The Transverse Crack Tension test revisited: An experimental and numerical study

Several problems arise when measuring the mode II interlaminar fracture toughness using a Transverse Crack Tension specimen; in particular, the fracture toughness depends on the geometry of the specimen and cannot be considered a material parameter. A preliminary experimental campaign was conducted on TCTs of different sizes but no fracture toughness was measured because the TCTs failed in an unacceptable way, invalidating the tests. A comprehensive numerical and experimental investigation is conducted to identify the main causes of this behaviour and a modification of the geometry of the specimen is proposed. It is believed that the obtained results represent a significant contribution in the understanding of the TCT test as a mode II characterization procedure and, at the same time, provide new guidelines to characterize the mode II crack propagation under tensile loads.

Characterization of the cold ductility degradation after aging in centrifugally cast 20Cr32Ni+Nb alloy tube

The mechanical properties (yield stress, ultimate tensile stress and elongation) of alloy 20Cr32Ni + Nb subject to isochronal aging at temperatures between 670 and 820 degrees C for 200 h were investigated using samples extracted from a centrifugally cast tube. The results confirm the occurrence of embrittlement in the aged samples, with maximum embrittlement observed around 770 degrees C without significant gain in strength. (C) 2008 Elsevier Ltd. All rights reserved.

An investigation of the interrelationship between manipulative therapy-induced hypoalgesia and sympathoexcitation

Objective: To investigate a proposed model in which manipulative therapy produces a treatment-specific initial hypoalgesic and sympathoexcitatory effect by activating a descending pain inhibitory system. The a priori hypothesis tested was that manipulative therapy produces mechanical hypoalgesia and sympatho-excitation beyond that produced by placebo or control. Furthermore, these effects would be correlated, thus supporting the proposed model. Design: A randomized, double-blind, placebo-controlled, repeated-measures study of the initial effect of treatment. Setting: Clinical neurophysiology laboratory. Subjects: Twenty-four subjects (13 women and 11 men; mean age, 49 yr) with chronic lateral epicondylalgia (average duration, 6.2 months). Intervention: Cervical spine lateral glide oscillatory manipulation, placebo and control. Outcome Measures: Pressure pain threshold, thermal pain threshold, pain-free grip strength test, upper limb tension test 2b, skin conductance, pileous and glabrous skin temperature and blood flux. Results: Treatment produced hypoalgesic and sympathoexcitatory changes significantly grater than those of placebo and control (p < .03). Confirmatory factor-analysis modeling, which was performed on the pain-related measures and the indicators of sympathetic nervous system function, demonstrated a significant correlation (r = .82) between the latencies of manipulation-induced hypoalgesia and sympathoexcitation. The Lagrange Multiplier test and Wald test indicated that the two latent factors parsimoniously and appropriately represented their observed variables. Conclusions: Manual therapy produces a treatment-specific initial hypoalgesic and sympathoexcitatory effect beyond that of placebo or control. The strong correlation between hypoalgesic and sympathoexcitatory effects suggests that a central control mechanism might be activated by manipulative therapy.

Characterisation of chronic lateral epicondylalgia using the McGill pain questionnaire, visual analog scales, and quantitative sensory tests

