Natural fiber reinforced unsaturated polyester composites - An approach on compression molding

This work has been performed at Tapetes Sao Carlos-Brazil with the cooperation of the DaimlerChrysler Research Center Team in Ulm - Germany. The objective of the present paper is to report the results obtained with natural fiber reinforced unsaturated polyester (UP) composites, concerning surface quality measurements. The fibers that have been chosen for this work were sisal and curaua. The samples were produced by compression molding technique and afterwards submitted to three different tests, namely: a) thermal aging; b) water absorption and c) artificial weathering. The surface parameters measured before and after the tests were gloss, haze, short and long-waviness. The results have shown that after the tests there is a high loss of gloss, a high increase in haze, and a high increase in short and long-waviness as well. Curaua reinforced composites had a slightly better behavior when compared with sisal reinforced composites. The effect of the presence of filler and the addition of thermoplastic polyester (TP) on the material behavior has not been evidently detected. This result shows that the conventional technology/methods applied to UP-Fiberglass systems cannot be transferred to natural fibers without any modification. The fiber-matrix interaction and its response to the presence of additives must be fully understood before a successful processing route can be developed for painted natural fibers reinforced UP. Copyright © 2001 Society of Automotive Engineers, Inc.

Unsaturated polyester based composites reinforced with curauá fiber - Preliminary studies

Curauá fiber processing characterization has been performed throughout the different processing steps. Unsaturated polyester has been used as matrix in the production of curauá reinforced composite samples. Compression molding process has been used to prepare the samples. Tensile strength, impact resistance, flexural strength, Young's modulus and elongation at break have been accessed for curauá composites in comparison with fiberglass composites. Mechanical properties were found not to attend the company's internal standards specification. However, the work has shown some alternatives to solve these problems such as the modification of equipment characteristics and resin formulation, the necessity of incorporation of a higher content of fiber and the possibility of using a new type of filler. Copyright © 2000 Society of Automotive Engineers, Inc.

Unsaturated polyester-poly(epsilon-caprolactone) hybrid nanocomposites: Thermal-mechanical properties

This paper reports on the thermal behavior and mechanical properties of nanocomposites based on unsaturated polyester resin (UP) modified with poly(ɛ-caprolactone) (PCL) and reinforced with an organically modified clay (cloisite 30B). To optimize the dispersion of 30B and the mixing of PCL in the UP resin, two different methods were employed to prepare crosslinked UP–PCL-30B hybrid nanocomposites. Besides, two samples of poly(ɛ-caprolactone) of different molecular weight (PCL2: Mn = 2.103g.mol−1 and PCL50: Mn = 5.104g.mol−1) were used at several concentrations (4, 6, 10 wt%). The 30B concentration was 4 wt% in all the nanocomposites. The morphology of the samples was studied by scanning electron microscopy (SEM). The analysis of X-ray patterns reveals that intercalated structures have been found for all ternary nanocomposites, independently of the molecular weight, PCL concentration and the preparation method selected. A slight rise of the glass transition temperature, Tg, is observed in UP/PCL/4%30B ternary nanocomposites regarding to neat UP. The analysis of the tensile properties of the ternary (hybrid) systems indicates that UP/4%PCL2/4%30B nanocomposite improves the tensile strength and elongation at break respect to the neat UP while the Young modulus remains constant

