Influence of processing temperature on microstructure and microhardness of copper subjected to high-pressure torsion

Cu samples were subjected to high-pressure torsion (HPT) with up to 6 turns at room temperature (RT) and liquid nitrogen temperature (LNT), respectively. The effects of temperature on grain refinement and microhardness variation were investigated. For the samples after HPT processing at RT, the grain size reduced from 43 mu m to 265 nm, and the Vickers microhardness increased from HV52 to HV140. However, for the samples after HPT processing at LNT, the value of microhardness reached its maximum of HV150 near the center of the sample and it decreased to HV80 at the periphery region. Microstructure observations revealed that HPT straining at LNT induced lamellar structures with thickness less than 100 nm appearing near the central region of the sample, but further deformation induced an inhomogeneous distribution of grain sizes, with submicrometer-sized grains embedded inside micrometer-sized grains. The submicrometer-sized grains with high dislocation density indicated their nonequilibrium nature. On the contrary, the micrometer-sized grains were nearly free of dislocation, without obvious deformation trace remaining in them. These images demonstrated that the appearance of micrometer-sized grains is the result of abnormal grain growth of the deformed fine grains.

Laser induced surface damage, thermal transport and microhardness studies on certain organic and semiorganic nonlinear optical crystals

N-alkyl-2,6-dimethyl-4(1H)-pyridinones, salts of 4-dimethylaminopyridine and 2-amino-5-nitropyridine are considered to be potential candidates for nonlinear optical (NLO) applications, in particular for the generation of blue-green laser radiation. Single crystals were grown following the slow evaporation technique at constant temperature. Single-shot laserinduced surface damage thresholds in the range 3–10 GW/cm2 were measured using a 18 ns Q-switched Nd:YAG laser. The surface morphologies of the damaged crystals were examined under an optical microscope and the nature of damage identified. The Vicker’s microhardness was determined at a load of 98.07 mN. The thermal transport properties, thermal diffusivity (α), thermal effusivity (e), thermal conductivity (K) and heat capacity (Cp), of the grown crystals were measured by an improved photopyroelectric technique at room temperature. All the results are presented and discussed.

Dentine microhardness after different methods for detection and removal of carious dentine tissue

There are several methods for identifying carious dentinal tissue aiming to avoid removal of healthy dentinal tissue. Objectives: The purpose of this study was to test different methods for the detection of carious dentinal tissue regarding the amount of carious tissue removed and the remaining dentin microhardness after caries removal. Material and methods: The dentin surfaces of 20 bovine teeth were exposed and half of the surface was protected with nail polish. Cariogenic challenge was performed by immersion in a demineralizing solution for 14 days. After transverse cross-section of the crown, the specimens were divided into four groups (n=10), according to the method used to identify and remove the carious tissue: "Papacarie", Caries-detector dye, DIAGNOdent and Tactile method. After caries removal, the cross-sectional surface was included in acrylic resin and polished. In a microhardness tester, the removed dentin thickness and the Vickers microhardness of the following regions were evaluated: remaining dentin after caries removal and superficial and deep healthy dentin. Results: ANOVA and Tukey's test (alpha=0.05) were performed, except for DIAGNOdent, which did not detect the presence of caries. Results for removed dentin thickness were: "Papacarie" (424.7 +/- 105.0; a), Caries-detector dye (370.5 +/- 78.3; ab), Tactile method (322.8 +/- 51.5; bc). Results for the remaining dentin microhardness were: "Papacarie" (42.2 +/- 10.5; bc), Caries-detector dye (44.6 +/- 11.8; bc), Tactile method (24.3 +/- 9.0; d). Conclusions: DIAGNOdent did not detect the presence of carious tissue; Tactile method and "Papacarie" resulted in the least and the most dentinal thickness removal, respectively; Tactile method differed significantly from "Papacarie" and Caries-detector dye in terms of the remaining dentin microhardness, and Tactile method was the one which presented the lowest microhardness values.

Influence of Remineralizing Gels on Bleached Enamel Microhardness In Different Time Intervals

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Thermocycling effect on microhardness of laboratory composite resins

Tha aim of this study was to evaluate the thermocycling effect on microhardness of laboratory composite resins, 30 disks were fabricated, 5mm of diameter and 2mm of width, using 3 laboratory resins: G1 (n=10) - RESILAB MASTER (Wilcos-Brasil), G2 (n=10) - Vita VMLC (VITA Zahnfabrik-Germany), and G3 (n=10) - Vita Zeta (VITA Zahnfabrik-Germany). Vickers microhardness (HV) of all specimens was evaluated using a microhardness tester FM-700 (Future Tech- 50 g/10s). The specimens were measured before and after the thermocycling (3,000 times and 12,000 times - 5°/55°C±1). The microhardness values before cycling were (mean±SD): G1: 55.50±4.6; G2: 35.54±2.5; G3: 27.97±1.6; after 3,000 thermocycles: G1: 55.54±3.9; G2: 29.92±2.73; G3:21.01±1.4 and after 12,000 cycles G1: 54.27±3.2; G2: 30.91±1.6; G3: 23.81±0.9. Variance analysis (ANOVA) and Tukey's test was accomplished (p<0.05), the highest microhardness values were observed in G1: G2 and G3 showed reduction of microhardness values. It was concluded that, after thermocycling, the tested laboratory composites resins are susceptible to the decrease of surface microhardness.