Aims: To characterise chronic lateral epicondylalgia using the McGill Pain Questionnaire, Visual Analog Scales for pain and function, and Quantitative Sensory Tests; and to examine the relationship between these tests in a population with chronic lateral epicondylalgia. Method: Fifty-six patients (29 female, 27 male) diagnosed with unilateral lateral epicondylalgia of 18.7 months (mean) duration (range 1-300), with a mean age of 50.7 years (range 27-73) participated in this study. Each participant underwent assessment with the McGill Pain Questionnaire (MPQ), Visual Analog Scales (VAS) for pain and function. and Quantitative Sensory Tests (QST) including thermal and pressure pain thresholds, pain free grip strength, and neuromeningeal tissue testing via the upper limb tension test 2b (ULTT 2b). Results: Moderate correlation (r = .338-.514, p = .000-.013) was found between all indices of the MPQ and VAS for pain experienced in the previous 24 hours and week. Thermal pain threshold was found to be significantly higher in males. A significant poor to moderate correlation was found between the Pain Rating Index (PRI) in the sensory category of the MPQ and ULTT2b scores (r = .353, p = .038). There was no other significant correlation between MPQ and QST data. Pain free grip strength was poorly yet significantly correlated with duration of pathology (r = 318, p = .038). Conclusion: The findings of this study are in agreement with others (Melzack and Katz, 1994) regarding the multidimensional nature of pain, in a condition conventionally conceived as a musculoskeletal pain state. The findings also suggest that utilisation of only one pain measurement tool is unlikely to provide a thorough clinical picture of pain experienced with chronic lateral epicondylalgia.

Resilience of concrete structures in the marine environment through microstructural innovation

Dissertação de mestrado integrado em Engenharia Civil

Kylmämuovattujen putkipalkkien X-liitosten äärikestävyyden ja jäykkyyden määrittäminen sekä materiaalimallin kehittäminen

Työssä on tutkittu elementtimenetelmän avulla kylmämuovattujen nelikulmaisten putkipalkkien materiaalimallin kehittämistä ja putkipalkkien X-liitosten jäykkyyden ja äärikestävyyden määrittämistä. Työn tavoitteena on tutkia kylmämuovauksen vaikutuksia putkipalkkiprofiilin materiaaliominaisuuksiin materiaalikokeiden ja elementtianalyysien avulla sekä kehittää putkipalkille anisotrooppista materiaalimallia. Työssä määritettyjä materiaalimalleja on sovellettu X-liitosten elementtimalleihin, joiden käyttäytymistä on verrattu äärikestävyyskokeiden tuloksiin. Tutkimuksen perusteella Eurocode 3:n mitoitusohjeita voidaan turvallisesti soveltaa kylmämuovattujen putkipalkkien X-liitosten laskennassa. Työssä tehtyjen materiaalikokeiden ja elementtianalyysien perusteella materiaalin anisotrooppisuuden vaikutus liitoksen kestävyyteen on vähäistä, ja putkipalkin pituussuuntaista materiaalimallia voidaan soveltaa myös kehäsuuntaisille materiaaliominaisuuksille. Materiaalikokeiden simulointi osoittaa, että elementtimenetelmää voidaan käyttää materiaalimallin määrittämisen apuvälineenä.

Fibras de licuri: um reforço vegetal alternativo de compósitos poliméricos

This research is based, at first, on the seeking of alternatives naturals reinforced in place of polymeric composites, also named reinforced plastics. Therein, this work starts with a whole licuri fiber micro structural characterization, as alternative proposal to polymeric composites. Licuri fiber is abundant on the Bahia state flora, native from a palm tree called Syagrus Coronata (Martius) Beccari. After, it was done only licuri fiber laminar composite developing studies, in order to know its behavior when impregnated with thermofix resin. The composite was developed in laminar structure shape (plate with a single layer of reinforcement) and produced industrially. The layer of reinforcement is a fabric-fiber unidirectional of licuri up in a manual loom. Their structure was made of polyester resin ortofitálica (unsaturated) only reinforced with licuri fibers. Fiber characterization studies were based on physical chemistry properties and their constitution. It was made by tension, scanning electron microscopy (SEM), x-ray diffraction (RDX) and thermal analyses (TG and DTA) tests, besides fiber chemistry analyses. Relating their mechanical properties of strength and hardness testing, they were determined through unit axial tension test and flexion in three points. A study in order to know fiber/matrix interface effects, in the final composites results, was required. To better understand the mechanical behavior of the composite, macroscopic and microscopic optical analysis of the fracture was performed

Effect of the surface treatment of plain carbon fiber posts on the retention of the composite core: an in vitro evaluation

