NMR study of the radiation-induced cross-linking of poly(tetrafluoroethylene-co-perfluoromethyl vinyl ether)

The gamma-radiolysis of poly(tetrafluoroethylene-co-perfuoromethyl vinyl ether) (TFE/PMVE) was investigated using solid state F-19 and C-13 NMR spectroscopy. Chain scission products identified in the polymer were saturated chain ends -CF2CF3 (G = 1.0), methyl ether end groups -CF2OCF3 (G = 0.9), acid end groups -CF2COOH (G = 0.5), and a small amount of terminal unsaturation -CF=CF2 (G = 0.2). A mechanism for the formation of these scission products was proposed and the G value for main chain scission, G(S), was determined to be 1.4. Cross-linking of TFE/PMVE was found to proceed via a Y-linking mechanism. The G value for cross-linking, G(X), was determined to be 0.9. A maximum of 0.2 mol % cross-links were formed under the experimental conditions.

Effect of temperature on the gamma-radiolysis of poly(tetrafluoroethylene-co-perfluoromethyl vinyl ether)

The effect of irradiation temperature on the polymer properties was investigated for the fluoroelastomer poly(tetrafluoroethylene-co-perfluoromethylvinyl ether) (TFE/PMVE). TFE/PMVE samples were gamma-irradiated to 150 kGy at temperatures ranging from 77 K to 373 K. Analysis of the sol/gel behaviour, tensile properties, and glass transition temperatures indicated that crosslinking commenced in the temperature range 195 to 263 K, for a dose of 150 kGy. The latter temperature was 13 K below the glass transition temperature. Crosslinking remained relatively constant to higher temperatures. Chain scission reactions were found to occur well below the glass transition temperature and increased at higher temperatures. The optimum temperature for the radiation crosslinking of TFE/PMVE, for the temperatures investigated, was 263 K. (C) 1998 Elsevier Science Ltd. All rights reserved.

Thermal and mechanical properties of radiation crosslinked poly(tetrafluoroethylene-co-perfluoromethyl vinyl ether)

The gamma-radiolysis of poly(tetrafluoroethylene-co-perfluoromethyl vinyl ether) (TFE/PMVE) was investigated using chemical and mechanical analyses. The polymer was found to form an insoluble network with a dose of gelation of 15.8 kGy. Tensile and glass transition temperature measurements indicated the predominance of crosslinking, with optimal elastomeric properties reached in the dose range of 120 to 200 kGy. Photoacoustic FTIR spectroscopy CPAS) showed the formation of new carboxylic acid end groups on irradiation. These new end groups were shown to decrease the thermal oxidative stability of the crosslinked network as determined by thermal gravimetric analysis. Electron spin resonance (ESR) studies of the polymer at 77 K indicated the presence of radical precursors. A G-value of 1.1 was determined for radical production at 77 K. Comparison of radical concentrations for a copolymer with a different mole ratio of PMVE, indicated that the PMVE units contribute to scission reactions. (C) 1998 Elsevier Science Ltd. All rights reserved.

The use of crosslinking promoters in the gamma-radiolysis of poly(tetrafluoroethylene-co-perfluoromethylvinyl ether). I

Incorporation of 1 wt % of triallyl isocyanurate (TAIC) significantly enhanced the radiation crosslinking of the perfluoroelastomer, poly(tetrafluoroethylene-co-perfluoromethylvinyl ether) (TFE/PMVE). The dose for gelation was lowered by 70% with the presence of TAIC. The additive also improved the tensile properties of TFE/ PMVE both before and after crosslinking by irradiation. Higher radical yields were obtained with the presence of TAIC at 77 K, indicating the crosslinking promoter was acting as a radical trap. ESR studies showed that radiolysis of TAIC and subsequent photobleaching cleaved an allyl branch from the ring structure. Upon thermal annealing, an allyl radical on the TAIC molecule was observed. (C) 1999 John Wiley & Sons, Inc.

An ESR study of irradiated poly(tetrafluoroethylene-co-perfluoropropyl vinyl ether) (PFA)

Poly(tetrafluoroethylene-co-perfluoropropyl vinyl ether) (PFA) with 2 mol% perfluoropropyl vinyl ether (PPVE) was exposed to gamma -irradiation in vacuum at both 77 K and room temperature and the ESR spectra recorded. Both the main chain, similar to CF2-(CF)-F-.-CF(2)similar to, and end chain, similar to (CF2CF2)-F-. radicals were identified at both temperatures and their thermal stabilities measured, No radicals unique to the radiolytic cleavage at the PPVE units were observed at room temperature, either due to the low concentration of the comonomer or beta -scission to form a chain end radical and a nonradical species. G-values for radical formation at room temperature and 77 K were found to be 0.93 and 0.16, respectively. (C) 2001 Elsevier Science Ltd. All rights reserved.