Unsaturated Polyester Resins from Recycled Polyethyleneterephthalate

Tämän diplomityön tarkoituksena oli tutkia miten kuluttajien kierrättämästä polyeteenitereftalaatista ( PET ) voi valmistaa tyydyttymättömiä polyesterihartseja. Työssä valmistettiin yleiskäyttöön soveltuva laminointihartsi sekä 'gel coat' -hartsi jota käytetään esim. veneiden pintamaalina. Yleishartsin depolymerointiin käytettiin propyleeniglykolia ja 'gel coat' -hartsin valmistamiseen neopentyyliglykolia. Polykondensaatiovaiheessa reaktioon lisättiin maleiinihappoa ja lopuksi hartsit liuotettiin styreeniin. Kirjallisuusosassa esitetään eri menetelmiä PET:n depolymeroimiseksi. Lisäksi esitetään eri vaihtoehtoja glykolien, happojen, katalyyttien ja vinyylimonomeerien valitsemiseksi tyydyttymättömien polyesterihartsien valmistuksessa. Analyysimenetelmiä nestemäisten ja kovetettujen hartsien tutkimiseen ja vertailuun käydään läpi kuten myös erilaisia sovelluksia polyesterihartsien käyttämiseksi. Kokeellinen osa todisti että PET-pullojäte voidaan prosessoida hartsiksiilman uusia investointeja prosessilaitteistoon. PET:n glykolyysi kesti viidestäseitsemään tuntia ja polykondensaatiovaihe kahdesta ja puolesta viiteen tuntiin. Hartsien molekyylipainot ja mekaanisten testien tulokset olivat vertailukelpoisia kaupallisten hartsien antamien tulosten kanssa. Glykolyysivaiheen momomeeri- ja oligomeeripitoisuudet mitattiin geelipermeaatiokromatografialla, jotta nähtiin miten pitkälle depolymerisaatio oli edennyt. Tätä tietoa voidaan hyödyntää uusien hartsireseptin suunnittelussa. Polymeeriketjussa jäljellä olevien C=C kaksoissidosten määrä ja niiden isomeraatioaste maleaattimuodosta fumaraattimuotoon mitattiin 1H-NMR -menetelmällä. Tislevesien koostumus määritettiin kaasukromatografialla, ja tulokset kertoivat katalyytin sisältämän kloorin reagoineen glykolien kanssa, johtaen suureen glykolikulutukseen ja muihin ei-toivottuihin sivureaktioihin. Hartsien sietokykyä auringon valolle mitattiin niiden UV-absorption avulla. Kummastakin hartsista valmistettiin 'gel coat' -maalit jotkalaitettiin sääkoneeseen, joka simuloi auringonpaistetta ja vesisadetta vuorotellen. Näistä 'gel coateista' mitattiin niiden kellastumista. Kummastakin hartsista tehdyt valut asetettiin myös sääkoneeseen ja IR-spektreistä ennen jajälkeen koetta nähtiin että C=O ja C-O esterisidoksia oli hajonnut.

Unsaturated Polyester Coatings containing Biocides

Vesistöissä laivojen pintaan tarttuvat eliöt ovat sekä taloudellinen että kosmeettinen ongelma. Kontrolloimattoman eliöiden kiinnittymisen seurauksena aiheutuu kitkaa, joka puolestaan hidastaa laivan nopeutta ja aiheuttaa polttoaineen kulutuksen kasvua. Tavallisesti eliöiden kiinnittymistä ehkäistään kiinnittymisenestomaalien avulla. Niiden toiminta perustuu biosidien liukenemiseen, jolloin veden ja pinnoitteen väliselle rajapinnalle muodostuu korkea biosidipitoisuus, joka estää eliöiden kiinnittymistä pinnalle. Maailmanlaajuinen orgaanisten tinayhdisteiden käyttökielto kiinnittymisen-estomaaleissa tulee voimaan vuoden 2003 alusta. Tällä hetkellä 70 % maailman laivastoista on suojattu orgaanista tinayhdistettä sisältävällä kiinnittymisenestomaalilla. Nyt onkin kasvava tarve kehittää uusia ympäristöystävällisempiä kiinnittymisenesto-pinnoitteita. Todennäköisesti tinayhdisteet tullaan korvaamaan synteettisillä orgaanisilla yhdisteillä käytettyinä yhdessä kuparin kanssa. Työn tarkoituksena oli valmistaa ympäristöystävällisempi tyydyttämätön polyesteripinnoite, joka itsessään ehkäisisi eliöiden kiinnittymistä. Kirjallisuusosassa tutustuttiin markkinoilla oleviin biosideihin, niiden myrkyllisyyteen ja vaikutuksiin ympäristölle sekä muuttuvaan lainsäädäntöön. Työssä tarkasteltiin myös tällä hetkellä markkinoilla olevia pinnoitteita ja niiden toimintamekanismeja sekä myrkyttömiä vaihtoehtopinnoitteita kiinnittymisenestoon. Kokeellinen osa koostui kahdesta osasta. Ensimmäisessä osassa tutkittiin biosidien sopivuutta käytettäväksi yhdessä tyydyttymättömän polyesterin kanssa. Yhteensopivuutta määritettiin applikaatiotesteillä ja pinnoitteen käyttäytymisen perusteella. Toinen vaihe oli selvittää pinnoitteen tehokkuus leväntarttumista vastaan. Tyydyttymätön polyesteri gel coat kiinnittymisenesto-ominaisuuksilla valmistettiin dispergoimalla biosideja tyydyttymättömään polyesterigeeliin. Yhteensopivuustestien tulosten perusteella huomattiin, ettei biosidien lisääminen geeliin vaikuta mainittavasti applikaatio-ominaisuuksien huononemiseen. Brookfield viskositeetin stabiilisuus jopa paranee ja yksi työssä käytetyistä biosideista parantaa pinnoitteen säänkestoominaisuuksia. Tässä työssä ei pystytty määrittämään eri biosidien välisiä eroja tehokkuudessa levää vastaan.

