Infiltration of Al2O3/Y2O3 mix into SiC ceramic preforms

Silicon carbide ceramics are very interesting materials to engineering applications because of their properties. These ceramics are produced by liquid phase sintering (LPS), where elevated temperature and time are necessary, and generally form volatile products that promote defects and damage their mechanical properties. In this work was studied the infiltration process to produce SiC ceramics, using shorter time and temperature than LPS, thereby reducing the undesirable chemical reactions. SiC powder was pressed at 300 MPa and pre-sintered at 1550 degrees C for 30 min. Unidirectional and spontaneous infiltration of this preform by Al2O3/Y2O3 liquid was done at 1850 degrees C for 5, 10, 30 and 60 min. The kinetics of infiltration was studied, and the infiltration equilibrium happened when the liquid infiltrated 12 mm into perform. The microstructures show grains of the SiC surrounded by infiltrated additives. The hardness and fracture toughness are similar to conventional SiC ceramics obtained by LPS. (c) 2007 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Improvement of the electrolytic properties of Y2O3-based materials using a crystallographic index

Y2O3 is a c-type rare earth oxide with a fluorite-related structure. This material has been used to refractory because of its high thermal stability and excellent resistance to hydration. In this study, the effective index was suggested in order to improve the electrolytic properties of Y2O3-based oxide. (CexY1-x)(2)O3+delta (x = 0.25 and 0.3) and [LaaSrbCe0.25Y(1-a-b)](2)O3+delta (a = 0.05, 0.1 and 0.15, b = 0, 0.006 and 0.0125) were prepared as the examples with intermediate and high index, respectively. The specimens with high index value such as (La0.15Ce0.25Y0.60)(2)O-3.25 and (La0.1Sr0.0125Ce0.25Y0.6375)(2)O-3.24 consisted of two phases such as c-type and fluorite, although (Ce0.25Y0.75)(2)O-3.25 with intermediate index value had a single phase of c-type rare earth oxide. Microanalysis indicates that a grain in the (La0.1Sr0.0125Ce0.25Y0.6375)(2)O-3.23(7) sintered body consists of c-type and fluorite phases. An interface between c-type and fluorite phases is coherent in a grain. This suggests that this effective index guides the crystal structure in the specimen to fluorite and the examined composition introduces the interface between c-type and fluorite in the microstructure. The electrochemical properties of specimens including Y2O3 were characterized on the basis of the suggested index. The electrical conductivity of Y2O3-based materials increased with an increase of the index. The apparent activation energy of Y2O3-based materials decreased with increasing index. The ionic transport number of oxygen of the specimens was improved by enhancement of the index, confirming validity of the index. The oxide ionic conductive region of (La0.1Sr0.0125Ce0.25Y0.(6375))(2)O-3.23(7) with high effective index extended up to P-O2 = 10(-18) atm at 800 degreesC, although the specimens with low or intermediate index showed p- or n-type semi-conduction in the same P-O2 region at 800 and 1000 degreesC. These results suggest that the interface between c-type and fluorite phases also contributes to improve the electrolytic properties in the grain. It is concluded that the improvement of electrolytic properties in Y2O3-based materials is attributable to the microstructure with interface between two phases in a grain and the fluorite structure guided by the suggested index. (C) 2001 Published by Elsevier Science B.V.

Efeito do teor em Y2O3 nos catalisadores suportados de 8%Ni/α-Al2O3 durante a reação de oxidação parcial do Metano para produção de Hidrogénio

Neste trabalho avaliou-se o desempenho de cinco catalisadores de Níquel suportados em α-Alumina, com diferentes teores em Ítria, durante a reação de Oxidação Parcial do Metano para a produção de Hidrogénio: 8%Ni/α-Al2O3, 8%Ni/2%Y2O3.α-Al2O3, 8%Ni/2,5%Y2O3.α-Al2O3, 8%Ni/5%Y2O3.α-Al2O3 e 8%Ni/Y2O3. Foram realizados testes catalíticos numa Unidade de Reação acoplada a um equipamento de análise, microGC. A reação decorreu à temperatura de 800 °C, num reator laboratorial de quartzo, durante 18 horas, com uma mistura pura de CH4 e O2 (Condição Concentrada). Os resultados demonstraram um aumento de atividade para os catalisadores de suporte misto com maior teor em Y2O3. Usando o mesmo procedimento, a reação de OPM foi realizada também para outra mistura reacional de CH4 e O2, mas agora diluída em Hélio (Condição Diluída). Estes resultados permitiram avaliar a velocidade de reação e a atividade dos catalisadores (TOF), para diferentes valores de temperatura, numa situação inicial de ausência de coque. Numa segunda etapa, avaliou-se o desempenho dos mesmos materiais durante 2 horas de reação à temperatura constante de 800 ℃. Finalmente, através da técnica de caraterização de XPS, identificaram-se as espécies presentes na superfície dos catalisadores. Os resultados sugerem que há formação de um composto intermediário NiYO3 formado entre o metal e o promotor Y2O3, conferindo atividade e estabilidade aos catalisadores e reduzindo a deposição de coque. O catalisador com maior teor em Y2O3 (8%Ni/5%Y2O3.α-Al2O3) foi o mais beneficiado com a adição do promotor, demonstrando melhor desempenho para a produção de H2 na Reação de Oxidação Parcial do Metano.