Microhardness assessment of different commercial brands of resin composites with different degrees of translucence

Owing to improvements in its mechanical properties and to the availability of shade and translucence resources, resin composite has become one of the most widely used restorative materials in present day Dentistry. The aim of this study was to assess the relation between the surface hardness of seven different commercial brands of resin composites (Charisma, Fill Magic, Master Fill, Natural Look, Opallis, Tetric Ceram, and Z250) and the different degrees of translucence (translucid, enamel and dentin). Vickers microhardness testing revealed significant differences among the groups. Z250 was the commercial brand that showed the best performance in the hardness test. When comparing the three groups assessed within the same brand, only Master Fill and Fill Magic presented statistically significant differences among all of the different translucencies. Natural Look was the only one that showed no significant difference among any of the three groups. Charisma, Opallis, Tetric Ceram and Z250 showed significant differences among some of the tested groups. Based on the results found in this study, it was not possible to establish a relation between translucence and the microhardness of the resin composites assessed. Depending on the material assessed, however, translucence variation did affect the microhardness values of the resin composites.

Microhardness of dual-polymerized resin cement around a translucent fiber post in the intraradicular environment

Aim: In this study, we evaluated the effect of photopolymerization on Vickers microhardness of dual-polymerized resin cement at three locations when a translucent quartz fiber post was used. Materials and Methods: Single-rooted bovine teeth received quartz fiber post systems (length: 12 mm) using a dual-polymerized resin cement. In Group 1, the posts were cemented but not photopolymerized, and in Group 2, the posts were both cemented and photopolymerized. After cementation, approximately 1.5-mm thick sections were obtained (two cervical, two middle, and two apical) for regional microhardness evaluations. Statistical Analysis: Statistical analyses were performed using the SPSS software (ver. 11.0 for Windows; SPSS, Inc., Chicago, IL, USA). Microhardness (kg/mm 2 ) data were submitted to two-way analysis of variance (two-way ANOVA) and repeated measures with microhardness values as the dependent variable and polymerization status (two levels: with and without) and root region (three levels: cervical, middle, and apical) as independent variables. Multiple comparisons were made using Dunnett's T3 post-hoc test. P values of <0.05 were considered to indicate statistical significance in all tests. Results: Photopolymerization did not significantly change the microhardness values when compared with no photopolymerization. Microhardness values also showed no significant difference between the three regions in the root canals in both groups. Conclusions: The mode of polymerization of the cement tested in combination with the translucent quartz fiber post system did not affect the microhardness of the cement at the cervical, middle, or apical regions of the root.

Effect of carbamide peroxide bleaching gel on composite resin flexural strength and microhardness

This study investigated the effect of 16% carbamide peroxide (Whiteness Perfect/FGM) on the Vickers microhardness and flexural strength of the restorative composites Filtek Z100 (hybrid), Filtek Z350 (nanofill), Brilliant (micro-hybrid) and Opallis (micro-hybrid). Discshaped (4×2 mm; n=5) and bar-shaped (12×2×1 mm; n=10) specimens of each restorative material were randomly divided into 2 groups: (G1) 16 weeks stored in distilled water; (G2) 16 weeks stored in distilled water, with 16% carbamide peroxide application during 6 h per day for the last 4 weeks. The mechanical properties were evaluated using a Vickers microhardness tester and a mechanical testing machine. Data were analyzed by twoway ANOVA and Tukey's (HSD) post-hoc test (α=0.05). Filtek Z100 presented the highest microhardness value, followed by Filtek Z350 and finally by Brilliant and Opallis (p=0.00). Filtek Z100 and Brilliant exhibited the highest flexural strength value, followed by Filtek Z350 and Opallis (p=0.00). Bleaching treatment decreased significantly microhardness of Brilliant and Opallis (p=0.00). The flexural strength of all studied materials was not affected by the home bleaching (p=0.28).

