Heroes on the home front : heroism and virtue in post-9/11 American cinema /

This thesis is intended to contribute to critical discussion of the American male hero in mainstream American war and action films post September 11, 2001 . The thesis investigates how these heroes' behaviour echoes a patriotic, conservative construction of the modern American as created through speeches given by George W. Bush in the wake of the events of September 11, 2001 . The thesis examines the hero in six primary sources: the war films We Were Soldiers, Behind Enemy Lines and The Great Raid and the action films Collateral Damage, Man on Fire and The Punisher. By analyzing the ideological subtext, political content, visual strategies and generic implications of the films, as well as the binary constructions of a selection of Bush speeches, and by reviewing historical representations of American male heroes on film produced in the wake of political events, the thesis concludes that the six films mobilize the USA's conservative viewpoint towards war and military action, and in concert with the speeches, contribute to an ongoing militarization of visual culture. Both systems echo a dangerous ideological fantasy of American history, life and patriotism.

Le cinéma d'animation : avènement d'une institution et naissance d'une industrie

Les premiers comptes rendus de l’histoire du cinéma ont souvent considéré les premiers dessins animés, ou vues de dessins animés, comme des productions différentes des films en prise de vue réelle. Les dessins animés tirent en effet leurs sources d’inspiration d’une gamme relativement différente d’influences, dont les plus importantes sont la lanterne magique, les jouets optiques, la féérie, les récits en images et les comics. Le dessin animé n’en demeure pas moins fondamentalement cinématographique. Les vues de dessins animés de la décennie 1900 ne se distinguent ainsi guère des scènes à trucs sur le plan de la technique et du style. D’abord le fait de pionniers issus de l’illustration comique et du croquis vivant comme Émile Cohl, James Stuart Blackton et Winsor McCay, le dessin animé s’industrialise au cours de la décennie 1910 sous l’impulsion de créateurs venant du monde des comics, dont John Randolph Bray, Earl Hurd, Paul Terry et Max Fleisher. Le processus d’institutionnalisation par lequel le dessin animé en viendra à être considéré comme une catégorie de film à part entière dépend en grande partie de cette industrialisation. Les studios de dessins animés développent des techniques et pratiques managériales spécifiquement dédiées à la production à grande échelle de films d’animation. Le dessin animé se crée ainsi sa propre niche au sein d’une industrie cinématographique dont il dépend toutefois toujours entièrement. Ce phénomène d’individuation repose sur des formules narratives et des personnages récurrents conçus à partir de modèles issus des comics des années 1910.

SiO2 nanoparticles as scatterers for random organic laser action in red fluorescent dye 4-(dicyanomethylene)-2-tert-butyl-6(1,1,7,7-tetramethyljulolidyl-9-enyl)-4H-pyran doped polystyrene films

Random multimode lasers are achieved in 4-(dicyanomethylene)-2-tert-butyl-6(1,1,7,7-tetramethyljulolidyl-9-enyl)-4H-pyran (DCJTB) doped polystyrene thin films by introducing silicon dioxide (SiO2) nanoparticles as scatterers. The devices emit a resonance multimode peak at a center wavelength of 640 nm with a mode linewidth less than 0.87 nm. The threshold excitation intensity is as low as 0.25 mJ pulse(-1) cm(-2). It can be seen that the microscopic random resonance cavities can be formed by multiple scattering of SiO2 nanoparticles.

Action of soil microorganisms on PCL and PHBV blend and films

Poly(hydroxybutyrate-co-valerate) (PHBV) and poly(epsilon-caprolactone) (PCL) PCL/PHBV (4:1) blend films were prepared by melt-pressing. The biodegradation of the films in response to burial in soil for 30 days was investigated by Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), differential scanning calorimetry (DSC) and thermogravimetry (TG). The PHBV film was the most susceptible to microbial attack, since it was rapidly biodegraded via surface erosion in 15 days and completely degraded in 30 days. The PCL film also degraded but more slowly than PHBV. The degradation of the PCL/PHBV blend occurred in the PHBV phase, inducing changes in the PCL phases (interphase) and resulting in an increase of its crystalline fraction.