Electron donor sites on Y2O3 catalyst as a function of the activation temperature

Cochin University of Science and Technology

Surface Electron Donor Properties of Dy2O3,Y2O3 and Their Mixed Oxides with Alumina Catalyst

The limit of electron transfer in electron affinity from the oxide surface to the electron acceptor (EA) are reported from the adsorption of EA on DY203, mixed oxides of DY203 with alumina and mixed oxides of Y203 with y-alumina. The extent of electron transfer is understood from magnetic measurements.

Nickel catalysts supported on ZrO2, Y2O3-stabilized ZrO2 and CaO-stabilized ZrO2 for the steam reforming of ethanol: Effect of the support and nickel load

Catalysts with various nickel loads were prepared on supports of ZrO2, ZrO2-Y2O3 and ZrO2-CaO, characterized by XRD and TPR and tested for activity in ethanol steam reforming. XRD of the supports identified the monoclinic crystalline phase in the ZrO2 and cubic phases in the ZrO2-Y2O3 and ZrO2-CaO supports. In the catalysts, the nickel impregnated on the supports was identified as the NiO phase. In the TPR analysis, peaks were observed showing the NiO phase having different interactions with the supports. In the catalytic tests, practically all the catalysts achieved 100% ethanol conversion, H-2 yield was near 70% and the gaseous concentrations of the other co-products varied in accordance with the equilibrium among them, affected principally by the supports. It was observed that when the ZrO2 was modified with Y2O3 and CaO, there were big changes in the CO and CO2 concentrations, which were attributed to the rise in the number of oxygen vacancies, permitting high-oxygen mobility and affecting the gaseous equilibrium. The liquid products analysis showed a low selectivity to liquid co-products during the reforming reactions. (c) 2007 Published by Elsevier B.V.

The effect of Eu3+ concentration on the Y2O3 host lattice obtained from citrate precursors

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Film based on Y2O3: Eu3+ (5 mol% of Eu3+) for flat panel display

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Photolumiscent Properties of Nanorods and Nanoplates Y2O3:Eu3+

Nanorods and nanoplates of Y2O3:Eu3+ powders were synthesized through the thermal decomposition of the Y(OH)(3) precursors using a microwave-hydrothermal method in a very short reaction time. These powders were analyzed by X-ray diffraction, field emission scanning electron microscopy, Fourrier transform Raman, as well as photoluminescence measurements. Based on these results, these materials presented nanoplates and nanorods morphologies. The broad emission band between 300 and 440 nm ascribed to the photoluminescence of Y2O3 matrix shifts as the procedure used in the microwave-hydrothermal assisted method changes in the Y2O3:Eu3+ samples. The presence of Eu3+ and the hydrothermal treatment time are responsible for the band shifts in Y2O3:Eu3+ powders, since in the pure Y2O3 matrix this behavior was not observed. Y2O3:Eu3+ powders also show the characteristic Eu3+ emission lines at 580, 591, 610, 651 and 695 nm, when excited at 393 nm. The most intense band at 610 nm is responsible for the Eu3+ red emission in these materials, and the Eu3+ lifetime for this transition presented a slight increase as the time used in the microwave-hydrothermal assisted method increases.

Y2O3:Eu3+ (5 mol%) with Ag nanoparticles prepared by citrate precursor

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of the substitution of Y2O3 for CeO2 on the mechanical and microstructural properties of silicon nitride

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Synthesis, characterization and catalytic properties of nanocrystaline Y2O3-coated TiO2 in the ethanol dehydration reaction

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Efeito da microestrutura na cintilação de nanopartículas de Y2O3 : EU3+

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Er3+-doped Y2O3 obtained by polymeric precursor: Synthesis, structure and upconversion emission properties

The relentless pursuit for materials containing rare earth ions with photoluminescent properties has led to several studies with applications in the development of new technologies. The main focus of this work is the preparation of Er3+-doped polycrystalline Y2O3 with photoluminescent properties using PEG as an organic precursor and heat-treated at different temperatures. The methodology used in this synthesis is highly attractive due to its high feasibility for improved technology and low cost for preparing materials. The behavior of the viscous resin has been evaluated and the final compounds exhibited the formation of a cubic polycrystalline phase, which is able to support variations in Er3+ doping concentrations up to 10 mol%, without significant changes in the polycrystalline parameters. The values of the nanocrystallite size calculated by Scherrer's equation showed direct dependence on the heat-treatment temperature as well as the Er3+ concentration. Intense emission in the visible region under excitation at 980 nm was attributed to an upconversion phenomenon assigned to the intraconfigurational f-f transitions of Er3+ ions. The upconversion mechanism was investigated and it was demonstrated that the higher intense emission in the red region in comparison to the emission in the green region is related to the crystallite size. The studies about the intensity showed the dependence of upconversion emission of power source, indicating that two-photon are responsible for the green and red photoluminescence. These polycrystalline materials exhibit properties that make them promising for use in solar energy systems, C-telecom band or solid-state laser devices. (C) 2014 Elsevier B.V. All rights reserved.