Investigations on valence-change behaviors of europium ions in Eu-doped aluminate and silicate phosphors

Compounds of Sr3Al2O6: Eu, Sr4Al14O25: Eu, and BaZnSiO4: Eu were synthesized by high-temperature solid state reactions. The doping Eu3+ ions were partially reduced to Eu2+ in Sr4Al14O25: Eu and BaZnSiO4: Eu prepared in an oxidizing atmosphere, N-2 + O-2. However, such an abnormal reduction process could not be performed in Sr3Al2O6: Eu, which was also prepared in an atmosphere of N-2 + O-2. Moreover, even though Sr3Al2O6: Eu was synthesized in a reducing condition CO, only part of the Eu3+ ions was reduced to Eu2+. The existence of trivalent and divalent europium ions was confirmed by photoluminescent spectra. The different valence-change behaviors of europium ions in the hosts were attributed to the difference in host crystal structures. The higher the crystal structure stiffness, the easier the reduction process from Eu3+ to Eu2+.

Luminescence centers and valence change of Eu2+ in KCaF3

The nature of the emission centers and the valence change of Eu2+ in KCaF3:Eu2+ depends strongly on preparation conditions. Experimental results show that there are two different d-->f emission bands, located at 425 and 510 nm, respectively. Their origin, relationship, and the effect of doping concentration on them are discussed. A Eu2+-Eu3+ valence change process is proposed. (C) 2000 Elsevier Science Ltd. All rights reserved.

Valence change and luminescence of divalent samarium in strontium berates

The valence change of samarium from trivalent to divalent state in strontium berates (SrB6O10) prepared in air was observed. The high resolution spectra of Sm2+ in matrix were studied between 10 K and 300 K. The results showed that three crystallographic sites for Sm2+ were available in the host. Energy transfer among these sites was possible. The vibronic transition of D-5(0) --> F-7(0) of Sm2+ was studied at room temperature and the Huang-Rhys factor S was calculated. Due to the thermal population, D-5(1) --> F-7(0) transition at room temperature was observed.

THE VALENCE CHANGE FROM RE3+ TO RE2+ (RE-EQUIVALENT-TO-EU, SM, YB) IN SRB4O7-RE PREPARED IN AIR AND THE SPECTRAL PROPERTIES OF RE2+

A valence change from RE3+ to RE2+ (RE=Eu, Sm, Yb) was observed in samples of SrB4O7: RE prepared by solid state reaction at high temperature in air. The phosphors SrB4O7: RE2+ show efficient luminescence at room temperature. The broad band d-f emissions of Eu2+ and Yb2+ are at 367 and 360 nm respectively. The sharp line f-f emissions of the Sm2+ ion (5D0-F-7(J)) are in the range 680-780 nm. The probable reasons for the valence change of Eu, Sm and Yb in this host are discussed.

DYNAMIC PROCESS OF VALENCE CHANGE OF EUROPIUM ION IN EUROPIUM DIFLUORIDE AT HIGH-TEMPERATURE

The dynamic process of the ionic valence changing from Eu~(2+) to Eu~(3+) in EuF_2 at high temperature has been investigated by ESCA, high,temperature X-ray diffraction, high temperature spectrum, high temperature magnetic Isusceptibility and Mssbauer spectrum. It has been shown that the formed Eu~(3+) exists in different compounds when EuF_2 is heated to high temperature in different atmospheres. In air, Eu~(3+) exists in the form of hexagonal EuOF, in nitrogen, in the form of orthogonal EuF_3 and non-hexa...