Foi avaliado o possível efeito de tratamentos superficiais em pinos de fibra de carbono lisos, quando comparados aos pinos serrilhados, na retenção à resina composta empregada na confecção de núcleos de preenchimento. Foram utilizados cinqüenta pinos de fibra de carbono, divididos em cinco grupos: os quatro primeiros grupos eram constituídos por pinos do tipo liso, cujas superfícies foram tratadas, e o último grupo por dez pinos do tipo serrilhado. Foram desenvolvidas matrizes de resina acrílica com um leito ajustado para conter o pino, com um alargamento na porção coronária para posterior preenchimento com resina composta. Após o tratamento superficial, todos os pinos receberam camadas de primer, foram secos e então ajustados à matriz de resina, colocando-se a resina composta autopolimerizável na porção coronária para um núcleo de preenchimento de 3 mm. As amostras foram submetidas a termociclagem e armazenadas em água destilada por uma semana. Os espécimes foram testados por meio de ensaios mecânicos de tração, à velocidade de 0,5 mm/min, até o deslocamento do conjunto ou a fratura da resina do núcleo. As conclusões foram as seguintes: a) o tratamento superficial nos grupos tratados por meio de jateamento (Grupo A), pontas diamantadas marcadoras de profundidade para facetas laminadas (Grupo C) e alteração da morfologia da extremidade coronária (Grupo D) conferiu aos pinos lisos valores de retenção comparáveis aos dos pinos serrilhados (Grupo E) nos ensaios de tração, porém sem diferença estatisticamente significativa entre estes grupos; b) os pinos tratados por meio de pontas diamantadas de granulação média (Grupo B) obtiveram valores de retenção menores que os demais grupos.

Processamento e caracterização mecânica da liga à base de titânio (Ti-7,5Mo) para confecção de prótese ortopédica

Pós-graduação em Engenharia Mecânica - FEG

Desenvolvimento de uma nova liga quaternária Ti25Ta25Nb3Sn para aplicações odontológicas

Pós-graduação em Engenharia Mecânica - FEG

Analysis of a Non-Traditional Micro Tube Hydroforming Process

As the demand for miniature products and components continues to increase, the need for manufacturing processes to provide these products and components has also increased. To meet this need, successful macroscale processes are being scaled down and applied at the microscale. Unfortunately, many challenges have been experienced when directly scaling down macro processes. Initially, frictional effects were believed to be the largest challenge encountered. However, in recent studies it has been found that the greatest challenge encountered has been with size effects. Size effect is a broad term that largely refers to the thickness of the material being formed and how this thickness directly affects the product dimensions and manufacturability. At the microscale, the thickness becomes critical due to the reduced number of grains. When surface contact between the forming tools and the material blanks occur at the macroscale, there is enough material (hundreds of layers of material grains) across the blank thickness to compensate for material flow and the effect of grain orientation. At the microscale, there may be under 10 grains across the blank thickness. With a decreased amount of grains across the thickness, the influence of the grain size, shape and orientation is significant. Any material defects (either natural occurring or ones that occur as a result of the material preparation) have a significant role in altering the forming potential. To date, various micro metal forming and micro materials testing equipment setups have been constructed at the Michigan Tech lab. Initially, the research focus was to create a micro deep drawing setup to potentially build micro sensor encapsulation housings. The research focus shifted to micro metal materials testing equipment setups. These include the construction and testing of the following setups: a micro mechanical bulge test, a micro sheet tension test (testing micro tensile bars), a micro strain analysis (with the use of optical lithography and chemical etching) and a micro sheet hydroforming bulge test. Recently, the focus has shifted to study a micro tube hydroforming process. The intent is to target fuel cells, medical, and sensor encapsulation applications. While the tube hydroforming process is widely understood at the macroscale, the microscale process also offers some significant challenges in terms of size effects. Current work is being conducted in applying direct current to enhance micro tube hydroforming formability. Initially, adding direct current to various metal forming operations has shown some phenomenal results. The focus of current research is to determine the validity of this process.