Epoxy-modiWed, unsaturated polyester hybrid networks

Hybrid polymer networks (HPNs) based on unsaturated polyester resin (UPR) and epoxy resins were synthesized by reactive blending. The epoxy resins used were epoxidised phenolic novolac (EPN), epoxidised cresol novolac (ECN) and diglycidyl ether of bisphenol A (DGEBA). Epoxy novolacs were prepared by glycidylation of the novolacs using epichlorohydrin. The physical, mechanical, and thermal properties of the cured blends were compared with those of the control resin. Epoxy resins show good miscibility and compatibility with the UPR resin on blending and the co-cured resin showed substantial improvement in the toughness and impact resistance. Considerable enhancement of tensile strength and toughness are noticed at very low loading of EPN. Thermogravimetric analysis (TGA), dynamic mechanical analysis (DMA) and diVerential scanning calorimetry (DSC) were employed to study the thermal properties of the toughened resin. The EPN/ UPR blends showed substantial improvement in thermal stability as evident from TGA and damping data. The fracture behaviour was corroborated by scanning electron microscopy (SEM). The performance of EPN is found to be superior to other epoxy resins

Modification of Unsaturated Polyester Resin by Polyurethane Prepolymers

Unsaturated polyester resins (UPRs) are extensively used by the fiber-reinforced plastic (FRPs) industry. These resins have the disadvantages of brittleness and poor resistance to crack propagation. In this study, UPRs were chemically modified by reactive blending with polyurethane prepolymers having terminal isocyanate groups. Hybrid networks were formed by copolymerisation of unsaturated polyesters with styrene and simultaneous reaction between terminal hydroxyl groups of unsaturated polyester and isocyanate groups of polyurethane prepolymer. The prepolymers were based on toluene diisocyanate (TDI) and each of hydroxy-terminated natural rubber (HTNR), hydroxy- terminated polybutadiene (HTPB), polyethylene glycol (PEG), and castor oil. Properties like tensile strength, toughness, impact resistance, and elongation-at-break of the modified UPRs show considerable improvement by this modification. The thermal stability of the copolymer is also marginally better

Epoxidized Phenolic Novolac: A Novel Modifier for Unsaturated Polyester Resin

Unsaturated polyester resins (UPRs) are used widely in the fiber-reinforced plastics (FRPs) industry. These resins have the disadvantages of brittleness and poor resistance to crack propagation. In this study, hybrid polymer networks (HPNs) based on UPR and epoxidized phenolic novolacs (EPNs) were prepared by reactive blending. A HPN is composed of a backbone polymer containing two types of reactive groups that can take part in crosslinking reactions via different mechanisms. EPNs were prepared by glycidylation of novolacs using epichlorohydrin. The novolacs had varying phenol: formaldehyde ratios. Blends of unsaturated polyester with EPN were then prepared. The physical properties of the cured blends were compared with those of the control resin. EPN shows good miscibility and compatibility with the resin and improves the toughness and impact resistance substantially. Considerable enhancement of tensile strength is also noticed at about 5% by weight of epoxidized novolac resin. TGA, DMA, and DSC were used to study the thermal properties of the toughened resin and the fracture behavior was studied using SEM. The blends are also found to have better thermal stability. Blending with EPN can be a useful and cost-effective technique for modification of UPR

Composite materials of thermoplastic starch and fibers from the ethanol-water fractionation of bagasse

The aim of this study was to evaluate the potential of the fibrous material obtained from ethanol-water fractionation of bagasse as reinforcement of thermoplastic starches in order to improve their mechanical properties. The composites were elaborated using matrices of corn and cassava starches plasticized with 30 wt%glycerin. The mixtures (0,5,10 and 15 wt% bagasse fiber) were elaborated in a rheometer at 150 degrees C. The mixtures obtained were pressed on a hot plate press at 155 degrees C. The test specimens were obtained according to ASTM D638. Tensile tests, moisture absorption tests for 24 days (20-23 degrees C and 53% RH, ASTM E104), and dynamic-mechanical analyses (DMA) in tensile mode were carried out. Images by scanning electron microscopy (SEM) and X-ray diffraction were obtained. Fibers (10 wt% bagasse fiber) increased tensile strength by 44% and 47% compared to corn and cassava starches, respectively. The reinforcement (15 wt% bagasse fiber) increased more than fourfold the elastic modulus on starch matrices. The storage modulus at 30 C (E(30 degrees C)`) increased as the bagasse fiber content increased, following the trend of tensile elastic modulus. The results indicate that these fibers have potential applications in the development of biodegradable composite materials. (c) 2011 Elsevier B.V. All rights reserved.

