Phase behavior of rare earth manganites

Among complex oxides containing rare earth and manganese BaLn(2)Mn(2)O(7)( Ln = rare earth) with the layered perovskite type and Ln(2)(Mn, M)O-7 with pyrochlore-related structure were studied since these compounds show many kinds of phases and unique phase transitions. In BaLn(2)Mn(2)O(7) there appear many phases, depending on the synthetic conditions for each rare earth. The tetragonal phase of so-called Ruddlesden-Popper type is the fundamental structure and many kinds of deformed modification of this structure are obtained. For BaEu2Mn2O7 at least five phases have been identified from the results of X-ray diffraction analysis with the space group P4(2)/mnm, Fmmm, Immm and A2/m in addition to the fundamental tetragonal I4/mmm phase. In the pyrochlore-related type compounds, Ln(2)Mn(2-x)M(x)O(7)(M = Ta, Nb, W etc), there also appear several phases With different crystal structures. With regard to every rare earth, Ln(2)MnTaO(7) phase is stable only for excess Ta and can be obtained under high oxygen partial pressure process. This group has trigonal structure with zirkelite type ( P3(1)21 space group).

Study on the phase behavior of BaEu2Mn2O7 through heat treatment of a single crystal

A new orthorhombic phase of BaEu2Mn2O7 with the space group of Ccmm (no.63) was identified for single crystals after heat treatment and its Crystal Structure was determined by single crystal X-ray diffractometry. The volume Of the unit cell has twice the fundamental tetragonal cell and corner-shared MnO6 octahedra are slightly distorted and Mn-O-Mn angle between the neighboring octahedra tilts with an angle by around 3 degrees from b-axis. It is concluded from the results of the heat treatment of single crystals at various temperatures that this orthorhombic phase changes into a tetragonal One With superstructure (P4(2)/mnm) at 402 K and changes once more into the fundamental tetragonal phase (I4/mmm) above 552 K. The tetragonal phase with superstructure which has been expected to be an unstable one is stable between the two temperatures.

Competing tetragonal and monoclinic phases in Ni2.2Mn0.80Ga

Temperature dependent synchrotron x-ray powder diffraction, differential scanning calorimetry, and magnetic measurements were performed on Ni2+xMn1-xGa (x=0.20 and 0.35) magnetic shape memory alloys. For x=0.20, though the monoclinic phase is thermodynamically stable, a trace of residual stress can stabilize a tetragonal phase. The residual-stress-induced tetragonal phase transforms to the cubic austenite phase over an unusually large temperature range (348 K < T < 693 K), suggesting extremely slow kinetics of transformation. In contrast to x=0.20, the thermodynamically stable phase of x=0.35 is tetragonal and this composition exhibits the usual features of a reversible martensitic transformation. The results suggest that for x=0.20 the monoclinic and tetragonal phases are nearly degenerate.

Diffusion and Creep in Silica-Doped Tetragonal Zirconia

Silica segregation at two grain junctions or in amorphous triple junction pockets can influence creep by altering the grain-boundary diffusion coefficient. Although the addition of silica to superplastic yttria-stabilized tetragonal zirconia enhances ductility, differences in reported creep parameters have limited critical identification of rate controlling mechanisms. The present study on a pure 3 mol% yttria-stabilized tetragonal zirconia (3YTZ) and 3YTZ with 0.39 or 3.9 wt% silica involved a detailed characterization of creep over a wide range of experimental conditions and also tracer diffusion measurements. The data broadly show transitions in creep stress exponents from n∼1 to ∼2 to ∼3 with a decrease in the stress. The data at high stresses are consistent with Coble diffusion creep, and creep at lower stresses is attributed to interface-controlled diffusion creep. Measurements indicated that silica does not have any significant influence on grain boundary or lattice diffusion, and this is consistent with the observation that 3YTZ and 3YTZ with 0.39% or 3.9% silica exhibit essentially identical creep behavior in the Coble creep regime. Silica influences the interface control process so that the transitions in stress exponents are pushed to lower stresses with an increase in silica content.