Avaliação por microdureza Vickers da profundidade de polimerização de cimentos resinosos na cimentação de pinos de fibra de vidro empregando diferentes fontes de luz

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influence of increment thickness on microhardness and dentin bond strength of bulk fill resin composites

OBJECTIVES To investigate the influence of increment thickness on Vickers microhardness (HV) and shear bond strength (SBS) to dentin of a conventional and four bulk fill resin composites. METHODS HV and SBS were determined on specimens of the conventional resin composite Filtek Supreme XTE (XTE) and the bulk fill resin composites SDR (SDR), Filtek Bulk Fill (FBF), x-tra fil (XFIL), and Tetric EvoCeram Bulk Fill (TEBF) after 24h storage. HV was measured either as profiles at depths up to 6mm or at the bottom of 2mm/4mm/6mm thick resin composite specimens. SBS of 2mm/4mm/6mm thick resin composite increments was measured to dentin surfaces of extracted human molars treated with the adhesive system OptiBond FL, and the failure mode was stereomicroscopically determined at 40× magnification. HV profiles and failure modes were descriptively analysed whereas HV at the bottom of resin composite specimens and SBS were statistically analysed with nonparametric ANOVA followed by Wilcoxon rank sum tests (α=0.05). RESULTS HV profiles (medians at 2mm/4mm/6mm): XTE 105.6/88.8/38.3, SDR 34.0/35.5/36.9, FBF 36.4/38.7/37.1, XFIL 103.4/103.9/101.9, TEBF 63.5/59.7/51.9. HV at the bottom of resin composite specimens (medians at 2mm/4mm/6mm): XTE (p<0.0001) 105.5>85.5>31.1, SDR (p=0.10) 25.8=21.9=26.0, FBF (p=0.16) 26.6=25.3=28.9, XFIL (p=0.18) 110.5=107.2=101.9, TEBF (p<0.0001) 63.0>54.9>48.2. SBS (MPa, medians at 2mm/4mm/6mm): XTE (p<0.0001) 23.9>18.9=16.7, SDR (p=0.26) 24.6=22.7=23.4, FBF (p=0.11) 21.4=20.3=22.0, x-tra fil (p=0.55) 27.0=24.0=23.6, TEBF (p=0.11) 21.0=20.7=19.0. The predominant SBS failure mode was cohesive failure in dentin. SIGNIFICANCE At increasing increment thickness, HV and SBS decreased for the conventional resin composite but generally remained constant for the bulk fill resin composites.

Microstructure and dry sliding wear resistance evaluation of plasma nitrided austenitic stainless steel type AISI 316LN against different sliders

In this work, Plasma Nitriding was carried out at a temperature of 570 degrees C on nuclear grade austenitic stainless steel type AISI 316 LN (316LN SS) in a gas mixture of 20% N-2-80% H-2 to improve the surface hardness and thereby sliding wear resistance. The Plasma Nitride (PN) treated surface has been characterized by Vickers microhardness measurements, Scanning Electron Microscopic (SEM) examination, X-ray Diffraction (XRD) and sliding wear assessment. The average thickness of the PN layer was found to be 70 mu m. Microhardness measurements showed a significant increase in the hardness from 210 HV25g (unnitrided sample) to 1040 HV25g (Plasma Nitrided sample). The XRD reveals that PN layer consists of CrN, Fe4N and Fe3N phases along with austenite phase. The tribological parameters such as the friction coefficient and wear mechanism have been evaluated at ambient conditions for PN treated ring (PN ring) vs. ASTM A453 grade 660 pin (ASTM pin), PN ring vs. Nickel based alloy hard faced pin (Colmonoy pin), PN ring vs. 316LN SS pin and 316LN SS ring vs. 316LN SS pin. The wear tracks have been analyzed by SEM, Energy Dispersive X-ray Analysis (EDX) and Optical Profilometry. The untreated 316LN SS ring vs. 316LN SS pin produced severe wear and was characterized by a combination of delamination and adhesion wear mechanism, whereas wear mechanism of the PN rings reveals mild abrasion and a transfer layer from pin materials. (C) 2012 Elsevier B.V. All rights reserved.

Characteristics of the interface of a laser-quenched steel substrate and chromium electroplate

The interface of a laser-discrete-quenched steel substrate and as-deposited chromium electroplate was investigated by ion beam etching, dissolving-substrate-away and using a Vickers microhardness tester, in an attempt to reveal the mechanism that the service life of the chromium-coated parts is increased by the duplex technique of laser pre-quenching plus chromium post-depositing. The laser quenching of the steel substrate can reduce the steep hardness gradient at the substrate/chromium interface and improve the load-bearing capacity of chromium electroplate. Moreover, the laser quenching prior to plating has an extremely great effect on the morphologies and microstructure of the substrate/chromium interface: there is a transient interlayer at the original substrate/chromium interface while there is not at the laser-quenchedzone/chromium interface; the near-substrate surface microstructure and morphologies of the free-standing chromium electrodeposits, whose substrate was dissolved away with nital 30% in volume, inherit the periodically gradient characteristics of the laser-discrete-quenched substrate surface. (c) 2006 Elsevier B.V. All rights reserved.