High pressure in situ diffraction studies of metal–hydrogen systems

“Hybrid” hydrogen storage, where hydrogen is stored in both the solid material and as a high pressure gas in the void volume of the tank can improve overall system efficiency by up to 50% compared to either compressed hydrogen or solid materials alone. Thermodynamically, high equilibrium hydrogen pressures in metal–hydrogen systems correspond to low enthalpies of hydrogen absorption–desorption. This decreases the calorimetric effects of the hydride formation–decomposition processes which can assist in achieving high rates of heat exchange during hydrogen loading—removing the bottleneck in achieving low charging times and improving overall hydrogen storage efficiency of large hydrogen stores. Two systems with hydrogenation enthalpies close to −20 kJ/mol H2 were studied to investigate the hydrogenation mechanism and kinetics: CeNi5–D2 and ZrFe2−xAlx (x = 0.02; 0.04; 0.20)–D2. The structure of the intermetallics and their hydrides were studied by in situ neutron powder diffraction at pressures up to 1000 bar and complementary X-ray diffraction. The deuteration of the hexagonal CeNi5 intermetallic resulted in CeNi5D6.3 with a volume expansion of 30.1%. Deuterium absorption filled three different types of interstices, Ce2Ni2 and Ni4 tetrahedra, and Ce2Ni3 half-octahedra and was accompanied by a valence change for Ce. Significant hysteresis was observed between deuterium absorption and desorption which profoundly decreased on a second absorption cycle. For the Al-modified Laves-type C15 ZrFe2−xAlx intermetallics, deuteration showed very fast kinetics of H/D exchange and resulted in a volume increase of the FCC unit cells of 23.5% for ZrFe1.98Al0.02D2.9(1). Deuterium content, hysteresis of H/D uptake and release, unit cell expansion and stability of the hydrides systematically change with the amount of Al content. In the deuteride D atoms exclusively occupy the Zr2(Fe,Al)2 tetrahedra. Observed interatomic distances are Zr–D = 1.98–2.11; (Fe, Al)–D = 1.70–1.75A˚ . Hydrogenation slightly increases the magnetic moment of the Fe atoms in ZrFe1.98Al0.02 and ZrFe1.96Al0.04 from 1.9 �B at room temperature for the alloy to 2.2 �B for its deuteride.

Mixed valency in the high-temperature phases of transition metal molybdates,AMoO4 (A=Fe, Co, Ni)

Transition metal molybdates of the formulaAMoO4 whereA=Fe, Co or Ni exhibit a first-order phase transition between 670K–970K. An investigation of the lowtemperature (lt) and high-temperature (ht) phases by x-ray photoelectron spectroscopy, x-ray absorption spectroscopy, magnetic susceptibility and other physical methods shows that the phase transition is associated with a valence change of the typeA 2++Mo6+αA 3++Mo5+ in the cases of iron and cobalt molybdates.

Gamma-ray induced color centers in Yb : YAG crystals grown by Czochralski method

20 at.% Yb:YAG single crystals have been grown by the CZ method and gamma-ray irradiation induced color centers and valence change of Fe3+ and Yb3+ ions in Yb:YAG have been studied. One significant 255 nm absorption band was observed in as-grown crystals and was attributed to Fe3+ ions. Two additional absorption (AA) bands located at 255 nm and 345 nm, respectively, were produced after gamma irradiation. The changes in the AA spectra after gamma irradiation and air annealing are mainly related to the charge exchange of the Fe3+, Fe2+, oxygen vacancies and F-type color centers. Analysis shows that the broad AA band is associated with Fe2+ ions and F-type color centers. The transition Yb3+ Yb2+ takes place as an effect of recharging of one of the Yb3+ ions from a pair in the process of gamma irradiation. (C) 2006 Elsevier Ltd. All rights reserved.

Reduction from Eu3+ to Eu2+ in BaAl2O4 : Eu phosphor prepared in an oxidizing atmosphere and luminescent properties of BaAl2O4 : Eu

A reduction phenomenon of Eu3+ -> Eu2+ was observed for the first time when Eu3+ ions were doped into an AlO4-tetrahedron-containing compound BaAl2O4 in an oxidizing atmosphere of air by high-temperature solid-state reaction. X-ray powder diffraction patterns and photoluminescent spectra are used to confirm the compound structure and detect the simultaneous existence of both divalent and trivalent europium ions, respectively. The abnormal Eu3+ -> Eu2+ reduction is explained by a charge compensation model. Spectroscopic properties of BaAl2O4:Eu are discussed and Eu2+ emission spectrum shows consistence with the results reported by Katsumata et a]. [J. Cryst. Growth 198/199 (1999) 869.] and Lin et al. [Mater. Chem. Phys. 70 (2001) 156.].

The optical spectroscopic properties of rare earth-activated barium orthophosphate in VUV-Vis range

The optical properties of rare earth ions-activated barium orthophosphate phosphors, Ba-3(PO4)(2):RE (RE = Ce3+, Sm3+, Eu3+, Eu2+, and Tb3+), were investigated in vacuum ultraviolet (VLTV)-Vis range. A band-band transition Of PO43- in Ba-3(PO4)(2) is observed in the region of 150-170 nm. The partial reduction of Eu3+ to Eu2+ was observed and confirmed by luminescent spectra under the VUV-UV excitation. It is proposed that the electronegative defects that formed by aliovalent substitution of Eu3+ on the Ba2+ site in the host are responsible for the reduction process.