Tetragonal bismuth bilayer: A stable and robust quantum spin hall insulator

Topological insulators (TIs) exhibit novel physics with great promise for new devices, but considerable challenges remain to identify TIs with high structural stability and large nontrivial band gap suitable for practical applications. Here we predict by first-principles calculations a two-dimensional (2D) TI, also known as a quantum spin Hall (QSH) insulator, in a tetragonal bismuth bilayer (TB-Bi) structure that is dynamically and thermally stable based on phonon calculations and finite-temperature molecular dynamics simulations. Density functional theory and tight-binding calculations reveal a band inversion among the Bi-p orbits driven by the strong intrinsic spin-orbit coupling, producing a large nontrivial band gap, which can be effectively tuned by moderate strains. The helical gapless edge states exhibit a linear dispersion with a high Fermi velocity comparable to that of graphene, and the QSHphase remains robust on a NaCl substrate. These remarkable properties place TB-Bi among the most promising 2D TIs for high-speed spintronic devices, and the present results provide insights into the intriguing QSH phenomenon in this new Bi structure and offer guidance for its implementation in potential applications.

Temperature dependence of g values in tetragonal ionic Cu++ salts

A temperature dependence has been observed in the spin-Hamiltonian parameters of the Cu++ ion in a tetragonal crystal field and the variation has been interpreted in terms of vibronic effects.

Unconventional mechanism of stabilization of a tetragonal phase in the perovskite ferroelectric (PbTiO3)(1-x)(BiFeO3)(x)

Temperature-dependent x-ray powder-diffraction study of the tetragonal compositions of PbTiO3-BiFeO3 series has revealed that, unlike for all the known ferroelectric perovskites, the compositions exhibiting giant tetragonality is stabilized from the cubic phase via a complex transition pathway which involve (i) formation of minor monoclinic phase with a large pseudotetragonality along with an intermediate tetragonal phase (major) with a small tetragonality, (ii) gradual vanishing of the intermediate tetragonal phase and concomitant increase in the monoclinic regions, and finally (iii) gradual transformation of the monoclinic phase to the tetragonal phase with giant tetragonality.The system seems to adopt such a complex transition pathway to create amicrostructure with very large number of domains and interfaces for stress relief, which would not have been possible in case of a direct cubic-tetragonal transition.

Phase Transformation Introduced by Mechanical and Chemical Surface Preparations of Tetragonal Zirconia Polycrystals

Cutting of Y2O3-doped TZP rods by a low-speed diamond saw introduces an unidentified, metastable phase X (x-ZrO2) coexisting with the tetragonal (t-ZrO2) and the monoclinic (m-ZrO2) phases initially present in the sample. Further mechanical deformation of the cut surface by indentation or polishing sustains the x-ZrO2. Chemical etching removes the x-ZrO2 and increases the m-ZrO2content.

The mechanical response of tetragonal zirconia polycrystal to conical indentation

Blocks of 3Y-TZP were indented with conical diamond indenters. indentation caused tetragonal to monoclinic phase transformation in a subsurface. Of the cracks generated in the subsurface, radial and lateral cracks can be accounted for by a continuum model of the indented subsurface, built using a combination of the Boussinesq and blister stress fields. Additional ring, median and cone cracks were also observed. It is hypothesized that the latter are motivated by the reduction in blister strength or residual energy brought about by the material damage caused by the phase transformation. This damage reduces the load bearing capacity of the material progressively with increasing normal load.

Surface damage of yttria-tetragonal zirconia polycrystals and magnesia-partially-stabilized zirconia in single-point abrasion

Commercially available 3Y-TZP and Mg-PSZ flats mere abraded by a 150 degrees diamond cone at -196 degrees, 25 degrees, 200 degrees, and 400 degrees C. The coefficient of friction, the track width, and the morphological features of the track were recorded. Raman spectroscopy mas used to record the tetragonal-to-monoclinic phase transformation (t --> m) as a function of distance away from the track. The study was undertaken to establish the influence of tangential traction on phase transformation and surface damage.

Amorphous, Monoclinic, and Tetragonal Porous Zirconia Through a Controlled Self-Sustained Combustion Route

Porous, large surface area, metastable zirconias, are of importance to catalytic, electrochemical, biological, and thermal insulation applications. Combustion synthesis is a very commonly used method for producing such zirconias. However, its rapid nature makes control difficult. A simple modification has been made to traditional solution combustion synthesis to address this problem. It involves the addition of starch to yield a starting mixture with a ``dough-like'' consistency. Just 5 wt% starch is seen to significantly alter the combustion characteristics of the ``dough.'' In particular, it helps to achieve better control over reaction zone temperature that is significantly lower than the one calculated by the adiabatic approximation typically used in self-propagating high-temperature synthesis. The effect of such control is demonstrated by the ability to tune dough composition to yield zirconias with different phase compositions from the relatively elusive ``amorphous'' to monoclinic (> 30 nm grain size) and tetragonal pure zirconia (< 30 nm grain size). The nature of this amorphous phase has been investigated using infrared spectroscopy. Starch content also helps tailor porosity in the final product. Zirconias with an average pore size of about 50 mu m and specific surface area as large as 110 m2/g have been obtained.