Mechanical properties of sheet metal under forming conditions

In the bulge test, a sheet metal specimen is clamped over a circular hole in a die and formed into a bulge by the hydraulic pressure on one side of the specirnen. As the unsupported part of the specimen is deformed in this way, its area is increased, in other words, the material is generally stretched and its thickness generally decreased. The stresses causing this stretching action are the membrane stresses in the shell generated by the hydraulic pressure, in the same way as the rubber in a toy balloon is stretched by the membrane stresses caused by the air inside it. The bulge test is a widely used sheet metal test, to determine the "formability" of sheet materials. Research on this forming process (2)-(15)* has hitherto been almost exclusively confined to predicting the behaviour of the bulged specimen through the constitutive equations (stresses and strains in relation to displacements and shapes) and empirical work hardening characteristics of the material as determined in the tension test. In the present study the approach is reversed; the stresses and strains in the specimen are measured and determined from the geometry of the deformed shell. Thus, the bulge test can be used for determining the stress-strain relationship in the material under actual conditions in sheet metal forming processes. When sheet materials are formed by fluid pressure, the work-piece assumes an approximately spherical shape, The exact nature and magnitude of the deviation from the perfect sphere can be defined and measured by an index called prolateness. The distribution of prolateness throughout the workpiece at any particular stage of the forming process is of fundamental significance, because it determines the variation of the stress ratio on which the mode of deformation depends. It is found. that, before the process becomes unstable in sheet metal, the workpiece is exactly spherical only at the pole and at an annular ring. Between the pole and this annular ring the workpiece is more pointed than a sphere, and outside this ring, it is flatter than a sphere. In the forming of sheet materials, the stresses and hence the incremental strains, are closely related to the curvatures of the workpiece. This relationship between geometry and state of stress can be formulated quantitatively through prolateness. The determination of the magnitudes of prolateness, however, requires special techniques. The success of the experimental work is due to the technique of measuring the profile inclination of the meridional section very accurately. A travelling microscope, workshop protractor and surface plate are used for measurements of circumferential and meridional tangential strains. The curvatures can be calculated from geometry. If, however, the shape of the workpiece is expressed in terms of the current radial (r) and axial ( L) coordinates, it is very difficult to calculate the curvatures within an adequate degree of accuracy, owing to the double differentiation involved. In this project, a first differentiation is, in effect, by-passed by measuring the profile inclination directly and the second differentiation is performed in a round-about way, as explained in later chapters. The variations of the stresses in the workpiece thus observed have not, to the knowledge of the author, been reported experimentally. The static strength of shells to withstand fluid pressure and their buckling strength under concentrated loads, both depend on the distribution of the thickness. Thickness distribution can be controlled to a limited extent by changing the work hardening characteristics of the work material and by imposing constraints. A technique is provided in this thesis for determining accurately the stress distribution, on which the strains associated with thinning depend. Whether a problem of controlled thickness distribution is tackled by theory, or by experiments, or by both combined, the analysis in this thesis supplies the theoretical framework and some useful experimental techniques for the research applied to particular problems. The improvement of formability by allowing draw-in can also be analysed with the same theoretical and experimental techniques. Results on stress-strain relationships are usually represented by single stress-strain curves plotted either between one stress and one strain (as in the tension or compression tests) or between the effective stress and effective strain, as in tests on tubular specimens under combined tension, torsion and internal pressure. In this study, the triaxial stresses and strains are plotted simultaneously in triangular coordinates. Thus, both stress and strain are represented by vectors and the relationship between them by the relationship between two vector functions. From the results so obtained, conclusions are drawn on both the behaviour and the properties of the material in the bulge test. The stress ratios are generally equal to the strain-rate ratios (stress vectors collinear with incremental strain vectors) and the work-hardening characteristics, which apply only to the particular strain paths are deduced. Plastic instability of the material is generally considered to have been reached when the oil pressure has attained its maximum value so that further deformation occurs under a constant or lower pressure. It is found that the instability regime of deformation has already occurred long before the maximum pressure is attained. Thus, a new concept of instability is proposed, and for this criterion, instability can occur for any type of pressure growth curves.