Preparation of divalent rare earth ions in air by aliovalent substitution and spectroscopic properties of Ln(2+)

When alkaline earth ions in borates, phosphates or borophosphates [SrB4O7, SrB6O10, BaB8O13, MBPO5 (M=Ca,Sr)] are substituted partially and aliovalently by trivalent rare earth ions such as Sm3+, Eu3+, these rare earth ions can be reduced to divalent state by the produced negative charge vacancy V-M". The matrices must have appropriate structure containing a rigid three-dimensional network of tetragonal AO(4) groups (A=B,P). These groups can surround and isolate the produced divalent RE2+ ions from the reaction with oxygen. Therefore, this reduction reaction can be carried out even in air at high temperature. The produced divalent rare earth ions can be detected by luminescence and XANES methods and their spectroscopic properties are discussed.

VUV-UV photoluminescence spectra of strontium orthophosphate doped with rare earth ions

The measurements of VUV-UV photoluminescence emission (PL) and photoluminescence excitation (PLE) spectra of rare earth ions activated strontium orthophosphate [Sr-3(PO4)(2):RE, RE = Ce, Sm, Eu, Tb] are performed. Whenever the samples are excited by VUV or UV light, the typical emission of Ce-3+,Ce- Sm3+, Eu3+, Eu2+ and Tb3+ ions can be observed in PL spectra, respectively. The charge transfer bands (CTBs) of Sm3+ and Eu3+ are found, respectively, peaking at 206 and 230nm. The absorption bands peaking in the region of 150-160 nm are assigned to the host lattice sensitization bands, i.e., the band-to-band transitions of PO43- grouping in Sr-3(PO4)(2). It is speculated that the first f-d transitions of Sm3+ (Eu3+), and the CTB of Tb3+ are, respectively, located around 165 (14 3) and 167 urn by means of VUV-UV PLE spectra and relational empirical formula, these f-d transitions or CT bands are included in the bands with the maxima at 150-160 nm, respectively. The valence change of europium from trivalent to divalent in strontium orthophosphate prepared in air is observe by VUV-UV PL and PLE spectra.

Luminescent properties of divalent samarium-doped strontium hexaborate

The valence change of samarium from trivalent to divalent in strontium hexaborate (SrB6O10) prepared in air is observed. The temperature dependence of the luminescence and vibronic transitions of Sm2+ are studied. The Sm2+ ions occupy three crystallographic sites. With increasing temperature, the D-5(0)-->F-7(0) transition line exhibits red shifts, and the half-width increases. At room temperature, due to the thermal population through the 4f(5)5d channel, the D-5(1)-->F-7(J) transitions are observed even though the vibrational energy is very close to the energy gap between the D-5(1) and D-5(0) levels in the host. A coupled phonon energy of about 108 cm(-1) is determined from the vibronic transitions of Sm2+ in the host.

Single crystal growth and spectroscopic properties of KZnF3:Eu3+

Single crystal of KZnF3 : Eu3+ has been grown by means of Bridgman-Stockbarger technique in Ar atmosphere, The emission and excitation spectra of europium ion were measured, The results show that a small amount of Eu2+ exists in the crystal, The existence of Eu2+ ions was also confirmed by ESR data, The valence change of Eu ions during the crystal growth is due to unequivalent substitution of Eu3+ ions for the lattice ions. The sites possibly occupied by Eu ions in this crystal were also discussed.

CHARGE COMPENSATION AND VALENCY STABILITY OF EU(II)-DOPED KMGF3 CRYSTAL

The spectrochemistry of Eu2+-doped perovskite KMgF3 was examined and discussed. Eu2+ can replace some of the K+ in the KMgF3 crystal, and simultaneously the corresponding cation hole can be compensated with the F- or O2- in the matrix. The emission intensity of Eu2+ due to the f --> f transition increased when Na+, Rb+ or F- was doped in KMgF3:Eu2+. Two mechanisms of charge compensation were proposed. No obvious valence change of Eu2+ occurred in KMgF3:Eu2+ after calcinating at high temperature, e.g. 900-degrees-C. It was found that the valence stability of Eu2+ improved after incorporation into the matrix.