Analysis of deformation mechanisms in superplastic yttria-stabilized tetragonal zirconia

There have been extensive experimental observations of changes in the apparent rate controlling creep parameters in studies on superplastic materials. The three most common explanations associated with these changes in the stress exponent, n, the activation energy Q and the inverse grain size exponent, p involve the effect of concurrent grain growth, the operation of a threshold stress or transitions in creep mechanisms. Each of these factors may influence experimental creep data in a similar manner. Therefore, a careful analysis of the consequences of all three factors must involve the development of a consistent set of experimental observations in order to adequately distinguish the effects of each. This paper discusses the role of concurrent grain growth, a threshold stress and transitions in creep mechanisms in superplastic materials. Specific attention is given to the analysis of data on superplastic yttria-stabilized zirconia ceramics for which an increase in n has been observed at low applied stresses. It is demonstrated that neither concurrent grain growth nor a threshold stress can account for all the relevant experimental observations in this material. It is concluded that the changes in rate controlling creep parameters are associated with the operation of two distinct sequential mechanisms as part of a grain boundary sliding process.

Gibbs’ energy of formation of YBa2Cu3O7-x (tetragonal)

The high temperature ceramic oxide superconductor YBa2Cu3O7-x (1–2–3 compound) is generally synthesized in an oxygen-rich environment. Hence any method for determining its thermodynamic stability should operate at a high oxygen partial pressure. A solid-state cell incorporating CaF2 as the electrolyte and functioning under pure oxygen at a pressure of 1·01 × 105 Pa has been employed for the determination of the Gibbs’ energy of formation of the 1–2–3 compound. The configuration of the galvanic cell can be represented by: Pt, O2, YBa2Cu3O7−x , Y2BaCuO5, CuO, BaF2/CaF2/BaF2, BaZrO3, ZrO2, O2, Pt. Using the values of the standard Gibbs’ energy of formation of the compounds BaZrO3 and Y2BaCuO5 from the literature, the Gibbs’ energy of formation of the 1–2–3 compound from the constituent binary oxides has been computed at different temperatures. The value ofx at each temperature is determined by the oxygen partial pressure. At 1023 K for O content of 6·5 the Gibbs’ energy of formation of the 1–2–3 compound is −261·7 kJ mol−1.

Nucleation-Growth Mode of Cubic-Tetragonal Transition with Coexistence of Phases over a Wide Temperature Interval in the High Temperature Ferroelectric Systems PbTiO3-BiMeO3:Me = Sc , and Zn1/2Ti1/2

Temperature dependent X-ray powder diffraction and dielectric studies have been carried out on tetragonal compositions of (1-x) PbTiO 3(x) BiMeO 3; Me similar to Sc and Zn 1/2 Ti 1/2. The cubic and the tetragonal phases coexist over more than 100 degrees C for 0.70 PbTiO 30.3 Bi ( Zn 1/2 Ti 1/2) O 3 and 0.66 PbTiO 30.34 BiScO 3. The wide temperature range of phase coexistence is shown to be an intrinsic feature of the system, and is attributed to the increase in the degree of the covalent character of the ( Pb +Bi ) O bond with increasing concentration of Bi at the Pb -site. The d-values of the {111} planes of the coexisting phases are nearly identical, suggesting this plane to be the invariant plane for the martensitic type cubic-tetragonal transformation occurring in these systems.

Self-Assembly of an Octanuclear Platinum(II) Tetragonal Prism from a New Pt-4(II) Organometallic Star-Shaped Acceptor and Its Nitroaromatic Sensing Study

2 + 4] self-assembly of a pyrene-functionalized Pt-8(II) tetragonal prism (2) is achieved using a newly designed star-shaped organometallic acceptor (1) in combination with an amide-based ``clip'' donor (L). The propensity of this prism (2) as a selective sensor for nitroaromatics (2,4-dinitrotoluene, 1,3,5-trinitrotoluene, and picric acid), which are the chemical constituents of many commercial explosives, has been examined.