Physical and Chemical Performance Testing of Ontario Asphalt Pavements

Thermal and fatigue cracking are the two of the major pavement distress phenomena that contribute significantly towards increased premature pavement failures in Ontario. This in turn puts a massive burden on the provincial budgets as the government spends huge sums of money on the repair and rehabilitation of roads every year. Governments therefore need to rethink and re-evaluate their current measures in order to prevent it in future. The main objectives of this study include: the investigation of fatigue distress of 11 contract samples at 10oC, 15oC, 20oC and 25oC and the use of crack-tip-opening-displacement (CTOD) requirements at temperatures other than 15oC; investigation of thermal and fatigue distress of the comparative analysis of 8 Ministry of Transportation (MTO) recovered and straight asphalt samples through double-edge-notched-tension test (DENT) and extended bending beam rheometry (EBBR); chemical testing of all samples though X-ray Fluorescence (XRF) and Fourier transform infrared analysis (FTIR); Dynamic Shear Rheometer (DSR) higher and intermediate temperature grading; and the case study of a local Kingston road. Majority of 11 contract samples showed satisfactory performance at all temperatures except one sample. Study of CTOD at various temperatures found a strong correlation between the two variables. All recovered samples showed poor performance in terms of their ability to resist thermal and fatigue distress relative to their corresponding straight asphalt as evident in DENT test and EBBR results. XRF and FTIR testing of all samples showed the addition of waste engine oil (WEO) to be the root cause of pavement failures. DSR high temperature grading showed superior performance of recovered binders relative to straight asphalt. The local Kingston road showed extensive signs of damage due to thermal and fatigue distress as evident from DENT test, EBBR results and pictures taken in the field. In the light of these facts, the use of waste engine oil and recycled asphalt in pavements should be avoided as these have been shown to cause premature failure in pavements. The DENT test existing CTOD requirements should be implemented at other temperatures in order to prevent the occurrences of premature pavement failures in future.

INVESTIGATIVE COMPARISON OF TANK AND RECOVERED ASPHALT SAMPLES THROUGH PHYSICAL PERFORMANCE TESTING AND CHEMICAL ANALYSIS

Despite the development of improved performance test protocols by renowned researchers, there are still road networks which experience premature cracking and failure. One area of major concern in asphalt science and technology, especially in cold regions in Canada is thermal (low temperature) cracking. Usually right after winter periods, severe cracks are seen on poorly designed road networks. Quality assurance tests based on improved asphalt performance protocols have been implemented by government agencies to ensure that roads being constructed are at the required standard but asphalt binders that pass these quality assurance tests still crack prematurely. While it would be easy to question the competence of the quality assurance test protocols, it should be noted that performance tests which are being used and were repeated in this study, namely the extended bending beam rheometer (EBBR) test, double edge-notched tension test (DENT), dynamic shear rheometer (DSR) test and X-ray fluorescence (XRF) analysis have all been verified and proven to successfully predict asphalt pavement behaviour in the field. Hence this study looked to probe and test the quality and authenticity of the asphalt binders being used for road paving. This study covered thermal cracking and physical hardening phenomenon by comparing results from testing asphalt binder samples obtained from the storage ‘tank’ prior to paving (tank samples) and recovered samples for the same contracts with aim of explaining why asphalt binders that have passed quality assurance tests are still prone to fail prematurely. The study also attempted to find out if the short testing time and automated procedure of torsion bar experiments can replace the established but tedious procedure of the EBBR. In the end, it was discovered that significant differences in performance and composition exist between tank and recovered samples for the same contracts. Torsion bar experimental data also indicated some promise in predicting physical hardening.