0.01). In contrast, the 4-point bending test did not show differences between the methods (P = 0.91, stiffness; P = 0.51, displacement). Thus, the end caps contributed to an increase in the construct stability for torsion and axial-bending forces but not for 4-point bending forces. Conclusions: These findings indicate that end caps fitted to elastic nails may contribute to the stabilization of fractures that our model mimics (small distal fragment, bone comminution, and distal bone fragment loss).

Bi-ventricular axial micropump: impact on blood cell integrity.

BACKGROUND AND OBJECTIVE: Off-pump coronary artery bypass grafting has stimulated the development of micro-pumps designed to prevent the hemodynamic instability induced by heart luxation for the exposure of target vessels of the posterior wall. Impella (Aachen, Germany) developed micro-pumps with a miniaturized propeller system for both sides of the heart. The aim of this study was to analyze the impact of both pumps working together on blood cell integrity. MATERIALS AND METHODS: Both right and left-sided micro-pumps were implanted in 5 calves (body weight, 72_4 Kg) during 3 h. Blood samples for hematology and hemolysis parameters were drawn hourly. RESULTS: Both pumps performed well with a flow of 3.6 L +/- 0.3 L during the 3 h of the experiment with stable hemodynamic conditions. Mixed venous oxygen saturation was 63.4 +/- 15.2% at baseline and 63.8 +/- 16.3% at the end of the experiment (P = ns). Red cell count, LDH and free plasma hemoglobin were 6.7 +/- 2.1 x 10(12)/L, 1807 +/- 437 IU/L, and 32 +/- 9 mg/L at baseline vs. 6.1 +/- 2.1 x 10(12)/L, 1871 +/- 410 IU/L, and 52 +/- 9 mg/L at the end of the experiment (P = ns for all comparisons). Platelet count exhibited a non-significant drop (872 +/- 126 vs. 715 +/- 22 x 10(9)/L). CONCLUSIONS: This double pump system based on the Archimed screw principle is hematologically well tolerated under conditions of prolonged cardiac assist.

Effect of combined bending strain and thermal cycling on the voltage-current characteristic curves of Bi-2223 tapes

High critical temperature superconductors are evolving from a scientific research subject into large-scale application devices. In order to meet this development demand they must withstand high current capacity under mechanical loads arising from thermal contraction during cooling from room temperature down to operating temperature (usually 77 K) and due to the electromagnetic forces generated by the current and the induced magnetic field. Among the HTS materials, the Bi2Sr2Ca2Cu3Ox, compound imbedded in an Ag/AgMg sheath has shown the best results in terms of critical current at 77 K and tolerance against mechanical strain. Aiming to evaluate the influence of thermal stress induced by a number of thermal shock cycles we have evaluated the V-I characteristic curves of samples mounted onto semicircular holders with different curvature radius (9.75 to 44.5 mm). The most deformed sample (epsilon = 1.08%) showed the largest reduction of critical current (40%) compared to the undeformed sample and the highest sensitivity to thermal stress (I-c/I-c0 = 0.5). The V-I characteristic curves were also fitted by a potential curve displaying n-exponents varying from 20 down to 10 between the initial and last thermal shock cycle.

Effect of mechanical loading on the I-c degradation behavior of Bi-2223 tapes

During the winding process of HTS coils the tapes of Bi-2223 are subjected to the influence of bending strain, axial strain, compressive force and torsional deformation resulting in I-c degradation. In the literature the effects of the individual strain components are separately analyzed in spite of during coil winding and energizing the strain-stress effects are combined. In this work using commercial tapes of Bi-2223 Ag/AgMg with and without stainless steel reinforcement several samples were wound on cylindrical FRP G-10 holder in which different combined strains are applied. Measurements of I - V characteristic curves are done to determine the degree of critical current degradation and the operational limits. The results are compared with the I, values of short samples and other specimens subjected to deformation generated by loading types such as tensile and bending strain.

Interaction between axial force, shear and bending moment in reinforced concrete elements

Il collasso di diverse colonne, caratterizzate da danneggiamenti simili, quali ampie fessure fortemente inclinate ad entrambe le estremità dell’elemento, lo schiacciamento del calcestruzzo e l’instabilità dei ferri longitudinali, ha portato ad interrogarsi riguardo gli effetti dell’interazione tra lo sforzo normale, il taglio ed il momento flettente. Lo studio è iniziato con una ricerca bibliografica che ha evidenziato una sostanziale carenza nella trattazione dell’argomento. Il problema è stato approcciato attraverso una ricerca di formule della scienza delle costruzioni, allo scopo di mettere in relazione lo sforzo assiale, il taglio ed il momento; la ricerca si è principalmente concentrata sulla teoria di Mohr. In un primo momento è stata considerata l’interazione tra solo due componenti di sollecitazione: sforzo assiale e taglio. L’analisi ha condotto alla costruzione di un dominio elastico di taglio e sforzo assiale che, confrontato con il dominio della Modified Compression Field Theory, trovata tramite ricerca bibliografica, ha permesso di concludere che i risultati sono assolutamente paragonabili. L’analisi si è poi orientata verso l’interazione tra sforzo assiale, taglio e momento flettente. Imponendo due criteri di rottura, il raggiungimento della resistenza a trazione ed a compressione del calcestruzzo, inserendo le componenti di sollecitazione tramite le formule di Navier e Jourawsky, sono state definite due formule che mettono in relazione le tre azioni e che, implementate nel software Matlab, hanno permesso la costruzione di un dominio tridimensionale. In questo caso non è stato possibile confrontare i risultati, non avendo la ricerca bibliografica mostrato niente di paragonabile. Lo studio si è poi concentrato sullo sviluppo di una procedura che tenta di analizzare il comportamento di una sezione sottoposta a sforzo normale, taglio e momento: è stato sviluppato un modello a fibre della sezione nel tentativo di condurre un calcolo non lineare, corrispondente ad una sequenza di analisi lineari. La procedura è stata applicata a casi reali di crollo, confermando l’avvenimento dei collassi.

A theory for the effect of mean stress on fatigue of metals under combined torsion and axial load or bending.

"Department of Army Project no. 5B99-01-004, Ordnance R and D Project no. TB2-0001, Office of Ordnance Research Project no. 1348, Contract no. DA-19-020-ORD-3250."

Axial tension and bending interaction curves for members loaded inelastically,

Mode of access: Internet.

Effects of Shallow Bi-Angle, Thin-Ply Laminates on the Structural Performance of Composite Wings

Thesis (Master's)--University of Washington, 2016-06