Action and Adventure

This chapter discusses the history of action and adventure films in Australian cinema. It focuses on those films starring Australian actors who have gained international fame, and on those films featuring a female protagonist.

SiC-like phase and room-temperature photoluminescence of low-k SiOCH films

Carbon-doped hydrogenated silicon oxide (SiOCH) low-k films have been prepared using 13.56 MHz discharge in trimethylsilane (3MS) - oxygen gas mixtures at 3, 4, and 5 Torr sustained with RF power densities 1.3 - 2.6 W/cm2. The atomic structure of the SiOCH films appears to be a mixture the amorphous SiO2-like and the partially polycrystalline SiC-like phases. Results of the infra-red spectroscopy reflect the increment in the volume fraction of the SiC-like phase from 0.22 - 0.28 to 0.36 - 0.39 as the RF power increment. Steady-state near-UV laser-excited (364 nm wavelength, 40±2 mW) photoluminescence (PL) has been studied at room temperatures in the visible (1.8 eV - 3.1 eV) subrange of photon spectrum. Two main bands of the PL signal (at the photon energies of 2.5 - 2.6 eV and 2.8 - 2.9 eV) are observed. Intensities of the both bands are changed monotonically with RF power, whereas the bandwidth of ∼0.1 eV remains almost invariable. It is likely that the above lines are dumped by the non-radiative recombination involving E1-like centres in the amorphous-nanocrystalline SiC-like phases. Such explanation of the PL intensity dependences on the RF power density is supported by results of experimental studies of defect states spectrum in bandgap of the SiOCH films.

Sensing Shape Recovery Using Conductivity Noise in Thin Films of NiTi Shape Memory Alloys

Low frequency fluctuations in the electrical resistivity, or noise, have been used as a sensitive tool to probe into the temperature driven martensite transition in dc magnetron sputtered thin films of nickel titanium shape-memory alloys. Even in the equilibrium or static case, the noise magnitude was more than nine orders of magnitude larger than conventional metallic thin films and had a characteristic dependence on temperature. We observe that the noise while the temperature is being ramped is far larger as compared to the equilibrium noise indicating the sensitivity of electrical resistivity to the nucleation and propagation of domains during the shape recovery. Further, the higher order statistics suggests the existence of long range correlations during the transition. This new characterization is based on the kinetics of disorder in the system and separate from existing techniques and can be integrated to many device applications of shape memory alloys for in-situ shape recovery sensing.

Effect of porosity on the indentation behaviour of nanoporous alumina films

Anodising aluminium in an acid electrolyte results in a porous alumina film. The pores are uniformly distributed and their structure can be controlled by varying the anodising parameters. In this study, the pore structure of the anodic alumina films is varied systematically by varying the anodising time and a subsequent pore widening chemical etch. The indentation behaviour of the resulting film is studied using a depth sensing nanoindenter. The hardness of the films was found to be decreasing with decreasing solid area fraction. Understanding the deformation behaviour of nanoporous alumina would help tailoring the mechanical properties by tuning the geometry.

Nanoindentation studies in NiTi films deposited on Si wafer

Nanoindentation tests were carried out at different locations in a Ti rich NiTi film deposited on a 3 `' silicon wafer by dc magnetron sputtering. The purpose of doing nanoindentation at different locations was to check the uniformity of the sample with respect to its mechanical behaviour and shape memory effect. The results showed that elastic modulus and hardness measured by nanoindentation was similar at different locations in the 3 `' wafer. Nanoindcntation coupled with depth profiling of residual indents using AFM also showed that the extent of shape memory recovery obtained by heating the film above its martensite to austcnite phase transformation temperature was also similar at different locations in the 3 `' wafer. However, the measured recovery ratio was lower than that predicted from theoretical calculations for indents made using Berkovich indenter. The results showed that the deposition process resulted in a NiTi film with uniform composition, mechanical properties and shape memory behaviour.