Copolymers obtained by the radiation-induced grafting of styrene onto poly(tetrafluoroethylene-co-perfluoropropylvinyl ether) substrates. 1. Preparation and structural investigation

A study has been made to investigate the radiation grafting of styrene onto poly(tetrafluoroethylene-co-perfluoropropylvinyl ether) (PFA) substrates, using the simultaneous irradiation method. Two PFA polymers of different comonomer perfluoropropyl vinyl ether (PPVE) content and degree of crystallinity were used. Effects of grafting conditions such as monomer concentrations, type of solvent, dose rate, and irradiation dose on the grafting yield were investigated. Of the six different solvents used, the most efficient in terms of increasing grafting yield were dichloromethane, benzene, and methanol. The degree of grafting increased with increasing radiation dose up to 500 kGy, stabilizing above this dose. However, the grafting yield decreased with an increase in the dose rate. The grafting of styrene onto the PFA substrates was confirmed by FTIR-ATR and micro-Raman spectroscopy, The increase in the overall grafting yield was accompanied by a proportional increase in the penetration depth of the grafts into the substrate.

Spectroscopic study of the penetration depth of grafted polystyrene onto poly (tetrafluoroethylene-co-perfluoropropylvinylether) substrates. 1. Effect of grafting conditions

This study concerns the radiation grafting of styrene onto poly(tetrafluoroethylene-co-perfluoropropylvinylether) (PFA) substrates and the penetration depth of the graft. Grafting was obtained by the simultaneous irradiation method, and the spectroscopic analysis was made with the micro-Raman technique. Effects of grafting conditions such as the type of solvent, dose rate, and irradiation dose on the grafting yield were investigated. Of the different solvents used, the most efficient in terms of increasing grafting yield were dichloromethane, benzene, and methanol, respectively. A mixture of methanol and dichloromethane used as a solvent for styrene achieved a higher degree of grafting and concentration of grafted polystyrene onto the surface of PFA substrates than solutions of the monomer in the separate solvents. The degree of grafting increased with increasing radiation dose up to 500 kGy, stabilizing above this dose. However, the grafting yield decreased with an increase in the dose rate. The increase in the overall grafting yield was accompanied by a proportional increase in the penetration depth of the grafts into the substrate. (C) 2002 Wiley Periodicals, Inc.

Comparative study of the radiation-induced grafting of styrene onto poly(tetrafluoroethylene-co-perfluoropropylvinyl ether) and polypropylene substrates. I: Kinetics and structural investigation

A comparative study has been made of the radiation grafting of styrene onto poly(tetrafluoroethylene-co-perfluoropropyl vinyl ether) (PFA) and polypropylene (PP) substrates, using the simultaneous irradiation method. Effects of grafting conditions such as monomer concentrations, type of solvent, dose rate and irradiation dose on the grafting yield were investigated. Under the same grafting conditions it was found that a higher degree of grafting of styrene was obtained using a mixture of dichloromethane/methanol solvents for PFA and methanol for PP and the degree of grafting was higher in PP than in PFA at all doses. However, the micro-Raman spectroscopy analysis of the graft revealed that, for the same degree of grafting, the penetration depth of the grafted polystyrene into the substrate was higher in PFA than in PP substrates. In both polymers the crystallinity was hardly affected by the grafting process and the degree of crystallinity decreased slightly with grafting dose. The dependence of the initial rate of grafting on the dose rate and the monomer concentration was found to be 0.6 and 1.4 order for PFA and 0.15 and 2.2 for PP, respectively. The degree of grafting increased with increasing radiation dose in both polymers. However, the grafting yield decreased with an increase in the dose rate. The increase in the overall grafting yield for PFA and PP was accompanied by a proportional increase in the penetration depth of the graft into the substrates. (C) 2003 Society of Chemical Industry.