Isora Fibre Reinforced Polyester and Epoxy Composites

The aim of this investigation is to study the effectiveness of isora fibre as reinforcement material in short and long forms, for unsaturated polyester and epoxy resins.Studies on the optimization of fibre length and fibre loading of randomly oriented isora-polyester composite are described.The salient features of the alkali treatment of short isora fibre on the properties of randomly oriented isora-polyester composite are outlined in this thesis.The effect of surface modification of the hydrophilic isora fibre by different chemical treatments on the properties of randomly oriented isora-polyester composite is outlined.The properties of oriented and randomly oriented isora fibre reinforced epoxy composites with special reference to the effect of fibre loading are reported and also the dynamic mechanical properties ofthe oriented and randomly oriented isora-polyester and isora-epoxy composites are presented and the water absorption kinetics of oriented and randomly oriented isora-polyester composites and oriented isoraepoxy composites are given. The effect of hot air oven aging on the tensile and flexural properties of oriented isora-polyester and isora-epoxy composites are also reported in this thesis.

Studies on the Toughening of Epoxy Resins

This thesis aims to develop new toughened systems for epoxy resin via physical and chemical modifications. Initially the synthesis of DGEBA was carried out and the properties compared with that of the commercial sample. Subsequently the modifier resins to be employed were synthesized. The synthesized resin were characterized by spectroscopic method (FTIR and H NMR), epoxide equivalent and gel permeation chromatography. Chemical modification involves the incorporation of thermoset resins such a phenolics, epoxy novolacs, cardanol epoxides and unsaturated polyester into the epoxy resin by reactive belnding. The mechanical and thermal properties of the blends were studied. In the physical modification route, elastomers, maleated elastomers and functional elastomers were dispersed as micro-sized rubber phase into the continuous epoxy phase by a solution blending technique as against the conventional mechanical blending technique. The effect of matrix toughening on the properties of glass reinforced composites and the effect of fillers on the properties of commercial epoxy resin were also investigated. The blends were characterized by thermo gravimetric analysis, differential scanning calorimetry, dynamic mechanical analysis, scanning electron microscopy and mechanical property measurements. Among the thermoset blends, substantial toughening was observed in the case of epoxy phenolic novolacs especially epoxy para cresol novolac (ECN). In the case of elastomer blending , the toughest blends were obtained in the case of maleic anhydride grafted NBR. Among functional elastomers the best results were obtained with CTBN. Studies on filled and glass reinforced composites employing modified epoxy as matrix revealed an overall improvement in mechanical properties

Block Copolymers of Unsaturated Polyesters and Functional Elastomers

Block copolymers of unsaturated polyester were prepared by condensation polymerization of hydroxyl or carboxyl terminated liquid rubbers with maleic anhydride, phthalic anhydride, and propylene glycol. The condensate obtained was mixed with styrene monomer to get an unsaturated polyester resin formulation. In this study, copolymers of unsaturated polyesters with hydroxy terminated polybutadiene, carboxy terminated nitrile rubber, and hydroxy terminated natural rubber were prepared. Mechanical properties such as tensile strength, tensile modulus, elongation at break, toughness, impact strength, surface hardness, abrasion resistance, and water absorption were evaluated after the resin was cured in appropriate molds for comparison with the control resin. The fracture toughness and impact resistance of CTBN-modified unsaturated polyester show substantial improvement by this copolymerization without seriously affecting any other property

Utilização de resíduo lignocelulósico na obtenção de chapa de madeira aglomerada homogênea e compósito reforçado com fibra de vidro-E