Formation of amorphous xenon nanoclusters and microstructure evolution in pulsed laser deposited Ti(62.5)Si(37.5) thin films during Xe ion irradiation

As deposited amorphous and crystallized thin films of Ti 37.5% Si alloy deposited by pulsed laser ablation technique were irradiated with 100 keV Xe(+) ion beam to an ion fluence of about 10(16) ions-cm(-2). Transmission electron microscopy revealed that the implanted Xe formed amorphous nanosized clusters in both cases. The Xe ion-irradiation favors nucleation of a fcc-Ti(Si) phase in amorphous films. However, in crystalline films, irradiation leads to dissolution of the Ti(5)Si(3) intermetallic phase. In both cases, Xe irradiation leads to the evolution of similar microstructures. Our results point to the pivotal role of nucleation in the evolution of the microstructure under the condition of ion implantation.

A General Route to Nanoparticle Thin Films and Coatings

Nanoparticles thin films have wide range of applications such as nanoelectronics, magnetic storage devices, SERS substrate fabrication, optical grating and antireflective coating. Present work describes a method to prepare large area nanoparticles thin film of the order of few square centimeters. Thin film deposition has been done successfully on a wide range of conducting as well as non conducting substrates such as carbon-coated copper grid, silicon, m-plane of alumina, glass and (100) plane of NaCl single crystal. SEM, TEM and AFM studies have been done for microstructural characterization of the thin films. A basic mechanism has been proposed towards the understanding of the deposition process.

Properties of Al2O3 films prepared by argon ion assisted deposition

Aluminum oxide films have been prepared by ion assisted deposition using argon ions with energy in the range 300 to 1000 eV and current density in the range 50 to 220 μA/cm2. The influence of ion energy and current density on the optical and structural properties has been investigated. The refractive index, packing density, and extinction coefficient are found to be very sensitive to the ion beam parameters and substrate temperatures. The as-deposited films were found to be amorphous and could be transformed into crystalline phase on annealing. However, the crystalline phases were different in films prepared at ambient and elevated substrate temperatures.

Evolution of metastable phases during crystallization of pulsed laser deposited amorphous Al–Fe films

Amorphous thin films of different Al–Fe compositions were produced by plasma/vapor quenching during pulsed laser deposition. The chosen compositions Al72Fe28, Al40Fe60, and Al18Fe82 correspond to Al5Fe2 and B2-ordered AlFe intermetallic compounds and α–Fe solid solution, respectively. The films contained fine clusters that increased with iron content. The sequences of phase evolution observed in the heating stage transmission electron microscopy studies of the pulsed laser ablation deposited films of Al72Fe28, Al40Fe60, and Al18Fe82 compositions showed evidence of composition partitioning during crystallization for films of all three compositions. This composition partitioning, in turn, resulted in the evolution of phases of compositions richer in Fe, as well as richer in Al, compared to the overall film composition in each case. The evidence of Fe-rich phases was the B2 phase in Al72Fe28 film, the L12- and DO3-ordered phases in Al40Fe60 film, and the hexagonal ε–Fe in the case of the Al18Fe82 film. On the other hand, the Al-rich phases were Al13Fe4 for both Al72Fe28 and Al40Fe60 films and DO3 and Al5Fe2 phases in the case of Al18Fe82 film. We believe that this tendency of composition partitioning during crystallization from amorphous phase is a consequence of the tendency of clustering of the Fe atoms in the amorphous phase during nucleation. The body-centered cubic phase has a nucleation advantage over other metastable phases for all three compositions. The amorphization of Al18Fe82 composition and the evolution of L12 and ε–Fe phases in the Al–Fe system were new observations of this work.