A detailed single chain model for molten poly(tetrafluoroethylene) from a novel structure refinement technique on neutron scattering data

We present a new methodology that couples neutron diffraction experiments over a wide Q range with single chain modelling in order to explore, in a quantitative manner, the intrachain organization of non-crystalline polymers. The technique is based on the assignment of parameters describing the chemical, geometric and conformational characteristics of the polymeric chain, and on the variation of these parameters to minimize the difference between the predicted and experimental diffraction patterns. The method is successfully applied to the study of molten poly(tetrafluoroethylene) at two different temperatures, and provides unambiguous information on the configuration of the chain and its degree of flexibility. From analysis of the experimental data a model is derived with CC and CF bond lengths of 1.58 and 1.36 Å, respectively, a backbone valence angle of 110° and a torsional angle distribution which is characterized by four isometric states, namely a split trans state at ± 18°, giving rise to a helical chain conformation, and two gauche states at ± 112°. The probability of trans conformers is 0.86 at T = 350°C, which decreases slightly to 0.84 at T = 400°C. Correspondingly, the chain segments are characterized by long all-trans sequences with random changes in sign, rather anisotropic in nature, which give rise to a rather stiff chain. We compare the results of this quantitative analysis of the experimental scattering data with the theoretical predictions of both force fields and molecular orbital conformation energy calculations.

Chain scission and branching in irradiated poly(tetrafluoroethylene-co-hexafluoropropylene)

The radiation chemistry of poly(tetrafluoroethylene-co-hexafluoropropylene) (FEP) with a TFE mole fraction of 0.90 has been studied under vacuum using Co-60 gamma-radiation over a range of temperatures and absorbed doses. The radiolysis temperatures were 300, 363, 423, 523 and 543 K. New structure formation in the copolymers was analysed by solid-state F-19 NMR spectroscopy. The new structures formed in the copolymers have been identified and the G-values for the formation of new chemical structures have been investigated at 363 and 523 K. These two temperatures are just above and just below the polymer T-g and T-m, respectively. At the lower temperature, there was no evidence for any chain branching and an estimate of G(S) of 1.0 was obtained. A value of G(S) of 1.3 and a minimum value of G(X)(Y) of 1.3 were obtained at 523 K. (C) 2003 Society of Chemical Industry.

Effect of temperature and a crosslinking promoter on the gamma-radiolysis of a perfluoroelastomer

Methods of promoting the radiation-induced cross linking of poly(tetrafluoro-ethylene-co-perfluoromethyl vinyl ether) (TFE/PMVE) have been investigated. Greater control of the crosslinking and chain-scission reactions was achieved by varying the radiolysis temperature. This was attributed to temperature affecting the mobilities of reactive species such as polymeric free radicals. These reactive species are precursors to radiation-induced cross links and chain-ends. Analysis of the sol/gel behaviour, tensile properties and FTIR indicated that the optimum temperature for the radiation crosslinking of TFE/PMVE, at a dose of 150 kGy, was 263 K. This temperature was 10 K below the glass transition temperature. Incorporation of 1 wt% triallyl isocyanurate (TAIC) greatly amplified the radiation crosslinking of TFE/PMVE, The dose for gelation was decreased by 70%, and the additive imparted superior mechanical properties compared to the neat irradiated TFE/PMVE. Electron spin resonance (ESR) measurements showed higher radical yields at 77 K with the 1 wt% TAIC, indicating that the crosslinking promoter was acting as a radical trap. (C) 1999 Society of Chemical Industry.

Thermal characterization of copolymers obtained by radiation grafting of styrene onto poly(tetrafluoroethyleneperfluoropropylvinylether) substrates: thermal decomposition, melting behavior and low-temperature transitions

Differential scanning calorimetric (DSC) and thermogravimetric analysis (TGA) have been used to study the thermal decomposition, the melting behavior and low-temperature transitions of copolymers obtained by radiation-induced grafting of styrene onto poly (tetrafluoroethylene- perfluoropropylvinylether) (PFA) substrates. PFA with different contents of perfluoropropylvinylether (PPVE) as a comonomer have been investigated. A two step degradation pattern was observed from TGA thermograms of all the grafted copolymers, which was attributed to degradation of PSTY followed by the degradation of the PFA backbone at higher temperature. One broad melting peak can be identified for all copolymers, which has two components in the samples with higher PPVE content. The melting peak, crystal-crystal transition and the degree of crystallinity of the grafted copolymers increases with radiation grafting up to 50 kGy, followed by a decrease at higher doses. No such decrease was observed in the ungrafted PFA samples after irradiation. This indicated that the changes in the heats of transitions and crystallinity at low doses are due to the radiation effects on the microstructure of PFA (chain scission), whereas at higher doses the grafted PSTY is the driving force behind these changes. (C) 2001 Elsevier Science Ltd. All rights reserved.