This research is about the use of the coconut´s endocarp (nucifera linn) and the waste of derivatives of wood and furniture as raw material to technological use. In that sense, the lignocellulosic waste is used for manufacture of homogeneous wood sheet agglomerate (LHWS) and lignocellulosic load which take part of a polymeric composite with fiber glass E (GFRP-WC). In the manufacturing of the homogeneous wood sheet agglomerate (LHWS), it was used mamona´s resin as waste s agglutinating element. The plates were taken up in a hydraulic press engine, heated, with temperature control, where they were manufactured for different percentage of waste wood and coconuts nucífera linn. Physical tests were conducted to determine the absorption of water, density, damp grade (in two hours and twenty-four hours), swelling thickness (in two hours and twenty-four hours), and mechanical tests to evaluate the parallel tensile strength (internal stick) and bending and the static (steady) flexural. The physical test´s results indicate that the LHWS can be classified as bonded wood plate of high-density and with highly water resistant. In the mechanical tests it was possible to establish that LHWS presents different characteristics when submitted to uniaxial tensile and to the static (steady) flexural, since brittle and elasticity module had a variation according to the amount of dry endocarp used to manufacture each trace of LHWS. The GFRP-WC was industrially manufactured by a hand-lay-up process where the fiber glass E was used as reinforcement the lignocellulósic´s waste as load. The matrix was made with ortofitalic unsaturated polyester resin. Physical and mechanical tests were performed in presence of saturated humidity and dry. The results indicated good performance of the GFRP-WC, as traction as in flexion in three points. The presence of water influenced the modules obtained in the flexural and tensile but there were no significant alteration in the properties analyzed. As for the fracture, the analysis showed that the effects are more harmful in the presence of damp, under the action of loading tested, but despite this, the fracture was well defined starting in the external parts and spreading to the internal regions when one when it reaches the hybrid load

Estudo da flamabilidade e resistência à chama de compósito de poliéster insaturado e fibra da folha do abacaxizeiro (PALF)

In the present research work, composites were prepared using pine apple leaf fibres (PALF) as reinforcement with unsaturated polyester resin as matrix, incorporating with fire retardant at different compositions. The PALF was obtained from the decortication of pine apple leaves obtained from Ramada 4 from Ielmo Marinho in the State of Rio Grande do Norte. The unsaturated polyester resin and the catalyzer were bought from the local establishment. The fire retardant, aluminium tri-hydroxide - Al(OH)3 was donated by Alcoa Alumínio S.A and was used in the proportions of 20%, 40% and 60% w/w. Initially the fibres were treated with 2% NaOH for 1 hour, to remove any impurities present on the fibre surface, such as wax, fat, pectin and pectate, in order to have a better adsorption of the fibres with the matrix as well as the flame retardant. The fibre mat was prepared in a mat preparator by immersion, developed in the Textile Engineering Laboratory, at the UFRN. The composites (300x300x3 mm) were prepared by compression molding and the samples (150x25x3 mm) for analysis of the properties were cut randomly using a laser cutter. Some of the cut samples were used to measure the smoke emission and fire resistance using UL94 standard. Mechanical tension-extension and flexural properties were carried in CTGás RN and the Laboratório de Metais e Ensaios Mecânicos Engenharia de Materiais UFRN , as well as SEM studies were carried out at Núcleo de Estudos em Petróleo e Gás Natural - UFRN . From the observed results, it was noted that, there was no marked influence of the fire retardant on the mechanical properties. Also in the water absorption test, the quantity of water absorbed was less in the sample with higher concentration of fire retardant. It was also observed that the increase in the proportion of the fire retardant increased the time of burning, may be due to the compactness of the composite due to the presence of fire retardant as a filling material even though it was meant to reduce the rate of inflammability of the composite

Desenvolvimento e análise de material compósito a base de penas de frango (fibras de queratina-KF) e matriz de poliéster insaturado

Use of natural fibres as a reinforcement material in the manufacture of composites show a series of advantages: availability, biodegradability, low weight and regeneration in relation to synthetic fibres, thus justifying its utilization. In the present research work, composites were developed with chicken feathers (KF), using unsaturated polyester resin as matrix, for diversified applications, mainly in the furniture/timber industry.At present, in Brazil the chicken feathers are used as part of the animal feed, even though this material possesses low aggregated value. The chicken feathers are hollow, light and resistant. After washing with water at room temperature, a part of the chicken feathers were treated with 2% NaOH. Composites were manufactured using treated and untreated chicken feathers with unsaturated orthothalic polyester resin and 1% peroxide as catalyser, obtained in the commerce. Samples with size 150x25x3 mm for mechanical tests were cut by laser in the composite plate. Mechanical analyses were carried out in the Laboratório de Metais e Ensaios Mecânicos UFRN. All the analyses were in accordance with ASTM standards. SEM analyses were also carried out on the samples.In the analyses of the results obtained, it was observed that the composites made with untreated chicken feathers showed better results (Traction 11.406 MPa and 9.107 MPa Bending 34.947 and 20.918 MPa for samples with and without treatment respectively) compared to the composite with treated feathers. Very low values of the water absorption results, evidenced the impermeability characteristic of the feathers. From the SEM images, the structure, fracture and the fibre/matrix adsorption can be evidenced. In the flammability test, it was observed that despite the feathers having sulfur as a constituent, natural inhibitor of flame, no burning support of the composites, because the manufacturing process of the composite