Caracterização metalúrgica de juntas de aço inoxidável superduplex soldadas por processo TIG autógeno

Os aços inoxidáveis do tipo duplex possuem grande importância na indústria, principalmente na do petróleo e gás natural, por apresentarem elevada resistência mecânica e excelente resistência à corrosão. Caracterizam-se por apresentar estrutura bifásica, constituída de proporções praticamente iguais de ferrita e austenita. O presente trabalho caracterizou juntas soldadas por TIG autógeno de aço inoxidável duplex UNS S32760. Foram confeccionados quatro grupos de amostras, provenientes da variação da corrente de soldagem e consequentemente do aporte térmico (corrente de pico: 25A e 40A - aporte térmico: 0,12KJ/mm e 0,19KJ/mm) e da composição do gás de proteção (argônio puro ou argônio contendo 2,5% nitrogênio). Foram utilizadas técnicas de caracterização por metalografia colorida, análise e processamento digital de imagens, ensaios de microdureza Vickers. Para avaliar a resistência à corrosão foram realizados ensaios de potencial em circuito aberto com solução de cloreto férrico (FeCl3) e eletrodo de referência de calomelano saturado. A análise quantitativa das fases ferrita e austenita presentes nas juntas soldadas mostrou que a adição de nitrogênio no gás de proteção favoreceu a formação da fase austenita, variando de 11% (sem nitrogênio) para 26% (com nitrogênio) a quantidade desta fase. Em uma análise qualitativa a variação do aporte térmico: 0,12KJ/mm para 0,19KJ/mm resultou no aumento do tamanho de grãos da fase ferrita.

Formation, thermal, optical and physical properties of GeS2-Ga2S3-AgCl novel chalcohalide glasses

Novel GeS2-Ga2S3-AgCl chalcohalide glasses had been prepared by melt-quenching technique, and the glass-forming region was determined by XRD, which indicated that the maximum of dissolvable AgCl was up to 65 mol%. Thermal and optical properties of the glasses were studied by differential scanning calorimetry (DSC) and Visible-IR transmission, which showed that most of GeS2-Ga2S3-AgCl glasses had strong glass-forming ability and broad region of transmission (about 0.45-12.5 mu m). With the addition of AgCl, the glass transition temperature, Tg decreases distinctly, and the short-wavelength cut-off edge (lambda(vis)) of the glasses also shifts to the long wavelength gradually. However, the glass-forming ability of the glass has a complicated evolutional trend depended on the compositional change. In addition, the values of the Vickers microhardness, H (v) , which decrease with the addition of AgCl, are high enough for the practical applications. These excellent properties of GeS2-Ga2S3-AgCl glasses make them potentially applied in the optoelectronic field, such as all-optical switch, etc.

The spectroscopic properties of Er3(+)-doped TeO2-Nb2O5 glasses with high mechanical strength performance

(100 - x)TeO2 - xNb(2)O(5) (x=5-20) mobic tellurite glasses doped with 0.5 mol.% Er2O3 were synthesized, and their thermal, mechanical, and spectroscopic properties were measured and compared to the properties of the typical 75TeO(2)-20ZnO-5Na(2)O (TZN) tellurite glass. The refractive index (n(d)), density (p), and glass transition temperature (T-g) of bulk glasses increase with the Nb2O5 content. The Vickers microhardness (H-v) of bulk glass in niobic tellurite glasses also increases with the Nb2O5 content. The values (2.5-3.2 GPa) of H, in the niobic tellurite glasses are 47-88% larger than that (1.7 GPa) in TZN glass. The effect of Nb2O5 content on absorption spectra, the Judd-Ofelt parameters Omega(t) (t = 2, 4, 6), fluorescence spectra and the lifetimes of Er3+ :I-13/2 level were also investigated, and the stimulated emission crosssection was calculated from McCumber theory. With increasing Nb2O5 content in the glass composition, the Omega(t) (t = 2, 4, 6) parameters, fluorescence full width at half maximum (FWHM) Of I-13/2 of Er3+ increase, while the I-4(13/2) lifetimes of Er3+ decreases. Compared with TZN glass, the gain bandwidth properties of Er3+-doped TeO2-Nb2O5 glass is much larger than in tellurite glass based TeO2-ZnO-Na2O system, bismush-based glass, germanate, and silicate glasses, which indicates that TeO2-Nb2O5 glasses are better choice as a practical available host material for broadband Er3+-doped amplifier. (c) 2005 Elsevier B.V. All rights reserved.